In-ground field test of scots pine (Pinus sylvestris L.) sapwood and heartwood
2004 - IRG/WP 04-30336
Scots pine (Pinus sylvestris L.) sapwood and heartwood stakes treated with CCA-C and creosote were tested for one- year in a field plot in Bartın region in Turkey.
Scots pine heartwood stakes had lower preservative retention than sapwood stakes. Bending strength of the stakes was decreased after impregnation and one-year field test. While the bending strength of untreated sapwood was 93....
H Sivrikaya, H Hafizoglu
Long term experiments for assessing the diffusion of boric acid and diluorides from local preservative pills in spruce and pine
1996 - IRG/WP 96-40065
For the experimental assessment of the diffusion of boric acid and difluorides over a three year period 2 tests were set up. In a test with large spruce blocks (150 x 150 x 300 mm³) 3 different pill types were exposed to 3 different climates: climate room (20°C, 65% r.h.), wet room (20°C, 95% r.h.), and to outside exposure. In a test with open L-joints without paint, with an alkyd paint and wit...
W J Homan, H Militz
Incomplete fixation of chromium in the pre-treated wood with a solution of copper and arsenic compounds
1995 - IRG/WP 95-50052
Ponderosa pine wood thin sections were treated with a combination of chromium, copper, and arsenic chemicals. The wood sections was analyzed by electron spin resonance spectrometry (ESR) and X-ray photoelectron spectrometry (XPS) to elucidate the mechanism of fixation of the chromated-copper preservatives. The wood subjected to the two-step treatment with copper and arsenic followed by chromium ex...
J N R Ruddick, K Yamamoto, F G Herring, P C Wong, K A R Mitchell
Borate diffusion in wood from rods and liquid product. Application to laminated beams
1988 - IRG/WP 3482
In the aim to use borate preservatives (fused rods and boracol) in fields of building construction other than external joineries, tests of diffusion of borate rods and secondary boracol, were carried out on different species of woods exposed to different moisture conditions. Tests were also applied on laminated beams very often subjected to high moisture contents and thus decay of rot fungi. Diffu...
D Dirol
New conception for shortering the duration of fungitoxic test of wood preservatives. Part 2: Computer-assisted miniaturisation of wood specimens
1994 - IRG/WP 94-20052
The mass loss of wood used as a criterion in the standarised agar-block method of evaluation of toxic value of preservatives depends upon the relationship between volume of specimens, their outspread planes and ratio of areas of particular anatomic sections. Upon the computer-assisted mathematical basis the dimensions of miniaturized specimens which make 1/2, 1/4, and 1/8 part of standarized ones ...
J Wazny, K J Krajewski
Evaluating the potential of amine chemicals for use as wood protecting agents. Part 1: Investigation of cation components of quaternary ammonium compounds
1994 - IRG/WP 94-30049
Quaternary ammonium compounds (quats) have shown a great potential as more environmentally acceptable wood preservatives. In order to identify chemicals possessing the wood protecting potential, an evaluation was carried out of a range of commercially available 'quats', using a modified soil block test. Ponderosa pine sapwood blocks were treated with selected 'quat&a...
Hang Tang, J N R Ruddick
Bacteria are important degraders of cooling tower timbers: New Zealand experience
1995 - IRG/WP 95-10128
Microscopic examinations of CCA-treated Pinus radiata timbers in industrial cooling towers in New Zealand showed bacteria and soft rot fungi to be primarily responsible for the decay of these timbers. Of these micro-organisms, erosion bacteria appeared to be most widespread, attacking wood cell walls independently as well as together with tunnelling bacteria and soft rot fungi. Tunnelling bacteria...
A P Singh, R N Wakeling
Treatment application method and CCA efficacy in Corsican pine - Assessment by serial exposure and soil burial tests
1993 - IRG/WP 93-40006
A previous report on this research (Newman and Murphy, 1992) identified possible variation in the efficacy of a CCA preservative applied to Corsican pine (Pinus nigra var. maritima) dependant upon the treatment application method (Bethel, Lowry or Steam/Bethel). This paper presents further data from biological testing of CCA treated Corsican pine using serial exposure and unsterile soil techniques...
P R Newman, R J Murphy
Tests with ammoniacal copper and alkyl ammonium compounds as wood preservatives
1984 - IRG/WP 3299
Formulations based on copper and alkyl ammonium compounds in ammonia solution have been tested in a fungus cellar on Pinus radiata and Fagus sylvatica. This type of products gives promising results as wood preservatives, especially on hardwood and are safe to destroy by e.g. combustion. The best results were achieved with a dialkyl ammonium compound, Cu/octyldecyl dimethyl ammonium chloride (NH3)....
C-E Sundman
Comparison of methods for monitoring CCA fixation
1994 - IRG/WP 94-40023
The CCA fixation status in the outer 12.5 mm of pole sections of southern pine (Pinus sp.), red pine (Pinus resinosa) and lodgepole pine (Pinus contorta var. latifolia) were followed during fixation at 21°C under non-drying conditions by the following procedures: - Qualitative CrVI indication by the chromotropic acid spot test. - Quantitative CrVI in the expressate by the diphenylcarbazide method...
P A Cooper, Y T Ung, G Zanjani
Field trials of Sinesto B at some sawmills in Portugal
1989 - IRG/WP 3512
The efficacy of SINESTO B as antistain chemical for use in Portugal has been studied. The studies were done during the years 1987-1988 at several Portuguese sawmills in co-operation with the Instituto dos Produtos Florestais and the APCIM (Associacao Portuguesa de Comercio e Industria de Madeiras). SINESTO B was used in 5% and 8% concentrations. The storage time varied from 10 weeks to 6 months. I...
I A Linderborg
On the laboratory use of X-rays in timber decay evaluations
1981 - IRG/WP 2144
The paper reports the results of laboratory experiments on the X-raying of some Pinus radiata sapwood blocks infected with Serpula lacrymans to determine the effect of density and moisture content on the absorption of X-rays by wood. It is concluded that with increasing moisture content there is a very marked increase in time required to pass a constant quantity of X-rays through a test block and ...
J D Thornton, J W Creffield, O Collett
On the occurrence of Phialophora species in preservative treated wood in ground contact
1977 - IRG/WP 163
Phialophora is a fairly large genus comprising about thirty described species. They are widespread in very diverse environments, such as soil, sea water, wood and wood pulps. Some species are known as parasites on plants and animals, including man. Phialophora species were early known for their ability to produce blue stain in timber. Later it was discovered that several species were able to produ...
T Nilsson, B Henningsson
Laboratory tests on the residual effects of pyrethroids against termites after one year
1983 - IRG/WP 1216
Due to recent restrictions of ecological nature which most of pesticides are been submitted, it is necessary in wood preservation to test new products and formulation with low mamalian toxicity for substitution of the traditional products. The efficiency of five synthetic pyrethroids in comparison to the traditional organo-chlorinated pesticide chlordane was evaluated. Wood blocks impregnated with...
A M F Oliveira
Evaluation of a new anti-sapstain formulation
1994 - IRG/WP 94-30035
A new anti-sapstain mixture, which consists of 2% IPBC (3-iodo-2-propynylbutyl carbamate) and 1.5% DCOI (4,5-dichloro-2-n-octylisothiazolin-3-one), was evaluated by three methods in the laboratory. A standardized test (JWPA standard 2) demonstrated that the new anti-sapstain formulation was highly effective in controlling growth of monocultures of five test fungi on wood substrate. When exposed to...
K Tsunoda, H Kumagai, M Sakurai
Rapid loss of lignin at wood surfaces during natural weathering
1992 - IRG/WP 92-2390
Thin veneers of radiata pine (Pinus radiata D. Don) were exposed to natural weathering over a period of 30 days. Incident UV radiation was monitored at the test site. FTIR internal reflectance spectroscopy was used to study the chemical changes taking place at the veneer surface during weathering. Spectra obtained show that after only 3 days exposure there was substantial delignification at veneer...
P D Evans, K J Schmalzl, A J Michell
Rainfall simulation to assess CCA permanence
1991 - IRG/WP 2373
During experimental work on accelerated fixation of chromium containing preservatives a method has been developed which compares the degree of preservative levels of contamination of simulated preservative fixation in timber with the levels of simulated rainfall. This method uses commercial sized wood sections wetted in a way that simulates actual rainfall and relates the associated run-off contam...
P Warburton, J A Cornfield
Surface accumulation of copper on CCA-impregnated Pinus patula stakes during marine preservative trials in the southern hemisphere
1992 - IRG/WP 92-4181
Pinus patula stakes treated with CCA to target retentions of 30 kg/m³ salts were exposed to sea water in marine and estuarine ecosystems off the coast of Southern Africa for two years. Samples were then analysed for copper and arsenic. Analysis of samples from the marine ecosystem showed (IRG/WP/4167) that arsenic was longitudinally and transversely leached from the wood, whereas the copper was r...
G D Shelver, C D McQuaid, M Tarin, A A W Baecker
Effect of test site, preservative and wood species on decay type Glenbervie pastoral and radiata pine forest sites
2000 - IRG/WP 00-30248
Pinus radiata stakes were treated with 0.8, 1.2, 1.8, 2.7 and 4.1 kg/m3 of CCA and Fagus sylvatica with 2.7, 4.1 and 6.1 kg/m3 of CCA. Both wood species were also treated with equivalent retentions of a copper plus triazole preservative (CT) (0.89, 1.3, 2 and 3 kg/m3 of copper for pine & 2.5 and 4 for beech) and chlorothalonil plus chlorpyriphos in oil (CC) (1.4, 2.1, 3.2 and 4.8 kg/m3 of chlo...
R N Wakeling
Permanence of permethrin and bifenthrin in framing timbers subjected to hazard class 3 exposure
2005 - IRG/WP 05-30383
End-sealed Pinus radiata specimens measuring 235 x 90 x 35 mm were treated using a modified Lowry schedule with permethrin or bifenthrin in white spirit to Hazard Class 2 (H2) retentions. After conditioning, the specimens were exposed at 45o on north facing racks near Melbourne (Australia). Samples of the specimens were taken before installation, and after three and six months exposure. Analyses o...
A C Hunt, D G Humphrey, R Wearne, L J Cookson
The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen
The effect of chemical treatment on the moisture distribution of Pinus radiata D.Don subjected to wick action
1999 - IRG/WP 99-40135
Radiata pine sapwood stakes were treated with a range of chemicals, including an ammoniacal copper quaternary ammonium compound (ACQ), a copper-chrome and arsenic (CCA) solution and a CCA-oil treatment, potassium linoleate copper linoleate, a paraffin wax and a proprietary alkyd resin. The effect of these treatments on the extent of water absorption and moisture movement through the stakes was inv...
J Hann, P Vinden
Assessment of residual retentions in creosote treated Scots pine (Pinus sylvestris) poles after 45 years ground contact service in the Lemstervaart in the Dutch polder
1994 - IRG/WP 94-50022
In a project funded by the Water State Authorities (RWS) and the Noordoostpolder Water Board, the residual retentions in ten creosote treated Scots pine (Pinus sylvestris) poles were examined after 45 years ground contact service along a canal (Lemstervaart) in the Dutch Noordoostpolder. The Lemstervaart location was selected due to the fact that the poles involved had been originally treated and ...
P Esser, W L D Suitela, A J Pendlebury, H Visscher
The comparative resistance to fungi of the wood munika (Pinus heldreichii Christ.), fir (Abies alba Mill.) and spruce (Picea excelsa Poir.) compared with Pinus sylvestris L. and some physical and mechanical characteristics of munika
1981 - IRG/WP 1129
The munika (Pinus heldreichii Christ.) is situated primarily in the Balkans, and partially in the south of the Apenine peninsula. As an endemic species, with a very little annual increment, it has not been used enough as a timber for mechanical conversion up till now, although the oldest trees can grow to 27 m in height, with a diameter at breast height of about 60 cm. According to data of many Ba...
M Petrovic, M Miric
The performance of metal-chromium-arsenic formulations after 32 to 38 years' in-ground exposure in Australia
2000 - IRG/WP 00-30240
Two trials of metal-chromium-arsenic preservatives were exposed in-ground in Australia. In Trial 1, Pinus radiata stakes treated with Boliden K.33, Boliden S.25, Celcure A, Tanalith C and Tanalith CA were installed at Sydney and Narrandera in 1961/1962. In Trial 2, P. radiata and Eucalyptus regnans sapwood were treated with Celcure A, Celcure A21-N, Celcure A 21-O and Tanalith CA (new) and install...
G C Johnson, J D Thornton, J Beesley