Assessment of untreated Papua New Guinean timbers against subterranean termites. Progress Report 1
1990 - IRG/WP 1436
Eight major commercial timber species (Intsia palembanica, Pometia pinnata, Homalium foetidum, Dracontomelon dao, Calophyllum spp., Eucalyptus deglupta, Nothofagus spp., and Alstonia scholaris) were exposed in ground contact against termites. Five replicates of heartwood stakes of 25x25x250 mm³ of each species were randomly embedded in the soil. Results after 24 months exposure showed that Kwila ...
M Rokova, H C Konabe
Factors affecting the resistance of fibre building boards to fungal attack
1975 - IRG/WP 252
Fungal decay is initiated at lower moisture contents in standard and tempered hardboards (18%) than in pine sapwood (26%). In contrast, in a saturated atmosphere, the equilibrium moisture contents of standard hardboard (14%) and of tempered hardboard (12.5%) are much lower than the moisture content permitting decay initiation whilst the equilibrium moisture content of pine sapwood (25.1%) approach...
C Grant, J G Savory
Susceptibility of heartwood of three Pinus species to attack by the subterranean termite Coptotermes acinaciformis (Froggatt)
1994 - IRG/WP 94-20026
Heartwood of plantation-grown Pinus elliottii (slash pine), Pinus caribaea (Caribbean pine) and Pinus radiata (radiata pine) was obtained from a range of locations throughout Australia and New Zealand for use in a field bioassey with subterranean termites. Timber stock was analysed for a number of stilbene and flavonoid heartwood extractive components which could contribute to variation in suscept...
M J Kennedy, L L Dixon, B C Peters
Effects of heart wood extractives in Dahoma (Piptadeniastrum africanum) on decay resistance to white- and brown-rot fungi
2004 - IRG/WP 04-10536
Dahoma (Piptadeniastrum africanum) is a durable but a lesser utilised tropical hardwood species from Ghana that has the potential of being used as an alternative to Iroko (Milicia excelsa) for many end uses. However, the timber gives off a strong odour especially when wet and during processing. The high durability and the strong odour of the timber could be due to the presence of extractives in th...
Zeen Huang, K Maher, S A Amartey
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
The resistance of wood coated with different water-borne paints against colonisation by decay fungi
1996 - IRG/WP 96-10165
The susceptibility of wood painted with model paints of known composition to decay fungi was tested without previous weathering. Included in the study were five alkyd emulsion paints and five acrylic paints; one linseed oil paint and two solvent-borne alkyd paints. It was found that several components influenced the susceptibility of these paints. The results of the present study indicate that the...
J Bjurman
Blue stain in timber in service. Progress review of Sub-group collaborative tests - 1981/82
1982 - IRG/WP 2178
Following from the discussions after reporting Document IRG/WP/2146 at the Meeting in Sarajevo, 1981, it was decided that 1.) more precise definition was needed of the artificial weathering schedules used in the work - participants to re-check Table 8 and send further details or amendments to Dr Bravery; 2.) a further test employing a wider range of chemicals was necessary using a smaller range of...
A F Bravery, D J Dickinson
Termite resistance of borate-treated lumber in a three-year above-ground field test in Hawaii
2000 - IRG/WP 00-30236
A protected above-ground field test simulating the sill plate (dodai) used in conventional Japanese housing construction was established in both Hawaii and Japan to examine the efficacy of disodium octaborate tetrahydrate (DOT, 2% and 3% shell and through) wood treatments. In Hawaii, chromated copper arsenate (CCA, 4 kg/m3) and ammoniacal copper zinc arsenate (ACZA, 4 kg/m3) were included in the t...
J K Grace, R J Oshiro, A Byrne, P I Morris, K Tsunoda
Laboratory Evaluation of Soft Rot Resistance of Non-Durable Lesser-Known Malaysian Hardwoods
2006 - IRG/WP 06-10582
Resistance of six non-durable lesser-known Malaysian hardwoods, Pulai (Alstonia spp.), Rubberwood (Hevea brasiliensis), Ludai (Sapium spp.), Jelutong (Dyera costulata), Gaham Badak (Blumeodendron tokbrai) and Kayu arang (Diospyros spp.) compared with temperate Scots pine sapwood (Pinus sylvestris), were evaluated using the unsterile soil burial (mixed with Chaetomium globosum) versus vermiculite-b...
A H H Wong
Decay resistance of coconut and rubber woods. Alternative wood species from Ghana
2006 - IRG/WP 06-10596
With the expanding local and world wide demand for tropical timbers, there is increased interest in the suitability of lesser–used timber species as alternatives for the forest based industries in order to ensure sustainable forest management. In the forests of Ghana, there are quite a number of timber species that are lesser known and have not been adequately used due to the absence of informat...
S Amartey, M Humar, B Donkor, F Pohleven
Resistance of pine and spruce heartwood against decay - The effect of wood chemical composition and coating with water-borne wood oil product
2006 - IRG/WP 06-10597
Natural durability of wood has been widely studied, but the combination of the natural durability and different treatments has not been the focus of many studies. The durability of wooden products is mainly based on the water permeability and the resistance against organisms. In this study, the water absorption and decay resistance of sapwood and heartwood of Scots pine and Norway spruce were exam...
H Viitanen, S Metsä-Kortelainen, T Laakso
Enhancing the Performance of Transparent Coatings by UV Protective Pre-treatments
2006 - IRG/WP 06-30399
Most industry observers anticipate a change from copper-based preservatives to metal-free combinations of organics for residential treated wood products in North America within the next one to five years. While the chromium copper provide considerable protection against UV, metal-free formulations will need UV protection in the form of additives or coatings. While transparent coatings can be made ...
P I Morris, S McFarling
Predicting the decay resistance of timber above-ground: 1. Climate effects
2006 - IRG/WP 06-20330
Despite the benefits of using timber as a building product, it is disadvantaged by current Australian Standard durability classifications which lack the sensitivity desired by engineers and architects. To address the need for more sensitive timber service-life information in Australia, an above-ground durability research program was established in 1987. One focus of research is the relationship be...
L P Francis, J Norton
Laboratory methods for assessing the resistance of wood plastic composites to fungal attack.
2006 - IRG/WP 06-20340
Wood plastic composites (WPC’s) have many attractive material features including dimensional stability and resistance to moisture, but the wood in these materials remains susceptible to fungal attack. Assessing WPC decay resistance in laboratory trials has proven difficult because the slow moisture sorption characteristics of this material do not allow for sufficient fungal attack over the trad...
J J Morrell
L-joint based testing for service life prediction of exterior plywood in out of ground contact conditions
2006 - IRG/WP 06-20342
Good biological performance of several plywood types in exterior conditions is most probably related to altered wood moisture behaviour compared to solid wood. Therefore a test set up was developed, using EN 330 L-joint testing methodology, to facilitate differentiation of plywood for exterior applications.
The proposed test set up is an adaptation of an accelerated L-joint method introduced by V...
J De Smet, I De Windt, J Van Acker
Field Tests on Poles. A report from practice
2006 - IRG/WP 06-20343
A routine field inspection of some 1000 creosote poles during summer 2005 in northern Jutland, Denmark. The routine inspection was done by hammering, Pilodyn testing and taking core samples with a Matson Borer. Additionally a drill resistance measurement was done with a device consisting of the drill machine with a long, flexible steel needle with 1,5mm diameter and the measuring computer/battery-...
A Peylo, C-G Bechgaard
High-energy multiple impact (HEMI)-test – Part 1: A new tool for quality control of thermally modified timber
2006 - IRG/WP 06-20346
Thermal modification processes improve durability and dimensional stability of wood, but the strength properties, especially the dynamic ones, are compromised and need to be considered with respect to industrial quality control. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability, and therefore require a high number of replicates. To overcome ...
C Brischke, A O Rapp, C R Welzbacher
The effect of woody and non woody plants extractives on microbial resistance of non-durable species
2006 - IRG/WP 06-30392
The effect of Elm (Zelkova carpinifolia), Oak (Quercus castanifolia), Mulberry (Morus alba), Ash (Fraxinus excelsior) as woody plants, Rose (Rosa damascene) and Fumitory (Fumaria sp) as non woody plants extractives on durability of Beech (Fagus orientalis), Maple (Acer insgin), Alder (Alnus subcordata), and Lime (Tilia sp) were studied. First wood species having extractives were cut to small piece...
S M Kazemi, A Hosinzadeh, M B Rezaii
Biological resistance of didecyl dimethyl ammonium tetrafluoroborate (DBF)-treated wood in soil-bed and Basidiomycetes tests
2006 - IRG/WP 06-30393
This study evaluated the decay resistance of treated wood with a new quaternary ammonia compound, didecyl dimethyl ammonium tetrafluoroborate (DBF) in laboratory soil bed and Basidiomycetes tests. Treated sugi sapwood specimens with DBF at various concentration levels were first subjected to soil bed tests using two types of soil. The specimens subjected to soil bed tests were then used for Basidi...
S N Kartal, C Brischke, A O Rapp, Y Imamura
Tree crown architecture: a tool for decay resistance evaluation
2013 - IRG/WP 13-10793
The variability of natural durability contributes to the bad perception of some wood end-users. In our search, we need to adjust our methods and strategies to estimate natural durability and extract higher value from wood resources. Architectural analysis is essentially a detailed, multilevel, comprehensive and dynamic approach to plant development. Numerous biological process which impact some wo...
N Amusant, J-B Anouhé Say, A Amissa, J Beauchène, F Niamké, E Nicolinni
Influence of Acetylation on Fire Resistance of Beech Plywood
2006 - IRG/WP 06-40326
Influence of acetylation on fire resistance was studied in beech plywood. Beech layers were acetylated in a reactor with acetic anhydride at 120ºC for varying durations. Plywoods were made from the acetylated layers and directly exposed to burning flame from their edges for 60s according to ISO 11925-3. Ignition and glowing time were measured in samples. Results were analyzed statistically based ...
B Mohebby, A Talaii, A Karimi , S Kazemi Najafi
Assessment of the Envelope Effect of Three Hot Oil Treatments: Resistance to Decay by Coniophora puteana and Postia placenta
2006 - IRG/WP 06-40344
Timber of Corsican pine (Pinus nigra var. maritima) and Norway spruce (Picea abies) was treated in hot linseed oil, rapeseed oil and a proprietary resin derived from linseed oil. The samples were immersed in oil or resin under reduced pressure at temperatures of 180°C and 200°C. Very high uptakes of the oils or resin were recorded for pine, while spruce showed lower weight percent gains, below...
M J Spear, C A S Hill, S F Curling, D Jones, M D C Hale
Furfurylated wood - An alternative to Preservative-treated wood
2006 - IRG/WP 06-40349
Chemically modified wood is currently being marketed as a non-toxic alternative to traditional preservative treated wood (wood impregnated with biocides). Over the last decade the authors have developed modernised processes for wood modified by furfurylation. These new systems do not add metals or halogens to the product, which is important for an environmentally acceptable product. This presentat...
S Lande, M H Schneider, M Westin, J Phillips
Wood-Plastic Composites and the Durability Dilemma: Observations from the Field
2006 - IRG/WP 06-40351
Wood-Plastic Composites (WPCs) used for decking, window & door moldings have experienced dramatic growth in North America over the last several years, with annual production increasing at rates greater than 20% per annum since 1998. A key factor contributing to this growth has been the successfully communicated message that they are "virtually maintenance free". The common perception being t...
M J Manning, F M Ascherl, M E Mankowski
Resistance of DMDHEU-treated pine wood against termite and fungi attack in field testing according to EN 252. Results after 30 months
2006 - IRG/WP 06-40354
The aim of this study was to determine the effectiveness against decay and termite attack of pine sapwood treated with pure and modified DMDHEU in a field test according to European Standard EN 252. Some of the treatments tested were able to increase, within the period of the test reported (30 months), the resistance of the wood both to micro-organisms and termites. The curing process seems to be ...
S Schaffert, L Nunes, A Krause, H Militz