Soft rot decay in CCA treated eucalypts in Queensland - A comment
1986 - IRG/WP 1301
A survey has been completed concerned with the distribution and severity of groundline soft rot decay in the CCA treated sapwood of eucalypt poles in Queensland. The survey encountered some 1000 poles of which 55% were slightly, 28% moderately and 17% severely decayed. Soft rot decay was more severe in urban than rural locations. Embedment of poles in concrete resulted in severe soft rot. No signi...
L E Leightley
The potential for reuse of treated wood poles removed from service
1993 - IRG/WP 93-50001-18
Poles removed from service in Ontario and Quebec, Canada were characterized by age, wood species, preservative type, residual preservative, dimensions and condition. Based on this charactarization, the potential for reuse as round poles or posts, sawn posts, timbers and lumber, cedar roof shingles and firewood was assessed. A pilot study was conducted to evaluate the recovery and grade of lumber p...
P A Cooper
Further studies on soft rot decay in CCA treated Eucalyptus power transmission poles in Queensland, Australia
1980 - IRG/WP 1115
Preliminary results on the examination of fungi isolated from CCA treated Eucalyptus power transmission poles were presented at the 10th Annual IRG Meeting. Since then further examination and identification of fungal isolates has been completed together with screening tests for wood decay ability and tolerance to creosote and CCA and its components. Chemical analyses for CCA retention have also be...
L E Leightley
The new method of detecting decay in poles
1984 - IRG/WP 2229
In 1982 the Swedish Telecoms Administration in corporation with the Swedish Dog Training Centre started to investigate the possibility of using dogs for detecting decay in poles. At present two German Sheppheards and two Labrador Retrievers are in operation and the results have up to now well fulfilled our expectations. The following results have been obtained: 1.) The dogs can with high reliabili...
A Ammer, B Svedberg
Comparison of the anti-fungal efficacy of Cobra with drill perforation on oscillating pressure treated spruce transmission poles -Laboratory test
1988 - IRG/WP 3469
A laboratory method for measuring the depth of penetration of the fungicidal concentrations effective against basidiomycetes (brown rot) was developed. The tests on CCB oscillating pressure treated spruce transmission poles have shown that the depth of salt penetration can be increased by about 10 mm by a drill perforation before the impregnation. An even better penetration is reached, however, if...
E Graf, B Zgraggen
Studies and experiences of occurrence and development of soft rot in salt-treated poles of pine (Pinus sylvestris) installed in Swedish transmission lines in the years 1940-1945
1977 - IRG/WP 277
The present work describes the result of microscopic examinations of some 2,000 borings extracted from 20 to 23-year-old salt-treated poles (Scots pine) from the southern and central parts of Sweden. The purpose was to map out the occurrence of soft rot in Sweden and its influence on the mechanical strength of the poles as well as to contribute to the development of new and more satisfactory metho...
H Friis-Hansen
Treatment groups and remedies for CCA treated hardwood and softwood poles
1999 - IRG/WP 99-40142
Different hardwood and softwood species from Bangladesh and Bhutan was investigated regarding density, green fiber stress, natural durability of heartwood and CCA treated sapwood, CCA treatability grades, sapwood thickness, and kiln-drying properties for long term use as electric poles. These properties along with the past service records for nineteen years, separated ten heardwood and five softwo...
A K Lahiry
Studies in an accelerated soil bed facility on the decay susceptibility of U.K. grown spruce and pine poles treated with copper/chrome/arsenic (CCA) by pressurised sap-displacement. Part 1: Setting up of soil beds and initial soft rot results
1990 - IRG/WP 2344
The paper describes the methodology used in the construction and early operation of an accelerated soil bed facility used to examine the decay susceptibility of U.K. grown Scots and Corsican pine and Sitka and Norway spruce treated with C.C.A. by high pressure sap-displacememt. The design and control of the facility as well as the preparation, soil exposure and soft rot decay analysis of quarter p...
A Bruce, S D Hainey, G M Smith, B King, P D Evans
Fluoride and chromium concentrations in soil adjacent to remedially treated distribution poles
1996 - IRG/WP 96-50066
Soils adjacent to Rentex treated 'on-line' distribution poles were analysed for total fluoride and chromium content for comparison with background values of these elements. Soil samples 6 cm and 25 cm downslope of selected poles were recovered at 1 week, 1 month, 6 and 12 months after treatment. Background soil samples were taken 50 m from the poles at sampling times. Fourteen po...
D C R Sinclair, G M Smith, A Bruce, H J Staines, P Durrant
Quantification of creosote migration down wooden poles and the prevention of its depletion during flood irrigation
1994 - IRG/WP 94-50032
Polyethylene field liners heat-shrunk onto soil-contact surfaces prevented decay of creosote-treated Eucalyptus grandis vineyard poles under flood-irrigation. The present work quantified losses of creosote from these poles after six and 24 months' service. After six months' service the mean creosote retention of unlined poles above the ground line was 12.62% (m/m dry wood), with ...
M Behr, A A W Baecker
LCA examination of preservative treated timber products and alternatives; initial results
1995 - IRG/WP 95-50040-04
Co-operative development of an LCA methodology suitable for application to preservative treated products has been carried out, based on scoping assessments of two products, CCA treated fenceposts and creosote treated distribution poles. The general results of these scoping exercices are described, based on the CCA case study. These include the identification of critical stages in the life-cycle on...
W Hillier, R J Murphy, D J Dickinson, J N B Bell
Quantification of creosote and fluoride in remedially-treated poles
1997 - IRG/WP 97-40097
Three creosoted transmission poles were put into service in 1961 and they were subsequently remedially-treated with a proprietary fluoride remedial paste formulation in 1981. The poles were removed from service in 1996 and their ground-contact regions were analysed for creosote and fluoride contents. It was found that the poles were undecayed. Creosote retentions decreased down the profiles of the...
B P Hill
A bioassay of remedially treated pole material
1987 - IRG/WP 3453
Stubs prepared from treated and untreated utility poles were installed in a test plot and pressure spade treated at the groundline with one of four preservative greases. At one and three year intervals, core samples were removed from the stubs and the improvement in the preservative efficacy due to the greases was assessed. The bioassay investigation showed that only bis(tributyltin) oxide (TBTO) ...
J N R Ruddick, L Parker
Removing Cu, Cr and As from CCA treated yellow pine by oleic acid
2003 - IRG/WP 03-50202
In this study, CCA treated yellow pine utility poles were cut into three different dimensions and 4 different pH levels (2, 2.5, 3.5 and 5) of Oleic acid was used. The leached wood samples were collected at the end of the 1, 3, 7 and 14 days to determine the remaining Cu, Cr and As concentrations. The concentrations of Cu, Cr and As were determined by X-RF. The effects of pH, dimension and duratio...
E D Gezer, Ü C Yildiz, S Yildiz, E Dizman, A Temiz
The effect of kerfing on check formation in treated white spruce (Picea glauca) poles
1981 - IRG/WP 3167
62 white spruce poles, 6 m in length, were cut from full size utility poles commercially pressure treated with preservative. 21 of the poles were treated with pentachlorophenol, while of the remainder, all of which were treated with ammoniacal copper arsenate, 22 were kerfed and 19 were unkerfed. The poles were installed in the Westham Island field test site, near Vancouver, and inspected annually...
J N R Ruddick
Relating CCA fixation to leaching of CCA components from treated products
1995 - IRG/WP 95-50045
The relationship between chromium fixation in CCA-C treated wood, as determined by CrVI analysis of solution expressed from treated wood and the leaching of Cu, Cr, As and CrVI in a simulated rain test are evaluated for dimension lumber (2"x6") and pole sections. Leachate concentrations after 2 hour exposure to a misting spray (about 300 mm cumulative rainfall) decrease rapidly with increased degr...
P A Cooper, R MacVicar, Y T Ung
Programme d'études sur le pentachlorophénol
1993 - IRG/WP 93-50001-09
In 1989, Hydro-Québec began a study program on pentachlorophenol (PCP), with a view to ensuring safe management of the product at all stages of its utilization. The topics under study include storage of treated poles, behavior of PCP in the environment, soil decontamination, water treatment, characterization and disposal of treated wood waste, and assessment of substitutes. This paper summarizes ...
G Beaulieu, A Bériault, R Chénier, L Houde
Soft rot in heartwood of preservative-treated pole stubs of Eucalyptus cypellocarpa L. Johnson
1983 - IRG/WP 1204
Pole stubs of Eucalyptus cypellocarpa L. Johnson, treated in the sapwood with certain waterborne preservatives and exposed for 21 to 23 years in a dry tropical region were severely soft-rotted in the heartwood, as well as the sapwood. They broke with a brash fracture when stress tested (loaded as a cantilever) in the field. The severe soft rot in the heartwood was not detected by the knife test or...
J E Barnacle, G C Johnson, M A Tighe
Residual CCA levels in CCA treated poles removed from service
2000 - IRG/WP 00-50152
Fifty-two CCA treated poles removed from service after 1 - 50 years were sampled at different depths from their below ground and above ground zones and the preservative levels and mass balances related to the location in the pole and pole age. Generally CCA retentions were still well above the toxic threshold for decay in even the oldest poles. This confirms the good leach resistance of CCA and th...
P A Cooper, D Jeremic, J L Taylor
Leachability of active ingredients from some CCA treated and creosoted poles in service. A progress report after 10 years testing
1990 - IRG/WP 3627
CCA K33 TYPE B treated or creosoted poles, 10 pieces of each treatment type, have been monitored from the treatment plant to an electricity line, which was build up in Southern Finland in 1978. Preservative retention was determined by taking borings at four different levels: 1.5 m from the top end, 1 m above ground line, ground line and 0.5 m below ground. Determinations were made before setting u...
A J Nurmi
Effect of barriers on moisture content of treated and non-treated utility poles
2007 - IRG/WP 07-40369
The potential for non-biocidal barriers to slow moisture sorption was investigated using butt treated western redcedar poles immersed in either water or moist soil over a 2 year period. Moisture sorption was initially slowed by the barriers, but openings at the bottoms of the barriers eventually allowed moisture to migrate upward. Moisture levels in wrapped poles eventually reached those found in...
C S Love, J J Morrell
Metal Migration from Douglas-fir Poles Treated with Ammoniacal Copper Zinc Arsenate According to Best Management Practices
2010 - IRG/WP 10-50272
The potential for migration of metal components from ammoniacal copper zinc arsenate treated (ACZA) poles was examined using pole sections treated using Best Management Practices. Copper and zinc levels were highest in runoff collected following the first rainfall events, then declined. Copper and zinc levels in runoff averaged 20 ppm and 5 pm respectively. The metal levels were then used to pr...
J J Morrell, C S Love, C Freitag
Performance superiority of CCA-C treated wooden jetty poles and piles used for 30 years in Bangladesh against marine borers
2012 - IRG/WP 12-30582
Observational study along with previous investigation and records revealed that chromated copper arsenate type C (CCA-C) impregnated southern pine poles and piles of jetty constructed in most vulnerable brackish water in Bangladesh are stable and resistant to attack of all types of marine borers after 30 years of use. It is evident from the service records of other construction materials that CCA-...
A K Lahiry
An assessment of soft rot in preservative-treated poles in two test sites and two network areas in New South Wales
2013 - IRG/WP 13-10801
This document presents an extended summary of recent investigations into soft rot attack of preservative treated power poles from the re-inspection of samples selected from two field sites and two in-service trials located in New South Wales, Australia. The in-ground sapwood of selected poles was assessed by probing and, after core sampling, by microscopy to determine the severity and extent of s...
W D Gardner, M A Powell, C Kirton
Incidence of soft rot attack on preservative treated Douglas-fir poles: a preliminary survey
2014 - IRG/WP 14-10818
Occurrence of soft rot decay in Douglas-fir poles treated with ammoniacal copper zinc arsenate (ACZA) or pentachlorophenol in oil was studied. Soft rot was less prevalent in poles treated with penta, but some soft rot was found in approximately 20 % of poles examined. Soft rot was more common in poles treated with ACZA, and, when present, was found in almost 20% of the cells examined. The potenti...
P Torres Andrade, J J Morrell