Borate Protection and Termites: Variation in Protection Thresholds Explained
2006 - IRG/WP 06-20324
Laboratory and field data reported in the literature are confusing with regard to ‘adequate’ protection thresholds for borate timber preservatives against subterranean termites. The confusion is compounded by differences in termite species, timber species and test methodology. Laboratory data indicate a borate retention of 0.5% mass/mass (m/m) boric acid equivalent (BAE) would cause > 90% t...
B C Peters, C J Fitzgerald
Micromorphological Characteristics of Degradation in Bamboo Attacked by White Rot Fungus Lentinus edodes
2006 - IRG/WP 06-10575
In comparison with micromorphological works for wood decay, little known is about the decay pattern of bamboos by wood decay fungi. The present work was undertaken to understand the general degradation pattern of bamboo and the influence of polylaminate layers in bamboo fiber walls on the restriction of fungal decay. The weight loss of bamboo species Phyllostachys puberscens against the white rot ...
Chang Hyun Cho, Kwang Ho Lee, Yoon Soo Kim
Blue Staining of Coated Modified and Unmodified Wood
2006 - IRG/WP 06-10589
We investigated resistance of unmodified, DMDHEU modified and oil heat treated uncoated and coated Scots pine wood against blue stain fungi. Both EN 152-1 and the reverse exposure tests showed excellent resistance of DMDHEU and especially of oil heat treated wood against blue staining. It is not needed to add any additional protective coating layers to prevent modified wood from staining. However,...
M Petric, M Pavlic, M Humar, M Tomažic
Resistance of pine and spruce heartwood against decay - The effect of wood chemical composition and coating with water-borne wood oil product
2006 - IRG/WP 06-10597
Natural durability of wood has been widely studied, but the combination of the natural durability and different treatments has not been the focus of many studies. The durability of wooden products is mainly based on the water permeability and the resistance against organisms. In this study, the water absorption and decay resistance of sapwood and heartwood of Scots pine and Norway spruce were exam...
H Viitanen, S Metsä-Kortelainen, T Laakso
Identification of fungi colonising coated and modified wood exposed outdoors using sequencing and T-RFLP profiling
2006 - IRG/WP 06-20326
Wood decay and staining fungi are known to colonize coated and modified wood. Rapid and reliable ways of identifying fungi on coated and modified wood may improve diagnostics and product development. In this work nine fungi growing in painted wood panels exposed outdoors at a test field in Uppsala, Sweden, were identified using sequencing and T-RFLP (Terminal Restriction Fragment Length Polymorphi...
U Råberg, J Bijelovic, C J Land, S Bardage, N Terziev
Re-sealing cut ends of envelope-treated softwood framing timber to protect against damage by the Australian subterranean termite Coptotermes acinaciformis: A revisitation
2006 - IRG/WP 06-20335
The claim that Australian Coptotermes acinaciformis (Froggatt) do not appear to initiate damage on timber from the end grain, thereby negating the need for treating exposed cut ends of softwood framing material (35 ? 90 mm) which has a repellent Tanalith? T envelope, was further investigated. Specimens of commercial Pinus radiata D.Don framing timber (untreated) and Pinus elliottii Englem. (untrea...
B C Peters, M Lenz, J W Creffield
High-energy multiple impact (HEMI)-test – Part 2: A mechanical test for the detection of fungal decay
2006 - IRG/WP 06-20339
The suitability of the high-energy multiple impact (HEMI)-test for detection of early fungal decay was examined. The HEMI – test characterizes the treatment quality of thermally modified wood by stressing the treated material by thousands of impacts of pounding steel balls. This method differentiates between heat treatment intensities, which are expressed by structural changes of the wood. Simil...
C R Welzbacher, C Brischke, A O Rapp
High-energy multiple impact (HEMI)-test – Part 1: A new tool for quality control of thermally modified timber
2006 - IRG/WP 06-20346
Thermal modification processes improve durability and dimensional stability of wood, but the strength properties, especially the dynamic ones, are compromised and need to be considered with respect to industrial quality control. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability, and therefore require a high number of replicates. To overcome ...
C Brischke, A O Rapp, C R Welzbacher
Performance of borate-treated lumber in a protected, above-ground field test in Japan
2006 - IRG/WP 06-30395
This document is supplemental to the previous IRG document (Tsunoda et al. 2004).
An experiment to simulate the sill plate (dodai) of the Japanese houses was conducted at the termite field test site of the Research Institute for Sustainable Humanosphere of Kyoto University in Kagoshima Pref., Japan where two economically important subterranean termite species [Coptotermes formosanus Shiraki and R...
K Tsunoda, A Byrne, P I Morris, J K Grace
Heat treatment of less-valuable Nigerian-grown Ceiba pentandra wood for improved properties
2006 - IRG/WP 06-40332
The hardwood Ceiba pentandra locally known as “ araba “ in Nigeria is rarely used for structural and construction works due to its high dimensional instability, low strength and durability values. Samples (10 x 10 x 150mm) were removed from four green boards (25 x 200 x 3000mm) of this species originating from a natural forest stand in Nigeria and subjected to 2-hour heat treatment at 160°C a...
L Awoyemi
Improvement of Grevillea robusta durability using heat treatment
2006 - IRG/WP 06-40333
Heat treatment of Grevillea robusta was carried-out under inert conditions to improve its durability. Resistance of heat treated samples was evaluated by malt agar block tests after three months of exposure to several wood rotting fungi. Results showed that the fungal durability was greatly improved after treatment. There was a good correlation between fungal resistance and mass loss which is a fa...
F Mburu, S Dumarçay, F Huber, M Petrissans, P Gérardin
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
CCB Preservative treatment of split muli (Melocanna baccifera ) bamboo by soaking process
2006 - IRG/WP 06-40336
This study was carried out in order to investigate the retention of chemicals inside the split muli ( Melocanna baccifera ) bamboo after preservative treatment by soaking process. Treatment with 10% aqueous solution of CCB (copper-chrome-boron) was applied in split bamboo of two sizes (1/4 part and 1/8 part) at three different moisture contents and five time periods (24, 48, 72, 96, 120 hours). It...
K Akhter, M H Chowdhury
Wood plastic composites from modified wood; Part 1 - Conceptual idea, mechanical and physical properties
2006 - IRG/WP 06-40338
Wood plastic composites, WPCs, are rapidly taking shares from preservative treated wood on the decking market. However, the long term performance of the WPC products in this application is uncertain. Therefore, in an attempt to increase the long term performance and durability, the substitution of the unmodified wood component with modified wood has been studied in the work presented in this paper...
P Larsson Brelid, B K Segerholm, M Westin, M E P Wålinder
The Effect of Flavonoids on Colour and Spectral Changes of the Wood Surface Caused by Heat Treatment or Ultra-violet Irradiation
2006 - IRG/WP 06-40341
Both heat treatment and UV irradiation can cause discolouration and change in the spectral properties of wood surface. Some of the characteristic flavonols have significant role on colour and spectral changes, despite of their relative small quantities in wood.
Colour changes and spectral properties of natural and extracted black locust (Robinia pseudoacacia L.) and poplar (Populus nigra L.) were...
R Csonka-Rákosa, L Molnár-Hamvas, E Börcsök, J Molnár, K Németh
Characteristics of treated oriented strand lumber using recycle chips
2006 - IRG/WP 06-40343
The Kyoto Protocol for preventing global warming has come into effect, and the Cabinet Council was decided on the amount of carbon dioxide exhaust to be reduced in Japan. Moreover, the recycling of demolition waste wood is mandated under the “Construction Material Recycling Law” as one of the mechanisms for Japan to form the recycling society. The law encourages the utilization of demolition w...
T Shibusawa, A Miyatake, K Yamamoto, K Hashimoto, H Sonobe
Surface and system treatments of wood for outdoor use
2006 - IRG/WP 06-30412
The project “Surface and system treatment of wood for outdoor use” was initiated the summer 2001. The project evaluates environmentally friendly preservatives and water borne coating systems, to find the best protection for timber indented for outdoor use. The wood species selected as test material were pine and spruce. The different treatments were exposed in several outdoor accelerated tests...
B Jacobsen, F G Evans
Non-pressure preservation technique of five less durable timber species – Kadam (Anthocephalus cadamba), Shimul (Bombax ceiba), Pithalu (Trewia nudiflora), Am (Mangifera indica) and Boroi (Ziziphus jujube) of Bangladesh
2006 - IRG/WP 06-40322
Wood is a versatile renewable resource, which has been extensively used as a reliable construction material as well in furniture ever since the beginning of civilization.
The Major disadvantage of wood is its susceptibility to biodeterioration by fungi, insects and bacteria. In tropical countries like Bangladesh, fungi is the most significant of these biodeterioration agents. Kadam (Anthocephalus...
G N M Ilias, A H Kabir, F Begum, M F Alam
Underwater shock treatment for improvement of penetration of wood
2006 - IRG/WP 06-40325
Many of conifers including Beimatsu (Pseudotsuga menziesii Franco; Dougras fir, Oregon pine), Akamatsu (Pinus densiflora Sieb. et Zucc.; Japanese red pine), Dafurica Karamatsu (Larix gmelinii Gordon; Dahurica larch) and Karamatsu (Larix leptolepis GORDON; Japanese larch) generally contains the high moisture content. Although subjected to the drying process, it is difficult to be dried up completel...
S Itoh, H Maehara, K Tanaka, T Echigo, K Morioka, E Shirai, K Nishimoto
Assessment of the ease of preservative treatment in the less-valuable Nigerian-grown Ceiba pentandra wood
2006 - IRG/WP 06-40330
The hardwood Ceiba pentandra locally known as “araba“ in Nigeria is rarely used for structural and construction works due to its high dimensional instability, low strength and durability values. Samples (25 x 50 x 600mm) were removed from four green boards (25 x 200 x 3000mm) of this species originating from a natural forest stand in Nigeria. The sapwood and heartwood were differentiated by me...
L Awoyemi, A J Pitman
Assessment of the Envelope Effect of Three Hot Oil Treatments: Resistance to Decay by Coniophora puteana and Postia placenta
2006 - IRG/WP 06-40344
Timber of Corsican pine (Pinus nigra var. maritima) and Norway spruce (Picea abies) was treated in hot linseed oil, rapeseed oil and a proprietary resin derived from linseed oil. The samples were immersed in oil or resin under reduced pressure at temperatures of 180°C and 200°C. Very high uptakes of the oils or resin were recorded for pine, while spruce showed lower weight percent gains, below...
M J Spear, C A S Hill, S F Curling, D Jones, M D C Hale
Wood plastic composites from modified wood. Part 2 - Durability in laboratory decay tests
2006 - IRG/WP 06-40353
The decay resistance of wood plastic composites, WPCs, was tested according to modified versions of AWPA E10 (soil-block test) and ENV 807 (tests in three un-sterile soils, terrestrial microcosms, TMCs). The WPC materials were conically extruded profiles with 30% polypropylene content. The 70% wood content was untreated Scots pine sapwood, acetylated pine and heat treated Norway spruce, respective...
M Westin, P Larsson Brelid, M L Edlund, G Alfredsen
Laboratory Leaching Tests to Study the Effects of Post-Treatment Storage Periods on CCA Leachability and Fixation in Treated Permeable and Refractory Malaysian Hardwoods
2006 - IRG/WP 06-50240
The biological resistance and environmental safety of CCA-treated wood relies on the extent of post-treatment storage fixation of CCA in wood prior to being utilized. A study on the comparative leachability (fixation) of CCA-treated refractory and permeable heartwoods of 3 Malaysian hardwoods subjected to different post-treatment storage (fixation) periods of up to 4 weeks, at 2 laboratory leachin...
A H H Wong, H C Lai, N P T Lim
Biological Protection of Composite Panel from Moulds and Decay
2007 - IRG/WP 07-10612
Composite panels, such as oriented strand board (OSB), are widely used in house construction in North America. These structural panels are normally made of non-durable wood species and are susceptible to moulds and decay when exposed to wet conditions. Building envelope failures due to moulds, decay or poor construction practices can negatively impact the image of wood. To ensure durability of com...
Dian-Qing Yang, Xiang-Ming Wang, Hui Wan
Bifenthrin recovery from glue-line-treated plywood
2007 - IRG/WP 07-20355
Plywood and laminated veneer lumber (LVL) can be protected from termite damage by addition of bifenthrin to the adhesive used in product manufacture. However, conditions associated with this manufacturing process may lead to deterioration or immobilisation of the active ingredient. In order to determine compliance with treatment specifications, it is important that the concentration of a preservat...
J Norton, L Stephens