Soft Rot Determines Service Life of L-joints with Low Borate Loading
2008 - IRG/WP 08-30470
As part of a research program on the potential use of borates by the Canadian wood products industry, Forintek set up an L-joint test of untreated and borate-diffusion treated hem-fir (western
hemlock and amabilis fir) in 1990. The treated material had a low initial retention of only 0.2% boric acid equivalent and analysis after 5 years revealed no detectable borate close to the tenon. Nev...
P I Morris, J Wang, J K Ingram
Penetration Depth of Borates in Historic Wooden Structures in Virginia City Montana
2008 - IRG/WP 08-30475
Virginia City, Montana contains some of the best preserved examples of gold boom construction in the United States. Unfortunately, even the dry climate and fortuitous lack of fire have not prevented decay from claiming parts of the historic fabric. This project aims to determine if borates should be integrated into the preservation plan of the Montana Heritage Commission. Solutions of disodium ...
A A Turner
Laboratory Studies on Copper Availability in Wood Treated with Soluble Amine Copper and Micronized Copper Systems
2008 - IRG/WP 08-30489
A laboratory method has been employed to investigate the level of soluble copper in wood treated with various copper-based preservative systems, such as micronized copper (particulate copper) and amine copper solutions. This report describes the methodology and preliminary results on determination of the soluble copper in the treating solutions and the treated wood by these systems, as well as th...
L Jin, P Walcheski, A Preston
Micronized Copper Preservative Systems: Observations on the Release of Cupric ion (Cu2+) from Treated Wood and Performance against Wood Decay Fungi
2009 - IRG/WP 09-30519
In an attempt to address the mechanism of action of micronized copper preservatives, a 20-week continuous water leaching study was conducted. The leaching results indicated that, once impregnated in wood, micronized copper preservatives continuously release cupric ion, and the levels of cupric ion released from micronized copper treated wood are higher than those released from CCA treated wood, a...
J Zhang, R Ziobro
Finite Element Modelling of the Checking of Wood Exposed to Accelerated Weathering
2010 - IRG/WP 10-20459
The surface checking that develops when wood is exposed to the weather reduces the visual appeal of treated wood products and can reduce the effectiveness of preservative treatments. There is strong interest in developing solutions to this problem and also a growing realization that such solutions may evolve from a deeper understanding of the mechanisms responsible for surface checking. In this pa...
S G Ribarits, P D Evans
Studies on Effect of pH on Copper Availability in Copper-Based Preservatives
2010 - IRG/WP 10-30549
Laboratory methods have been employed to investigate the pH effect on the copper solubility of basic copper carbonate. The pH was controlled using two different approaches. One was with the adjustment of pH of the solutions by acid or base using sulfuric acid or sodium hydroxide until the solution equilibriums were obtained for each defined pH. A second approach was to control pH with buffer sol...
L Jin, P Walcheski, A F Preston
Influence addition of boron compounds to adhesives on the bonding quality and fungicidal properties of glued wood
2010 - IRG/WP 10-40497
Wood is one of the most important construction materials. However, users of wood face two issues: limited dimensions and insufficient durability. These issues have been overcome with the development of bonding and wood preservation. The preservation of glued wood is elucidated in this paper. Through the addition of boric acid to adhesives, we tried to improve the fungicidal properties of glued woo...
M Humar, B Lesar, A Ugovsek, M Kariz, P Kralj, M Šernek
Ambient-temperature borate dip-diffusion treatment of green railroad crossties
2011 - IRG/WP 11-40556
In the USA, borates are increasingly being applied prior to air seasoning and creosote treatment of railroad ties (railway sleepers). Borates are typically applied to green ties by vacuum pressure application at 1 to 10% disodium octaborate tetrahydrate (DOT) concentration or by traditional dip-diffusion treatments at elevated temperatures. Higher temperatures are used to maintain the 30 to 50% so...
Jae-Woo Kim, A M Taylor, C Köse
Performance of boron diffused wood products used indoors for 144 months in Bangladesh
2012 - IRG/WP 12-30581
In this service performance study of boron diffused hardwoods, boron in the form of boric acid (H3BO3) was applied separately through paste and through wet cloth. The born diffused woods were kept indoors for 144-months in Bangladesh to ascertain the performance of treated wood against wood destroying insects. The new easy application processes of cost effectual boric acid have been found effectiv...
A K Lahiry, T Lahiry
Steam accelerated borate diffusion: Optimizing dry tie treatment
2015 - IRG/WP 15-40713
A small laboratory study was carried out which demonstrated that dry wood dip treated in a high concentration borate solution could not be subsequently treated properly with oil borne copper naphthenate unless it was subsequently steam treated to accelerate borate penetration into the wood and re-dry the wood beforehand. A larger study with commercial sized cross ties (railway sleepers) was carri...
J-W Kim, J D Lloyd
Durability of energy efficient wooden buildings: a building physical point of view
2017 - IRG/WP 17-40812
The drive for more energy efficient and sustainable buildings resulted in an increased popularity of wooden buildings, even in countries with a masonry tradition. Often guidelines and prescriptions then are copied from other countries. Different climatic boundary conditions and tradition of finishing, though, do require different moisture tolerance criteria. This is clearly the case for water vapo...
S Roels, J Langmans
Boron dual-treatments for Douglas-fir utility poles: Tracking boron migration over time
2019 - IRG/WP 19-30739
The potential for using boron pressure-treatment prior to over-treatment with conventional, heavy-duty wood preservatives to limit internal decay in-service was investigated in two field tests on Douglas-fir utility poles. Pole sections were pressure-treated with disodium octaborate tetrahydrate (DOT) and then over-treated with either pentachlorophenol or copper naphthenate in oil. Alternatively, ...
J Cappellazzi, M J Konkler, J J Morrell
Wood Protection Through Diffusion: Dimensional Stabilisation with Amine Oxides
2019 - IRG/WP 19-30747
Wood is a phenomenal construction material. In addition to its great physical properties and its beautiful appearance, it possesses many environmental-friendly virtues like the sequestration of carbon dioxide. It is however subject to dimension changes when submitted to fluctuating moistures levels, which can lead to warps, cracks and the peeling of paints. Many water repellents can slow down the ...
S Pepin, P Blanchet, V Landry
Limiting Polysaccharide Motion Protects Wood From Decay
2020 - IRG/WP 20-40890
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
C G Hunt, S L Zelinka, J E Jakes
Application of suberin fatty acids extracted from birch bark for wood coating
2021 - IRG/WP 21-40914
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
A Kumar, Risto Korpinen, Veikko Möttönen
Preservative Treatment of CLT: An Example at Shimojishima Airport
2019 - IRG/WP 19-30748
Cross laminated timber (CLT) is a relatively new construction method that allows multi-storey construction using solid wood instead of concrete or steel. It is a method favoured by progressive architects and recognized for its much lower environmental footprint. Wood is an excellent construction material and is a long-term carbon sink that also performs well in the event of earthquakes and fire....
J Lloyd, N Yamashita, A Taylor
Significance of the thermal design and the sorption isotherm shape in hygroscopic wood moisture dynamics and service life
2022 - IRG/WP 22-20682
Moisture dynamics are considered important for predicting the service performance of wood in exterior applications. Above a critical moisture content, water acts a softener on the structural polymer matrix of the wood cell wall, enabling the necessary diffusion of molecular species involved in the fungal degradation mechanism of wood. Water may enter solid wood in either liquid form or in vapor fo...
W Willems