Ancillary properties of vapor boron-treated composites
2001 - IRG/WP 01-40210
This paper discusses the water absorption, thickness swelling, and internal bond strength of North American composites treated using a vapor boron treatment process. For oriented strandboard, high boron loadings led to lower internal bond strength and lower thickness swelling. Water absorption results were variable but no deleterious effect of treatment was noted. For medium density fiberboard, th...
W A Jones, H M Barnes, R J Murphy
The effect of steam conditioning on Southern yellow pine treated with copper naphthenate
1997 - IRG/WP 97-40086
The current study was undertaken to investigate the influence of steam conditioning on Southern yellow pine treated with copper naphthenate (Cu-N). Pre-steamed and /or kiln-dried Southern yellow pine were pressure treated with Cu-N. After treatment, one group of samples were post-steamed. It was found that samples changed color from green to dark-brown after post-steaming. To elucidate the effect ...
Jun Zhang, D P Kamdem, M H Freeman, R D Arsenault
The use of the Pilodyn for detecting soft-rot decay in CCA treated eucalypt poles
1986 - IRG/WP 2251
A 6 Joule Pilodyn unit with 2.5 mm diameter pin was used to inspect CCA treated eucalypt poles, suspected of suffering groundline soft-rot decay. Pole plugs were removed at the inspection region and the amount of soft-rot decay present determined microscopically. High correlation (R² = 0.73) was obtained between the amount of soft-rot and Pilodyn pin penetration. The Pilodyn is recommended as a u...
L E Leightley, G A Willoughby
Patterns of bacterial attack in preservative treated eucalypt power transmission poles
1984 - IRG/WP 1223
Patterns of bacterial decay have been examined using light and scanning electron microscopy. Two morphologically distinct patterns have been recognised in preservative treated eucalypt power transmission poles. Bacterial Decay I (BDI) involves the removal of the secondary wall layers initiating with erosion of the S3 layer from the cell lumen. As decay progresses the S2 layer and S1 layer are degr...
G A Willoughby, L E Leightley
The effect of treatment temperature on the biological performance of CCA treated wood
1990 - IRG/WP 3624
Birch and Scots pine sapwood blocks were treated with several concentrations of CCA at three different temperatures: 5, 20 and 35°C. The treated wood was maintained at the appropriate temperature for the fixation period. Leached and unleached samples were then exposed in a soft rot monoculture test using Chaetomium globosum and a brown rot monoculture test using Coniophora puteana. The treatment ...
S M Gray
Laboratory simulation of leaching from creosote treated wood in aquatic exposures
2000 - IRG/WP 00-50157
Creosote has a long history of use as a preservative particularly in industrial wood products, but its use has come under increasing scrutiny as a result of concerns about its potential effects on aquatic and terrestrial non-target organisms. Despite its long use, there is relatively little data on the rates of creosote loss in many exposures. In this report, we describe small scale leaching tank ...
Ying Xiao, J Simonsen, J J Morrell
Visualization of inorganic element distribution in preservative treated wood by SEM-EDXA
2001 - IRG/WP 01-40208
SEM-EDXA was found to be an effective way of visualizing inorganic element distribution in wood as it was possible to examine some inorganic elements at the same time and map the concentration differences in color. Japanese cedar sapwoods were impregnated by vacuum treatment with CuAz or by pressure treatment with CCA preservatives and then distribution of Cu, Cr and As elements in wood were exami...
H Matsunaga, R Matsumura, K Oda
Effect of EDTA on removal of CCA from treated wood
2002 - IRG/WP 02-50182
Since substantial amounts of chromated copper arsenate (CCA) remain in the wood for many years, the disposal of CCA-treated wood causes escalating environmental concerns. Additionally, wood waste is generated when treated wood is put into service, for which environmentally benign disposal technologies need to be developed. Novel approaches to remove copper, chromium, and arsenic from CCA-treated w...
S N Kartal
Marine performance of preservative treated Southern pine panels. Part 2: Exposure at Mourilyan Harbour, Queensland, Australia
2000 - IRG/WP 00-10337
Southern yellow pine panels treated with ACQ type B, ACQ type A, CCA type C, creosote, and copper naphthenate have been exposed at Mourilyan Harbour, north Queensland, Australia for almost 6 years. These panels have been inspected and rated for fouling and attack by Teredinid, Limnoria, Martesia, and Sphaeroma during this exposure. After 70 months exposure, overall performance of ACQ type B was eq...
A R Zahora, A F Preston, K J Archer, S Kleinschmidt
Investigation of some technical properties of heat-treated wood
2003 - IRG/WP 03-40266
The objective of this study was to investigate some technical properties of heat-treated wood.
Wood heat-treated according to a process intended for wood in above-ground end-uses (European hazard class 3) was subject to the following:
· A delamination test according to EN 391 with glulam beams made of heat-treated pine (Pinus sylvestris) and spruce (Picea abies) laminations, assembled with PR...
C Bengtsson, J Jermer, A Clang, B Ek-Olausson
Dimensional stability, biological resistance, and mechanical properties of phenol-resin-treated particleboard
1990 - IRG/WP 3622
Particleboards were treated with a low molecular-weight phenol-formaldehyde (PF) resin and their enhanced properties were evaluated. Besides dipping of particles in aqeous solutions of resin, and spraying of resin solutions before spray of the conventional phenol-formaldehyde resin for adhesive binder, one step treatment by spraying of the mixture of the low molecular-weight resin and the adhesive...
Y Imamura, H Kajita
Biological resistance of phenol-resin treated wood
1990 - IRG/WP 3602
Biological resistance of PF (phenol formaldehyde resin) - treated wood has been tested in relation to the resin properties, wood species and biological factors. When tested using water-soluble PF (mol. wt. 170), ca. 10% RI (resin impregnation) was enough to suppress the decay of Japanese cedar (Cryptomeria japonica) and western hemlock (Tsuga heterophylla) blocks exposed to Tyromyces palustris (br...
M Takahashi, Y Imamura
Testing a diffusion and reaction model for the leaching of CCA components from unfixed CCA-treated wood
2002 - IRG/WP 02-50193
A previously described physical model applicable to the leaching of any substance undergoing a first-order fixation reaction with wood is applied to the leaching of CCA components from unfixed wood. Using this model and laboratory leaching experiments with small wood samples immersed in water, the diffusion coefficients and reaction rate constant of Cr6+, total Cr, Cu and As in unfixed CCA-treated...
L Waldron, P A Cooper
Highly virulent wood-rotting Basidiomycetes in cooling tower timbers
1995 - IRG/WP 95-10125
Over the past ten years most industrial cooling towers changed their water treatment systems in order to meet environmental requirements. Since this alterations wood rot attack has been reported more frequently. Several Basidiomycete fungi were isolated and determined. Amongst the most important ones are strains of Physisporinus vitreus (Pers.:Fr.) P. Karst., Phellinus contiguus (Fr.) Pat. and Don...
J Van Acker, M Stevens, V Rijckaert
Chemical analysis for TBTN in LOSP-treated wood and preservative fluids
1994 - IRG/WP 94-20027
Tributyltin napthenate (TBTN) is being substituted for tributyltin oxide (TBTO) in LOSP preservative formulations because its lower reactivity/better stability allows co-formulation with synthetic pyrethroids. Better stability may reduce molecular degradation both in-service and during analysis. It was considered necessary to check whether TBTO analysis methods were suitable for use on TBTN treate...
D P Wraight, M J Kennedy
Long term performance of CCA preservatives in ground contact
2000 - IRG/WP 00-30223
Copper-chrome-arsenate (CCA) preservatives have been use extensively in New Zealand since the mid-1950s for a wide range of ground contact uses, radiata pine being the main species treated. They have been the subject of a comprehensive field testing programme in up to five sites in New Zealand, the earliest tests being established in 1955. Main factors affecting performance have been formulation t...
M E Hedley, D R Page, B E Patterson
Leaching of copper, chromium and arsenic from CCA-treated slash pine heartwood
1994 - IRG/WP 94-50020
Drying green slash pine with any of three high temperature drying schedules produced a product in which both the sapwood and the heartwood could be penetrated with CCA using a modified Bethell treatment schedule. Required H3 retentions were achieved in both sapwood and heartwood, from 200 litres per m³ charge uptake. Post-treatment fixation/drying was accomplished by three different regimes, incl...
M J Kennedy, G Palmer
Bending properties of treated western hemlock plywood
1996 - IRG/WP 96-40064
This study investigated the mechanical properties of western hemlock plywood after treatment with waterborne preservatives and redrying. Unlike previously reported results for southern pine plywood, western hemlock plywood was more sensitive to redrying temperature than to preservative treatment. Generally, western hemlock plywood was affected by temperature and other variables. Losses in mechanic...
H M Barnes, A Khouadja, D E Lyon
Isolation and identification of bacteria from CCA-treated eucalypt power transmission poles
1987 - IRG/WP 1317
Bacteria have been isolated from CCA treated Eucalyptus maculata poles which possessed characteristic bacterial decay patterns. Cultures were isolated on a number of different media which had been inoculated with a splinter of degraded wood. Primary tests indicated that most isolates belonged to the genera Pseudomonas and Bacillus. The species Pseudomonas cepacia was most frequently isolated....
G A Willoughby, A C Hayward, L E Leightley
Leaching of CCA preservative from treated timber in marine environment
2001 - IRG/WP 01-30254
Knowledge on the amount of preservatives leaching out of treated wood is essential to optimise the chemical loading in various species of timber required for different end uses. In order to gain more insight into this aspect, the residual CCA content in 40 treated timber panels belonging to 14 species removed on destruction by marine organisms from a series of durability tests conducted in Kochi w...
M V Rao, V Kuppusamy, K S Rao, L N Santhakumaran
Volumes and weights of different CCA-C treated wood poles, anchor logs and crossarms of REB at air dry condition
1996 - IRG/WP 96-40073
Researches revealed the unit volumes and weights at air-dry condition (12% MC) of different poles, anchor logs and crossarms species of REB from this world. The softwood products are lighter than hardwood products. Inversely the unit volumes of softwood poles are higher than those of hardwood poles. Red pine (Pinus resinosa), radiata pine (Pinus radiata), blue pine (Pinus wallichiana), fir (Abies ...
A K Lahiry
Leaching of CCA components from treated wood under acidic conditions
1993 - IRG/WP 93-50004
The leaching of CCA components from treated wood under acidic conditions were investigated. Western hemlock treated with three types of CCA and two levels of target retention was subjected to leaching at four different levels of pH. After leaching tests, leached samples were subjected to laboratory decay and soft rot tests. The amount of CCA components leached was dependent on acidity of leaching ...
Jae-Jin Kim, Gyu-Hyeok Kim
Effects of artificial UV weathering and soft rot decay on heat treated wood
2005 - IRG/WP 05-40302
Oil and inert gas oven heat treated pine wood strips 100 µm thick were mildly heat treated (200°C, 30 mins linseed oil, 120 mins oven). Following treatment, specimens were exposed to UV weathering (300 hours) and decay by the soft rot fungus, Chaetomium globosum. The effects of each treatment were assessed by zero span tensile testing, microscopy and by FTIR.
Tensile testing of heat treated s...
M D C Hale, S C Ghosh, M J Spear
Changes to New Zealand Timber Treatment Specifications
2004 - IRG/WP 04-20288
Changes have been made to the New Zealand timber treatment specifications in response to frequent incidences of decay in framing timber and doubts about the long-term performance of tributyltin formulations when used in exposed situations.
Changes have been made to Hazard Class H1 to allow a level of treatment to provide short to medium decay resistance to framing which would protect it, should l...
M E Hedley
The hydrolysis of organo-boron compounds in treated particleborard
2000 - IRG/WP 00-40180
Standard particleboard (manufactured for interior applications) was treated with trimethylborate and modified trimethylborate and then left to hydrolyse for specified periods. The percentage residual trimethylborate was determined by placing samples in kerosene and analysing the kerosene for boron after 3 days of leaching. There was a significant correlation between the percentage hydrolysis of tr...
K M Filcock, P Vinden