Leaching of preservative components from pine decking treated with CCA and copper azole, and interactions of leachates with soils
2001 - IRG/WP 01-50171
Radiata pine decking was treated with CCA and copper azole preservatives to Australian H3 retention using conventional and modified Bethel schedules, and air-dried. Treated decking boards and durable hardwood controls were subjected to leaching in weather-exposed decks, and matching 19mm cubes were leached in extended AWPA E11-97 lab tests. Deck runoff and E11 leachate water was analysed after rai...
M J Kennedy, P A Collins
Microwave digestion of preserved wood for the determination of Cu, Cr, As, B and P in quality control
1991 - IRG/WP 2364
A microwave digestion method for the determination of copper, chromium, arsenic, boron and phosphorus in preserved woods is described. Samples were digested with nitric acid in pressure-relief type teflon PFA vessels by microwave heating in a commercial laboratory microwave oven. Fast, efficient and complete digestion was achieved within 29 min for 12 samples. The digestion time compared favourabl...
N Bernth, L B Sheard
Laboratory Evaluation and Field Trial of Chlorothalonil and Copper-based Preservatives and Leaching Performance of Copper in Copper Treated Wood
2002 - IRG/WP 02-30279
Soil block test and field trial of some Chinese plantation wood species pine and poplar treated with chlorothalonil formulations and copper-based preservatives such as ACQ-B and copper citrate (CC) were conducted. The results of soil block test indicated that chlorothalonil formulations and ACQ-B as well as CC are very effective for controlling the 2 fungi species Corious versicolor and Poria plac...
Mingliang Jiang, Ping Wang, Chungen Piao, Zhaobang Li, Quan Lu, Lei Liu
Diffusion modeling of inorganic wood preservative leaching in service
2005 - IRG/WP 05-50224-5
To evaluate the potential environmental and health implications of leaching of inorganic wood preservatives in service under different conditions, there is a need for a predictive model that provides estimates of the rate and extent of leaching over a wide range of product dimensions and exposure conditions. In this paper, we show that the leaching behavior of inorganic preservative components fr...
L Waldron, P A Cooper, Y T Ung
Determination of the amine to copper ratio remaining in wood after leaching
2002 - IRG/WP 02-30285
The effectiveness of the protection and the environmental impact of the treated wood are two of the most important aspects that need to be understood for all preservatives. Both are particularly influenced by the loss of biocidal components from treated wood. For amine copper preservatives, copper fixation determines the leaching resistance of the copper and amine compounds formed in wood. Previou...
N Lucas, J N R Ruddick
Leaching of arsenic, copper and chrome from preservative-treated timber in playground equipment
1984 - IRG/WP 3149
Samples were taken from CCA-treated timber in sand play boxes and other play ground equipment. Sand was also sampled. Sand and wood samples were analysed for copper, chrome and arsenic by AAS. About 20-25% of the arsenic had leached from the timber after 2-4 year's exposure in the playgrounds. Very little of the copper and chrome had been leached. Sand collected in the close vicinity of t...
B Henningsson, B Carlsson
Microwave treatment to Accelerated fixation of copper-ethanolamine (Cu-EA) treated wood
2004 - IRG/WP 04-40271
This study evaluated the use of microwave post-treatment to accelerate fixation of copper-ethanolamine (Cu-EA) treated 19 mm southern yellow pine sapwood cubes. Cubes were pressure treated at 3.2 and 6.4 kg/m3 Cu retention target, after which they were microwave post treated during different duration periods. An accelerated AWPA leaching test was conducted during 300 hours to determine the amount...
Jinzhen Cao, D P Kamdem
Moderate temperature fixation of CCA-C
1989 - IRG/WP 3522
Several Canadian treating plants are using moderate temperature (40-60C°) fixation chambers to reduce drippage and leaching from fresh CCA treated wood. In this study, chromium reduction and surface leaching properties of CCA-C treated red pine (Pinus resinosa) pole sections were monitored during exposure to temperatures of 50-60C° and 90-100% RH conditions. Chromium-VI concentration in the abso...
P A Cooper, Y T Ung
Effect of species, retention and conditioning temperature on copper stabilization and leaching for ACQ-D
2004 - IRG/WP 04-30342
The time to stabilization or equalization of the copper component of ACQ-D was highly dependent on treating solution concentration (preservative retention) and post treatment temperature. Stabilization was rapid for low preservative retentions but extended times were needed for wood treated with higher concentration solutions. The extent of stabilization was also concentration dependent with a h...
Y T Ung, P A Cooper
Studies of the mechanism of chromated-copper preservative. Fixation using electron spin resonance
1992 - IRG/WP 92-3701
Two softwoods and one hardwood species were treated with chromium trioxide, copper sulphate, chromated-copper wood preservative (CCA). The treated wood samples were analyzed during fixation by electron spin resonance (ESR). ESR spectra indicated that more than one Cr(V) species was generated from Cr(VI) soon after CCA treatment. The Cr(V) signal became strong within increased several hours followe...
K Yamamoto, J N R Ruddick
Efficacy of waterborne copper naphthenate as preservative for northern hardwood species
1995 - IRG/WP 95-30091
Northern red oak (Quercus rubra) and red maple (Acer rubrum) cubes pressure treated with waterborne formulation of copper naphthenate were evaluated for resistance to attack by brown fungi Gloeophyllum trabeum (Pers. ex Fr.) Murr. (Madison 617 ATCC 11539) and Poria placenta (Fr.) Cooke (Madison 698, ATCC 11538), white rot fungi Trametes versicolor (L. ex Fr.) Pilat (R-105 from Jeff Morrell), Irpex...
D P Kamdem, R Fair, M H Freeman
Chromated copper arsenate preservative treatment of hardwoods. Part 2: leaching performance of seven North American hardwoods
1997 - IRG/WP 97-30132
Seven North American hardwood species were treated with 2% CCA-C solution and fixed at temperatures of 21°C and 50°C and conditions of high relative humidity (95%) as described in Part 1 of this presentation. Red pine (Pinus resinosa) was included as a softwood for comparison. Adequately fixed wood blocks (99.9% chromium fixation) were exposed to leaching tests according to AWPA E11-87 test. Par...
T Stevanovic-Janezic, P A Cooper, Y T Ung
Fouling organisms as indicators of the environmental impact of marine preservative-treated wood
1995 - IRG/WP 95-50063
This study evaluates the use of fouling organisms (epibiota) to assess the environmental impact of preservative treated wood. This paper presents initial findings from treated panels exposed for 6 months at Sagres, Algarve, Portugal. Panels were treated with CCA, two copper-containing quaternary ammonium (ACQ) formulations and creosote, with nominal retentions from 10 to 40 kg/m³ (creosote 25 pcf...
R M Albuquerque, S M Cragg
Basilit CCFZ. Further studies on ecotoxicological behaviour
1992 - IRG/WP 92-3722
Basilit CCFZ is a new developed water based preservative for the protection of timber in hazard class 4 and 5 (ground-, fresh- and salt-water contact). The active components of this salt are copper, chromium, zinc and fluorine. In addition to primarily studies on the acute toxicity against organisms of the aquatic food chain a long term ecotoxicological study was performed. In a prolonged toxicity...
H W Wegen
Fouling assemblage development on copper-chromium-arsenic-treated timber submerged in European waters
2002 - IRG/WP 02-50181
The effect of the anti-marine-borer timber preservative CCA on community development of non-target marine fouling animals was investigated. Panels of Scots pine treated to target retentions of 12, 24 and 48 kg CCA per m3 of wood, plus untreated controls were submerged at seven coastal sites (Portsmouth, UK; La Tremblade (2 sites), France; Ria Formosa, Portugal; Sagres, Portugal; Kristineberg, Swed...
C Brown, R J Eaton, S M Cragg, P Goulletquer, A Nicolaidou, M J Bebianno, J Icely, G F Daniel, T Nilsson, A J Pitman, G Sawyer
Recovery of copper, chromium, and arsenic compounds from the waste preservative-treated wood
1991 - IRG/WP 3651
In Japan, about 40 percents of waste wood is incinerated and the residue is dumped into the landfill site. The waste preservative-treated wood, which is mixed in nontreated wood, is incinerated in the same way, too. However, it will cause the serious problems that the gases contained with high concentration arsenic compounds are discharged from the smokestacks of the incineration facilities and th...
A Honda, Y Kanjo, A Kimoto, K Koshii, S Kashiwazaki
The content and mobility of copper, chromium and arsenic in the soil of a wood preserving plant using CCA
1998 - IRG/WP 98-50122
Analyses were carried out on soil and water samples obtained from a wood preserving plant using CCA-type preservatives. The plant has been in operation since 1969. The soil samples were obtained on 8 points from 4 different depths. The estimation of the type of soil was followed by investigations of copper, chromium and arsenic contents, and the mobility of these elements. The soil samples were al...
N Erdin, S N Kartal, A Dilek Dogu, M O Engür
Comments on leaching in view of accelerated testing
1977 - IRG/WP 294
We developed an accelerated test for leaching at elevated temperatures (75-85°C). This test was used for the examination of 11 preservative formulations containing Cu, Zn and As. The data obtained from these experiments were compared with data on some formulations tested by ASTM standard leaching test. The method consists in making a large surface to volume ratio of wood from a treated block by c...
J Rak
A comparison of the leaching resistance of copper 2-ethanolamine and copper ethylenediamine treated Scots pine
2000 - IRG/WP 00-30233
The depletion of copper from copper 2-ethanolamine and copper ethylenediamine treated Scots pine blocks was investigated. A greater leaching resistance was found for copper 2-ethanolamine, which retained ca. 86% and ca. 50% copper after water and buffer leaching, respectively. Leached amine treated blocks also contained significant residual amine. This was consistent with other observations linked...
Xiao Jiang, J N R Ruddick
The effect of soil pre-exposure on the results of laboratory Basidiomycete testing
1991 - IRG/WP 2385
Scots pine sapwood blocks were treated with several concentrations of copper chrome arsenic (CCA), copper chrome boron (CCB) and a copper modified quaternary ammonium compound (CMAAC). Leached and unleached samples were exposed in a basidiomycete monoculture test using Coniophora puteana, a copper tolerant brown rot. Prior to testing half of the blocks were buried in unsterile soil for 4 weeks. Th...
S M Gray
Recycling and disposal of timber treated with waterborne copper based preservatives
1993 - IRG/WP 93-50008
Recycling and disposal technologies are briefly reviewed. Details are given of chemical extraction techniques suitable for recovery of copper from timber treated with a new copper based preservative, and traditional chromium based products. Details of thermal decomposition tests according to the DIN 53436 protocol under flaming and non-flaming conditions are given. The decomposition products were ...
J A Cornfield, S Vollam, P Fardell
Modelling of copper emission fron treated wood leached according to NEN 7345 and ENV 1250.2
1996 - IRG/WP 96-20097
A series of water leaching experiments is carried out investigating pine and spruce treated and fixed using different copper-containing preservative solutions and process technologies. Water changes took place as prescribed in the Dutch standard NEN 7345 and the European test method ENV 1250.2, each of the leachates being chemically analysed for their copper content. Irrespective of the preservati...
G M F Van Eetvelde, S G L Michon, M Stevens
Inter-laboratory comparison of assessment methods for wood preservatives against subterranean termites: Determination of protection threshold limits for CCA
1999 - IRG/WP 99-10317
In 1996, several institutes conducted laboratory bioassays on the efficacy of unleached Pinus radiata specimens treated with copper-chromium-arsenic (CCA) and copper naphthenate (Cu Naph) at retentions of 0.5, 1.0, 2.0 and 4.0 kg/m3 (total salt for CCA; elemental copper for Cu Naph) against a range of species of subterranean termites (IRG/WP/96-10174). Each participant employed the standard test m...
J W Creffield, M Lenz
Comparison of laboratory tests and field experiments for the estimation of emissions from treated wood
2005 - IRG/WP 05-50224-6
The authorisation procedure for biocidal products according to the European Biocides Direc¬tive in¬cludes the assessment of possible environmental risks by the emission of ac¬tive ingre¬dients. This needs an input of data on the expected emissions of biocides into environmental com¬part¬ments. The procedures for the estimation of these emissions should be harmonised. La¬boratory test proceÂ...
U Schoknecht
Impact of leachates from CCA- and copper azole-treated pine decking on soil-dwelling invertebrates
2002 - IRG/WP 02-50183
This study assessed the short-term effects on non-target soil invertebrates of leachates from a naturally durable hardwood and timber treated with two copper-based wood preservatives. Natural rainwater leachates from kwila decking, and radiata pine-decking treated with CCA or copper-azole, were collected and applied on mown lawn soil in Brisbane, Queensland. The soil study consisted of 5 treatment...
N Crumière, A House, M J Kennedy