Effect of soil chemistry and physical properties on wood preservative leaching
1998 - IRG/WP 98-50111
When treated wood is placed in contact with soil, complicated mass transfer and chemical reactions occur which causes the preservative components to leach from the wood. There are several factors that are known to affect the amount of chemical leached from wood. These are properties of the preservative and carrier, preservative retention, degree of fixation, exposure time, grain orientation, surfa...
Joan-Hao Wang, D D Nicholas, L S Sites, D E Pettry
The control and pretreatment decay in air seasoning Scots and Corsican pine poles in England
1990 - IRG/WP 1451
Previous work clearly showed that air-seasoned, British grown Scots and Corsican pine poles are subject to serious pretreatment decay. In order to control these infections a range of pretreatments are currently being investigated. One series of treatments is designed not only to control decay but also allow the development of mould and stain fungi in order to achieve the desired increases in poros...
D J Dickinson, A R Zahora, A P Dodson
Fixation and leaching characteristics of Douglas-fir treated with CCA-C
2004 - IRG/WP 04-50213
Fixation and leaching characteristics of CCA-treated Douglas-fir was evaluated using the expressate method and the AWPA E11-97 leaching procedure. CCA fixation, as monitored by the chromium reduction, was much faster in heartwood than in sapwood; however, copper and arsenic fixation in heartwood appeared to be incomplete regardless of the extension of fixation time. This poor fixation of copper a...
Gyu-Hyeok Kim, Yun-Sang Song, Dong-heub Lee
CCA type C depletion of Southern yellow pine utility poles
1995 - IRG/WP 95-50049
Depletion and redistribution of preservative components were evaluated on five CCA-C treated poles in service for over six years in Conley, Georgia. A statistical approach was taken in which retentions below ground were compared to retentions above ground due to a lack of initial data on individual poles. It was hypothesized that the below ground retentions should be lower than the corresponding a...
P D Osborne, R F Fox
Preliminary indications of the natural durability of Spruce bark board
1999 - IRG/WP 99-10312
A board material made from pressed bark, with no added adhesive, has been developed by Forintek's composites group and tested for durability by Forintek's treated-wood group and the University of Hawaii. This material was also manufactured with veneers in a one-step process. Since one role of bark on the tree is protection against pests and diseases, barkboard was expected to hav...
P I Morris, J K Grace, G E Troughton
Influence of fungal exposure on the redistribution of copper in treated spruce wood
2002 - IRG/WP 02-10450
The redistribution of copper in treated wood after exposure to basidiomycete decay fungi is described. The micro-distribution of copper in copper(II) sulphate or copper(II) octanoate/ethanolamine treated Norway spruce wood before and after exposure to 3 different wood decay fungi was studied using transmission electron microscopy with X-ray microanalysis. The copper content of the mycelium and the...
M Humar, F Pohleven, R J Murphy, D J Dickinson, I Moris, M Zupancic, P Kalan, M Petric
The potential of high pressure pulsation processes to treat white spruce lumber with water-borne preservatives
1988 - IRG/WP 3471
Laboratory work using end sealed 4x8x46 cm³ white spruce samples has been done to explore the suitability of three variants of a 2.1 MPa pulsation process for the impregnation of white spruce with CCA. The results showed that the process improved significantly the penetration of the preservatives and reduced significantly cell collapse, when compared with the results of treatment using a 2.1 MPa ...
J P Hösli, J N R Ruddick
Amenability of radial permeability of Sitka spruce (Picea sitchensis (Bong.) Carr.) as affected by aspects of cell ends in uniseriate ray parenchyma tissue
2003 - IRG/WP 03-40252
The principal objective of this article was to recognise and understand the amenability of ray parenchyma cell ends (end platform) in uniseriate ray tissue to influence the radial permeability of Sitka spruce (Picea sitchensis (Bong.) Carr.) by examination of most (Queen Charlotte Islands in Rhondda, South Wales) and the least (South Oregon in Dalby, North-East England) seed origins that grown in ...
I Usta, M D C Hale
Protection of pine sawtimber and sawn timber against blue stain in Poland
1983 - IRG/WP 3193
The purpose of this paper is the synthesis of more important results of basic and applied research that have been grouped in the following problems: 1.: Fungi causing blue stain in the pine wood, occurring in Poland. 2.: Moisture content changes of pine sawtimber and sawn timber as the factor of blue stain producing fungi development. 3.: Effect of sapwood moisture content on the degree of wood st...
E Tarocinski, M H Zielinski
Biological Control of Bluestain - Log Field Trials in Canada
2002 - IRG/WP 02-10423
In the summer of 2000 we ran two field experiments (in Alberta and British Columbia) to test the feasibility of using an albino bluestain isolate (Cartapip97TM) to protect lodgepole pine logs from being stained by wild-type bluestain fungi. Results showed that Cartapip applied at the recommended concentration significantly reduced the amount of stain found in the Alberta
trials. Cartapip applie...
A Uzunovic, D Minchin, A Byrne
Evaporation and redistribution of creosote in pine poles during storage
1996 - IRG/WP 96-50064
During the work with European standards for pressure treated wood, it has been questioned if the lapse of time between impregnation and chemical analysis of the retention is critical, especially for creosote. "The Norwegian Control Scheme for Preservative Treated Wood" has not discovered any retention problems analysing CCA preservatives in wood. If the lapse of time between impregnation with creo...
F G Evans, B Nossen
Multiple-Phase Pressure (MPP) Process: One-stage CCA treatment and accelerated fixation process. 3. Effect of process variables on sapwood treatment and CCA fixation.
1998 - IRG/WP 98-40114
The Multiple-Phase Pressure (MPP) Process achieves treatment and fixation as combined process using hot CCA, within a 2-3 hour time-frame. Timber is treated to saturation with hot CCA using an empty cell process. During the pneumatic pressure phase, hot solution is held in the wood in an otherwise liquid-free treatment vessel until fixation is >95% complete.
This report details a factorial des...
H Pearson, K Nasheri, J A Drysdale, G Durbin, M E Hedley
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
Fungal degradation of wood treated with metal-based preservatives. Part 1: Fungal tolerance
1996 - IRG/WP 96-10163
In recent years, concerns have arisen about the leaching of heavy metals from wood treated with chromated copper arsenate (CCA), particularly because of the large amount of CCA treated wood that will be discarded in the coming years. The long term objectives of this work are to determine the fate of copper, chromium and arsenic with the aging and potential decay of CCA-treated wood, and to develop...
B Illman, T L Highley
Changes in transverse wood permeability during the drying of rimu and radiata pine
1990 - IRG/WP 3636
When softwoods are dried and subsequently impregnated with waterborne preservatives two problems frequently occur, preservative screening of multi-salt preservatives and difficult re-drying. To study the causes, the permeability of rimu and radiata pine wood has been measured along the three principal directions. The radial and tangential permeabilities of the green sapwood of the two species were...
R E Booker
Diffusion treatment of gauged radiata pine timber using "Boracol 20"
1987 - IRG/WP 3437
Green gauged 100 x 50 mm radiata pine timber was preservative treated by brush application of "Boracol 20" followed by diffusion storage. Preservative retention analyses indicated that retention requirements in the core could be achieved within a six week diffusion period, thus representing a time saving of 25% over conventional boron treatment of rough-sawn radiata pine. Similar treatment of kiln...
D R Page, P Vinden, S Retter
Partial seasoning and preservative treatment systems for pine roundwood
1982 - IRG/WP 3187
Experimental trials at FRI, Rotorua showed that the steaming schedule normally used for steaming and venting is also suitable for steaming and vacuum seasoning. Applying vacuum of up to -84 kPa immediately after steaming did not increase the initial loss of wood moisture significantly in comparison to steam/venting. The main improvement to wood condition by using steam/vacuum appeared to be to dis...
A J Bergervoet
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
Efficacies of an insecticide and a fungicide for preventing blue-stain of Japanese red pine logs
2006 - IRG/WP 06-20329
We examined blue-stain fungi on Japanese red pine at 3 forests and 2 saw mills in Iwate Prefecture, Japan. The isolated ophiostomatoid fungi were Leptographium sp and Ophiostoma sp. There were 3 routes of the blue-stain; fungal growth from the spore or hypha stuck on the cross cut surfaces, fungal spread through the inner bark by bark beetles and fungal invasion around whorled knot. The larger ext...
H Taniuchi, T Koiwa, H Masuya, S Doi
Moisture correction for ultrasonic MOE measurements above fibre saturation point in Scots pine sapwood
2006 - IRG/WP 06-20333
There is a high correlation between methods for dynamic modulus of elasticity (MOEdyn) and static modulus of elasticity (MOEstat). MOEdyn methods have been found sensitive to detect early stages of decay and may be seen as an option for non-destructive wood durability testing. As the MOEstat measurements do not change after reaching the fibre saturation point, the uncorrected MOEdyn data from ultr...
E Larnøy, G Alfredsen, H Militz
Performance of boron-treated radiata pine in above ground field tests in New Zealand
2006 - IRG/WP 06-30406
Boron treatment was approved for exterior, above ground use in New Zealand in 1958, provide treated commodities were painted with a three-coat paint system. Above ground tests of rail units and L-joints were established at the NZ Forest Research Institute (now Scion) between 1967 and 1980 to monitor performance of boron treatment in relation to that of untreated and CCA-treated timber.
Results sh...
M Hedley, D Page
Qualitative and quantitative assessment of chemicals used for wood durability improvement by Near Infrared Spectroscopy
2006 - IRG/WP 06-20349
The Near infrared spectroscopy (NIRS) could be a suitable technique to assess chemicals used for wood durability improvement in the forest products industry. NIRS methodology can be used to obtain results more quickly, less costly and without damaging the wood. In this study, wood samples selected from heartwood and sapwood of Maritime Pine (Pinus pinaster) were prepared to assess the artificial d...
S Zahri, F Charrier, H Baillères, B Charrier
Addition of boron compounds and octanoic acid for improvement of biocidal properties and copper fixation at copper-ethanolamine based wood preservatives
2006 - IRG/WP 06-30408
Copper-ethanolamine based wood preservatives became important active substance (formulation) for wood protection, novelty. As copper itself can not ensure sufficient protection against wood destroying organisms and fixation in wood we combine it with other biocides like ethanolamine, boron and octanoic acid. This investigates were performance on spruce wood impregnated with different combination o...
F Pohleven, M Humar
Ionic liquids with organic and inorganic anions as highly active wood preservatives
2006 - IRG/WP 06-30411
Quaternary ammonium tetrafluoroborates, nitrates(V), propionates, acetates and formates with alkoxymethyl substituents were prepared and tested on wood destroying and sapstaining fungi. These new compounds are ionic liquids (ILs), which penetrate very well into Scot pine wood. Alkoxymethyldecyldimethylammonium tetrafluoroborates and nitrates(V) show better microbial activity against Coniophor...
J Zabielska-Matejuk, A Skrzypczak
Underwater shock treatment for improvement of penetration of wood
2006 - IRG/WP 06-40325
Many of conifers including Beimatsu (Pseudotsuga menziesii Franco; Dougras fir, Oregon pine), Akamatsu (Pinus densiflora Sieb. et Zucc.; Japanese red pine), Dafurica Karamatsu (Larix gmelinii Gordon; Dahurica larch) and Karamatsu (Larix leptolepis GORDON; Japanese larch) generally contains the high moisture content. Although subjected to the drying process, it is difficult to be dried up completel...
S Itoh, H Maehara, K Tanaka, T Echigo, K Morioka, E Shirai, K Nishimoto