A comparative study of CCA type C and B treated poles in service
1993 - IRG/WP 93-50001-05
CCA K33 type B and C treated utility poles, 9 pieces of each treatment type, were analyzed for preservative retention after 11 years in use. Borings were taking 1 m above and 0.3 m below the ground line. Also total amount of copper, chromium and arsenic was determined in soil surrounding the poles. The solubility of these active components in soil was monitored by using different leaching procedur...
A J Nurmi
The shower test method. A leaching test for assessing preservative losses from treated timber under simulated open storage conditions
1993 - IRG/WP 93-50001-04
In the late 1980's against the background of increasing environmental concern a laboratory based accelerated leaching test method for assessing preservative losses-from stored, treated timber was developed by the Dutch organisation for applied Scientific Research (TNO). This test method quantifies the amount of specific preservative components which leach from treated timber under simulat...
J B G A Havermans, W J Homan, M J Boonstra
Premature decay of CCA-treated pine posts in horticultural soils - An overview
1984 - IRG/WP 1241
The recent discovery in New Zealand of early decay in CCA-treated pine posts set in horticultural soils led to the establishment of a comprehensive research programme. The objectives and outline of this programme are presented together with an overview of research progress to date. Results suggest that premature decay of CCA-treated timber is restricted to material placed in highly cultivated soil...
J A Butcher
Fixation of chromated copper arsenate (CCA) wood preservative in Australian hardwoods: A comparison of three Eucalyptus species
1996 - IRG/WP 96-30107
New environmental guidelines for the management of CCA treatment plants were released in Australia in 1995. This has stimulated interest in techniques for controlling or accelerating the fixation of CCA in freshly treated timber products. The ability to understand, then effectively control and/or accelerate fixation of CCA in treated timber products can be an economic, technical and environmental ...
J Holmes
A Preliminary Report on the Properties of Engineered Wood Composite Panels Treated with Copper Naphthenate
2005 - IRG/WP 05-40294
This paper reports on our preliminary investigation of the properties of randomly oriented strandboard which had waterborne or powdered copper naphthenate (CuN) incorporated into the board during manufacture. When compared to zinc borate-treated controls (ZnB), the mechanical properties of strandboard (MOR, MOE, work-to-maximum load, internal bond strength) were not adversely affected by treatmen...
J W Kirkpatrick, H M Barnes
Leachability And Decay Resistance of Copper-Treated Wood
2004 - IRG/WP 04-30337
Samples of scots pine sapwood (Pinus sylvestris L.) were treated with solutions of (Copper II sulfat-5 hydro + fluoroboric acid) and (Copper II sulfat-5 hydro + fluoroboric acid + boric acid) in order to determining to leachability and decay resistance against brown rot fungus (Postia placenta) and white rot fungus (Coriolus versicolor).
Results indicated that the copper in treated wood is less s...
A Temiz, T Nilsson, I Deemirtas, Ü C Yildiz
Sampling variation in a copper chrome arsenic treated power transmission pole
1990 - IRG/WP 2351
The Queensland Forest Service routinely samples poles treated at all treatment plants throughout the State. Each treatment plant is issued with a Certificate of Registration and the accompanying documents list the different levels of preservative retention required for performance in various service conditions. The posted levels represent the.minimum permissible, and it is to these concentrations ...
J Norton
Bending properties of TCMTB-treated Southern pine sapwood using supercritical carbon dioxide impregnation process
1997 - IRG/WP 97-40080
The effects of elevated pressure and treatment with thiocyanomethylthiobenzothiazole (TCMTB) on the bending properties of Southern pine sapwood were evaluated at pressures ranging from 1,800 to 3,600 psi. All bending properties were affected to some extent by supercritical fluid treatment. Modulus of elasticity and work to maximum load were not significantly affected by pressure levels. Modulus of...
Gyu-Hyeok Kim, S Kumar, E S Demessie, K L Levien, J J Morrell
Decrease of the antidecay resistance of beech wood treated with organotin fungicides after its natural ageing
1998 - IRG/WP 98-30185
The antidecay resistance of beech-wood samples (120 x 8.5 x 8.5 (MM)) treated with tributyltin fungicides gradually decreased due to prolongation of their natural ageing:
tributyltin fungicides (TBTO, TBTS, TBTCA, TBT-DEDTK were applied by pressure impregnation technique in ethanole solutions (c = 0. 1%, 0.33% or 1%);
treated beech-wood samples were naturally aged without their contact with grou...
L Reinprecht
Soft rot studies on CCA treated eucalypt power transmission poles
1981 - IRG/WP 1132
Initial results found for sixty CCA treated eucalypt poles, from a soft-rot survey are discussed. Retentions of CCA within above and below ground pole samples were variable. The variation was attributed mostly to biodegradation and effect of soil environment, rather than leaching. Bacterial decay was found in many poles and was severe in some cases. Although found in the presence of soft-rot decay...
L E Leightley
Effect of vegetable compost on leaching of CCA components from treated wood - An Update
1995 - IRG/WP 95-50048
In an earlier study, the effect of compost on CCA-C leaching was compared with leaching losses under different exposure conditions. Small treated cubes (25 mm³) were destructively sampled over a 12 month period and the residual CCA determined for exposure to compost in a compost bin, exposed to natural rain and buried in soil. This study provides a comparison after 3 years of samples exposed to c...
P A Cooper, Y T Ung
Moisture condition in treated wood exposed outdoors. A progress report
1989 - IRG/WP 3533
Wood treated with water-borne preservatives, mainly CCA (copper/chromium/arsenic), CCB (copper/chrome/boron) or CC (copper/chrome) is often said among users in Sweden to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed but no field tests have been carried out in Sweden to study this phenomenon. In 1986 a project was started to compare water absorptio...
M-L Edlund, C E Sundman
Sampling rates and the probability of detecting defective treatment in the sampling of preservative treated timber
1987 - IRG/WP 2277
When attempting to enforce standards of penetration and retention set for treated timber, the regulating authority must establish a sampling or inspection scheme which will prevent large quantities of substandard product entering the market. On the other hand, the scheme should not penalise treaters for the small quantities of such material which are inevitably produced by any industrial process. ...
M J Kennedy, L E Leightley
Relationship between bond strength and surface characteristics of CCA-treated Douglas-fir
1993 - IRG/WP 93-30008
Chromated-copper-arsenate (CCA) treated Douglas-fir was laminated using a commercial phenol-resorcinol resin. CCA treatment enhanced the water repelleney of wood espeeially in the presence of extractives. However, the shear strength of CCA treated wood was 12% lower in dry condition and 38% lower in wet condition after six cycles of vacuum-pressure test than that of untreated wood. Slight removal ...
K Yamamoto, J N R Ruddick
An investigation of organotin compounds in treated wood using Mössbauer spectroscopy
1983 - IRG/WP 3249
The influence of sample preparation on the 119mSn Mössbauer spectrum of tributyltin chloride in ponderosa pine was investigated. Initial studies with sawdust and compressed discs concluded that the latter were clearly superior. Further studies showed that compressed discs prepared from 0.4 g of treated wood and 0.1 g of cellulose were robust and gave excellent Mössbauer spectra. The possibility ...
J N R Ruddick, J K Ingram
Leaching Characteristics of Copper in Copper Treated Wood
2003 - IRG/WP 03-30316
The leaching characteristics of copper in copper treated bamboo and other wood species such as slash pine and poplar has been conducted in this paper according to AWPA M11-87 standard, the result indicates that:
--Copper fixation rate of salts from organic acids such as citrate and oxalate and malate is less than other non-organic acid formulations.
--Copper fixation rate of oven-dried bamboo sa...
Mingliang Jiang, Junliang Liu, Daochun Qin, Yamei Wang, Zehui Jiang
Durability of plywood made from soft- and hardwoods assessed according to ENV 12038 after artificial and natural ageing
2000 - IRG/WP 00-20191
Plywood was prepared from Norway Spruce and pure heartwood of Douglas Fir, Scots Pine, European Oak, False Acacia and Macoré using a phenol-formaldehyde glue. The panels of 38 mm in thickness were pre-conditioned according to the following procedures: a) 12 weeks storage at 20°C/65% rh, b) 2 weeks artificial weathering (with rain and UV-radiation at changing temperatures), and c) a natural weath...
H Leithoff, R-D Peek
A study of decay type variability in variously treated Fagus sylvatica and Pinus radiata field test stakes exposed at a vineyard for 30 - 45 months
1998 - IRG/WP 98-10271
Pinus radiata test stakes were treated with 10 kg/m3 of CCA plus 4 lower retentions in a geometric series of 1.5. Fagus sylvatica was treated with 15 kg/m3 and 2 lower retentions. Both timber species were also treated with equivalent retentions of various new generation preservatives (P. radiata was also treated with creosote). Whilst these stakes were exposed at 11 sites in New Zealand (NZ) and 2...
R N Wakeling, A P Singh
Leaching and fixation characteristics of chrome-copper-fluoride-zinc (CCFZ) treated wood
1996 - IRG/WP 96-30096
The leaching characteristics of radiata pine sapwood blocks treated with CCFZ were evaluated by the AWPA standard leaching test. The rate of fixation of the preservative components in CCFZ treated radiata pine were also evaluated by quantitative analysis of solution expressed from the treated wood. Both leaching and fixation characteristics of CCFZ were compared with CCA-Type C treated wood sample...
Gyu-Hyeok Kim, Jong-Bum Ra
An in-ground natural durability field test of Australian timbers and exotic reference species. Part 5: Extensive data from a site where both decay and termites are active. Results from a full-replicated set of heartwood specimens from each of ten myrtaceous hardwoods after 18, 19 and 20 years' exposure - A discussion paper
1988 - IRG/WP 2324
Extensive data are presented on the decay situation, the termite situation and the decay-termite associations; all gathered from a fully-replicated set of heartwood specimens of 10 hardwood timbers after 18, 19 and 20 years' exposure in the ground at a single test site, i.e. a semi-arid steppe site. Sixteen tables are presented in addition to the one table providing the rating data; the l...
J D Thornton, G C Johnson, J W Creffield
Kiln drying of CCA-treated wood - Some safety and environmental considerations
1987 - IRG/WP 3443
Vapours and condensate from a condenser kiln in which CCA-treated wood was being dried have been collected and analysed. The concentrations of arsenic, copper and chromium found in the vapours from the drying process were well below Swedish threshold limit values. The contents of arsenic and chromium were also low in the condensate, although the copper content was fairly high. The latter result wa...
J Jermer, B Lundberg
Applications of the shower test. Part B: Results from CC and CCB treated wood: influence of fixation process
1993 - IRG/WP 93-50010
This report outlines the results of shower tests conducted on CC and CCB treated wood. The results indicate the fairly good fixation of chromium and the reasonable fixation of copper in CC and CCB formulations, as judged by the leaching limits within the Environmental Regulations. In general boron leaches to a higher extent than chromium and copper. The shower test has proven to be a useful qualit...
W J Homan, H Militz
Assessment of dehydrogenase activity, fluoride content and total chromium content of soil profiles exposed to preservative treated wood within a model system
1993 - IRG/WP 93-10015
The development and prospective use of a closed model system to facilitate study of a number of indicators of environmental impact of wood preservatives laboratory conditions has been described (IRG/WP/2395-92). Chemical analysis of leachate samples collected from drained soil profiles containing creosoted pole sections remedially treated with a chromated fluoride preservative indicated small incr...
G M Smith, D C R Sinclair, A Bruce, H J Staines
An illustrated comment on the soft rot problem in Australia and Papua New Guinea
1977 - IRG/WP 296
A brief survey of soft rot is presented, with particular reference to attack of preservative treated hardwood transmission poles in Australia. Possible explanations of why the preservatives are failing to protect the poles are discussed, together with current efforts to produce control measures. Examples of soft rot in variously treated eucalypt or pine specimens are shown to illustrate the morpho...
H Greaves
Appearance of PEC-treated poles in service
1985 - IRG/WP 3323
Poles treated with conventional high temperature creosote (HTC) are banned for use in Australia by the major union handling them. Pigment emulsified creosote (PEC) is an acceptable alternative because it provides much dryer and cleaner commodities than does HTC. More than 5000 poles have so far been treated with PEC and many are being installed into service. The brown pigmented PEC 30 B has given ...
H Greaves, C-W Chin, K J McCarthy, J B Watkins