Leaching of components from CCF treated timber in ground contact
1998 - IRG/WP 98-50108
In order to investigate the depletion of different CCF-salts during service small stakes (10*10*450mm³) were treated with five water-borne wood preservatives and after fixation brought into ground contact for several years. After failing some of the broken down stakes were used to determine the remaining concentration of relevant ions and their distribution in different segments of the stakes.
A...
E Melcher
The effects of pH on leaching of copper-chrome-arsenate (CCA) from pressure-treated Kenyan-grown Eucalyptus saligna and Acacia mearnsii: Initial findings.
2002 - IRG/WP 02-30298
The effects of pH on leaching of CCA from pressure-treated Kenyan-grown Eucalyptus saligna and Acacia mearnsii were tested under laboratory conditions. Small samples of the two species (100mm x 30mm x 40mm) were smooth sawn from 8-year old trees to represent equal amounts of both sapwood and heartwood, air-dried to 12% moisture content, end-sealed, and pressure-treated at a commercial treatment p...
R Venkatasamy
Changes of copper and chromium content after leaching in wood impregnated with the CCB and CB preservatives
2000 - IRG/WP 00-50147
The objective of the study was impregnated with CCB and CB preservatives pine wood of moisture content varying from 12% to 55% subjected to leaching. Losses of copper and chromium were determined for individual layers of wood up to 3 cm from the girth. The results were compared to the total amount of metals determined in water extracts. The degree of leaching of metal ions from wood of 55% moistur...
B Mazela
Speciation of leachates from CCA-treated wood
2005 - IRG/WP 05-50224-27
Different species of arsenic and chromium are characterized by different toxicities and different mobilities. The environmental impacts of CCA-treated wood would therefore be a function of the chemical forms of the metal releases. As a consequence a series of tasks were undertaken to evaluate arsenic and chromium species from CCA-treated wood. The intent of these tasks was to quantify the total...
H M Solo-Gabriele, T G Townsend, Yong Cai, B I Khan, Jin-Kun Song, J Jambeck, B Dubey, Yong-Chul Jang
Long-Term Release of Arsenic, Chromium, and Copper from CCA-Treated Wood and Ash
2005 - IRG/WP 05-50227
In this study, laboratory long-term leaching studies were conducted to characterize the leaching behavior of arsenic, chromium, and copper from CCA-treated wood samples (block, chip, and sawdust) and CCA-wood ash and to determine the rate of release of the metals from the CCA wood products. The leaching solutions were periodically collected and analyzed for the concentrations of arsenic, chromium,...
Hyunmyung Yoon, Heeseok Kang, Yong-Chul Jang
Leaching tests on CCA-treated wood using inorganic salt solutions
1984 - IRG/WP 3310
Pinus radiata sapwood treated to approximately 10 kg/m³ with Tanalith NCA or Tanalith C-type CCA preservatives was ground to a fine powder and samples were then leached with solutions of calcium chloride, calcium nitrate, magnesium nitrate, or a mixture of potassium di-hydrogen orthophosphate and di-potassium hydrogen orthophosphate, at 0.03M-1.00M solution concentrations. Leached wood samples we...
D V Plackett
Analysis of the boron content of preservative treated oak and pitch pine heartwood before and after leaching
1992 - IRG/WP 92-3697
Studies to determine the effects, if any, of a variety of boron formulations on heartwood of English oak and American Pitch pine have been previously reported (King et al (1991)). Small wood blocks were treated, at 10°C or 45°C, with borax, polybor or Boracol 20 for periods of 1 month or 4 months then analysed or continuously leached with tap water for a period of 1 month. Reported results showe...
S McCutcheon, G M Smith, J W Palfreyman, B King
Relating CCA fixation to leaching of CCA components from treated products
1995 - IRG/WP 95-50045
The relationship between chromium fixation in CCA-C treated wood, as determined by CrVI analysis of solution expressed from treated wood and the leaching of Cu, Cr, As and CrVI in a simulated rain test are evaluated for dimension lumber (2"x6") and pole sections. Leachate concentrations after 2 hour exposure to a misting spray (about 300 mm cumulative rainfall) decrease rapidly with increased degr...
P A Cooper, R MacVicar, Y T Ung
A new process for in situ polymerization of vinyl monomers in wood to delay boron leaching
1998 - IRG/WP 98-40110
Efforts were accelerated on effective use of boron compounds in wood preservation owing to their environmentally safe characteristics and relatively low costs in addition to their well-known high bioactivity and fire resistant properties. Although having these unique favorable properties, they are readily leachable from treated wood at humid conditions. Therefore, they had limited market for exter...
M K Yalinkilic, W Dwianto, Y Imamura, M Takahashi
Effect of soil chemistry and physical properties on wood preservative leaching
1998 - IRG/WP 98-50111
When treated wood is placed in contact with soil, complicated mass transfer and chemical reactions occur which causes the preservative components to leach from the wood. There are several factors that are known to affect the amount of chemical leached from wood. These are properties of the preservative and carrier, preservative retention, degree of fixation, exposure time, grain orientation, surfa...
Joan-Hao Wang, D D Nicholas, L S Sites, D E Pettry
Fixation of chromated wood preservatives through technical drying
1990 - IRG/WP 3623
Twin samples of sawn timber of Pinus sylvestris and Picea sp. were treated with copper-chromate-containing wood preservatives and subsequently kiln resp. air dried. After drying, the distribution of preservative and rate of fixation were determined. Drying of freshly treated wood in a condenser type kiln at temperatures of 60°C and 80°C and in a vacuum type kiln at 55°C with a pressure of about...
R-D Peek, H Klipp
Fixation and leaching characteristics of Douglas-fir treated with CCA-C
2004 - IRG/WP 04-50213
Fixation and leaching characteristics of CCA-treated Douglas-fir was evaluated using the expressate method and the AWPA E11-97 leaching procedure. CCA fixation, as monitored by the chromium reduction, was much faster in heartwood than in sapwood; however, copper and arsenic fixation in heartwood appeared to be incomplete regardless of the extension of fixation time. This poor fixation of copper a...
Gyu-Hyeok Kim, Yun-Sang Song, Dong-heub Lee
Effects of the sulfuric acid modification of CCA treating solution
1987 - IRG/WP 3415
Sulfuric acid modification of CCA treating solution is often used to control the formation of sludges and undesirable deposits on the surface of treated wood. The consequences of sulfuric acid addition are examined in this work and negative effects are shown to far outweigh any benefits. Major risks include the loss of copper due to leaching from treated wood and the accelerated corrosion of treat...
R F Fox, H J Fry, E A Pasek, A S Ross
Residual CCA levels in CCA treated poles removed from service
2000 - IRG/WP 00-50152
Fifty-two CCA treated poles removed from service after 1 - 50 years were sampled at different depths from their below ground and above ground zones and the preservative levels and mass balances related to the location in the pole and pole age. Generally CCA retentions were still well above the toxic threshold for decay in even the oldest poles. This confirms the good leach resistance of CCA and th...
P A Cooper, D Jeremic, J L Taylor
Environmental Impacts of CCA-Treated Wood: A Summary from Seven Years of Study Focusing on the U.S. Florida Environment
2003 - IRG/WP 03-50205
Wood treated with chromated copper arsenate (CCA) was identified in 1995 as the cause of elevated arsenic concentrations within wood fuel used for cogeneration within Florida. Since this time a research team from the University of Miami and University of Florida has evaluated the environmental impacts of CCA-treated wood within the State. Research has focused on two distinct areas: in-service l...
H M Solo-Gabriele, T G Townsend, J D Schert
Leaching from field test stakes. Results from two different methods of analysis
1993 - IRG/WP 93-50013
Field test stakes treated with Boliden K33 containing copper, chromium and arsenic exposed at three different fields in Sweden and rejected due to decay, have in two studies been analysed regarding leaching and remaining preservatives. The stakes have been exposed during 20 to 43 years. The density of the stakes and content of copper, chromium and arsenic have been determined in the top part of th...
F G Evans, M-L Edlund
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
The influence of UV and IR radiation on leaching of copper and chromium from preservative-treated pine and spruce
1992 - IRG/WP 92-3687
The influence of artifical UV- and IR-radiation on the leaching of copper and chromium components of a CCB-preservative from freshly treated pine and spruce was evaluated. On small pinewood samples it could be shown, that the leaching of copper and chromium can considerabely be reduced by UV-radiation. A Philips HPA lamp type reduced the leaching most effective. IR-radiation lead to higher leachin...
H Militz
Comparative study on the leaching of wood preservatives between natural exposure and accelerating laboratory conditions
1999 - IRG/WP 99-50134
Impregnated specimens with CCA, ACQ, and BAAC were subjected to leaching tests. Specimens of 2x2x1 cm3 in size were used for the laboratory leaching test for 10 days according to JIS K 1571. Specimens of 25x1 x1 cm3 were used for outdoor leaching test for 6 months. Total leaching amounts of boron per cm3 of specimens treated with BAAC were 325 µg in the laboratory test and 206 µg in the outdoor ...
K Yamamoto, S Motegi, A Inai
Effects of hard water, sea water and humic acid on the release of CCA components from treated wood
2005 - IRG/WP 05-50228
Leaching medium is an important factor affecting release of preservative components from treated wood because physical and chemical characteristics of medium increase or decrease the solubility of fixed preservative components. This study evaluated the leaching properties of copper, chromium and arsenic elements from chromated copper arsenate (CCA)-treated wood specimens subjected to laboratory le...
S N Kartal, W J Hwang, Y Imamura
A comparison of shower test results from CCF, CCZF, CCB and Cu-quat treated timber
1995 - IRG/WP 95-50054
The shower test quantifies the amount of specific preservative components which leach from treated timber under simulated open storage conditions. The test method measures leaching from both organic and inorganic salt treated timber. Shower tests of CCF, CCZF, CCB and Cu-quat treated timber which have been performed over the last 5 years by TNO are reviewed and compared. Leached components are qua...
M J Boonstra, A J Pendlebury, P Esser
New research data confirming the suitability of bifenthrin as a wood preservative
1996 - IRG/WP 96-30116
Bifenthrin has been further tested against wood destroying insects, and its behaviour in wood has been extensively studied. Bifenthrin proved to be highly effective as a curative and preventative treatment against Anobium punctatum and Hylotrupes bajulus, after both leaching and evaporative ageing. Results of penetration tests with water and solvent based formulations, applied by brushing, dipping...
S Shires, P Héloir, B Chen, G Rustenburg
Above and Below-Ground Depletion of Copper, Chromium and Arsenic from Pinus radiata and Fagus sylvatica at Thirteen Test Sites in New Zealand and Australia
2006 - IRG/WP 06-30402
The objective was to determine the significance of site and wood species on preservative depletion for a copper chrome arsenate preservative (CCA) from 20 x 20 x 500 mm field test stakes after 5.5 and 4.5 years for pine and beech respectively. At least 5 sacrificial stakes were used to produce site means. Site and wood species had a major effect on copper, chromium and arsenic loss from CCA treate...
R Wakeling
Ionic liquids with organic and inorganic anions as highly active wood preservatives
2006 - IRG/WP 06-30411
Quaternary ammonium tetrafluoroborates, nitrates(V), propionates, acetates and formates with alkoxymethyl substituents were prepared and tested on wood destroying and sapstaining fungi. These new compounds are ionic liquids (ILs), which penetrate very well into Scot pine wood. Alkoxymethyldecyldimethylammonium tetrafluoroborates and nitrates(V) show better microbial activity against Coniophor...
J Zabielska-Matejuk, A Skrzypczak
Laboratory Leaching Tests to Study the Effects of Post-Treatment Storage Periods on CCA Leachability and Fixation in Treated Permeable and Refractory Malaysian Hardwoods
2006 - IRG/WP 06-50240
The biological resistance and environmental safety of CCA-treated wood relies on the extent of post-treatment storage fixation of CCA in wood prior to being utilized. A study on the comparative leachability (fixation) of CCA-treated refractory and permeable heartwoods of 3 Malaysian hardwoods subjected to different post-treatment storage (fixation) periods of up to 4 weeks, at 2 laboratory leachin...
A H H Wong, H C Lai, N P T Lim