Effect of polyurea coatings on performance of Douglas-fir in tropical above ground exposures
2014 - IRG/WP 14-40665
The potential for using polyurea barriers to limit fungal and termite attack was investigated on Douglas-fir lumber and timbers. Termites were capable of penetrating the barrier to attack non-treated wood as well as wood dip-treated with disodium octaborate. The coatings were also exposed above ground for 48 months in Hilo Hawaii. Samples were dissected to detect internal decay. Coated non-trea...
S Uysal, J J Morrell
Lignin Modification to Produce Sustainable Polyurethane Resin for Wood Coatings
2014 - IRG/WP 14-40682
The use of lignin as the most abundant aromatic natural polymer has been evaluated for use in the production of lignin-based polyurethane resin for coating applications. Coatings are made of resins (ca. 50%), which today are mainly derived from petroleum-based polymers. This study is focused on the development of an environmentally friendly method of modifying lignin to be used as source of natura...
M Nejad, M Arefmanesh, S Chandra, J Mostaghimi, E Master
Acceptance levels of surface disfigurement - tolerance to defects of coated wood
2015 - IRG/WP 15-20564
Service life planning (PSL) has become an important issue in performance based building and substantial progress has been made in recent years. The role of predicting the aesthetical service life of wooden building components has been underestimated for quite long time but is recently attracting more and more notice. It is influenced by numerous factors such as discoloration, fading, flaking, crac...
C Brischke, P Kaudewitz
Indentation and pendulum hardness tests: two convenient assessment methods of the performance of exterior wood coatings
2015 - IRG/WP 15-40689
Developing formulations of exterior wood coatings with long service life is a big challenge. For many years in Europe the performances have been mainly evaluated through weathering tests (within the EN 927 series) followed by visual assessment (blistering, flaking, mould growth, chalking and cracking), colour and gloss measurements, and adhesion tests. Very recently the importance of the mechanica...
L Malassenet, L Podgorski, M Truskaller, G Grüll
Application of nanoparticles of silver and nanoparticles of titanium dioxide in reinforcement of wood and coating for wood in Costa Rica
2015 - IRG/WP 15-40698
Wood is one of the most widely used materials in last 20 years by society in many applications, with a considerable proportion of this material coming from forest plantations. Plantations usually produce timber with reduced strength properties and low natural durability. On the other hand, nanotechnology applications have the potential to increase wood properties. Likewise, nanotechnology cannot o...
A Berrocal Jiménez, R Moya Roque, A Lucrecia Rodríguez, J R Vega Baudrit
How to Increase the Lifespan of Exterior Wood Coatings
2015 - IRG/WP 15-40700
In addition to aesthetic appeal, coatings are designed to protect the wood from weathering degradation in outdoor conditions. This paper gives an overview of the effects of main components of coating, coating properties, and wood treatments on coating performance. Understanding how different type of resins (alkyd, acrylic or polyurethane), amount of pigments, type of solvents (organic or water), a...
M Nejad
Investigation of Dimensional Stability and Coating Performance of Different Heat-Treated Poplar Wood Before and After Accelerated Aging
2015 - IRG/WP 15-40702
In this investigation, coating performance of heat-treated poplar wood (Populus tremuloioes) in different environments, before and after accelerated aging was studied. Specimens with 150×100×20 mm and 20×20×20 mm in dimensions were prepared. Heat treatments were performed in air, steam and linseed oil media. Specimens were coated by alkyd based stain. Adhesion strength before and after aging, ...
A Talaei, D Ansari Movahed, G Rassam
Accelerated Weathering Performance of Impregnated Wood Samples Coated with Zinc by Means of Plasma-Assisted Particle Deposition
2016 - IRG/WP 16-30682
Many different methods are currently applied for wood protection against outdoor conditions. The most important of these is the process of impregnation with liquid substances. However, this kind of wood preservatives cannot provide a long-term protection of wooden surfaces. Weathering-resistant surfaces can be obtained by applying UV absorbing agents. In this study, the influence of zinc particles...
A Can, H Sivrikaya
Variation in coating hardness during the EN 927-6 weathering test: influence of pigmentation
2016 - IRG/WP 16-40739
The objective of the SERVOWOOD project is to develop and establish European Standards that will facilitate the prediction of service life for exterior wood coatings. Within this project an extensive round robin exercise has been carried out by five partners to establish the repeatability and reproducibility of the EN 927-6 artificial weathering test. This round robin included the exposure of the I...
L Podgorski, L Malassenet, C Reynaud
A non-VOC approach of solvent-based wood preservatives for remedial treatment
2016 - IRG/WP 16-30681
Solvent-based wood preservatives are the workhorses in the field of remedial treatment. Due to new European regulations on the indoor air quality there is an increasing pressure on the VOC-content on these solvent-based product types. The transfer of these European regulations into national law is left up to each European member state and handled in different ways. E.g. France has introduced a VO...
M Pallaske, S Hellkamp, P Jüngel
Development of methodologies to evaluate tanning blocking coatings
2016 - IRG/WP 16-40760
In Europe an increased interest in using home-grown hardwoods as sustainable and renewable construction materials started a few years ago. Amongst these species oak and chestnut are two interesting candidates as their heartwood contain a significant amount of tannins which contribute to their natural durability. To avoid wood greying and dimensional variations, oak and chestnut must be protected b...
C Reynaud, L Podgorski
Fungal growth on coated wood exposed outdoors: influence of coating pigmentation, cardinal direction and inclination of wood surfaces
2017 - IRG/WP 17-10896
The objective of the SERVOWOOD project was to develop and establish European Standards that will facilitate the prediction of service life for exterior wood coatings. One of the objective of this project was to study fungal growth of the field exposed panels. Two coatings applied in 2 and 3 coats were exposed for one year outdoors at 45° south: one solventborne (alkyd based) and one waterborne (a...
L Podgorski, C Reynaud, M Montibus
Susceptibility to filamentous fungi of plywood for furniture coated with waterborne acrylic lacquers
2017 - IRG/WP 17-40778
Filamentous fungi (mould), thanks to their little trophic requirements belong to organisms which grow exceptionally easy and fast in favorable hygrothermal conditions and attack both organic and inorganic materials even with only trace amounts of organic substances on the surface. The fungi often cause spoilage of foodstuffs, worsen the aesthetic of wood-based elements, and pose a threat to the en...
A Fojutowski, M Nowaczyk-Organista, P Hochmańska
The Comparison of Weathering Resistance of New Generation Wood-Coating Systems
2017 - IRG/WP 17-40789
In this study, the performance of wood-coating systems containing different UV absorbers was evaluated in artificial weathering conditions. Acrylic-based resin containing three different UV absorbers was applied on oriental beech and scots pine surfaces. Weathering conditions were sustained for 84 days. After the weathering test, the change of color and roughness on the wood surface was measured t...
Ö Özgenç, S Durmaz
Studying Weathering Performance of Coatings on Thermally Modified Wood
2017 - IRG/WP 17-40805
Thermal modification and degree of improved properties depends on wood species and treatment parameters. Southern pine and spruce are the two common wood species for decking, fences and siding in North America. This study was the first to evaluate coating performance when applied on oil-heat-treated southern pine and spruce wood samples. Water uptake, colour and gloss changes of samples were analy...
M Nejad, M Dadbin, P Cooper
Evaluation of coating applied in treated wood: experiences in Brazil
2017 - IRG/WP 17-40814
Weathering assays study the coating degradation caused by its exposure to the action of ultraviolet radiation, winds, heat and humidity. The use of test specimens in different arrangements and exposure angles is intended to reproduce various conditions in which a product can be used. The purpose of this paper is to present the efficacy of an oil-borne varnish applied on treated wood exposed to wea...
M F Natale, J M Vidal
In-service performance of wood claddings and windows – a Norwegian survey
2018 - IRG/WP 18-20632
The overall aim of the study was to strengthen the empirical data on decay frequency and in-service performance of claddings and windows in Norway. Data from a survey of claddings and windows from 38 Norwegian houses is presented. The main findings for wooden claddings: 1) predominance of decay was detected in east facing claddings, while the largest decayed areas were located on south facing clad...
L Ross Gobakken, G Alfredsen
In-line quality control of the film thickness in industrial coating processes for exterior cladding
2018 - IRG/WP 18-40835
The production of industrially coated wood cladding has been strongly increasing in Scandinavia during the last years. In the beginning of this development, industrial coating processes included solely the application of pigmented primers; these however provide only a short protection of the wood surface and the application of a top coat is required during the first 6 to 12 months after mounting t...
U Hundhausen, M Slabohm
Improvement of short rotation teak wood properties through thermal modification
2018 - IRG/WP 18-40842
Teak (Tectona grandis L.f) is one of the most popular tropical timber species. Nowadays, the source of long rotation teak is limited in the availability. Many wood processing industries use short rotation teak, which has lower quality especially in durability and dimensional stability. Heat treatment is an eco-friendly method improving dimensional stability and durability of wood. The objectives o...
L A Pratiwi, I W Darmawan, B George, A Merlin, C Gérardin, S Dumarçay, T Priadi, P Gérardin
Gloss and hardness variations as early indicators of wood coating failure during weathering tests
2019 - IRG/WP 19-40866
The objective was to track early changes which ultimately will lead to coating failure when exposed to artificial weathering. Two different coatings (one waterborne acrylic paint and one solventborne alkyd stain) were exposed to artificial weathering for 2016 hours according to EN 927-6. Every 168 hours, samples were removed from the artificial weathering device for assessment (general appearance,...
L Podgorski
Monitoring of wood preservatives exposed to weathering: Extraction and analysis methods of organic biocides from treated wood and collected rain runoff
2020 - IRG/WP 20-30753
Weathering is the cause of numerous damages for outdoor joineries. Protection of wood using a preservative treatment covered with a coating is a process widely used to limit these damages. However, biocides from preservative treated wood are prone to degradation and leaching, having a direct influence on the joinery service life. This document deals with extraction and analytical methods for bioci...
O Ouali, K Le Ménach, E Raphalen, L Podgorski, S Legay, H Budzinski
PlasmaSolution – Curing of coating formulations using non-thermal plasmas
2020 - IRG/WP 20-40904
Coatings are an important part of wood protection, especially for outdoor applications. In order to provide a good protection, protective coatings need to exhibit good adhesion, mechanical resistance, and weathering resistance. Plasma pre-treatments are an established method to increase the performance of existing coatings including those on wood and wood-based substrates. Moreover, plasma deposit...
S Dahle, J Žigon, M Petrič
Thermal spray coatings to protect wood from termites
2020 - IRG/WP 20-40905
Protecting buildings and construction materials against subterranean termites in Europe relies on combined physical and chemical approaches. Buildings can be protected by physical or physico-chemical barriers such as gravel aggregates, steel mesh or plastic films impregnated with insecticides. Wood and wood-based materials are traditionally protected by insecticides applied on the surface or deepl...
L Podgorski, H Myalska, A Dinoirjean, M Kutnik
Wood protection with cement – Part 1: Coating matters and durability of cement coated wood
2020 - IRG/WP 20-40911
The use of wood in geotechnical applications has seen renewed interest. However, concerns related to the durability and service life of wood in ground contact applications remain. Wood has the potential to substitute commonly used steel and concrete in the geotechnical engineering sector, but solutions to extending the service life and maintenance intervals require long-lasting wood protection sys...
S Hirschmüller, B Marais, C Brischke, A Krey, J Bösing
Application of suberin fatty acids extracted from birch bark for wood coating
2021 - IRG/WP 21-40914
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
A Kumar, Risto Korpinen, Veikko Möttönen