The effect of acid rain on CCA treated timber
1990 - IRG/WP 3579
The effect of acid precipitation on the leaching of copper, chromium and arsenic from timber treated with different CCA preservatives was studied in the presence of three types of soil under simulated field conditions. Pine sapwood, embedded in soil, was subjected to simulated rainfall at three different levels of acidity. The CCA preservative formulations tested were:- American Wood Preservers&am...
R J Murphy, D J Dickinson
The effect of soil pre-exposure on the results of laboratory Basidiomycete testing
1991 - IRG/WP 2385
Scots pine sapwood blocks were treated with several concentrations of copper chrome arsenic (CCA), copper chrome boron (CCB) and a copper modified quaternary ammonium compound (CMAAC). Leached and unleached samples were exposed in a basidiomycete monoculture test using Coniophora puteana, a copper tolerant brown rot. Prior to testing half of the blocks were buried in unsterile soil for 4 weeks. Th...
S M Gray
Effect of post-treatment processing on leachability of ACZA-treated douglas-fir lumber
1998 - IRG/WP 98-50109
The effect of post-treatment procedures that more rapidly precipitate copper, zinc, and arsenic in douglas-fir treated with ammoniacal copper zinc arsenate (ACZA) on subsequent leaching resistance were investigated at two retentions (6.4 and 40 kg/m3). Total leaching was greater from boards treated to the higher retention. At both levels, copper was lost at the highest rate. Post-treatment process...
J J Morrell, C S Love, S Kumar, C M Freitag
Biological and chemical investigations for the assessment of the environmental impact of wood preservative components
1999 - IRG/WP 99-50127
This study was carried out in order to investigate the suitability of biological and chemical techniques to evaluate the environmental impact of wood preservatives depleted from impregnated wood. Small specimens (15*25*50 mm3) of Scots pine sapwood (Pinus sylvestris) were treated with a CCB salt. After fixation the treated and untreated samples were washed-out according EN 84, and the different le...
E Melcher, H-W Wegen
Leaching of CCA from Bombax ceiba catamarans in operation for 15 years
2002 - IRG/WP 02-50191
Core samples of wood at random were collected from all the timber pieces of each of the three catamarans made of CCA treated logs of Bombax ceiba put to continuous service for the last 15 years at the Lawson's Bay fishing village, Visakhapatnam. The samples were dried to constant weight, powdered, digested and analyzed for the residual salts of the preservative. The residual content of ...
V Kuppusamy, M Balaji, M V Rao, K S Rao
A review of the efficacy and uses of deltamethrin for wood preservation
1996 - IRG/WP 96-30105
The synthetic pyrethroid deltamethrin, is one of the most active insecticides available for protecting and curing wood from attack by beetles and termites. Freshly felled trees can be protected against bark beetles by spraying to run off with a 0.025% Al solution (K-Otek EC25) with negligible leaching. Alternatively, sawn timber may be dipped in a 0.0125% Al solution for short to medium term prote...
A J Adams, J L Lindars
Modelling of copper emission fron treated wood leached according to NEN 7345 and ENV 1250.2
1996 - IRG/WP 96-20097
A series of water leaching experiments is carried out investigating pine and spruce treated and fixed using different copper-containing preservative solutions and process technologies. Water changes took place as prescribed in the Dutch standard NEN 7345 and the European test method ENV 1250.2, each of the leachates being chemically analysed for their copper content. Irrespective of the preservati...
G M F Van Eetvelde, S G L Michon, M Stevens
Evaluation of wood preservatives for Nordic wood preservation class AB
2002 - IRG/WP 02-30297
In the Nordic countries there are restrictions in the use of wood preservatives based on chromium and arsenic. For above ground use, class AB according to the Nordic system, only
copper based preservatives are allowed in Sweden. Thus several new preservatives, copper based or metal free are now used. They have been approved by the Nordic Wood Preservation Council after passing laboratory tests ag...
M-L Edlund, J Jermer
Comparison of laboratory tests and field experiments for the estimation of emissions from treated wood
2005 - IRG/WP 05-50224-6
The authorisation procedure for biocidal products according to the European Biocides Direc¬tive in¬cludes the assessment of possible environmental risks by the emission of ac¬tive ingre¬dients. This needs an input of data on the expected emissions of biocides into environmental com¬part¬ments. The procedures for the estimation of these emissions should be harmonised. La¬boratory test proceÂ...
U Schoknecht
Investigation of copper fixation in timber by sodium nitrit
1992 - IRG/WP 92-3707
Solutions containing mixtures of water soluble copper salts and sodium nitrite have been shown to be capable of producing leach resistant copper treatments when impregnated into timber. A rapid leaching trial showed that copper fixation levels of 85-90% were possible which compared well with the fixation level obtained with conventional hexavelant chromium containing systems in the same test regim...
C Waldie, J A Cornfield
FTIR characterization of copper ethanolamine - wood interaction
1999 - IRG/WP 99-20154
The interaction of copper ethanolamine (Cu-EA) and wood components was studied by using Fourier transform infrared spectroscopy (FTIR). In Cu-EA treated wood, significant reduction was noticed on the band attributed to carbonyl vibration from carboxylic groups at 1735±5 cm-1 and an increase in band intensity was obtained from carbonyl in carboxylate at 1595±5 cm-1. The same observation was made ...
Jun Zhang, D P Kamdem
The development of a new boron-based wood preservative
1995 - IRG/WP 95-30085
The paper describes a new boron based wood preservative for the treatment of green timber. The product offers many benefits over conventional boron diffusion treatment including: 1. high viscosity, high concentration formulation; 2. permits dip treatment of a wide range of sawn board and pole sizes at ambient temperatures; 3. permits full cross section diffusion of borates without block stacking a...
P Turner, D Conradie
Study on leaching of a magnesium fluorosilicate product (SF salt) from wood-boards by rain in the open and by artificial shower
1976 - IRG/WP 264
The test was performed in 1961 to obtain information about (1) the comparative leaching effect of natural rain and of artificial shower in the laboratory; (2) the comparative leaching effect on the active ingredient in proportion to the dye-stuff of the product. The results show that a continuos light rainfall with low precipitation has a much stronger leaching effect than short heavy showers with...
S Cymorek
Differential retention and leaching of CCA (C) in sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii)
2005 - IRG/WP 05-30371
Retention and leaching of CCA(C) in small samples of sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii) were tested under laboratory conditions. Clear samples (100mm x 30mm x 40mm) were removed from the sapwood and heartwood of sampled defect-free and sound plantation trees of the two species. These were separately air-dried to 15% MC, end-seal...
R Venkatasamy
A technique for measuring preservative loss or redistribution during leaching
1983 - IRG/WP 2199
Radiata pine sapwood stakes were treated with benzalkonium chloride (AAC) or copper-chrome-arsenate (CCA). After fixation and drying the outer 2 mm and 2-4 mm layers were removed from one radial longitudinal face. The planed face was coated with a waterproof coating and AAC-treated stakes were leached for 6, 12 or 18 weeks; 12 weeks for the CCA-treated stakes. After airdrying three 2 mm layers (0-...
J A Drysdale
Detoxification of salt impregnated wood by organic acids in a pulping process
1993 - IRG/WP 93-50012
The paper descibes a novel method to detoxify pine wood (Pinus silvestris L.) treated with CCB-, CCF- CC-, and Cu-HDO-type salt preservatives. In the process of biological detoxification organic acids produced by strains of Antrodia vaillantii and other brown rot fungi are used for the dissolution of the previously fixed inorganic compounds. These findings are the basis for applying an acid pulpin...
I Stephan, H H Nimz, R D Peek
Impact of leachates from CCA- and copper azole-treated pine decking on soil-dwelling invertebrates
2002 - IRG/WP 02-50183
This study assessed the short-term effects on non-target soil invertebrates of leachates from a naturally durable hardwood and timber treated with two copper-based wood preservatives. Natural rainwater leachates from kwila decking, and radiata pine-decking treated with CCA or copper-azole, were collected and applied on mown lawn soil in Brisbane, Queensland. The soil study consisted of 5 treatment...
N Crumière, A House, M J Kennedy
Effect of leaching temperature and water acidity on the loss of metal elements from CCA treated timber in aquatic applications. Part 1: Laboratory scale investigation
1995 - IRG/WP 95-50046
In order to investigate the applicability of current prestandard leaching test methods, a series of experiments has been performed on CCA impregnated wood dealing with the influence of pH, temperature and agitation of the surrounding water. The leaching method used in this first part of the investigation is the European prestandard drafted by CEN/TC38/WG11, a short term dynamic leaching test under...
G M F Van Eetvelde, R J Orsler, G E Holland, M Stevens
Fluoride and chromium concentrations in soil adjacent to remedially treated distribution poles
1996 - IRG/WP 96-50066
Soils adjacent to Rentex treated 'on-line' distribution poles were analysed for total fluoride and chromium content for comparison with background values of these elements. Soil samples 6 cm and 25 cm downslope of selected poles were recovered at 1 week, 1 month, 6 and 12 months after treatment. Background soil samples were taken 50 m from the poles at sampling times. Fourteen po...
D C R Sinclair, G M Smith, A Bruce, H J Staines, P Durrant
Interaction of copper-amine complexes with wood: Influence of copper source, amine ligands and amine to copper molar ratio on copper retention and leaching
1999 - IRG/WP 99-30203
The absorption and leachability of copper in copper amine (Cu-EA) treated wood are influenced by the formulation and the composition of copper amine treating solutions. The sources of copper used, Cu(OH)2, CuCO3, CuSO4 and Cu(NO3)2, in the copper amine complex formulation affect the leachability of copper. Data show that copper amine from CuSO4 and Cu(NO3)2 treated wood has less copper loss during...
Jun Zhang, D P Kamdem
Quantification of creosote migration down wooden poles and the prevention of its depletion during flood irrigation
1994 - IRG/WP 94-50032
Polyethylene field liners heat-shrunk onto soil-contact surfaces prevented decay of creosote-treated Eucalyptus grandis vineyard poles under flood-irrigation. The present work quantified losses of creosote from these poles after six and 24 months' service. After six months' service the mean creosote retention of unlined poles above the ground line was 12.62% (m/m dry wood), with ...
M Behr, A A W Baecker
Influence of water soluble extractives on CCA fixation and leaching performance of red maple and red oak
1997 - IRG/WP 97-30133
We have observed several peculiarities in relation to CCA fixation in red maple and red oak woods such as high variability in fixation rates and leaching performance in maple and precipitate formation in solutions expressed from CCA treated red oak wood blocks at different stages of fixation. We have postulated that the extractives could be the factor of influence, as this has already been reporte...
T Stevanovic-Janezic, P A Cooper, Y T Ung
Depletion of preservatives from treated wood: Results from laboratory, fungus cellar and field test
1993 - IRG/WP 93-50001-07
This paper compares results of preservative component losses using a range of test procedures with several different water-borne preservatives. The data shows that laboratory leaching tests are in some cases comparable to, but in other cases significantly underestimate preservative component losses when compared with field or fungus cellar depletion tests. The results also suggest that preservativ...
L Jin, A F Preston
Leaching of Copper from ACQ treated wood exposed above ground
2004 - IRG/WP 04-50219
The leaching of chemicals of ACQ Type C treated wood exposed above ground for 16 months was studied. Commercially treated Hem-fir boards (Tsuga heterophylla Raf. and Amabilis fir Forb) of 37.5 mm by 87.5 mm were used. The amounts of chemical leached monthly by the rainfall were determined and the leachate was collected and analyzed. Also, the environmental factors influencing the leaching were ...
P A Chung, J N R Ruddick
Preservative leaching from copper-chrome-arsenic treated timber: Towards an international standard for environmental monitoring
1996 - IRG/WP 96-50076
A review of standards and legislative requirements around the world relating to environmental contamination from copper-chrome-arsenic wood preservative indicates a plethora of methodologies for expressing and determining contamination levels. The imposition of arbitrary quarantine periods for treated timber, or special fixation processes, appear to be applied without a rational analysis of what l...
S Walley, P R S Cobham, P Vinden