Preservative performance of copper naphthenate (SANPRESER-OGR) in brush treatment of timber
1991 - IRG/WP 3663
Preservative efficacy of copper naphthenate (SANPRESER-OGR) was evaluated in the laboartory and field trials when timber was treated by brushing. Results of field trial indicated that service life of the brush-treated timber could be approximately 10 years or longer under ground contact conditions, although life span was slightly varied with timber species and test sites. After four years&apos...
Y Sugai, K Hamada, M Kitada, K Tomoi
Ten year field test with a copper-borate ground line treatment for poles
1993 - IRG/WP 93-30017
A wood preservative paste consisting of borax and copper naphthenate has been tested to determine its efficiency in protecting wood from decay fungi and insects. The paste was applied to polyethylene-backed wraps that were fastened to the below-ground portions of unseasoned southern pine pole stubs. After 4 years of exposure in Mississippi, the untreated control stubs were completely deteriorated....
T L Amburgey, M H Freeman
Durability of wood in the area of wood-inhabiting termites in Slovenia
1981 - IRG/WP 1139
This report describes a research dealing with resistance and durability of five different species of wood. The experiment was made in natural conditions in the Slovene area of wood-inhabiting termites. The results of our experimental field, which correspond to the results of the former laboratory experiments, show a very weak resistance of spruce-wood, fir-wood, and beech-wood. They also show thei...
L Kervina
Issues Facing Wood Preservation in New Zealand Today
2003 - IRG/WP 03-30326
In New Zealand, the three major issues facing the wood preservation industry today are:
Extension of use of LOSP preservatives, chiefly tributyltin naphthenate, for treatment of products in Hazard Class H3 exposed to the weather for which LOSP have not been traditionally used. Concerns have been expressed about the long-term durability of such products.
Restrictions on the use of CCA preservativ...
M E Hedley
A Preliminary Report on the Properties of Engineered Wood Composite Panels Treated with Copper Naphthenate
2005 - IRG/WP 05-40294
This paper reports on our preliminary investigation of the properties of randomly oriented strandboard which had waterborne or powdered copper naphthenate (CuN) incorporated into the board during manufacture. When compared to zinc borate-treated controls (ZnB), the mechanical properties of strandboard (MOR, MOE, work-to-maximum load, internal bond strength) were not adversely affected by treatmen...
J W Kirkpatrick, H M Barnes
An investigation of organotin compounds in treated wood using Mössbauer spectroscopy
1983 - IRG/WP 3249
The influence of sample preparation on the 119mSn Mössbauer spectrum of tributyltin chloride in ponderosa pine was investigated. Initial studies with sawdust and compressed discs concluded that the latter were clearly superior. Further studies showed that compressed discs prepared from 0.4 g of treated wood and 0.1 g of cellulose were robust and gave excellent Mössbauer spectra. The possibility ...
J N R Ruddick, J K Ingram
Copper naphthenate: An analysis of the materials found in the worldwide marketplace using a new analytical technique
2000 - IRG/WP 00-30224
Naphthenic acid has been recovered from products of petroleum refining for well over 100 years. The metal soaps, specifically copper and zinc naphthenate, have been evaluated and used as commercial wood preservatives for in excess of 60 years. Most of the early data supporting the continued use of copper naphthenate as a wood preservative was based on materials manufactured from naturally occurrin...
J A Brient, R E Moyer, M H Freeman, H Jiang
Diffusion of a copper naphthenate/boron paste through Douglas fir heartwood
1991 - IRG/WP 3671
Groundline wraps are an important portion of the remedial treatment strategies for protecting utility poles in North America from surface decay. The compositions of these wraps have recently shifted away from pentachlorophenol and creosote to formulations containing copper naphthenate and boron. These formulations have not yet been extensively tested, although the chemicals have been used for many...
P G Forsyth, J J Morrell
Serviceability of copper naphthenate-treated poles
2000 - IRG/WP 00-30214
Copper naphthenate-treated poles in service were inspected for deterioration, penetration, retention, and serviceability. The study to date has included poles in all hazard zones in the United States. Poles installed by 12 different utilities and eight different treating companies are included in the survey. Both southern pine and Douglas-fir poles and distribution and transmission poles are inclu...
H M Barnes, M H Freeman, J A Brient, C N Kerr Jr
The chemical nature of bis(tributyltin) oxide in Pinus sylvestris sapwood
1989 - IRG/WP 3508
Tributyltin compounds have been used for many years as wood preservatives. This study has provided, for the first time, an explanation for the previously reported dealkylation and/or volatilisation of the tributyltin species in, and from, Scots pine (Pinus sylvestris) sapwood. Thus, 119 Sn nuclear magnetic resonance studies have shown that, on impregnation into this timber, bis(tributyltin) oxide ...
S J Blunden, R Hill
Some data on the activity of alternative fungicides for wood preservation
1985 - IRG/WP 3333
Data from laboratory tests against basidiomycete fungi are presented for 9 alternative fungicides in organic solvent formulations and also in water for one product. Results are compared with data for reference preservatives, tributyltin oxide, copper and zinc naphthenates and pentachlorophenol. Of special interest is the apparently better than additive effect of mixing tributyltin naphthenate and ...
A F Bravery, J K Carey
The compatability of tributyltin fungicides and synthetic pyrethroid insecticides as wood preservatives
1987 - IRG/WP 3414
The stability of three synthetic pyrethroids, cypermethrin, deltamethrin and permethrin, to selected tributyltin compounds, Bu3SnX {where X = OSnBu3, Cl, 02CC6H5, O2C (Naphthenyl), OSO2Et}, (Bu3SnO)3PO and {NBu4} {Bu3SnCl2}, in toluene solution was investigated by infra-red spectroscopy over a six month period. It was found that only (Bu3Sn)2O reacted with the pyrethroids and that their order of r...
S J Blunden, R Hill
Laboratory evaluation of metallic naphthenates as wood preservatives
1991 - IRG/WP 3654
Fungicidal and termiticidal efficacy of copper and zinc naphthenates was appraised according to Japanese standardized laboratory testing methods. Copper and zinc naphthenates succeeded in protecting wood from decay fungi at retentions of 0.5 and 1.0 kg/m³ as metal, respectively. [JIS A 9302 (1976)] when they were applied to vacuum/soak impregnation [JIS A 9301 (1976)]. With respect to the fungici...
K Tsunoda, M Sakurai
Low polymer levels containing bioactive monomer polymerized in situ provide resistance to Gloeophyllum trabeum
1995 - IRG/WP 95-30066
Wood preservation based on in situ polymerization of potentially bioactive monomers has been studied. Tributyltin oxide acrylate (TBTOA) and pentachlorophenol acrylate (PCPA) were synthesized. Wood samples were treated at 2, 5, 10, 15 and 20% by weight solutions with varying amounts of crosslinker (trimethylolpropane trimethacrylate, TMPTM) and polymerized in situ in wood samples (2.54 x 2.54 x 0....
R E Ibach, R M Rowell
Preservation of robinia wood (Robinia pseudoacacia L.) stakes by vintners
1982 - IRG/WP 3194
This work discusses decay resistance of robinia wood to fungi Trametes versicolor (L.ex Fr.) Pil. and Coniophora puteana (Schum. ex Fr.) Karst., and also the possibility of influencing its resistance by means of chemical protection. The results showed that natural resistance of robinia wood to these two different agents of wood decay is not the same. It is much less resistant to the fungus Conioph...
R Benko
Copper naphthenate-treated Southern Pine pole stubs in field exposure: - Part 1: Gradient & biodeterioration analysis 12 years after treatment
2000 - IRG/WP 00-30242
Naphthenates have been used for the preservation of timber and cellulose since their original identification in Russia in the early 1880's as part of a series of petroleum characterizations. Later work in the development of copper naphthenate as a heavy-duty preservative for poles led to the development of various treating cycles similar to other oil-borne systems. Recent work concerning ...
H M Barnes, M H Freeman
Termite and fungal resistance of in situ polymerized tributyltin acrylate and acetylated Indonesian and USA wood
2000 - IRG/WP 00-30219
Wood [Indonesian pine (IP), Indonesian Jabon (IJ) and USA southern yellow pine (USP)] was either in situ polymerized with tributyltin acrylate (TBTA) or acetylated and then exposed to termite and fungal degradation both in laboratory tests and field exposure. The TBTA woods had an average weight percent gain (WPG) of 11% for IP, 12% for IJ, and 10% for USP. The acetylated woods had a WPG of 15-27%...
R E Ibach, Y S Hadi, D Nandika, S Yusuf, Y Indrayani
Tendency of the preservative use for impregnation industries in Japan
1998 - IRG/WP 98-50101-05
In Japan, since 1997, the acceptable limit of the arsenic in the waste water become to 0,1 mg/l and the additional regional severer restriction can be established. In this reason, Japanese wood preservation industries intend to use other than CCA, like DDAC, ACQ, Tanalith CuAz, copper-naphthate and zinc-naphthenate, as replacing from CCA. In Jan-June 1997, the share of CCA preservatives was less t...
K Suzuki
Giftwirkung einiger organischer Zinn-Verbindungen auf Eilarven von Hylotrupes bajulus (L.). [Toxic efficacy of some organic tin compounds against egg larvae of Hylotrupes bajulus (L.)]
1978 - IRG/WP 2120
The toxic values of 12 organic tin compounds towards newly hatched larvae of Hylotrupes bajulus were determined after 4- and 12-week test periods in comparison with bis-tri-n-butyltin oxide (TBTO). Tri-n-butyltin benzoate as well as the 2-, 3- and 4-methyl benzoate of tributyltin oxide were equally effective as TBTO and the latter two were somewhat more effective after a 12-week test period. Almos...
G Becker
International collaborative laboratory comparison of two wood preservatives against subterranean termites: Update
1994 - IRG/WP 94-20032
It was agreed by members at the termite workshop at the 24th annual meeting of IRG in Orlando, USA, in May 1993 to initiate an international subterranean termite laboratory bioassay to compare the various preferred termite protocols used by IRG termitologists. The author was nominated to co-ordinate this comparative laboratory evaluation of two wood preservatives (CCA and Cu-naphthenate) against t...
J R J French
Marine trials with water-borne salts and organotin compound
1986 - IRG/WP 4128
Pinus sylvestris blocks treated with water-borne salts (CCA, CCB, CCF) and organotin compounds (TBTO, TBTCl) were submerged in the sea at Follonica station. The results obtained after 12 years of immersion are presented. The samples treated with CCA, CCB and CCF at the lowest concentration (2%) were destroyed after 7-9 years and the samples treated with CCB and CCF at the highest concentrations (4...
A Gambetta, E Orlandi
Water-Borne Copper Naphthenate: An Emerging Wood Preservative
2002 - IRG/WP 02-30280
Waterborne copper naphthenate (WB Cu-N) was used to treat southern yellow pine (Pinus spp) and red maple (Acer rubrum) stakes. The treated stakes were exposed in test sites located in Florida, Michigan and Mississippi for 3 to 6 years. Copper Chromium Arsenate (CCA),
Ammoniacal Copper Quat (ACQ) and Oil-borne Copper Naphthenate (OB Cu-N) were also used to treat some stakes for comparison. Results...
P Nzokou, D P Kamdem, M H Freeman
The effect of preservative distribution in small blocks of Pinus sylvestris on the toxicity of tributyltin oxide to Reticulitermes santonensis Feytaud
1971 - IRG/WP 206
Small blocks of Pinus sylvestris (50x25x15 mm³) were treated by a full-cell method with various concentrations of tributyltin oxide in benzene. Replicate blocks were then freeze dried, rapidly air dried or slowly air dried and exposed to surface attack by the subterranean moistwood termite Reticulitermes santonensis Feytaud. At all concentrations it was found that the freeze-dried blocks were mor...
M P Levi, D N R Smith
Laboratory evaluation of copper naphthenate pressure treatments against the Formosan subterranean termite
1993 - IRG/WP 93-10005
Southern pine wafers and Douglas-fir cubes pressure treated with copper naphthenate in AWPA P9 Type A oil or in toluene were evaluated for resistance to attack by the Formosan subterranean termite, Coptotermes formosanus Shiraki (Isoptera: Rhinotermitidae). Wood samples were pressure treated to target copper retentions of 0.040, 0.075, 0.095, or 0.150 pcf, conditioned to simulate field exposure, a...
J K Grace, R T Yamamoto, P E Laks
Tributyltin compounds in wood preservation: Health and safety aspects
1986 - IRG/WP 3396
The toxicity of organotin compounds of the general formula RnSnX(4-n) depends strongly on the type of organic substituent R and on the degree of substitution n. The residues X, not bound through a tin-carbon bond, are however of much smaller influence. Furthermore, there is evidence that hydrolysis of tributyltin esters will occur under environmental as well as under physiological conditions to TB...
H Schweinfurth, P Günzel, H A B Landsiedel, R Lang, R Reimann, C Schöbel, F Siegmund