Leaching of the copper component from full scale decking boards during one summer season
2009 - IRG/WP 09-50260
The leaching of copper has been tested in laboratory and in outside exposure for freshly treated pine sapwood samples with three different copper preservatives, Cu HDO, copper quat and copper triazoles. We found in the laboratory leaching test that a fixation with warming to 60 °C (140 °F) for 48 hours without drying and then drying in the laboratory in room temperature gave the lowest leaching of copper. We also found that surface treatments with wood oils reduced the leaching, and that washing of the surface before testing had no effect.
Full scale decking board samples (0.25 m2) were then exposed outdoors for rain. The rain water was collected and analysed for copper. After one summer season (about 600 mm rain) we found that the leaching differ for the three preservatives. All samples with a water borne surface treatment had the lowest leaching, about half the amount of untreated.
F G Evans
Evaluation of ACQ-D treated Chinese fir and Mongolian Scots pine with different post-treatments after 20 months of exposure
2010 - IRG/WP 10-30530
The performance of alkaline copper quat-type D (ACQ-D) treated Chinese fir (Cunninghamia lanceolata Hook.) and Mongolian Scots pine (Pinus sylvestris Linn. var. mongolica Litv.) stakes after 20 months exposure in Chengdu and Guangzhou of southern China were evaluated according to AWPA standard E07-07. The ACQ-D treatments used two concentration levels (0.5 and 1.0%) and four different post-treatme...
Lili Yu, Jinzhen Cao, Wei Gao, Haitao Su
Phytosanitary standards and the potential for acceptance of chemical treatments as a phytosanitary measure
2011 - IRG/WP 11-30558
Regulations governing international trade in forest products must balance the economic and social benefits of trade with the potential risks of transporting invasive species. The International Plant Protection Convention (IPPC) is an international agreement intended to manage this process. It develops international phytosanitary standards (ISPMs) that are recognised by the World Trade Organisation...
A Uzunovic, R Stirling, J J Morrell, P I Morris, C F Schauwecker
Novel Approaches to the Development and Testing of Anti After-glow Additives for CCA-based Treatments of Poles
2011 - IRG/WP 11-30561
In this paper, a field fire stake testing screen method is described. This method uses stake samples from matched wood sources allowing replicates from different boards to be included. The method is easy to control and can provide quick comparative fire resistance test results. The parameters measured from the tests are percentage weight loss, minimum residual circumference and residual thicknes...
L Jin, P Walcheski, A Preston
Protective Levels of Borates in timber Foundation Piles 5 – 18 Years after In-situ Remedial Treatment in Areas with Wet Clay Ground Conditions. The Jerbor and Eurobor Protocol, Part 1.
2011 - IRG/WP 11-30571
Timber has been used as foundation piles and grillages for decades or even centuries. Since the late 1970s a method for investigate, analyze and treat building timber foundations in soft clay grounds against decay fungus with a biocide have been developed and used by the late professor Allan Jerbo. Settling of buildings in soft clay grounds is continuously monitored and if damages to the building ...
M Theorin, K-M Bandh
Effectiveness of Water Based Bentonite-Borate Slurry for In-situ Remedial Protection of Historic Wooden Piles: The Eurobor Protocol, Part 2
2011 - IRG/WP 11-30574
The study of the biocide product Eurobor®, water mixture of boric acid, borax and sodium bentonite, aimed to verify previous findings regarding borates penetration from a clay-water mixture of foundation timber. The product was applied on samples from 100 year old timber foundation from the city of Göteborg. Although in ground for this long the timber was in acceptable god condition due to groun...
M. Theorin, K. Fimmerstad, K-M. Bandh
In-situ experimental treatment and consolidation of degraded timber elements from a XIX century building
2012 - IRG/WP 12-10767
This paper presents the in situ experimental conservation work performed on three timber structural elements from a XIX century building: two floor beams and one roof beam. The palace was built in 1877 in the centre of Lisbon initially with residential purposes. It has four floors, with timber structural horizontal elements, stairs and roof beams (generally of Pinus sylvestris L.). The exterior wa...
D F Henriques, J de Brito, L Nunes
Inhibition of Basidiospore Germination by Copper from MCQ, ACQ and CCA Leachates
2012 - IRG/WP 12-10778
The long-term decay resistance of refractory wood shell-treated with chromated copper arsenate (CCA) in above-ground exposures has been attributed to mobile copper that migrates into checks and inhibits the germination of basidiospores. Copper from micronized copper quat (MCQ) has also been shown to migrate into checks suggesting similar performance as a shell treatment, but questions have been ra...
R Stirling, J Drummond, P I Morris
Use of Variable Pressure Scanning Electron Microscopy for in situ Observation of Degradation of Wood Surfaces during Artificial Weathering
2012 - IRG/WP 12-20489
Variable pressure scanning electron microscopy (VPSEM) is capable of observing electrically non-conductive materials like wood without the need to render the surface conductive by applying a coating of gold, platinum or carbon. Hence, there is the possibility that VPSEM could be used to non-destructively follow the structural changes occurring at wood surfaces during weathering, because specimens ...
F Hatae, Y Kataoka, M Kiguchi, H Matsunaga, J Matsumura
KERUING and APITONG: A Timely Review of the Perfect Choice Wood Species for Crossarms and Brace Arms, Including Data on Copper Naphthenate Treatments
2012 - IRG/WP 12-40603
Apitong or the wood species more commonly known as Keruing is an important tropical hardwood known for its high strength to weight ratio and its reasonable durability and preservative treatability. This wood has been exported from managed permanent forest estates in Malaysia into the United States for over 4 decades for its widespread use in wooden utility industry brace arms and crossarms, yet cu...
A Wong, M Freeman
An assessment of soft rot in preservative-treated poles in two test sites and two network areas in New South Wales
2013 - IRG/WP 13-10801
This document presents an extended summary of recent investigations into soft rot attack of preservative treated power poles from the re-inspection of samples selected from two field sites and two in-service trials located in New South Wales, Australia. The in-ground sapwood of selected poles was assessed by probing and, after core sampling, by microscopy to determine the severity and extent of s...
W D Gardner, M A Powell, C Kirton
Quasi-in-situ durability tests on oak timber bridges
2013 - IRG/WP 13-20510
This study aims on developing a method for determination of wood durability on samples taken from real structures in service. Therefore quasi-in-situ durability tests have been conducted exemplarily on timber bridges made from English oak (Quercus robur L.). Drilling cores were found to be a feasible alternative to standard specimens for laboratory durability tests against pure cultures of Basidio...
C Brischke, C J Behnen, M-T Lenz, K Brandt, E Melcher
System treatments of Pinus sylvestris - influence on moisture, decay and discoloration
2013 - IRG/WP 13-30612
Biological activity can cause challenges for the use of wood in outdoor exposure. Decay and discolouring fungi influence the service life of wooden constructions, and the moisture content of the wood is often an important factor. The aim of this study was to evaluate the performance of different combinations of preservative/modified wood protection treatments and surface treatments for wooden deck...
A Schabacker, G Alfredsen, L Ross Gobakken, H Militz, P O Flæte
Characterization of wood modification prepared by in situ polymerization with pre-polymer and the mechanism of modification
2013 - IRG/WP 13-40633
Chemical modification of wood is a potential way to obtain high quality wood. In this study, the fast-growing poplar was impregnated with modifier using a pulse-dipping machine by in situ polymerization. Fungal decay analysis, mechanical properties and dimension stability of the natural and modified woods were investigated. The wood samples were also characterized by X-ray diffraction (XRD) Therma...
Qian Lang, Zeng Bi, Junwen Pu
Critical moisture levels and mould resistance of five different wood treatments
2013 - IRG/WP 13-30632
Mould resistance of five different treatments were tested using two methods, a recently
developed method for the determination of critical moisture levels of building materials (RHcrit),
and ASTM D3273-94. The critical moisture level method exposed samples at 22 °C and 98, 92,
86 and 82% relative humidity (RH) for 12 weeks. ASTM D3273-94 was performed at 29 °C and
about 95% RH.
Treatments c...
G Bok, P Johansson, A Ekstrand Tobin, S Bardage
On-site remediation treatments for framing timber in leaky buildings
2014 - IRG/WP 14-20549
Weathertightness failures in New Zealand buildings due to the combined effects of cladding choices, design and construction faults and the use of untreated framing timber has led to the so called ‘leaky building syndrome’. The latest estimated cost of the leaky building crisis in New Zealand is about NZ$11 billion.
This research was conducted to provide a better understanding of the option...
T Singh, D Page, A Bennett
Potential for migration of boron from fused boron rods used as internal remedial treatments of utility poles
2014 - IRG/WP 14-50301
The distribution of boron in Douglas-fir utility poles and in the surrounding soil was assessed over a 54 month period following application of fused boron rods. Boron levels in the wood never reached the levels that might be predicted if diffusion were to produce a uniform chemical distribution, nor did levels in the soil suggest that boron was becoming more concentrated. The results suggest th...
M Konkler, C Freitag, C S Love, J J Morrell, J Renfroe
Development of new wood treatments combining boron impregnation and thermo modification - Effect on decay and termites durability
2014 - IRG/WP 14-40666
Environmental pressures appeared in most European countries during the last decade has lead to the development of more environmentally acceptable preservation methods. In this context, wood heat treatment has been one of the most investigated alternative methods during the last years. Treated at temperatures ranging between 180 and 220°C, wood components undergo more or less important chemical mo...
S Salman, A Pétrissans, M-F Thévenon, S Dumarçay, B Pollier, P Gérardin
Performance of some wood modification treatments against marine borers
2014 - IRG/WP 14-40668
Since some years, new treatment technology to protect wood against wood destroying fungi is introduced. Limited knowledge on their resistance to water organisms is available. Therefore, the resistance of chemically modified wood was assessed in a field test according to the European Standard EN 275 over a period of 3 resp. 5 years at sites in the North Sea and the Baltic Sea. Scots pine (Pinus syl...
A Klüppel, C Mai, H Militz, S Cragg
Encapsulation Systems Combined with DOT Borate Treatments – The Future of Treated Crossties
2014 - IRG/WP 14-40670
Borates have been utilized in wood protection systems for many decades but only recently have been used in North America to treat crossties. This colorless, ordorless and very effective wood protection chemical has the ability to arrest and prevent the colonization of wood by both basidiomycete decay fungi and insects such as beetles and termites while ties are air seasoning or in service. Since ...
S C Kitchens, T L Amburgey
Study of in-situ gel polymerization established by Si-O-Si framework within wood micropores
2014 - IRG/WP 14-40672
Sodium silicate was used to form Si–O–Si framework by gel process and optimize the effect of the methylolurea impregnation on poplar wood. The modifier cured within the wood micropores by in-situ gel polymerization during the kiln drying. The results showed that treated wood acquired higher mechanical strength, but lower hygroscopicity. New positions of the XRD peaks appeared which caused by s...
Zeng Bi, Qian Lang, Heyu Chen, Junwen Pu
Functional silicones used as a potential tool for the development of non-biocidal wood treatments
2015 - IRG/WP 15-30665
The increase of wood resistance against biological agents for outdoor use is conventionally performed by deep impregnation with preservatives. However, some of the traditional wood preservatives, used for decades for wood protection and regarded as the most effective, are currently subjected to severe restrictions because of their toxicity. In fact, new preservation technologies are constantly ent...
F Lhumeau, C Delaite, F Marchal, F Pochon, M Kutnik
Polyamidoamines (PAA) functionalized with siloxane fragments as potential wood preservatives
2015 - IRG/WP 15-40708
Polyamidoamines (PAAs) utilized in this research were obtained by the reaction between N,N-methyl-bis-acrylamide (MBA) and Ethanolalmine (EtA) and/or aminopropytriethoxysilane (APTES). Different combinations between them were tested as wood preservatives against fungal decay. First, in situ impregnations of PAAs, with the reagents above described in different ratio, were performed and the effectiv...
S Palanti, G Predieri, E Feci, L Bergamonti
Termiticidal Effect of Bitumen and Creosote oil Treatments on Selected Nigerian Wood Species
2016 - IRG/WP 16-30689
Termites attack has been a major threat to wood materials in construction. The study investigated the termiticidal effect of bitumen and creosote oil mixture on the resistance of some commonly used indigenous wood species namely: Celtis zenkeri, Terminalia ivorensis, Albizia lebbeck, Cola gigantea and Terminalia superba to termites in Akure, Ondo State, Nigeria. The wood species were obtained from...
Termiticidal Effect of Bitumen and Creosote oil Treatments on Selected Nigerian Wood Species
Evidence for a role for precipitated copper on the chemistry of micronized copper treatments
2016 - IRG/WP 16-30690
Micronized copper preservative treatments of softwoods, result in mobile copper being formed by reaction of the basic copper carbonate (BCC) with the carboxylic acid functional groups in hemicellulose and pectic substances present in wood. Typically, the amount of reacted copper formed is approximately 0.3% Cu m/m. In this paper, two examples are discussed where remaining unreacted basic copper ca...
Wei Xue, P Kennepohl, J N R Ruddick