Fluoride and chromium concentrations in soil adjacent to remedially treated distribution poles
1996 - IRG/WP 96-50066
Soils adjacent to Rentex treated 'on-line' distribution poles were analysed for total fluoride and chromium content for comparison with background values of these elements. Soil samples 6 cm and 25 cm downslope of selected poles were recovered at 1 week, 1 month, 6 and 12 months after treatment. Background soil samples were taken 50 m from the poles at sampling times. Fourteen po...
D C R Sinclair, G M Smith, A Bruce, H J Staines, P Durrant
Interaction of copper-amine complexes with wood: Influence of copper source, amine ligands and amine to copper molar ratio on copper retention and leaching
1999 - IRG/WP 99-30203
The absorption and leachability of copper in copper amine (Cu-EA) treated wood are influenced by the formulation and the composition of copper amine treating solutions. The sources of copper used, Cu(OH)2, CuCO3, CuSO4 and Cu(NO3)2, in the copper amine complex formulation affect the leachability of copper. Data show that copper amine from CuSO4 and Cu(NO3)2 treated wood has less copper loss during...
Jun Zhang, D P Kamdem
Quantification of creosote migration down wooden poles and the prevention of its depletion during flood irrigation
1994 - IRG/WP 94-50032
Polyethylene field liners heat-shrunk onto soil-contact surfaces prevented decay of creosote-treated Eucalyptus grandis vineyard poles under flood-irrigation. The present work quantified losses of creosote from these poles after six and 24 months' service. After six months' service the mean creosote retention of unlined poles above the ground line was 12.62% (m/m dry wood), with ...
M Behr, A A W Baecker
Influence of water soluble extractives on CCA fixation and leaching performance of red maple and red oak
1997 - IRG/WP 97-30133
We have observed several peculiarities in relation to CCA fixation in red maple and red oak woods such as high variability in fixation rates and leaching performance in maple and precipitate formation in solutions expressed from CCA treated red oak wood blocks at different stages of fixation. We have postulated that the extractives could be the factor of influence, as this has already been reporte...
T Stevanovic-Janezic, P A Cooper, Y T Ung
Depletion of preservatives from treated wood: Results from laboratory, fungus cellar and field test
1993 - IRG/WP 93-50001-07
This paper compares results of preservative component losses using a range of test procedures with several different water-borne preservatives. The data shows that laboratory leaching tests are in some cases comparable to, but in other cases significantly underestimate preservative component losses when compared with field or fungus cellar depletion tests. The results also suggest that preservativ...
L Jin, A F Preston
Leaching of Copper from ACQ treated wood exposed above ground
2004 - IRG/WP 04-50219
The leaching of chemicals of ACQ Type C treated wood exposed above ground for 16 months was studied. Commercially treated Hem-fir boards (Tsuga heterophylla Raf. and Amabilis fir Forb) of 37.5 mm by 87.5 mm were used. The amounts of chemical leached monthly by the rainfall were determined and the leachate was collected and analyzed. Also, the environmental factors influencing the leaching were ...
P A Chung, J N R Ruddick
Preservative leaching from copper-chrome-arsenic treated timber: Towards an international standard for environmental monitoring
1996 - IRG/WP 96-50076
A review of standards and legislative requirements around the world relating to environmental contamination from copper-chrome-arsenic wood preservative indicates a plethora of methodologies for expressing and determining contamination levels. The imposition of arbitrary quarantine periods for treated timber, or special fixation processes, appear to be applied without a rational analysis of what l...
S Walley, P R S Cobham, P Vinden
Preliminary Studies on ZiBOC- A Potential Eco-friendly Wood Preservative
2005 - IRG/WP 05-30372
Over the past decade, the wood processing industry has been increasingly involved in strategies to minimize the environmental impacts of treated wood. One sign of this is the dramatic increase in the use of preservatives based on inorganic metal oxides, which fix in wood. Among such preservatives the most common is chromated-copper-arsenate. In Ascu chromium and arsenic both are carcinogenic thus...
S Tripathi, J K Bagga, V K Jain
Leaching Characteristics of Alder Wood Treated with Copper Based Wood Preservatives
2005 - IRG/WP 05-50225
In this study, it was designed for determining leaching characteristics of CCA and alternatives wood preservatives. Alder wood blocks were treated with CCA (1 % and 2 %), ACQ-1900 (2 % and 3 %), ACQ-2200 (1 % and 2 %), Tanalith E 3491 (2 % and 2.8 %), Wolmanit CX-8 (% 1 and 2 %). Leaching studies were conducted according to AWPA E11-97. Copper analyses of leachate were determined Atomic absorption...
A Temiz, Ü C Yildiz, E D Gezer, S Yildiz, E Dizman
Leaching of components from CCF treated timber in ground contact
1998 - IRG/WP 98-50108
In order to investigate the depletion of different CCF-salts during service small stakes (10*10*450mm³) were treated with five water-borne wood preservatives and after fixation brought into ground contact for several years. After failing some of the broken down stakes were used to determine the remaining concentration of relevant ions and their distribution in different segments of the stakes.
A...
E Melcher
The effects of pH on leaching of copper-chrome-arsenate (CCA) from pressure-treated Kenyan-grown Eucalyptus saligna and Acacia mearnsii: Initial findings.
2002 - IRG/WP 02-30298
The effects of pH on leaching of CCA from pressure-treated Kenyan-grown Eucalyptus saligna and Acacia mearnsii were tested under laboratory conditions. Small samples of the two species (100mm x 30mm x 40mm) were smooth sawn from 8-year old trees to represent equal amounts of both sapwood and heartwood, air-dried to 12% moisture content, end-sealed, and pressure-treated at a commercial treatment p...
R Venkatasamy
Speciation of leachates from CCA-treated wood
2005 - IRG/WP 05-50224-27
Different species of arsenic and chromium are characterized by different toxicities and different mobilities. The environmental impacts of CCA-treated wood would therefore be a function of the chemical forms of the metal releases. As a consequence a series of tasks were undertaken to evaluate arsenic and chromium species from CCA-treated wood. The intent of these tasks was to quantify the total...
H M Solo-Gabriele, T G Townsend, Yong Cai, B I Khan, Jin-Kun Song, J Jambeck, B Dubey, Yong-Chul Jang
Changes of copper and chromium content after leaching in wood impregnated with the CCB and CB preservatives
2000 - IRG/WP 00-50147
The objective of the study was impregnated with CCB and CB preservatives pine wood of moisture content varying from 12% to 55% subjected to leaching. Losses of copper and chromium were determined for individual layers of wood up to 3 cm from the girth. The results were compared to the total amount of metals determined in water extracts. The degree of leaching of metal ions from wood of 55% moistur...
B Mazela
Long-Term Release of Arsenic, Chromium, and Copper from CCA-Treated Wood and Ash
2005 - IRG/WP 05-50227
In this study, laboratory long-term leaching studies were conducted to characterize the leaching behavior of arsenic, chromium, and copper from CCA-treated wood samples (block, chip, and sawdust) and CCA-wood ash and to determine the rate of release of the metals from the CCA wood products. The leaching solutions were periodically collected and analyzed for the concentrations of arsenic, chromium,...
Hyunmyung Yoon, Heeseok Kang, Yong-Chul Jang
Leaching tests on CCA-treated wood using inorganic salt solutions
1984 - IRG/WP 3310
Pinus radiata sapwood treated to approximately 10 kg/m³ with Tanalith NCA or Tanalith C-type CCA preservatives was ground to a fine powder and samples were then leached with solutions of calcium chloride, calcium nitrate, magnesium nitrate, or a mixture of potassium di-hydrogen orthophosphate and di-potassium hydrogen orthophosphate, at 0.03M-1.00M solution concentrations. Leached wood samples we...
D V Plackett
Analysis of the boron content of preservative treated oak and pitch pine heartwood before and after leaching
1992 - IRG/WP 92-3697
Studies to determine the effects, if any, of a variety of boron formulations on heartwood of English oak and American Pitch pine have been previously reported (King et al (1991)). Small wood blocks were treated, at 10°C or 45°C, with borax, polybor or Boracol 20 for periods of 1 month or 4 months then analysed or continuously leached with tap water for a period of 1 month. Reported results showe...
S McCutcheon, G M Smith, J W Palfreyman, B King
Relating CCA fixation to leaching of CCA components from treated products
1995 - IRG/WP 95-50045
The relationship between chromium fixation in CCA-C treated wood, as determined by CrVI analysis of solution expressed from treated wood and the leaching of Cu, Cr, As and CrVI in a simulated rain test are evaluated for dimension lumber (2"x6") and pole sections. Leachate concentrations after 2 hour exposure to a misting spray (about 300 mm cumulative rainfall) decrease rapidly with increased degr...
P A Cooper, R MacVicar, Y T Ung
A new process for in situ polymerization of vinyl monomers in wood to delay boron leaching
1998 - IRG/WP 98-40110
Efforts were accelerated on effective use of boron compounds in wood preservation owing to their environmentally safe characteristics and relatively low costs in addition to their well-known high bioactivity and fire resistant properties. Although having these unique favorable properties, they are readily leachable from treated wood at humid conditions. Therefore, they had limited market for exter...
M K Yalinkilic, W Dwianto, Y Imamura, M Takahashi
Effect of soil chemistry and physical properties on wood preservative leaching
1998 - IRG/WP 98-50111
When treated wood is placed in contact with soil, complicated mass transfer and chemical reactions occur which causes the preservative components to leach from the wood. There are several factors that are known to affect the amount of chemical leached from wood. These are properties of the preservative and carrier, preservative retention, degree of fixation, exposure time, grain orientation, surfa...
Joan-Hao Wang, D D Nicholas, L S Sites, D E Pettry
Fixation of chromated wood preservatives through technical drying
1990 - IRG/WP 3623
Twin samples of sawn timber of Pinus sylvestris and Picea sp. were treated with copper-chromate-containing wood preservatives and subsequently kiln resp. air dried. After drying, the distribution of preservative and rate of fixation were determined. Drying of freshly treated wood in a condenser type kiln at temperatures of 60°C and 80°C and in a vacuum type kiln at 55°C with a pressure of about...
R-D Peek, H Klipp
Fixation and leaching characteristics of Douglas-fir treated with CCA-C
2004 - IRG/WP 04-50213
Fixation and leaching characteristics of CCA-treated Douglas-fir was evaluated using the expressate method and the AWPA E11-97 leaching procedure. CCA fixation, as monitored by the chromium reduction, was much faster in heartwood than in sapwood; however, copper and arsenic fixation in heartwood appeared to be incomplete regardless of the extension of fixation time. This poor fixation of copper a...
Gyu-Hyeok Kim, Yun-Sang Song, Dong-heub Lee
Effects of the sulfuric acid modification of CCA treating solution
1987 - IRG/WP 3415
Sulfuric acid modification of CCA treating solution is often used to control the formation of sludges and undesirable deposits on the surface of treated wood. The consequences of sulfuric acid addition are examined in this work and negative effects are shown to far outweigh any benefits. Major risks include the loss of copper due to leaching from treated wood and the accelerated corrosion of treat...
R F Fox, H J Fry, E A Pasek, A S Ross
Residual CCA levels in CCA treated poles removed from service
2000 - IRG/WP 00-50152
Fifty-two CCA treated poles removed from service after 1 - 50 years were sampled at different depths from their below ground and above ground zones and the preservative levels and mass balances related to the location in the pole and pole age. Generally CCA retentions were still well above the toxic threshold for decay in even the oldest poles. This confirms the good leach resistance of CCA and th...
P A Cooper, D Jeremic, J L Taylor
Environmental Impacts of CCA-Treated Wood: A Summary from Seven Years of Study Focusing on the U.S. Florida Environment
2003 - IRG/WP 03-50205
Wood treated with chromated copper arsenate (CCA) was identified in 1995 as the cause of elevated arsenic concentrations within wood fuel used for cogeneration within Florida. Since this time a research team from the University of Miami and University of Florida has evaluated the environmental impacts of CCA-treated wood within the State. Research has focused on two distinct areas: in-service l...
H M Solo-Gabriele, T G Townsend, J D Schert
Leaching from field test stakes. Results from two different methods of analysis
1993 - IRG/WP 93-50013
Field test stakes treated with Boliden K33 containing copper, chromium and arsenic exposed at three different fields in Sweden and rejected due to decay, have in two studies been analysed regarding leaching and remaining preservatives. The stakes have been exposed during 20 to 43 years. The density of the stakes and content of copper, chromium and arsenic have been determined in the top part of th...
F G Evans, M-L Edlund