Economical analysis of the chemicals used on remediation copper, chromium and arsenic from out of service CCA-treated utility poles in Turkey
2004 - IRG/WP 04-50217
There are 20.7 million hectare forested area in Turkey. However, the wood products supplies do not meet demand. One of the wooden products is the utility poles. In Turkey, impregnation of utility poles has been started since 1960's and 5 million utility poles have been used until today since then. Although life time of the utility poles may vary depending on climatic conditions, average s...
E D Gezer, D Toksoy, Ü C Yildiz
Leaching of active components from preservative-treated timber - Ongoing research: Status after approx. 4 months’ out-door exposure
2003 - IRG/WP 03-20276
The Danish Technological Institute is together with manufacturers of active ingredients and formulators of wood preservatives running a project aiming at finding realistic leaching rates from preservative treated wood in hazard class 3 (above ground). The project is focussed on developing a field trial method for investigating leaching.
According to BPD hazard assessment has to be carried out f...
N Morsing
Adsorption of ACQ and CuMEA Wood Preservatives in Red pine
2005 - IRG/WP 05-30374
The rates of stabilization or fixation of ACQ subcomponents (CuO, DDAC and MEA) in red pine (Pinus resinosa) were compared for different solution concentrations (0.75%, 1.5%, 2.25% and 3% ACQ-D) and post treatment conditioning temperatures. Preservative solutions were impregnated into red pine sapwood by a full-cell treatment. Copper and MEA adsorptions from copper monoethanolamine solutions witho...
C Tascioglu, P A Cooper, Y T Ung
X-ray photoelectron spectroscopic analysis of CCA treated wood
1992 - IRG/WP 92-3700
Ponderosa pine and Douglas-fir wood sections were treated with CCA preservative. To elucidate the mechanism of fixation of the CCA, the wood surface was analyzed by X-ray photoelectron spectroscopy (XPS). CCA treatment increased C1 (carbon bonded to carbon and/or hydrogen) and decreased C2 (carbon bonded to one oxygen) in XPS C1s spectra, both in unextracted and pre-extracted sections. This sugges...
J N R Ruddick, K Yamamoto, P C Wong, K A R Mitchell
Distribution of copper/chrome/boron preservative in light red meranti (Shorea leprosula) before and after exposure test for 72 months
1995 - IRG/WP 95-20073
Copper/chrome/boron (CCB) preservative at 6% w/w was impregnated into light red meranti (Shorea leprosula) by full cell process. The quantitative analysis for copper, chrome and boron contents in treated wood samples was carried out by Inductive Couple Plasma (ICP). Electron Probe Microanalyser (EPMA) was used to monitor the distribution of copper, chrome and boron in the various treated wood tiss...
S Salamah, S Ani
Tendency of the preservative use for impregnation industries in Japan
1998 - IRG/WP 98-50101-05
In Japan, since 1997, the acceptable limit of the arsenic in the waste water become to 0,1 mg/l and the additional regional severer restriction can be established. In this reason, Japanese wood preservation industries intend to use other than CCA, like DDAC, ACQ, Tanalith CuAz, copper-naphthate and zinc-naphthenate, as replacing from CCA. In Jan-June 1997, the share of CCA preservatives was less t...
K Suzuki
Multiple-Phase Pressure (MPP) Process: Pilot plant trials for disposal of kickback using reverse osmosis membrane filtration
2001 - IRG/WP 01-40202
The MPP Process (a one-stage CCA treatment and accelerated fixation process) generates ~ 250 litres of kickback per cubic metre of timber treated. Composition of kickback is mainly wood sugars and traces of copper, chromium and arsenic. In pilot plant scale trials, MPP process kickback was filtered through a Reverse Osmosis (RO) membrane of a type found from earlier small-scale trials to be the mo...
H Pearson, G Durbin, M E Hedley
Field performance of novel antisapstain formulations
1997 - IRG/WP 97-30125
The effectiveness as antisapstain formulations of combinations of oxine copper (Cu-8), carbendazim, hexaconazole, cyproconazole, flusilazole, didecyldimethyl ammonium chloride (DDAC), an alkanolamine borate (SB), benzalkonium chloride (BAC), 2-n-octylisothiazolin -3-one (isothiazoline) and p-chlorophenyl-3-iodopropagilformal (CPIPF) was determined for freshly sawn, block-stacked radiata pine in th...
D R Eden, R N Wakeling, C M Chittenden, J G Van der Waals
A note on the distribution of copper-chrome-boric (CCB) along the culm length of freshly felled bamboo treated by modified Boucherie process
2005 - IRG/WP 05-40317
Preservative treatment of green and dry bamboo poses severe problems. A number of bamboo/ wood preservatives (Chemical formulations) for the destroying organism like fungi, borers and termites etc. In this paper we reported preliminary results of treatment of fresh green round bamboo attached with baranches by modified Boucheri process. Sample full length of an Indian species of bamboo Dendrocalam...
R Lal, C N Vani
A survey of the incidence of decay in copper-chrome-arsenate treated trellis support posts used in horticulture in New Zealand
1984 - IRG/WP 1225
Copper-chrom-arsenate treated softwood posts used as trellis support structures in 5 major horticultural districts of New Zealand were systematically examined for presence of decay. Principal crops on properties examined were grapes and kiwifruit; a minority of properties grew hops, boysenberries, and dwarf apples. Occurrence and severity of decay were variable within specific age classes of posts...
M E Hedley, J A Drysdale
Kinetics and mechanism of fixation of Cu-Cr-As wood preservatives. Part 5: Effect of wood species and preservative composition on the leaching during storage
1975 - IRG/WP 354
Conversion reactions during storage of CCA treated wood take place even at and below the fiber saturation point as long as ion transport is possible. Increase in drying temperature increases the final pH of the treated wood and the leachability of Cu and decreases slightly the leachability of Cr, while the leachability of As is not affected. This temperature effect is considered to be of no techni...
S-E Dahlgren
Preservative treatment of different thatching materials for low cost housing
1999 - IRG/WP 99-40144
Preservative treatment were made in seven different roofing materials with Copper-Chrome-Boron (CCB) at different concentration by soaking process. These were paddy straw, wheat straw, jute stick, sungrass, ulu grass, sugercane leaf and Nipa fruticans. It was observed that retention of preservative chemicals varies from species to species at the same concentration. From the service test it was obs...
K Akhter, M Younusuzzaman, M H Chowdhury
Characterization of checks and cracks on the surface of weathered wood
2000 - IRG/WP 00-40153
The surface roughness of unweathered and untreated pine; unweathered copper chromium arsenate type C (CCA) - treated pine; weathered CCA-treated pine; and weathered CCA-plus-water-repellent (WR) - treated pine was evaluated by a stylus tracing method. Surface roughness parameters Ra, Rz, Rmax, Rk, Rpk, and Rvk were measured. Ra, Rpk, and Rvk were the most appropriate parameters for describing modi...
D P Kamdem, Jun Zhang
International collaborative laboratory comparison of two wood preservatives against subterranean termites: Update
1994 - IRG/WP 94-20032
It was agreed by members at the termite workshop at the 24th annual meeting of IRG in Orlando, USA, in May 1993 to initiate an international subterranean termite laboratory bioassay to compare the various preferred termite protocols used by IRG termitologists. The author was nominated to co-ordinate this comparative laboratory evaluation of two wood preservatives (CCA and Cu-naphthenate) against t...
J R J French
Performance of preservative-treated timber against biodeterioration in Indian waters
1984 - IRG/WP 4106
Results on the investigation on the durability of panels of 32 timber species, pressure-treated with various preservatives and exposed along the Indian coast for varying periods upto a maximum of 15 years, are summarised. Panels of even non-durable timber gave excellent results against biodeterioration after treatment. Their life was comparable to that of treated durable timber. The preservative t...
L N Santhakumaran, J C Jain, M C Tewari
Preservative treatment of Golpata (Nypa fruticans) using CCA (Chromated Copper Boric Acid)
1999 - IRG/WP 99-40131
Golpata (Nypa fruticans) leaves provide a cheap but practical source of roof thatches. This study was carried out to determine whether the life span of Golpata could be extended by using CCB (Chromated Copper Boric Acid) treatment. Both leaves and midribs of Golpata , with different moisture contents ranging 16.63% to 70.67%, at the start of the experiment were treated with four different concentr...
G N M Ilias, F Abdullah, M O Hannan, S M Feroz
Oxine copper (NYTEK® GD) for the control of mould and sapstain on lumber in North America
1989 - IRG/WP 3517
NYTEK® GD is a new, water-based, micro-dispersible formulation of oxine copper registered in the United States and Canada for control of mold and sapstain-causing fungi. NYTEK GD is noncorrosive and of low hazard to applicators and people handling treated lumber, when used according to the label. The product is an effective wood protectant applied as a dip or spray treatment at concentrations of ...
D F Myers, J M Fyler, C H Palmer, G D Rosebery
Remediation of CCA-treated wood by chitin and chitosan
2005 - IRG/WP 05-50229
Chitin and chitosan are naturally abundant biopolymers which are interest of to research concerning the sorption of metal ions since the amine and hydroxyl groups on their chemical structures act as chelation sites for metal ions. This study evaluated the removal of copper, chromium, and arsenic elements from chromated copper arsenate (CCA)-treated wood via biosorption by chitin and chitosan. Expo...
S N Kartal, Y Imamura
Lignin degradation by a non-enzymatic system supposed to be active in white rot fungi
2000 - IRG/WP 00-10340
Electron microscopic investigations have shown that ligninolytic enzymes of white-rot fungi are only able to penetrate the wood cell wall in late stages of degradation. Thus, the selective degradation of lignin of certain white-rot fungi can only be explained on the basis of a low molecular weight, highly diffusible system. A system, consisting of copper, a coordination compound and either H2O2 or...
P Lamaipis, W Gindl, T Watanabe, K Messner
Soluble nutrient influences on toxicity and permanence of CCA preservatives in wood
1980 - IRG/WP 3144
The influence of soluble carbohydrate and nitrogenous components concentrated at evaporative surfaces of wood on the toxicity and permanence of CCA preservatives has been examined using soil-burial techniques. Nutrient concentrations in lime (Tilia vulgaris Hayne) have been shown to be associated with reduction of toxic limits of preservatives to an extent in which a 100% increase in preservative ...
B King, G M Smith, A Bruce
Comparison of methods for monitoring CCA fixation
1994 - IRG/WP 94-40023
The CCA fixation status in the outer 12.5 mm of pole sections of southern pine (Pinus sp.), red pine (Pinus resinosa) and lodgepole pine (Pinus contorta var. latifolia) were followed during fixation at 21°C under non-drying conditions by the following procedures: - Qualitative CrVI indication by the chromotropic acid spot test. - Quantitative CrVI in the expressate by the diphenylcarbazide method...
P A Cooper, Y T Ung, G Zanjani
Tolerance of Wood Decay Fungi to Commercial Copper Based Wood Preservatives
2002 - IRG/WP 02-30291
Due to the use of copper based preservatives like CCB or CCA for more than a century, copper tolerant fungi have appeared in some European countries in recent times. It is therefore important to find out whether this phenomenon is specific for only classical copper ingredients, or generally for all copper based formulation. Thus, we tested the tolerance of three commercial copper based
pres...
F Pohleven, M Humar, S A Amartey, J Benedik
Rainfall simulation to assess CCA permanence
1991 - IRG/WP 2373
During experimental work on accelerated fixation of chromium containing preservatives a method has been developed which compares the degree of preservative levels of contamination of simulated preservative fixation in timber with the levels of simulated rainfall. This method uses commercial sized wood sections wetted in a way that simulates actual rainfall and relates the associated run-off contam...
P Warburton, J A Cornfield
Surface accumulation of copper on CCA-impregnated Pinus patula stakes during marine preservative trials in the southern hemisphere
1992 - IRG/WP 92-4181
Pinus patula stakes treated with CCA to target retentions of 30 kg/m³ salts were exposed to sea water in marine and estuarine ecosystems off the coast of Southern Africa for two years. Samples were then analysed for copper and arsenic. Analysis of samples from the marine ecosystem showed (IRG/WP/4167) that arsenic was longitudinally and transversely leached from the wood, whereas the copper was r...
G D Shelver, C D McQuaid, M Tarin, A A W Baecker
The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen