Chromium in wood preservation: Health and environmental aspects
1978 - IRG/WP 3120
The majority of water-borne salts in current use contain hexavalent chromium, usually as dichromate or chromium trioxide. In about 1913 it was suggested that chromates, phosphates or borates could be added to the sodium fluoride and dinitrophenol mixtures then in use in order to inhibit corrosion. Dichromates were found to be most suitable and the resulting mixture known as Thriolith and later Tri...
T R G Cox, B A Richardson
Mechanisms of Protection by NHA Against Fungal Decay
2002 - IRG/WP 02-10429
Treating wood with the water-borne sodium salt of N'-N-naphthaloylhydroxylamine (Na-NHA) protects wood against decay and termite damage. Initial testing indicated little or no inhibition of sapstain fungi, molds, or soft-rot fungi by Na-NHA, suggesting that the
mechanism by which this compound protected wood was complex and not that of a broad-spectrum biocide. Previously, we (Green et...
F Green III, W Henry, T Schultz
Heat transfer and wood moisture effects in moderate temperature fixation of CCA treated wood
1994 - IRG/WP 94-40022
Practical aspects of heat transfer and fixation of wood exposed to drying conditions after CCA treatment are considered. The rates of heat transfer and CCA fixation are substantially influenced by the cooling effect of water evaporating from the wood surface when drying occurs during fixation. At least in the early stages of fixation, the wood temperature approaches the wet bulb temperature, rathe...
J Chen, M Kaldas, Y T Ung, P A Cooper
Difference of CCA efficacy among coniferous wood species
1990 - IRG/WP 3601
Wood blocks of Cryptomeria japonica, Tsuga heterophylla, and Pinus radiata successively extracted with n-hexane, ether, and methanol were treated with various concentrations of CCA type 3, which were subjected to the decay by Tyromyces palustris. The weight loss were different among species and kinds of extraction. Cryptomeria japonica treated with CCA had higher fungal resistance than Tsuga heter...
K Yamamoto, M Inoue
Fundamentals on steam fixation of chromated wood preservatives
1988 - IRG/WP 3483
Weathering of treated wood directly after impregnation leaches up to 2% of copper-chromate-containing wood preservatives. Almost total fixation of Cr+6 is achieved by steaming the treated wood at 100°C to 120°C, preferably 110°C. To initiate such spontaneous fixation 85°C to 90°C inside the wood are essential, which requires heating times ranging from 20 to 80 min, depending on timber species...
R-D Peek, H Willeitner
Leachabilty and efficacy of fatty acid derived boron esters as wood preservatives - leachability and efficacy of fatty acid derived boron esters as wood preservatives
2004 - IRG/WP 04-30351
Borates have many advantages as wood preservatives. However, boron is susceptible to depletion under humid conditions and this restricts its outdoor use. In order to reduce boron leachability in treated wood, one of the anticipative approaches is to use organic fixed boron-based preservatives. This study investigated the leachability of six boron ester compounds as potential preservatives. Scots p...
A Mohareb, J Van Acker, M Stevens
Changes in fat and moisture contents, and nitrogen fixation in laboratory maintained termites
1984 - IRG/WP 1242
Orphaned groups of termites of Coptotermes acinaciformis and Mastotermes darwiniensis were maintained in the laboratory for several months on two dietary regimes, and changes in their fat contents, moisture contents and nitrogen fixation rates were examined. There were no significant feed or feed time effects for either species. For Coptotermes acinaciformis, there was a highly significant time ef...
J R J French, P J Robinson, L G Turner, P J Pahl
Assessing the importance of degradation mechanisms on the loss of effectiveness of wood preservatives
2000 - IRG/WP 00-20193
Accelerated ageing systems developed for application to samples in the laboratory prior to biological tests, should reflect those natural deterioration processes that are likely to occur in the hazard classes defined in EN 335-1. Losses through evaporation or the effects of leaching have been recognised, however their importance, relative to other mechanisms has not been quantified. Degradation me...
E D Suttie, R J Orsler, T Dearling
Dimensional stabilization and decay resistance of wood treated with brown-rotted lignin and copper sulfate
1990 - IRG/WP 3608
The objective of this study was to evaluate the potential usefulness of brown-rotted lignin (BRL) as a dimensional stabilization and copper complexing agent for wood treatment. For dimensional stabilization, aqueous solutions of the lignin extract were combined with either copper sulfate, glyoxal or other additives. Anti-shrink efficiency (ASE) values as high as 42% were obtained with wood treated...
L Jin, D D Nicholas, T Schultz
Laboratory Evaluation and Field Trial of Chlorothalonil and Copper-based Preservatives and Leaching Performance of Copper in Copper Treated Wood
2002 - IRG/WP 02-30279
Soil block test and field trial of some Chinese plantation wood species pine and poplar treated with chlorothalonil formulations and copper-based preservatives such as ACQ-B and copper citrate (CC) were conducted. The results of soil block test indicated that chlorothalonil formulations and ACQ-B as well as CC are very effective for controlling the 2 fungi species Corious versicolor and Poria plac...
Mingliang Jiang, Ping Wang, Chungen Piao, Zhaobang Li, Quan Lu, Lei Liu
Utilization of coconut timber from north Sulawesi, Indonesia. Part 2: Treatability
1994 - IRG/WP 94-40025
Under tropical conditions coconut wood is quickly degraded by mold and blue stain fungi. Low density wood in ground contact is commonly decomposed by wood destroying fungi within a period of only a few months, higher density wood from the outer stem regions within 24 to 30 months (MOSTEIRO, CASIN, SERIBAN 1976; McQUIRE 1975). Moreover, according to McQUIRE (1975) green wood of lower density is hig...
R-D Peek
Fixation of CCA preservatives in cocos-, oil- and rattan-palm
1986 - IRG/WP 3371
In previous tests with jubaea-palm almost no fixation of a CCA-preservative Type B could be achieved, consequently, further leaching tests were carried out with samples of 1 cocos-, 1 oil- and 2 rattan-palms from Malaysia. A good fixation of chromium and copper took place in cocos-palm after 4 weeks storage at 28°C. Nevertheless the fixation was slower than in pine-wood and demanded an elevated t...
H Willeitner, K Brandt
Oxidation of wood components during CCA-C fixation
1993 - IRG/WP 93-30024
Pre-extracted radial sections of southern yellow pine sapwood were treated with CCA-C and analyzed by X-ray photoelectron spectroscopy (XPS). The ratio of C1 (carbon bonded to carbon and/or hydrogen) to C2 (carbon bonded to one oxygen) in XPS Cls spectra was taken as a measure of the progress of oxidation of wood components during CCA fixation. This ratio was 0.82 before CCA treatment and increase...
M Kaldas, P A Cooper
Rapid fixation of Chromated Copper Arsenate (CCA) wood preservatives by microwave treatment
2000 - IRG/WP 00-40184
Rapid microwave heating of freshly chromated copper arsenate (CCA) treated timber indicates that rapid preservative fixation is possible within approximately 40 seconds. The leaching of CCA was evaluated using simulated rainfall. Cost analyses indicates that microwave fixation using an on-line conveyor belt fixation process with an output of 4m3/hour using a microwave power supply of 230 kW costs ...
G Torgovnikov, P Vinden, E Mapanda, P R S Cobham
Microwave treatment to Accelerated fixation of copper-ethanolamine (Cu-EA) treated wood
2004 - IRG/WP 04-40271
This study evaluated the use of microwave post-treatment to accelerate fixation of copper-ethanolamine (Cu-EA) treated 19 mm southern yellow pine sapwood cubes. Cubes were pressure treated at 3.2 and 6.4 kg/m3 Cu retention target, after which they were microwave post treated during different duration periods. An accelerated AWPA leaching test was conducted during 300 hours to determine the amount...
Jinzhen Cao, D P Kamdem
Some practical implications from recent research on the fixation of CCA preservatives
1975 - IRG/WP 358
The mechanism of fixation of CCA preservatives is briefly described. If the temperature is increased during the primary fixation period, the formation of intermediate fixation compounds is less extensive. The length of the primary fixation period is of practical interest. It is determined by preservative composition and concentration, temperature and wood species. Diagrams are given for Pinus sylv...
S-E Dahlgren
Moderate temperature fixation of CCA-C
1989 - IRG/WP 3522
Several Canadian treating plants are using moderate temperature (40-60C°) fixation chambers to reduce drippage and leaching from fresh CCA treated wood. In this study, chromium reduction and surface leaching properties of CCA-C treated red pine (Pinus resinosa) pole sections were monitored during exposure to temperatures of 50-60C° and 90-100% RH conditions. Chromium-VI concentration in the abso...
P A Cooper, Y T Ung
Studies of the mechanism of chromated-copper preservative. Fixation using electron spin resonance
1992 - IRG/WP 92-3701
Two softwoods and one hardwood species were treated with chromium trioxide, copper sulphate, chromated-copper wood preservative (CCA). The treated wood samples were analyzed during fixation by electron spin resonance (ESR). ESR spectra indicated that more than one Cr(V) species was generated from Cr(VI) soon after CCA treatment. The Cr(V) signal became strong within increased several hours followe...
K Yamamoto, J N R Ruddick
Industrial fixation systems: key factors, limitations and optimisation through the use of computer simulation modelling. Discussion paper
1994 - IRG/WP 94-40026
This paper briefly describes four fixation operative in the Netherlands, namely: circulating and non-circulating steam fixation cylinders, steam fixation chambers and controlled climate rooms. The general limitations of industrial practice are reviewed against the background of established fixation theory. The controlling variables, both material and process-related, for fixation processing are sp...
A J Pendlebury, M Riepen, M J Boonstra, W Gard
Differences and their causes of CCA and CCB efficacay among some softwoods and hardwoods
1991 - IRG/WP 3656
Wood blocks from two softwoods and two tropical hardwoods species treated with different concentrations of CCA, CCB, and combinations of CrO3, CuS04, H3BO3 were subjected to the decay by brown rot fungus, Tyromyces palustris. CCA maintained good effect both in softwoods and hardwoods, while CCB and the other combinations lost their effectiveness after leaching. Chemicals leached from CCA treated w...
K Yamamoto, M Rokova
Effect of compression wood on leaching of chromium, copper, and arsenic from CCA-C treated red pine (Pinus resinosa Ait.)
2000 - IRG/WP 00-30232
In this study, the effect of compression wood formation on the release rate of chromium, copper, and arsenic elements from red pine (Pinus resinosa Ait) was investigated. Wood blocks from red pine containing compression and normal wood portions were treated with a 1.0% CCA-C solution and were then allowed to fix at 23 ± ??2°C (74 ± 4°F) for 0, 6, 24, 48, 96, 192, and 336 hours. After each fixa...
S N Kartal, S T Lebow
Copper based water-borne preservatives: Copper adsorption in relation to performance against soft rot
1987 - IRG/WP 3452
As part of a fundamental study concerned with the performance of copper based water-borne preservatives the adsorption of copper from aqueous solutions by 4 hardwood and 1 softwood species has been studied. Experiments were conducted to determine the influence of solution pH, solution concentration and solution temperature. The results obtained were consistent with an acid form ion-exchange mechan...
P M S Rennie, S M Gray, D J Dickinson
Industrial fixation of chromium based wood preservatives
1990 - IRG/WP 3630
Fixation is an abstract and non-defined process. Nevertheless it is a specified requirement in most impregnation standards. The impregnation industry is facing increased pressure to deliver fixed products and to increase the safety of the handling of impregnated products. Industrial fixation of impregnated wood can be obtained by using different methods. The purpose of the process is to transform ...
T Christensen
A diffusion and reaction model for the leaching of Cr-VI from unfixed CCA-treated wood
2001 - IRG/WP 01-50169
A physical model applicable to the leaching of any substance undergoing a first-order fixation reaction with wood is presented. Using this model and a laboratory leaching experiment with small wood samples immersed in water, the radial and tangential diffusion coefficients and the reaction rate constants of Cr-VI in unfixed CCA-treated red pine (Pinus resinosa Ait.) are measured. Reaction rate con...
L Waldron, P A Cooper
The multi-phase pressure (MPP) process. One-stage CCA treatment and accelerated fixation process
- The process as a new concept in preservative treatment
1997 - IRG/WP 97-40078
The background to current commercial CCA treatment schedules used in New Zealand and fixation processing is reviewed. The limitations of these conventional practices with respect to treated product quality and CCA solution handling issues are defined. A novel, patented treatment schedule has been developed using a combination of hydraulic and pneumatic pressure phases and hot (~ 75°C) CCA solutio...
K Nasheri, A J Pendlebury, J A Drysdale, H Pearson, M E Hedley