Your search resulted in 1153 documents. Displaying 25 entries per page.
Chemical analyses of IRG/COIPM INTERNATIONAL MARINE TEST (to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water) samples
1987 - IRG/WP 4114
Chemical analysis of CCA and CCB treated timber was carried out after exposure at tropical and temperate marine sites. Results indicated that losses of all elements had occurred. In particular, losses of boron were severe. Arsenic and copper were also lost. The chromium components in both formulations was the most dominant metal remaining. The results suggest that chromium modification was importa...
L E Leightley
Second international symposium on wood preservation "The challenge safety-environment" 8-9 February 1993, Cannes-Mandelieu, France
1993 - IRG/WP 93-50001
Contains the following 34 Documents (IRG/WP 93-50001/1 - IRG/WP 93-50001/34) and 4 abstracts:
A methodology for the life-cycle assessment of treated timber products (IRG/WP 93-50001/1)
Initial results and observations of a model system to assess the efficacy and environmetal impact of preservative treated wood (IRG/WP 93-50001/2)
Borates as wood preservatives - an environmental, health and safe...
Anonymous
Comparison of decay rates of preservative-treated stakes in field and fungus cellar tests. Results after 40 months fungal cellar exposure
1983 - IRG/WP 2200
Decay rates of preservative-treated Pinus radiata stakes during 40 months exposure in the FRI fungus cellar were compared with those of similarly treated material in a field test. Decay rates in the fungus cellar were from 4 to 100 times higher than in the field, although for the majority of preservatives the rate was between 7 and 12 times higher. The lag phase before onset of decay, noticeable w...
M E Hedley
Chromium on the surface of CCA-treated wood
1978 - IRG/WP 386
Chromium in solutions of CCA preservatives is predominantly in the hexavalent state (Cr VI). It is well known that Cr VI is associated with dermatitis and skin ulceration in workers handling chromium containing products and processes. When reduced to the trivalent state, however, chromium is considerably safer. An essential part, therefore, of safety procedures in any chromium - using industry is ...
C R Coggins, P Hiscocks
Retention and distribution of copper/chrome/arsenic (CCA) in pressurised sap-displaced UK grown spruce and pine
1986 - IRG/WP 3366
Increment cores were taken from UK grown Scots pine (Pinus sylvestris L.), Corsican pine (Pinus nigra var. maritima Ait), Sitka Spruce (Picea sitchensis (Bong) Carr), and Norway spruce (Picea abies (L) Karst) distribution poles treated by pressurised sap-displacement using a 1.8% copper, chrome, arsenic (CCA) solution. Each increment core was sectioned radially and the copper, chrome, and arsenic ...
P D Evans, G M Smith, B King
The volatilization of arsenic on burning copper-chrome-arsenic (CCA) treated wood
1978 - IRG/WP 3111
Small scale burning experiments are described involving copper-chrome-arsenic treated wood. Approximately 20 per cent of the arsenic was volatilised when the wood was burned in air but 60 per cent when burned in an oxygen-enriched atmosphere, this increase is attributed to an increase in combustion temperature. Although a small increase in arsenic evolution was found with an increased concentratio...
A-J Dobbs, C Grant
Initial microbial colonisation of CCA-treated, creosote-treated and untreated Pinus sylvestris L. blocks in seawater
1996 - IRG/WP 96-10171
CCA-treated, creosote-treated and untreated Pinus sylvestris sample blocks were immersed in a seawater through-flow system for periods of between 1 and 265 hours. Samples were fixed immediately on removal and examined both qualitatively and quantitatively using the scanning electron microscope. This study of primary microbial colonisation showed differences between treatments in the diversity of m...
K Sturgess, A J Pitman
Modelling the control of decay in freshly felled pine poles
1997 - IRG/WP 97-10206
In a recent study investigating control of decay in freshly felled pine utility poles, it became apparent that the efficacy of different treatment methods was strongly related to the size of the material being treated. A topical application of 5% w/v disodium octaborate tetrahydrate (DOT), brush applied to the cut surfaces of logs with otherwise intact bark was just as effective at excluding white...
M W Schoeman, W Van der Werf, J F Webber, D J Dickinson
Ultrastructure of degraded, CCA-treated Pinus radiata wood from a marine pile
1990 - IRG/WP 1461
During an inspection of marine piles, 12 years after installation, severe degradation was noted on one of them in the vicinity of a corroded eye-bolt. The wood was dark brown in colour and tended to crumble easily. Wood fragments were examined by light microscopy and scanning and transmission electron microscopy and were also analysed for carbohydrates and lignin. Light microscopy showed numerous ...
A P Singh, M E Hedley
International standards can we make them simple?
1996 - IRG/WP 96-20092
The earth is round and therefore limited in space. A consequence is that we - earthlings - are convicted to mutual understanding with a basic need to pay attention to others. Leading countries have been developing standards for years (i.e. USA/CANADA - AUSTRALIA/NEW ZEALAND - SOUTH AFRICA - EUROPE). They are keen and proud to argue on their peculiarities and advantages. A survey of the various sch...
G Ozanne
Effectiveness of Busan 30 treated birch blocks in a soil medium
1987 - IRG/WP 3409
TCMTB based formulation has been anticipated for use in dip-diffusion treatment in Papua New Guinea to replace BFCA Wood preservative. One such formulation is the Penacide (TCMTB + MBT Boron) which is currently being tested against fungi and insects. Accelerated laboratory test in soil exposure was employed to test a related formulation (Busan 30) to determine its effectiveness against soil inhabi...
H C Konabe
Fungal colonization of CCA-treated decking
2003 - IRG/WP 03-10491
The identification of fungi isolated from CCA treated decking in Vancouver is reported. About two thousands locations were sampled from over sixty boards recovered from six decks. Wood chips from each location were placed onto four different types of media. Of the large number of isolates obtained, around 15% were obtained from the interior of the boards. The succession of colonization in CCA-...
S Choi, J N R Ruddick, P I Morris
Chemical Analysis of Southern Pine Pole Stubs Thirty-Nine Months Following Treatment with Three Methylisothiocyanate-Based Fumigants
2004 - IRG/WP 04-30349
Agricultural fumigants have been commercially used in the United States for over 20 years to control internal decay in utility poles and other wooden structures. Of the four fumigants which are currently used in the remedial treatment of utility poles, three are based on methylisothiocyanate (MITC) as being the principal fungitoxic component. Two of these MITC-based fumigants, liquid metham sodi...
R J Ziobro, J Fomenko, D J Herdman, J Guzzetta, T Pope
Determination of total fluoride in preservative-treated wood by ion selective electrode, without steam distillation
1996 - IRG/WP 96-20086
An analytical method was developed to determine total fluoride in wood treated with aqueous fluoride or borate-fluoride formulations. Ground wood was mixed with 60% sodium hydroxide solution and oven-dried overnight before furnacing at 600°C. The cool fused product was dissolved in warm water before adding a powerful complexant/buffer solution containing sulphosalicylic acid and EDTA. Fluoride wa...
M J Kennedy
Moisture condition in treated wood exposed outdoors. A progress report after 5 years
1992 - IRG/WP 92-3720
Wood treated with water-borne preservatives, mainly CCA (copper, chromium and arsenic) and CCB (copper, chromium and boron) is often said to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed (Johansson 1977). In 1986 a project was started to compare water absorption during outdoor exposure between wood stakes of pine, Pinus sylvestris L, and spruce, P...
M-L Edlund
The use of a physical field model to study the effects of remedially treated timber on the growth of perennial ryegrass (Lolium perenne) and rye (Secale cereale), and the accumulation of toxic preservative constituents in Lolium perenne
1995 - IRG/WP 95-50040-02
Low cost laboratory model systems can be used to give relatively rapid indications of the environmental effects of preservative treated timber in soil contact. This paper details the effects of remedially treated timber on the growth of crops of Lolium perenne and Secale cereale seeded on soilbeds of different texture in close proximity to remedially treated creosoted pole sections. Lolium perenne...
D C R Sinclair, G M Smith, A Bruce, H J Staines
The evaluation of the occurrence of soft rot in creosoted wooden poles
1988 - IRG/WP 1368
The occurrence of soft rot decay in creosoted wooden poles for overhead power lines was investigated by collection of field samples, their subsequent microscopic examination and statistical analysis of the data collected. Examination of samples collected from 296 poles revealed that approximately 15% of the pole population studied (Eastern Electricity Board) showed the presence of soft rot decay. ...
A Wylde, D J Dickinson
Mechanical resistance of Pinus radiata CCA treated and face jointed with PVA adhesive
1999 - IRG/WP 99-40140
Due to the increased use of Pinus radiata timber composites (laminated structural members, panels, etc), its low natural durability and the toxicity of phenol-formaldehyde type adhesives, a PVA (polyvinyl acetate) adhesive was evaluated in machined and rough CCA treated and untreated face joint samples under DIN 68602 (EN 204-205) standard for groups of requirement 3 and 4. The results showed that...
M C Rose, L Reyes, P León
The shower test method. A leaching test for assessing preservative losses from treated timber under simulated open storage conditions
1993 - IRG/WP 93-50001-04
In the late 1980's against the background of increasing environmental concern a laboratory based accelerated leaching test method for assessing preservative losses-from stored, treated timber was developed by the Dutch organisation for applied Scientific Research (TNO). This test method quantifies the amount of specific preservative components which leach from treated timber under simulat...
J B G A Havermans, W J Homan, M J Boonstra
Premature decay of CCA-treated pine posts in horticultural soils - An overview
1984 - IRG/WP 1241
The recent discovery in New Zealand of early decay in CCA-treated pine posts set in horticultural soils led to the establishment of a comprehensive research programme. The objectives and outline of this programme are presented together with an overview of research progress to date. Results suggest that premature decay of CCA-treated timber is restricted to material placed in highly cultivated soil...
J A Butcher
High CCA retentions and the protection of eucalypt power poles
1983 - IRG/WP 3226
Tasmanian power pole material treated to high retentions, was analysed to accurately determine the amount of CCA preservative in the timber. Material from the same disc was subsequently exposed in unsterile soil in order to determine the effectiveness of treatment. Results showed that even at high retention levels, soft-rot attack was not prevented. Fourteen further poles were sampled, but this ti...
L E Leightley, J Norton
Summarized comparison of four techniques for detecting defects in poles
1979 - IRG/WP 2126
Since our discussions in open session of Working Group II at Peebles, a number of workers in Australia have collaborated in comparing the efficacy of X-ray, sonic testing, or resistivity measurements for detecting internal defects in poles. The purpose of this circular is to draw to your attention some of the results, in summary form. No attempt has been made to compare techniques. More detailed a...
H Greaves
A Preliminary Report on the Properties of Engineered Wood Composite Panels Treated with Copper Naphthenate
2005 - IRG/WP 05-40294
This paper reports on our preliminary investigation of the properties of randomly oriented strandboard which had waterborne or powdered copper naphthenate (CuN) incorporated into the board during manufacture. When compared to zinc borate-treated controls (ZnB), the mechanical properties of strandboard (MOR, MOE, work-to-maximum load, internal bond strength) were not adversely affected by treatmen...
J W Kirkpatrick, H M Barnes
Leachability And Decay Resistance of Copper-Treated Wood
2004 - IRG/WP 04-30337
Samples of scots pine sapwood (Pinus sylvestris L.) were treated with solutions of (Copper II sulfat-5 hydro + fluoroboric acid) and (Copper II sulfat-5 hydro + fluoroboric acid + boric acid) in order to determining to leachability and decay resistance against brown rot fungus (Postia placenta) and white rot fungus (Coriolus versicolor).
Results indicated that the copper in treated wood is less s...
A Temiz, T Nilsson, I Deemirtas, Ü C Yildiz
Bending properties of TCMTB-treated Southern pine sapwood using supercritical carbon dioxide impregnation process
1997 - IRG/WP 97-40080
The effects of elevated pressure and treatment with thiocyanomethylthiobenzothiazole (TCMTB) on the bending properties of Southern pine sapwood were evaluated at pressures ranging from 1,800 to 3,600 psi. All bending properties were affected to some extent by supercritical fluid treatment. Modulus of elasticity and work to maximum load were not significantly affected by pressure levels. Modulus of...
Gyu-Hyeok Kim, S Kumar, E S Demessie, K L Levien, J J Morrell