Factors affecting decay rates in a fungus cellar
1985 - IRG/WP 2242
Birch and pine stakes treated with chromated copper arsenate and didecyldimethylammonium chloride were incubated in two soils in a "Fungus Cellar" test. At three month intervals, sets of stakes were inspected and assigned visual ratings or removed from the soil beds for weight loss determination. Preliminary results after nine months exposure have shown differences in the decay rates between birch...
P A McKaig
Collaborative soft rot tests: Specific gravity loss resulting from soft rot
1973 - IRG/WP 227
It was proposed at the 5th meeting of Working Group II of the IRG in June 1973 in Lahti, Finland, that the specific gravity (swollen volume basis) of test blocks used in the IRG Collaborative Soft Rot Tests should be determined on all the blocks at the completion of the exposure period. Specific gravity determined on the basis of the oven dry weight and water swollen volume was selected because (1...
C R Levy
The use of organic wood preservatives in ground contact and the suitability of laboratory test procedures to determine their efficacy
1999 - IRG/WP 99-20175
Organic fungicides, such as propiconazole, have proven to be highly effective when used as a co-biocide in recently developed wood preservative formulations. They have however been ineffective when used as a stand alone preservative, particularly when used in ground contact (European Hazard class 4). Previous research, using the test methods of ENV 807 (1993), provided conflicting evidence regardi...
I J Herring, D J Dickinson
Bethoguard; A new wood protecting fungicide for use in metal free ground contact wood preservatives
2002 - IRG/WP 02-30301
Research has identified the limitations in both the spectrum of activity and permanence of organic biocides placed in wood in high hazard environments, particularly in the absence of heavy metals such as copper. More specifically, the control of soft rot decay in wood in soil contact has proven to be most problematic.
The new organic biocide, Bethoguard; an oxathiazine, has demonstrated excellen...
S C Forster, G R Williams, M Van Der Flaas, M Bacon, J Gors
Soft rot - Soil burial - Tests. Influence of the addition of nitrogen compounds to the soil on wood decay by soft rot
1972 - IRG/WP 213
The decay of wood specimens buried in soil is influenced by various factors. Decisive are the water content, the content of organic substances, the pH-value, the content of mineral nutritive salts, nitrogen content, etc. of the soil. These tests were carried out in order to investigate if the decay of wood in the soil will be influenced by additions of various nitrogen-compounds in different conce...
O Wälchli
Preliminary indications of the natural durability of Spruce bark board
1999 - IRG/WP 99-10312
A board material made from pressed bark, with no added adhesive, has been developed by Forintek's composites group and tested for durability by Forintek's treated-wood group and the University of Hawaii. This material was also manufactured with veneers in a one-step process. Since one role of bark on the tree is protection against pests and diseases, barkboard was expected to hav...
P I Morris, J K Grace, G E Troughton
Upgrading the fungal resistance of OSB
1999 - IRG/WP 99-40138
There is a perception that oriented strand board (OSB) is less resistant to fungl than plywood under conditions of moderate exposure to moisture. Douglas fir-faced plywood (DFP) has been suggested as a benchmark for acceptable durability under such conditions. This project was initiated to determine the minimum level of low-toxicity chemical treatment needed to upgrade the fungal resistance of OSB...
P I Morris, J E Clark, D Minchin, R Wellwood
Decay rates and strength and stiffness loss in foundation beams
1992 - IRG/WP 92-1563
The TNO Centre for Timber Research has executed an extensive research programme into the rate of decay in foundation beams, as a result of lowering of ground water tables. The aim of the research was to develop a method, predicting the decrease in strength and stiffness in beams, due to wood decay during drytime of foundation beams. With the calculated extremes in decay, the damage caused by local...
P Esser, H S Buitenkamp
Soft rot in heartwood of preservative-treated pole stubs of Eucalyptus cypellocarpa L. Johnson
1983 - IRG/WP 1204
Pole stubs of Eucalyptus cypellocarpa L. Johnson, treated in the sapwood with certain waterborne preservatives and exposed for 21 to 23 years in a dry tropical region were severely soft-rotted in the heartwood, as well as the sapwood. They broke with a brash fracture when stress tested (loaded as a cantilever) in the field. The severe soft rot in the heartwood was not detected by the knife test or...
J E Barnacle, G C Johnson, M A Tighe
Preservation of basidiomycete hyphae in ancient waterlogged wood materials
1992 - IRG/WP 92-1536
Studies on waterlogged archaeological wood show that basidiomycete hyphae may persist as long as 800 years. In two pine wood samples with Phellinus pini heartrot, one from the foremast of the ship Vasa and the other from a bulwark constructed in the first part of the 12th century, numerous resin covered hyphae were observed. Hyphae with clamp connections that were associated with brown and white r...
T Nilsson, G F Daniel
Interactions between soft rot fungi and CCA preservatives in Betula verrucosa
1988 - IRG/WP 1367
Ultrastructural investigations were carried out to obtain information on the cell wall distribution of CCA elements during soft rot decay of 4% K33 CCA preservative treated birch (Betula verrucosa) wood. TEM observations on fibres at various stages of S2 cavity formation by mutabilis showed a distinct pattern of electron dense materials to occur within the S2 cell wall region. These materials (gra...
G F Daniel, T Nilsson
PXTS; A Metal Free Oligomer Wood Preserving System - A Summary of Data To Date
2004 - IRG/WP 04-30350
The world is continually looking for new wood preservative technology, especially to address environmental concerns. Recent changes in the USA have limited the use of arsenical containing formulations to industrial use through a negotiated voluntary cancellation of most residential label uses. PXTS (Polymeric Alkylphenol Polysulfide) offers a brand new technology that is an all organic system, lik...
M H Freeman, D D Nicholas, D Renz, R Buff
Effects of heart wood extractives in Dahoma (Piptadeniastrum africanum) on decay resistance to white- and brown-rot fungi
2004 - IRG/WP 04-10536
Dahoma (Piptadeniastrum africanum) is a durable but a lesser utilised tropical hardwood species from Ghana that has the potential of being used as an alternative to Iroko (Milicia excelsa) for many end uses. However, the timber gives off a strong odour especially when wet and during processing. The high durability and the strong odour of the timber could be due to the presence of extractives in th...
Zeen Huang, K Maher, S A Amartey
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
Use of the enzyme-linked immunoassay (ELISA) and immunocytochemistry to detect soft rot in preservative treated and untreated wood
1990 - IRG/WP 2347
A polyclonal antibody was raised against mycelial extracts from the soft rot fungus Phialophora mutabilis. In ELISA assays, the antibody showed strong reactions with its own antigen and strong to moderate cross reactions with 6 other Phialophora soft rot species. With the exception of Ceratocystis albida, the antibody gave only weak or negative reactions with 11 other mold, blue stain and rot fung...
G F Daniel, T Nilsson
Influence of the nature of the substrate and the method of inoculation on the degradative activity of soft rot fungi
1998 - IRG/WP 98-20133
The European Standard (ENV-807) determines the threshold of effectiveness of wood preservatives against the action of soft rot Ascomycetes fungi. Its application in the treatment of wood used in the hazard class 4 does not always offer repeatable results, which could be expected in an experimental norm.
For this reason, in this paper, we have evaluated the diverse variables that might influence t...
M T De Troya, A M Navarrete, F Rubio, J Jiménez, D Muñoz-Mingarro, C Rodríguez-Borrajo, F Llinares, M Yuste
The influence of cement and calcium compounds on the performance of CCA preservatives
1983 - IRG/WP 3221
The influence of cement and calcium compounds on the durability of untreated and CCA treated wood is considered. Calcium compounds were found to reduce the toxicity of a CCA preservative to a soft rot fungus at copper to calcium ratios of 1:1 and 1:10 using a cellulose filter paper technique. Further studies are outlined and some possible mechanisms by which cement and calcium compounds may affect...
R J Murphy
Common Decay Micromorphology “Anomalies” Challenge Current Decay Classification
2006 - IRG/WP 06-10578
Decay micromorphology was studied systematically for diversely preservative treated Pinus radiata and Fagus sylvatica 20 x 20 x 500 mm stakes across 13 in-ground field test sites, during a 6.5 year exposure. New insight into the micromorphology of the early stages of decay enabled new and more detailed interpretation of the mechanism of their formation and suggested that current decay classificati...
R Wakeling
Resistance of pine and spruce heartwood against decay - The effect of wood chemical composition and coating with water-borne wood oil product
2006 - IRG/WP 06-10597
Natural durability of wood has been widely studied, but the combination of the natural durability and different treatments has not been the focus of many studies. The durability of wooden products is mainly based on the water permeability and the resistance against organisms. In this study, the water absorption and decay resistance of sapwood and heartwood of Scots pine and Norway spruce were exam...
H Viitanen, S Metsä-Kortelainen, T Laakso
Phenol oxidase activity and one-electron oxidation activity in wood degradation by soft-rot deuteromycetes
2007 - IRG/WP 07-10615
Wood degradation, one-electron oxidation activity as assayed by ethylene generation from 2-keto-4-thiomethylbutyric acid (KTBA), and phenol oxidase activity were measured in cultures of six deuteromyce fungi, with glucose or wood as the carbon source. The four fungi that degraded Japanese beech wood had higher one-electron oxidation activities in wood-containing cultures than in glucose-containing...
H Tanaka, M Yamakawa, S Itakura, A Enoki
Detection of Anti-Fungal Sapwood Extractives in Non-Durable Scots Pine (Pinus sylvestris), Rubberwood (Hevea brasiliensis) and Jelutong (Dyera costulata)
2007 - IRG/WP 07-10634
A general laboratory bioassay method of Woodward and Pearce (1985) was adopted to detect anti-fungal activity of sapwood or heartwood extractives of 5 Malaysian hardwoods [dark red meranti heartwood (Shorea spp.), red balau heartwood (Shorea spp.), kulim heartwood (Scorodocarpus borneensis), jelutong sapwood (Dyera costulata) and rubberwood sapwood (Hevea brasiliensis), including the temperate Pin...
A H H Wong, R B Pearce
Decay Resistance Properties of Hemicellulose-Extracted Oriented Strand Board
2008 - IRG/WP 08-10644
There is increasing interest in using cellulosic biomass as the basis for a renewable source of energy. Although the traditional focus has been on cellulose, researchers are also exploring the possibility of using hemicelluloses because they can be removed with hot water leaving the wood product intact for other applications. However, there is concern that removing hemicelluloses from the precur...
C Howell, J Paredes, S Shaler, J Jellison
Decay resistance of propionylated Iranian beech against the white rot fungus Tramets versicolor
2008 - IRG/WP 08-30449
In this study, the decay resistance of propionylated beech was investigated against the white rot fungus Trametes versicolor. Iranian beech (Fagus orientalis) was modified with propionic anhydride at different temperatures, concentrations and times without using any catalyst. Different weight percentage gains (WPGs) were obtained under different conditions. The decay resistance of the esterifed wo...
M R M Farahani, S M Hosseini
Soft Rot Determines Service Life of L-joints with Low Borate Loading
2008 - IRG/WP 08-30470
As part of a research program on the potential use of borates by the Canadian wood products industry, Forintek set up an L-joint test of untreated and borate-diffusion treated hem-fir (western
hemlock and amabilis fir) in 1990. The treated material had a low initial retention of only 0.2% boric acid equivalent and analysis after 5 years revealed no detectable borate close to the tenon. Nev...
P I Morris, J Wang, J K Ingram
The susceptibility of hardwood plywood to white rot
2008 - IRG/WP 08-40397
The subject of the tests was resistance of veneer hardwood plywood to activity of pure culture of white rot fungus Trametes versicolor. The tested plywood was made with the use of the following glues: urea-formaldehyde (UF), melamine-urea-formaldehyde (MUF) or phenol-formaldehyde (FF). 4, 12 and 15 mm thick plywood was tested. External veneer of the plywood was mostly alder and the inner veneer (c...
A Fojutowski, A Kropacz