Your search resulted in 549 documents. Displaying 25 entries per page.
Susceptibility of angiosperm sapwood to white-rot fungal colonization and subsequent degradation: a hypothesis
1997 - IRG/WP 97-10211
It has long been recognized that angiosperm sapwood in nature is relatively easily and preferentially degraded by white-rot fungi. This susceptibility to white-rot fungi is generally believed to be mainly caused by the structure and concentration of angiosperm lignin. However, an explicit explanation as to why lignin structure makes a particular wood vulnerable to white-rot colonisation and subseq...
T Schultz, D D Nicholas
A comparative field test of the effectiveness of anti-sapstain treatments on radiata pine roundwood
1986 - IRG/WP 3376
Peeled radiata pine posts were sprayed with one of six antisapstain formulations, with and without a wax water-repellent additive, to evaluate the protection given by each treatment. After 3 months' outside storage the best treatments tested were 4% product Busan 30, 2% product Busan 1009, and 2% active sodium pentachlorophenoxide (NaPCP) with 1.5% borax. After 6 months' storage ...
J A Drysdale, R M Keirle
Radio frequency heating times for sterilization radiata pine solid piles
2017 - IRG/WP 17-40815
In this work was sterilized wood packaging material of radiata pine, stacked as solid piles without stickers, for determining the heating times using radiofrequency treatment. The experiments were performed in a radio frequency semi-industrial equipment. The results showed that the radio frequency heating times increases with wood volume and that radio frequency treatments were faster than convent...
H Esquivel, V Sepúlveda, J Torres, L Salvo, R A Ananías
Kinetic modelling of adsorption of quaternary ammonium compounds by Scots pine wood sawdust (Pinus sylvestris L.)
2005 - IRG/WP 05-30369
The adsorption of new quaternary ammonium compounds from aqueous solutions onto Scots pine wood (Pinus sylvestris L.) sawdust was studied. The pseudo first- and second- order kinetic models were used for the mathematical description of the sorption dynamic process of QACs onto wood. The highest correlation coefficients were obtained for the pseudo-second order kinetic model, those suggest that che...
J Zabielska-Matejuk
Experimental test site to prevent maritime pine logs from bluestaining: water-spraying and water-immersion methods
2003 - IRG/WP 03-10497
Following a storm which led to windfall wood, a research project was launched to develop preservation methods with a low environmental impact for maritime pine logs. These preservation methods are intended to be suitable for large-scale storage areas of maritime pine. In addition the aim was to maintain wood quality during long term storage. An experimental field test with 1 900 m3 of maritime pin...
I Le Bayon, H Callot, D Reuling, C Brunet, P Castéra
A fixation model, based on the temperature dependence of CCA-C fixation
2000 - IRG/WP 00-40163
A model was prepared for the fixation of 1% CCA-C in red pine that allows the prediction of extent of fixation based on the temperature history of the treated wood following pressure treatment. The reaction kinetics of the rapid initial reaction and the slower main reaction were characterized using the Van t'Hoff equation. The initial reaction could be represented by a 10th order chemical...
P A Cooper, K M F Kazi, Jianbin Chen, Y T Ung
Tests on preservation of wood against marine borers
1976 - IRG/WP 417
The Instituto del Legno has carried out for some years a series of trials about the biodeterioration of wood in the sea. The investigations included the settlement and activity of marine borers, the natural durability of indigenous and tropical woods and the preservation of wood for marine use. This paper reports the trials on the effectiveness of some preservatives in protecting wood against mari...
A Gambetta, E Orlandi
Immunogold labelling of size marker proteins in brown rot-degraded pine wood
1990 - IRG/WP 1428
Pine wood degraded by Fomitopsis pinicola was infiltrated with a mixture of ovalbumin (45 kDa) and myoglobin (16.7 kDa). After crosslinking of the proteins with glutaraldehyde and preparation for electron microscopy ultrathin sections were labeled with gold-conjugated antibodies. Simultaneous labeling of both proteins on the same section showed that at 50-70% weight loss ovalbumin did not penetrat...
E Srebotnik, K Messner
CCA component distribution in the heartwood of treated lodgepole pine and white spruce
1998 - IRG/WP 98-30173
As part of a comprehensive study on the influence of drying on heartwood permeability, the distribution of copper, chromium and arsenic (CCA) in lodgepole pine (Pinus contorta Dougl.) and white spruce (Picea glauca (Moench) Voss.) heartwood was examined with light microscopy. Stained microtomed sections were examined to determine the penetration pathway for the CCA. The microscopic observations re...
Y An, J N R Ruddick, P I Morris
A field test with anti-sapstain chemicals on sawn pine timber in Finland
1986 - IRG/WP 3368
Fourteen formulations, each in two concentrations, were tested for effectiveness against sapstain, mould and decay on Scots pine (Pinus sylvestris L.) in a field test in South-Finland. The trial was commenced in June 1985 and finished in October 1985. During the test the boards were infected mainly by mould fungi. In kiln dried boards the protective effects of nine and in green boards of four trea...
L Paajanen
Practical testing of wood preservatives to prevent weathering damage and infection by micro-organisms on spruce and pine
1989 - IRG/WP 3530
Brush application, is generally used to prevent wooden window frames from decay caused by influence of weathering and fungi. Accordingly 10 boards of pine (Pinus sylvestris) and spruce (Picea abies) were treated with 10 commercially used wood preservatives. The efficiency of fungicides by using chiptest and blue stain test (EN 152), the effectiveness against weathering as well as the course of col...
R Gründlinger, O Janotta, H Melzer, K Messner
Influence of bark damage on bluestain development in pine logs
1997 - IRG/WP 97-10197
Mechanized harvesting of conifers can lead to extensive bark damage, with the resulting wounds providing suitable entry points for bluestain fungi that are not associated with bark beetle vectors. However, the amount of bluestain colonisation can vary greatly between the different types of wound. To evaluate the effect of wound type seven different types of wounds were artificially created on fres...
A Uzunovic, J F Webber, D J Dickinson
Spatial arrangement of lignin peroxidase in pine decayed by Phanerochaete chrysosporium and Fomitopsis pinicola
1988 - IRG/WP 1343
By applying immunoelectronmicroscopic methods, lignin peroxidase of the white rot fungus Phanerochaete chrysosporium has been localized in the cytoplasm of hyphae, close to the plasmalemma and on the plasmalemma. Infiltration of wood specimen with culture filtrates, concentrated 300-fold, gave clear information on the penetration of the enzyme into the wood cell wall. Penetration was restricted to...
E Srebotnik, K Messner
Insect transmission of fungal sapstain to freshly sawn unseasoned softwood lumber
1994 - IRG/WP 94-20025
Chemical dip treatments were used to investigate micro-arthropod transmission of fungal sapstain to unseasoned pine sapwood boards. Saptain, mould and basidiomycete defacement of chemically treated sawn boards of Corsican pine was recorded during a 14 week field trial. Boards were treated with either a fungicide, an insecticide/acaricide, a combination of the fungicide with the insecticide/acarici...
M A Powell, R A Eaton, J F Webber
Emission of trimethyl borate and methanol from radiata pine (Pinus radiata D. Don)
1995 - IRG/WP 95-30088
Sawn and kiln dried radiata pine conditioned to 3, 6, and 12% moisture content was treated with trimethyl borate (TMB). The treated wood samples were placed in mini-desiccators maintained at 20 or 40°C. The air space within the mini-desiccator was analysed for TMB and methanol. An initial period of emission of TMB and methanol was observed. This was followed by a period of gradual dissipation of ...
F J Romero, P Vinden, J A Drysdale
A laboratory evaluation of the susceptibility to biological attack of glued laminated pine timber
1991 - IRG/WP 2387
In the scope of a research programme concerning the use of maritime pine (Pinus pinaster) to produce glued laminated timber structures in Portugal, the natural durability of this material was checked by using laboratory test methods. An European standard, EN 113, was used to test durability against basidiomycetes and a test method developed at LNEC for termites was adapted for this purpose. From t...
L Nunes, H Cruz
Biological degradation resistance of pine wood treated with dimethylol compounds
1989 - IRG/WP 3528
The study reports the increase of dimensional stability and biological degradation resistance of pine wood (Pinus sylvestris L) after impregnation with dimethyloldibydroxyethyleneurea. Decay resistance was determined according to BS 838:961. Nearly complete protection against Coniophora puteana, (Schum.ex Fr. Karst) weight loss of 2-3% was shown when modification, expressed as weight gain, exceede...
C L Videlov
Effect of borate on uptake and efficacy of an anti-sapstain treatment
2005 - IRG/WP 05-30380
The potential for using borates to enhance uptake and efficacy of propiconazole-based anti-sapstain chemicals was assessed on ponderosa pine sapwood wafers. Borates had no consistent effect on either net solution absorption or propiconazole distribution in the wood. Even small amounts of borate, however, markedly improved the performance of propiconazole against fungal discoloration. These resul...
Jianju Luo, Hua Chen, J J Morrell
TBTO absorption and penetration in pine joinery treated by various processes
1989 - IRG/WP 3523
Matched sections of several White pine (Pinus strobus) and Ponderosa pine (Pinus ponderosa) mouldings were treated with TBTO by Double vacuum, modified empty-cell, 15 second dip and several preheating treatments followed by a 15 s dip treatments. As expected the double vacuum and empty-cell (batch) treatments resulted in much greater retentions and penetrations than the dip treatments. The absorpt...
P A Cooper, Y T Ung
The influence of age on retention and fixation of CCA in pressure-treated Kenyan-grown Eycalyptus saligna: Summary of findings
2002 - IRG/WP 02-30296
The present study investigates the influence of age on retention and fixation of copper-chrome-arsenate (CCA) in Kenyan-grown Eucalyptus saligna. Samples for the study were obtained from sound trees aged 4, 8, 12, 16, 20 and 24 years.
Test samples were radially cut from round material to represent total sapwood and heartwood for each age class, and measured 50mm in thickness, 100mm long, with wi...
R Venkatasamy
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell
Correlation between a laboratory bioassay and field trial conducted to determine the termiticidal effectiveness of bifenthrin
2002 - IRG/WP 02-20248
Details are given of a laboratory bioassay and field trial undertaken to determine the termiticidal effectiveness of the synthetic pyrethroid bifenthrin, when impregnated into Pinus radiata D. Don sapwood specimens. Results show a strong correlation between the laboratory and field methods of evaluation. Protection threshold limits obtained were the same for the two test species of termite employe...
J W Creffield, K Watson
Decay resistance of Scots pine (Pinus sylvestris) heartwood against brown rot
2002 - IRG/WP 02-10433
Natural decay resistance of wood is mainly restricted in the heartwood and based on wood microstructure and chemical composition. The genetic variation in the durability of Scots pine (Pinus sylvestris L.) wood against decay and the relationship between resistance and chemical composition was studied. The laboratory tests of 6 and 8 weeks were carried out with a brown rot fungus Coniophora puteana...
H Viitanen, A M Harju, P Kainulainen, M Venäläinen
Performance of treated and untreated sawn fence posts of Scots pine and Norway spruce
2000 - IRG/WP 00-30247
Sawn fence posts are a rather important product and the objective of this trial was to assess their durability. In 1985 a field trial with treated and untreated fence posts of Scots pine (Pinus sylvestris L.) and Norway spruce (Picea abies (L.) Karst.) was set out at the test field in Ultuna, Uppsala, Sweden. The posts had a dimension of 75 x 100 x 1400 mm3. The preservatives applied were a CCA, a...
Ö Bergman
Water sprinkled pine wood: A microscope study on boards showing streaking
1993 - IRG/WP 93-10033
Boards sawn from the outer sapwood of pine lumber previously water sprinkled for periods of 10-18 weeks and kiln dried, showed streaking after staining. Two types of enhanced stain uptake were noted: 1) a more concentrated and localized form after 10 weeks and 2) a more diffuse type which developed in later stages of water sprinkling. Areas showing enhanced stain uptake were examined using light a...
G F Daniel, T Elowson, T Nilsson, A P Singh, K Liukko