On the use of miniaturized wood specimens in fungal decay experiments – mini-blocks versus EN 113 test specimens
2024 - IRG/WP 24-11044
Preliminary evaluation and classification of wood durability against decay fungi using laboratory monoculture experiments has been a longstanding practice because these tests offer quicker results than field tests. Various methods, including miniaturized specimen formats and different incubation periods, have been explored to expedite decay processes and assess wood preservation efficacy. The 'min...
C Brischke, G Alfredsen
Exposure tests on railroad ties treated with DOT
2024 - IRG/WP 24-20705
Keruing railroad ties were treated with disodium octaborate tetrahydrate (DOT) to retentions of 0.7 to 1.7% boric acid equivalent (BAE) and selected borate treated ties were subsequently over treated with creosote/diesel fuel mixture. The treated ties were exposed in a simulated railway track test bed in Malaysia. The leaching of borate was measured over 5 years. BAE in the ties after 5 years of e...
L Arthur, J-W Kim
International joint field trial on the moisture performance of wood – Set up and first results
2024 - IRG/WP 24-40996
Wood durability to decay stems from its inherent resistance to fungi resistance to fungi. In this regard, wood's ability to withstand moisture uptake plays an important role as the lower threshold for wood decay is a moisture content of 25%. However, the aspect of moisture resistance is not yet sufficiently emphasized as a durability factor, both in the assessment of durability as a material prope...
C Brischke, et al. (33 co-authors)
Evaluation of the water exclusion ability and inherent bioactivity of heartwood against decay in Japanese and European wood species via above-ground exposure and water absorption tests
2024 - IRG/WP 24-40998
The natural durability of wood has been thought to mainly depend on bioactive extractives and the water exclusion ability. To clarify the contribution of each factor to wood durability, above-ground exposure tests were conducted on Japanese and European wood species. A double-layer test was carried out using heartwood specimens of four wood species, i.e., Japanese cedar, Japanese cypress, Scots pi...
T Osawa, R Noda, K Yamamoto
Performance of Chromated Copper Arsenic Treated and Untreated Papua New Guinea Timber Species in Marine Exposure after 95 weeks (664 days)
2025 - IRG/WP 25-11062
A Masters’ thesis on the topic was successfully completed and submitted in September 2024. The thesis reports on results obtained from exposure of five Papua New Guinea (PNG) timber species (obtained from secondary growth or plantation grown) after 218 days (31 weeks) in a marine environment in sub-tropical Queensland, Australia. The species studied were: Hopea iriana (Hopea, heavy), Vitex cofas...
E Galore, J Norton, T Singh
Natural and enhanced durability of wood exposed above ground
2025 - IRG/WP 25-11079
Understanding and predicting the durability of wood is essential for ensuring its effective use, long-term reliability, and sustainability in various applications. To address this need, the "Wood Above Ground" project was initiated in 1999 at the Danish Technological Institute (DTI) to investigate the natural durability of wood species under a wide range of above-ground exposure scenarios. This ex...
R Digaitis, J Stenbaek, A W Christof, N Morsing, B Lindegaard
Real-time evaluation of connected in-ground termite stations in laboratory colonies of Coptotermes gestroi and Prorhinotermes sp.
2025 - IRG/WP 25-11082
Subterranean termites represent a major challenge in infestation management and monitoring. This study evaluates the effectiveness of connected in-ground stations for termite control, incorporating an advanced electronic device developed and patented by Groupe Berkem (Novaterm®). These stations are linked to a gateway unit that collects the detected signals and transmits them remotely via a 4G ne...
M Butin, F Chopinet, S Savriama, D Messaoudi
ProFume® pre-shipment treatments of round wood against infestations with bark-breeding beetles - technical improvements
2025 - IRG/WP 25-41017
Since 2018, climate change and temperature shifts associated with this, increased the occurrence of bark-beetle induced calamity wood. Consequently, the significant Ips typographus outbreak in German spruce forests prompted harvesting, thus temporarily increasing timber market supply. This situation made Germany a key player in Europe’s log exports to China. In order to prevent the further sprea...
S Kümmritz, G M Kroos
Moisture uptake in CLT during the construction phase: real construction conditions versus specimens exposed to environment
2025 - IRG/WP 25-41019
The rapid growth in the use of Cross-Laminated Timber (CLT) in construction highlights the need to address durability concerns, particularly in regions with less experience in Mass Timber Construction and favourable climatic conditions for the biological degradation of wood, such as Mediterranean countries. A lack of awareness and deficient construction management can negatively impact the public ...
D Lima, S Duarte, J M Branco, L Nunes (†)
Experimental characterizing of liquid water uptake and release – key to understand moisture-induced decay risk analysis
2025 - IRG/WP 25-41020
Wood can absorb water vapour (sorption) or liquid water (capillarity). Moisture from liquid water (rain, spray water) is often a problem for the performance of wood products used in outdoor structures. Wood is prone to biodegradation when is it too moist for too long periods. Experimental studies that allow conclusions to be drawn about the practical use of wood water uptake are limited due to the...
M Nopens, J T Benthien, J Trautner, C Brischke
Evaluation of moisture exclusion ability of wood using double-layer outdoor exposure tests
2025 - IRG/WP 25-41021
The material resistance of wood to decay must be due to the combined effects of heartwood extractives and the moisture content state. Evaluating the moisture exclusion ability of wood is important for assessing its durability in outdoor use. We conducted previously double-layer outdoor exposure tests and investigated the relationship between moisture content over time and the progress of decay usi...
T Osawa, R Noda, K Yamamoto