Effectiveness of wood preservatives by IUFRO's method
1984 - IRG/WP 3305
Pinus elliottii and Eucalyptus saligna stakes treated with 4.9; 6.9; 9.6 and 13.5 kg/m³ of CCA-A, CCA-C and CCB and with 30-50; 60-80; 90-110 and 120-140 kg/m³ of Benzotar and CNSL (cashew-nut shell liquid) were exposed in seven test sites in Sao Paulo State, Brazil. After 4 years it was concluded that the mean useful life of untreated Pinus elliottii stakes was 8 months and of untreated Eucalyp...
G A C Lopez, E S Lepage, O B Neto
Use of compression strength loss for measuring decay in the soil block test
1996 - IRG/WP 96-20083
The possibility of using radial direction compression strength of wood, rather than mass loss, was evaluated for both a brown-rot fungus (Gloeophyllum trabeum) and white-rot fungus (Trametes versicolor). With untreated pine wafers (5 x 19 x 19 mm³ - l x r x t) exposed to Gloeophyllum trabeum in a soil block test for five days, the compression strength loss was nearly 50% compared to a 5% mass los...
D D Nicholas, Zhongwei Jin
IRG/COIPM INTERNATIONAL MARINE TEST - to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water. Progress Report 19: Report on the condition of specimens at Sekondi, Ghana after 42 months
1984 - IRG/WP 4109
The results of the first formal inspeation of CCA- and CCB- treated test panels exposed at Sekondi, Ghana, in June 1980, are presented. All untreated control panels of both reference and local species have been destroyed. Of the% CCA- treated specimens, only those of Pinus sylvestris (reference species) and Mitragyna stipulosa (local species) have not been attacked. 3% CCB-treated local species ha...
F F K Ampong
Comparison of two laboratory methods for screening potential anti-sapstain chemicals
1993 - IRG/WP 93-10036
Two methods were used to screen a number of potential anti-sapstain chemicals in the laboratory. In one method miniature boards of freshly felled Scots pine sapwood were dip treated with the candidate chemical, sprayed with a suspension of stainers or moulds and incubated for five weeks. In the other method antibiotic assay discs were treated with precise quantities of chemical, plated out on malt...
S M Gray, D J Dickinson
New experiences with Dry Rot in Danish buildings, heat treatment and viability tests
1989 - IRG/WP 1423
An increasing number of concealed dry rot attacks, especially in older multi-storey houses under renovation, have been detected during the last few years. A necessary consequence is a demand for cheaper methods of repair, compared to the standard method used in Denmark for many years otherwise severely attacked houses will by pulled down. A heat-treatment has been developed and tested in practice....
A P Koch, C Kjerulf-Jensen, B Madsen
Termite resistance classification of some tropical and temperate species based on the laboratory choice test results against formosan termite, Coptotermes formosanu
2004 - IRG/WP 04-20291
The results of classification of termite durability were varied. We carried out
laboratory evaluation of the classification of termite durability on various species by
the choice test against formosan termite, Coptotermes formosanus. We classified five
grades (very sensitive to very resistant). According to our results, azobe, ipe, keruing,
intsia, kapur, yellow meranti, jarraah, malas, cypres...
K Suzuki
Resistance of borate-treated lumber to subterranean termites under protected, above-ground conditions
2000 - IRG/WP 00-30239
An experiment to simulate the dodai (sill plate) of the Japanese houses was conducted at the termite field test site of Wood Research Institute in Kagoshima, Japan where two economically important subterranean termite species [Coptotermes formosanus Shiraki and Reticulitermes speratus (Kolbe)] are established. DOT(disodium octaborate tetrahydrate)-treated hem-fir samples [Tsuga heterophylla (Raf.)...
K Tsunoda, A Adachi, T Yoshimura, A Byrne, P I Morris, J K Grace
The accelerated L-joint test method for determination of the out of ground natural durability
1998 - IRG/WP 98-20146
The accelerated L-joint test incorporates a moistening device and uses a close end water trap in an open joint connection with a laminated tenon member consisting of the perishable reference wood species scots pine sapwood and beech.
After one year of exposure it is possible to show a distinct identification of natural durability classes 4 and 5 against the more durable wood species. Both weight ...
J Van Acker, C Brauwers, M Stevens
Aureobasidium or Hormonema? A Genetic Approach.
2004 - IRG/WP 04-10529
Aureobasidium pullulans is the main organism causing disfigurement of coatings on wood and the surface of exposed timber. This disfigurement of timber in-service is referred to as “bluestain in-service”. A. pullulans is also associated with the sapstaining of dead wood in the forest and in-service. A. pullulans is noted for its highly variable growth forms (polymorphisms). This variability pre...
M J Ray, D J Dickinson, M Buck
Fouling organisms as indicators of the environmental impact of marine preservative-treated wood
1995 - IRG/WP 95-50063
This study evaluates the use of fouling organisms (epibiota) to assess the environmental impact of preservative treated wood. This paper presents initial findings from treated panels exposed for 6 months at Sagres, Algarve, Portugal. Panels were treated with CCA, two copper-containing quaternary ammonium (ACQ) formulations and creosote, with nominal retentions from 10 to 40 kg/m³ (creosote 25 pcf...
R M Albuquerque, S M Cragg
Marine performance of preservative treated Southern pine panels. - Part 1: Exposure in Newport, Oregon
2000 - IRG/WP 00-10368
The ability of selected wood preservative to protect southern pine sapwood against marine borer attack was evaluated over a 6 year period in Yaquina Bay, Oregon. The site exposed the wood to potential attack by both Teredo navalis and Limnoria spp. Both creosote and CCA provided excellent protection at moderate retentions, while ACQ produced slight differences in performance depending on the coppe...
R G Rhatigan, J J Morrell, A R Zahora
The ecotoxicology assessment of wood preservatives and their active ingredients by means of germination tests using cress - A critical consideration
1999 - IRG/WP 99-50125
With putting the Biocidal Products Directive 98/08/EC (BPD) in place an environmental risk assessment for wood preservatives and impregnated timber is requested. To assess possible risks, suitable test methods are required, which reveal the ecotoxicological profile including environmental fate and behaviour of treated commodities. Germination and growth tests could contribute to the determination ...
P Jüngel, A O Rapp, E Melcher
Studies on the determination of the durability of wooden poles and fence posts
1982 - IRG/WP 3195
This study was carried out by the Forestry Research Institute. 5 Turkish main tree species, Oak (Quercus), pine (Pinus sylvestris), beech (Fagus orientalis) and Fir (Abies bornmülleriana) wooden poles and fence posts, were treated with Tanalith-U and creosote applying pressure process. Tanalith-U was applied by full-cell process and creosote was applied by empty cell process. Treated and untreate...
R Ilhan, O Taskin, A P Erten
Accelerated weathering test for the evaluation of wood preservative efficacy
2003 - IRG/WP 03-20262
Wood samples treated with ammonium copper quat (ACQ-1900 and ACQ-2200), Chromated copper arsenate (CCA), Tanalith E 3491 and Wolmanit CX-8 have been studied in accelerated weathering experiments.
The weathering experiment was performed by cycles of 2 hours UV-light irradiation followed by water spray for 18 minutes. The changes on the surface of the weathered samples were characterized by FTIR Sp...
A Temiz, M Eikenes, Ü C Yildiz, F G Evans, B Jacobsen
Development of a mini-block test method for the rapid evaluation of preservative performance against Basidiomycte fungi
1991 - IRG/WP 2379
Screening procedures for new biocides used as wood preservatives can be a time consuming process using conventional Basidiomycete assay procedures. This is due mainly to the long exposure periods required to achieve adequate levels of decay (weight loss) in the test blocks. A number of alternative methods have been developed but most utilise artificial substrates such as filter paper or agar in wh...
J Brown, S Caswell, G R Williams
Performance of copper-chrome formulations in ground contact in five test sites in New Zealand
1996 - IRG/WP 96-30113
Copper-chrome-arsenate (CCA), copper-chrome-boron (CCB), copper-chrome-fluoride (CCF) and copper-chrome-phosphate (CCP) have been tested at four retentions each in ground contact (25 x 50 x 500 mm³ radiata pine sapwood stakes) for 16 years in five test sites in New Zealand. Results to date show that test site characteristics have a marked effect on relative performance. In a warm and wet site (an...
M E Hedley, R N Wakeling, J Foster, B E Patterson
The potential application of rapid gas-chromatographic assay of microbial respiration to the monitoring of wood decay in field trial situations
1983 - IRG/WP 2196
Gas chromatographic detection of microbial activity (C02 production) within stakes in a field trial situation would appear to provide a sensitive, non-destructive and relatively rapid method for the quantitative assessment of preservative treatments. Most consistent results were obtained when stakes were removed from the soil, washed, saturated with water and incubated in sealed PVC tubes at 25°C...
M A Line
Preliminary results from the field experiment to determine the performance of preservative treated hardwoods with particular reference to soft rot. The four reference timber
1980 - IRG/WP 3164
The results given in the Tables 1-4 each refer to one of the four reference species treated with four solution concentrations of CCA as recorded from each test site. The species are: Alstonia scholaris, Betula pendula, Fagus sylvatica, Pinus sylvestris. The treatments were: Untreated, 0.66% CCA, 1.53% CCA, 3.01% CCA, 5.60% CCA. Each figure is an average of the ratings recorded for each replicate o...
J F Levy, D J Dickinson
Termite likes steamed larch wood
1995 - IRG/WP 95-10113
Steamed wood of Japanese larch (Larix leptolepis (Sieb. et Zucc.) Gord.) was preferably attacked by termites. Steam treatments have often been applied to Japanese larch wood for improving its penetrability or color. For preventing termite attack on steamed timber, we have to elucidate why termite likes it. Choice tests with Coptotermes formosanus Shiraki were conducted using larch boards steamed f...
S Doi, M Kubota, M Takahashi, T Yoshimura, A Adachi
Performance of Borate-Treated Wood Against Reticulitermes flavipes in Above-Ground Protected Conditions
2003 - IRG/WP 03-30309
Termites cause economically significant damage in Canada only in a few localized areas. However, one of those is in Canada’s largest city, Toronto, Ontario. In 1996, a test was set up of borate-treated lumber above ground, protected from rain but exposed to subterranean termites (Reticulitermes flavipes) in Kincardine Ontario. The material included western hemlock and amabilis fir lumber trea...
P I Morris, J K Grace, K Tsunoda, A Byrne
Evaluation of polymeric alkylphenol polysulfide as a new wood preservative compound
2000 - IRG/WP 00-30251
At the 30 th IRG meeting held in Rosenheim, Bavaria, Germany, we reported on a Polymeric Alkylphenol Polysulfide (PXTS) which shows potential as a new non-leachable, environmentally compatible wood preservative compound exhibiting excellent biocidal efficacy. Comparative soil-block test results showed that PXTS was twice as effective as Creosote when evaluated against both white- and brown-rot fun...
J Goswami, A Abramson, R Buff, D D Nicholas
An aquaria test of the natural resistance against marine borers of some commercial timbers available in Australia
1996 - IRG/WP 96-10145
The natural resistance of the heartwood of 22 different timbers grown or commercially available in Australia was examined. Radiata pine sapwood both untreated, and treated with 5.4 kg/m³ CCA salt, was included for comparison. Small timber blocks were exposed for one year in tanks containing either Limnoria tripunctata or Lyrodus pedicellatus. Four softwood species tested were heavily attacked and...
L J Cookson
Hardwood Field Experiment: Progress Report 1977-1986
1986 - IRG/WP 3391
The international hardwood field experiment was planned in l976 and set up in same 30 different sites around the world. The test stakes include 4 reference species common to each site and in most cases at least 2 species of local importance. It was hoped that a picture of performance of a range of economically important species would be built up and at the same time provide vital background inform...
D J Dickinson, S M Gray
Leaching from field test stakes. Part 2: The distribution in and leaching from different parts of test stakes
1994 - IRG/WP 94-50026
Field test stakes treated with Boliden K33 (copper, chromium and arsenic) and Cuprinol Tryck (CT86) (copper and N-alkylbenzyldimethylammoniumchloride) respectively were exposed in ground contact at two different test fields in Sweden and rejected due to decay after 2 to 28 years. Stakes treated with the same preservatives were also exposed during 7 years above ground. The test stakes have been ana...
F G Evans, B Nossen, M-L Edlund
Stake test with ammoniacal copper in combination with different agents started in 1962
1997 - IRG/WP 97-30130
In 1962 a stake test was started with ammoniacal copper in combination with chromium, arsenic, pentachlorophenol, boron, salicylic acid, benzoic acid, sorbic acid, pyridine and tannin. Different concentrations of the copper component were used as well as the added agents. For each concentration and test site, ten stakes of Pinus sylvestris L. sapwood were treated. The stakes were set out at two te...
B Häger, Ö Bergman