Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
Paintability and gluability of wood treated with arsenic-free and chromium free preservative treatments
2006 - IRG/WP 06-40342
The objective of this project was to study, in comparison with traditional CCA treatment, the paintability and gluability of wood treated with arsenic-free and chromium-free preservative treatments.
Four formulations, all certified CTB P+, were selected in accordance with their representativeness of the preservative product market: one CCA reference formulation and three chromium and arsenic free...
L Podgorski, G Legrand
Influence of Acetylation on Fire Resistance of Beech Plywood
2006 - IRG/WP 06-40326
Influence of acetylation on fire resistance was studied in beech plywood. Beech layers were acetylated in a reactor with acetic anhydride at 120ºC for varying durations. Plywoods were made from the acetylated layers and directly exposed to burning flame from their edges for 60s according to ISO 11925-3. Ignition and glowing time were measured in samples. Results were analyzed statistically based ...
B Mohebby, A Talaii, A Karimi , S Kazemi Najafi
Assessment of the Envelope Effect of Three Hot Oil Treatments: Resistance to Decay by Coniophora puteana and Postia placenta
2006 - IRG/WP 06-40344
Timber of Corsican pine (Pinus nigra var. maritima) and Norway spruce (Picea abies) was treated in hot linseed oil, rapeseed oil and a proprietary resin derived from linseed oil. The samples were immersed in oil or resin under reduced pressure at temperatures of 180°C and 200°C. Very high uptakes of the oils or resin were recorded for pine, while spruce showed lower weight percent gains, below...
M J Spear, C A S Hill, S F Curling, D Jones, M D C Hale
Wood-Plastic Composites and the Durability Dilemma: Observations from the Field
2006 - IRG/WP 06-40351
Wood-Plastic Composites (WPCs) used for decking, window & door moldings have experienced dramatic growth in North America over the last several years, with annual production increasing at rates greater than 20% per annum since 1998. A key factor contributing to this growth has been the successfully communicated message that they are "virtually maintenance free". The common perception being t...
M J Manning, F M Ascherl, M E Mankowski
Wood plastic composites from modified wood. Part 2 - Durability in laboratory decay tests
2006 - IRG/WP 06-40353
The decay resistance of wood plastic composites, WPCs, was tested according to modified versions of AWPA E10 (soil-block test) and ENV 807 (tests in three un-sterile soils, terrestrial microcosms, TMCs). The WPC materials were conically extruded profiles with 30% polypropylene content. The 70% wood content was untreated Scots pine sapwood, acetylated pine and heat treated Norway spruce, respective...
M Westin, P Larsson Brelid, M L Edlund, G Alfredsen
A New Decay Hazard Map for North America Using the Scheffer Index
2008 - IRG/WP 08-10672
Wood decay experts in the USA and Canada use the Scheffer Index for above-ground wood decay potential to decide among design and treatment options to ensure the durability of wood construction. This paper provides an updated North American decay hazard map and includes data on Central America. Index values calculated from recent climate data are higher than published values due to directional or c...
P I Morris, J Wang
Wood decay fungi from New Zealand ‘leaky’ buildings: PCR identification and laboratory decay tests of wood preservative-treated Pinus radiata (Part 1)
2007 - IRG/WP 07-10620
Fungi colonising Pinus radiata D. Don framing timber of ‘leaky’ New Zealand buildings were isolated to produce pure cultures. Mycelia from these cultures on agar media were collected to extract DNA. To identify the fungi to the species level, polymerase chain reaction (PCR) with primer pairs ITS1-F and ITS4 were performed followed by sequencing of the internal transcribed spacer (ITS) region. ...
D Stahlhut, R L Farrell, R Wakeling, M Hedley
Detecting fungal DNA in treated and non-treated wood
2007 - IRG/WP 07-10621
Isolating fungi from wood has long involved culturing on selective media followed by identification using various keys. This process can be cumbersome, costly, and, most importantly, not always capable of detecting all of the fungi present. The recent development of molecular methods for isolation and identification of fungi has created tremendous opportunities for expanding our knowledge of the...
C Freitag, M Freitag, J Morrell
The use of X-ray diffraction for analyzing biomodification of crystalline cellulose by wood decay fungi
2007 - IRG/WP 07-10622
X-ray diffraction (XRD) is based on the creation of an interference pattern by x-rays when they encounter a regularly spaced matrix. In wood, this process has been used to determine, among other things, the average width of the cellulose microcrystals, the percent of crystalline cellulose within the wood, and can be used to examine the changes in these parameters during degradation. Enhanced under...
C Howell, A C Steenkjær Hastrup, J Jellison
The characteristics of biodegradation mechanism of gamma-irradiated wood
2007 - IRG/WP 07-20352
Gamma radiation, as an easy, fast and effective sterilisation method, changes molecular structure in pest’s living cells, but also in wooden cell walls. Radiation-induced depolymerisation causes significant changes in wood properties crucial for laboratory testing of wood-preservative effectiveness. Natural durability of wood against rot fungi in lab conditions dependency on different sterilisat...
R Despot, M Hasan, F Pohleven, M Humar, G Rep
Decay Hazard Classifications in China for Exterior Above-Ground Wood
2007 - IRG/WP 07-20357
A decay hazard map for exterior above-ground wood structures is presented based on Scheffer’s Climate Index, with the major purpose of promoting awareness for proper protection of wood structures in different locations in China. A very large area in the South, including southern Yunnan, most of Sichuan Province and Chongqing, and part of Hunan, Hubei, Anhui, Jiangxi, and Zhejiang, as well as all...
J Wang, X Wu, M Jiang, P I Morris
Predicting the decay resistance of timber above-ground: 2. When can reliable field data be obtained?
2007 - IRG/WP 07-20368
Application of modern performance-based engineering and design requires building products that are thoroughly characterised in terms of their ability to perform as expected over time. The engineering community is attempting to use this information to provide predicted service-lives for various building elements. Increasingly, this service-life prediction must be based on objective measurement coup...
L P Francis, A J Swain, J J Morrell
Study of natural durability of Spanish Eucalyptus globulus wood
2007 - IRG/WP 07-10617
In some countries such as Australia, the wood of Eucalyptus globulus is recommended, due to its high durability, in risk situations where attack by organisms is likely to occur. In Galicia this species has been used for many decades for timber structures, which are still used. However, European Standard EN-350-2 places Eucalyptus globulus in the worst category of natural durability, a situation th...
D Lorenzo, M T Troya, M J Prieto, C Baso, M Touza
Chelator-Mediated Fenton Chemistry in Wood Degraded by Fungi
2007 - IRG/WP 07-10618
Wood specimens were colonized by individual isolates of brown rot, white rot, soft rot and blue (sap) stain fungi. Ethyl acetate extracts of the ground wood were analyzed for their iron-reducing capabilities using a ferrozine-based assay. Extracts from wood colonized by brown rot fungi showed a significantly greater iron-reducing capability than extracts from wood colonized by white rot fungi or n...
B Goodell, G Daniel, J Jellison, Yuhui Qian
Effects of heat treatments on decay resistance and material properties of ponderosa pine and yellow poplar
2007 - IRG/WP 07-40374
The potential for using heat treatment to improve the properties of North American fenestration species was evaluated on ponderosa pine (Pinus ponderosa L) and yellow poplar (Liriodendron tulipifera L) treated using the ThermoWood process at various treatment temperatures and times. Soil block tests using Gloeophyllum trabeum, Postia placenta, or Trametes versicolor showed that durability was enh...
C Vidrine, C Freitag, J Nicholson, J J Morrell
Marine Borer Resistance of Modified Wood - Results from Seven Years in Field
2007 - IRG/WP 07-40375
Wood modified by several methods has been tested for seven years in a marine field with high marine borer activity. Several wood modification methods were included, e.g. thermal modification (with different processes), acetylation, maleoylation, succinylation, furfurylation, treatment with methylated melamine resin and modification with reactive linseed oil derivative. Furthermore, some combinatio...
M Westin, A O Rapp, T Nilsson
Effects of chlorothalonil (CTN) and butylated hydroxytoluene (BHT) on microbial communities involved in the deterioration of wood using T-RFLP II: Results from field studies
2007 - IRG/WP 07-30429
The effects of Chlorothalonil (CTN) and Butylated Hydroxytoluene (BHT) on microbial species diversity in wood and the surrounding soil are being assessed by Terminal Restriction Fragment Length Polymorphism (T-RFLP). CTN was selected as a trial organic wood preservative, and the non-biocidal BHT was evaluated for its synergistic effects with CTN. ACQ-C was a positive control and untreated SYP sta...
G T Kirker, M L Prewitt, S V Diehl
Synthesis of boric acid ammonium oleate salt for wood preservation: Leachability and termite resistance test
2007 - IRG/WP 07-30435
A new chemical compound coupling boric acid and oleic acid through a joint of ammonium salt has been produced and its synthesis followed and validated by Fourier Transformed Infra Red (FTIR). This compound named ammonium borate oleate (BAO) combining biocidal properties of boron and water repellence of fatty acids has then been studied as a wood preservative.
Synthesis of BAO involved different...
F Lyon, A Pizzi, Y Imamura, M F Thevenon, S N Kartal, J Gril
Mold resistance of heat-treated wood
2007 - IRG/WP 07-40358
The resistance of heat-treated sugi sapwood against three mold fungi was evaluated. Wood specimens were first subjected to heat treatments at 180 and 220ºC for 2 and 4 hours. Mold growth on the surface of the specimens was measured 1, 2, 4 and 6 weeks after the inoculation with the fungi in laboratory conditions. Laboratory decay tests were performed using two brown and white-rot fungi along with...
S N Kartal
Fire, flame resistance and thermal properties of oil thermally-treated wood
2007 - IRG/WP 07-40361
Oil thermal treatment, first developed by German scientists, is a promising technology for improving the durability and dimensional stability of wood for outdoor above-ground residential uses such as siding and shingles. The present authors’ previous research showed that 220ºC is an optimal treatment temperature, with 2 hours’ treatment producing wood with significantly improved moisture and ...
Jieying Wang, P Cooper
Water repellency and dimensional stabilIty of wodd treated with waterborne resin acids/TOR
2007 - IRG/WP 07-40364
Wood used in above ground applications such as decking undergoes undesired dimensional changes leading to the lumber warping, cupping, splitting, etc. This is a major concern to consumers but it can be reduced by treating lumber with a water repellent. The ability of resin acids, hydrophobic compounds naturally present in southern yellow pines, was examined as a possible water repellent. A wate...
T P Schultz, D D Nicholas, J Shi
Durability of some alternatives to preservative-treated wood. Progress report 2: Results from field tests after 5 years’exposure
2007 - IRG/WP 07-30442
A number of alternatives to preservative-treated wood have been tested according to EN 252 (stake test) and a specially designed ground-proximity field test, the latter in Sweden as well as in Hawaii, USA. Seven untreated wood species and four alternative wood treatments labelled as environmentally friendly (acetylation, linseed oil, heat treatment, vinyl polymer) were included in the study. Four ...
M-L Edlund, J Jermer
Antifungal activity and synergistic effect of cinnamaldehyde combined with antioxidants against wood decay fungi
2007 - IRG/WP 07-30445
The objective of this study was to investigate the antifungal activity and synergistic effect of cinnamaldehyde combined with antioxidants against wood decay fungi. Five antioxidants, propyl gallate, octyl gallate, quercetin, eugenol and catechin were tested against various wood decay fungi. Octyl gallate and eugenol were found to be the only two antioxidants processed antifungal activities. IC50 ...
Fu-Lan Hsu, Tsair-Bor Yen, Hui- Ting Chang, Shang-Tzen Chang
Developments in Borate Treatment of Canadian Species for Decay and Termite Resistance
2007 - IRG/WP 07-30443
The increased interest in boron treatment of wood over the past 20 years is mainly due to its environmental acceptability, potentially deep penetration in wood, and its efficacy against decay and termites. Based on Forintek’s research in the past two decades, the boron penetration and retention requirements for decay and termite protection in various national and international standards for Cana...
Jieying Wang, P Morris, S McFarling, T Byrne