Performance of naturally durable decks after 15 years of field exposure
2020 - IRG/WP 20-10963
A decking test of Canadian species considered to be naturally durable was inspected after 15 years of exposure at test sites in Ontario and British Columbia. Based on the materials used in this experiment, Douglas-fir and yellow cypress had the greatest decay resistance, followed by eastern white cedar and western redcedar, and then by western larch and tamarack. All materials tested were more dur...
R Stirling, D Wong
Observed and projected changes in the climate based decay hazard of timber in the United Kingdom
2020 - IRG/WP 20-20665
The risk of microbiological attack on wood is determined by both material and climatic factors and indeed the hazard for a component is based on its intrinsic durability and the conditions in which it is used. The use of wood and organic materials in construction is increasing but ultimately all these materials will be susceptible to microbiological attack. The Scheffer Climate index applies clima...
S F Curling, G A Ormondroyd
Profiling fungal degradation of Scots pine sapwood by short wave infrared hyperspectral image analysis
2020 - IRG/WP 20-20667
Hyperspectral image analysis of Scots pine sapwood wood affected by decay fungi has been carried out as part of a Ph.D. thesis within the project Remote Inspection of Wooden Utility Poles (RIWUP).
In a lab experiment, Petri-dishes with Scots pine sapwood samples on malt agar medium were infected with two types of decay fungi, a brown rot and a white rot. The wood samples were scanned with a HySpe...
A Jochemsen, G Alfredsen, I Burud
Limiting Polysaccharide Motion Protects Wood From Decay
2020 - IRG/WP 20-40890
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
C G Hunt, S L Zelinka, J E Jakes
Long-term field exposure of wood-plastic composites processed on a commercial-size extruder
2020 - IRG/WP 20-40894
Wood-plastic composites (WPC) contain wood fiber (or flour), thermoplastics and additives and are exposed to UV light, moisture, and biological deterioration in outdoor installations. Accelerated laboratory tests can help to predict the durability of WPCs, but long term evaluations are needed to validate these results. Field exposed above-ground WPC deck boards (30.5 x 139.7 x 609.6 mm) and in-gro...
R E Ibach, C M Clemmons, N M Stark
Biological durability of sapling wood
2020 - IRG/WP 20-10967
Sapling-wood products from different wood species such as willow (Salix spp.) and Common hazel (Corylus avellana) are frequently used for gardening and outdoor decoration purposes. Remaining bark is suggested to provide additional biological durability. Even for temporary outdoor use it seemed questionable that durability of juvenile sapwood can provide acceptably long service lives of horticultur...
C Brischke, L Emmerich, D G B Nienaber, S Bollmus
Modelling decay rates of timber exposed above ground on four different continents
2020 - IRG/WP 20-20670
Durability performance data from an international decking trial were analysed to explore relationships with climate variables, particularly those related to temperature and rainfall. Matched decking samples of slash pine (Pinus elliottii) sapwood and heartwood, spotted gum (Corymbia citriodora), Norway spruce (Picea abies) and Scots pine sapwood (Pinus sylvestris) were exposed to the weather above...
L P Francis, J J Morrell, C Brischke, P B Van Niekerk, J Norton
Impact of fungal decay on the bending properties of wood
2020 - IRG/WP 20-20671
Wood used outdoors is generally prone to fungal degradation, and its impact on the structural integrity of wood is an immanent factor for service life planning with timber. Wood decayed to very small mass losses can suffer from a significant reduction in mechanical strength and elastic properties. Hence, the latter are preferred indicators to detect decay in wood durability studies. Numerous previ...
S Bollmus, P B van Niekerk, C Brischke
A summary of decay performance with citric acid and sorbitol modification
2020 - IRG/WP 20-40898
Application of wood-based products as construction materials is one piece of the big puzzle to mitigate climate change. Wood is susceptible to biological deterioration. Environmentally motivated legislation is making the use of biocides less attractive from a commercial perspective. Ideally, a wood modification technology should be of low cost, water based and make use of thermal curing. This rese...
G Alfredsen, E Larnøy, G Beck, J Biørnstad, L R Gobakken, C A S Hill, A Treu
Durability of acetylated Radiata pine: Laboratory tests and performance in practice
2020 - IRG/WP 20-40899
Wood acetylation is an established process to enhance biological durability and dimensional stability of lower valuable wood species without the use of biocides. Acetylated Radiata pine (ACCOYA® wood) has been on the market for more than 10 years now, starting in 2007.
Numerous lab tests have confirmed the high durability of acetylated Radiata pine. Here, additional data with four Radiata pine ...
K Jacobs, W Scheiding, B Weiß
Sterilization of Large Timbers during Preservative Treatment: How Quickly We Forget
2020 - IRG/WP 20-40902
Air seasoning is a common method of moisture management in utility poles and is done de facto during pole storage prior to treatment. However, extended air drying prior to treatment encourages fungal attack and can facilitate establishment of decay fungi in poles before a protective preservative barrier is applied. This problem can be mitigated by proper air-seasoning methods coupled with heat ste...
G Presley, J Cappellazzi, M Konkler, K Maguire, R Nelson, J J Morrell
Bioremediation technology for cleaning-up of the soil contaminated with creosote oil – the overall concept of BIOREM project
2020 - IRG/WP 20-50363
The aim of the communication paper is to present the conceptual framework of the BIOREM project, which started in May 2019. The final result of the entire project will be an innovative bioremediation technology that can be used in areas contaminated with creosote oil – a commonly used wood preservative being a complex mixture of various compounds such as polycyclic aromatic hydrocarbons (PAHs). ...
M Sydow, J Zabielska-Matejuk, A Stangierska
Assessing the risk of marine borer attack of the timber trestles and decay of timber above the intertidal zone of the Barmouth Viaduct
2021 - IRG/WP 21-10974
The Barmouth Viaduct is a Grade II* listed structure which carries the single track of the Dovey Junction to Pwllheli line and footway over the Mawddach estuary. It is in a marine environment where timber below the high tide mark is at most risk in Use Class 5 and all timber above in Use Class 3.2, permanently exposed to the risk of wetting. The structure consists of a timber trestle viaduct of ...
J R Williams
Studies on the material resistance and moisture dynamics of Douglas fir and Sitka spruce from Slovenia
2021 - IRG/WP 21-20677
Wood in outdoor applications is subject to various decomposition factors. Wood degradation can be prevented by construction details, biocide protection of wood, wood modification, or selection of naturally durable wood species. Unfortunately, the majority of timber species in Europe do not have naturally durable wood. Imported tree species represent a new pool from which we can draw wood species w...
M Humar, B Lesar, D Krzisnik, E Kerzic, R Brus
Estimation of residual compressive strength on cross laminated timber with biodeterioration damage
2021 - IRG/WP 21-40918
CLT is susceptible to biodeterioration such as fungal decay and termite attack during long-term use for buildings. It is necessary to know the residual strength performance of biodegraded CLT for estimating future performance and aging of CLT. In this study, compression tests of CLT damaged by brown rot fungi and termites were conducted to clarify the relationship between residual strength and mas...
R Inoue, T Mori, K Kambara, W Ohmura
Evaluation of decay and energy properties from thermally modified biomasses during fungal deterioration by NIR-spectrometry
2021 - IRG/WP 21-40922
This study is focused on the prediction of fungal weight loss (WL) and high heating value (HHV) from raw and torrefied waste lignocellulosic feedstocks, according to their exposure duration to wood-destroying fungi, using near infrared spectroscopy (NIR) and chemometrics models.
Sugarcane bagasse, coffee husk, eucalyptus and pine shavings were torrefied at 290 °C in a screw reactor, during 5, 7...
B de Freitas Homem de Faria, P Santana Barbosa, J Valente Roque, A de Cassia Oliveira Carneiro, P Rousset, K Candelier, R F Teofilo
Application of suberin fatty acids extracted from birch bark for wood coating
2021 - IRG/WP 21-40914
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
A Kumar, Risto Korpinen, Veikko Möttönen
Decay capacity and degradation patterns of Xylaria hypoxylon on different wood species
2022 - IRG/WP 22-10985
A host of physical and environmental factors may influence fungal decay including the wood substrate, temperature, moisture, oxygen, light, pH, and nitrogen. Understanding the effects of these factors on fungal decay is important for the effective utilization of wood decay fungi in biotechnological processes and for understanding the role of these organisms in global carbon cycling. The ascomycete...
E Bari, G Daniel, A Singh, J J Morrell
The effect of sapwood and heartwood differences on durability of short rotation teak wood
2022 - IRG/WP 22-10991
Short rotation teak has been developed to overcome the limited supply of long rotation teak. The aim of this study was to investigate the effect of sapwood and heartwood differences on durability of short rotation teak. The following basic properties were studied: extractive content, dimensional stability (volumetric swelling and water uptake), decay resistance, and termite resistance. The result...
R Martha, M Mubarok, F O Akong, B George, C Gérardin, S Dumarçay, I S Rahayu, I Batubara, W Darmawan, P Gérardin
Introduction to the project ‘Deterioration and decay of wooden cultural heritage in Arctic and Alpine environments’ (ArcticAlpineDecay)
2022 - IRG/WP 22-10997
The Arctic is already affected by climate change, and this is expected to accelerate over the coming decades. Alpine regions in Norway are projected to face similar challenges. Current knowledge on Norwegian wooden cultural heritage in Arctic and Alpine regions is scattered and contains significant knowledge gaps. Historically, - scientists, sectorial governance, tourist trade and commerce have ma...
G Alfredsen, L Ross, A W Hegnes, M S Austigard, J Mattsson, N B Pedersen, A Sinitsyn, V V Martens, A-C Flyen
Evaluation of Decay Resistance of Copper-based Preservatives Treated-Wood exposed to different field test sites in Korea
2022 - IRG/WP 22-20679
In Korea, preservative treated wood is required to have a stamp on the surface which contains information such as wood species, use categories, and the company that treated the wood. Such stamping is necessary to safely and appropriately use the treated wood. Since majority of treated wood is being used outdoor environment, the treated wood must have efficacy against wood decay fungi or termite. I...
W-J Hwang, S-M Yoon, Y Park, Y-S Choi, H-M Lee, J-W Kim
Combining MRI and X-ray CT to monitor fungal decay of plywood and OSB in a lab test
2022 - IRG/WP 22-20683
Bio-based building materials, such as wood and wood-engineered products, are susceptible to degradation by decay fungi. In-depth knowledge on the intricate material-fungus relationship as well as performance data for many bio-based building materials are still lacking, and especially knowledge on how a material’s structure and moisture properties affect the degradation process is missing. Althou...
L De Ligne, T Núñez Guitar, C Vanhove, J Van Acker, J Van den Bulcke
Properties of Iron (II) Sulphate treated Norway Spruce
2022 - IRG/WP 22-30765
Exterior wood is exposed to various environmental factors that cause weathering. Weathering is important primarily from an aesthetic standpoint. However, not all parts of the building are equally susceptible to weathering. Parts exposed to moisture will discolour faster than protected parts, such as wood under roof overhangs. To achieve fast and uniform artificial greying, a surface treatment with...
B Lesar, M Humar, M Škamlec
Effects of Borax and Boric Acid as Fire Retardants on the Resistance of Pterygota macrocarpa Wood to Fire Tests
2022 - IRG/WP 22-30770
The combustible nature of wood as a building material, when exposed to hazards of fire underscores the reason for fire retardant treatments. Pterygota macrocarpa wood is commonly used by builders in Nigeria for roof and other structural applications. Therefore, this study was carried out to assess the effect of Borax and Boric acid on the fire-retardant properties of P. macrocarpa wood. Wood sampl...
J M Owoyemi, O Apogbona, T O Akinwamide
Field tests of different tropical wood species in sea water
2022 - IRG/WP 22-30773
A number of tropical timbers have been tested according to EN 275 at Kristineberg Marine Research Station in Sweden since 1999. Most of these tests have started during the last 5-8 years.
Wood species included have been Lophira alata (Azobé/Ekki), Minquartia guianensis (Manwood/Acaria), Chlorocardium rodiei (Greenheart), Cyclodiscus gabonensis (Okan/Denya), Shorea spp. (Bankirai), Dicorynia guia...
M Westin, P Larsson Brelid