The effects of impregnation with secondary metabolite extracted from Ipe on durability of Japanese cedar and beech wood
2013 - IRG/WP 13-30618
Ipe wood is known for its high durability; it has been widely used in exterior structures that are exposed to the weather. In this paper, to increase the durability of less durable wood, Japanese cedar and beech specimens were impregnated with a secondary metabolite from Ipe. In a previous study, secondary metabolites extracted by a Soxhlet extraction method showed antifungal properties. Therefore...
T Iida, R Konuma, K Kawarada
Preparation of Copper Rosinate Emulsion and Its Resistance against Wood Decay Fungi
2013 - IRG/WP 13-30619
A leaching-resistant water-borne copper preservative was prepared by means of the following three steps: (1) Gum rosin was saponified with potassium hydroxide. (2) The soap reacted with copper sulfate to form copper rosinate. (3) The copper rosinate was emulsified with a mixture of Tween 20 and Span 80. Poplar (Populus ussuriensis) wood was impregnated with 0.5%, 1.0%, 1.5%, or 2.0% of the copper ...
Mingxin Zhang, Shujun Li, Qian Wang, Bo Li, Qiong Wu
Copper leaching from copper-ethanolamine treated wood during exposure to terrestrial microorganisms
2013 - IRG/WP 13-30621
Copper-ethanolamine based wood preservatives are still the most important solutions for protection of wood in ground applications in Europe. Wood in ground is exposed to variety of organisms, which can act synergistically. In order to simulate these conditions in laboratory, Scots pine (Pinus sylvestris) specimens impregnated with copper-ethanolamine preservative of three different concentrations ...
M Humar, N Thaler, B Lesar
Performance of untreated wood and wood impregnated with copper-ethanolamine based preservative solutions in Northern Adriatic Sea
2013 - IRG/WP 13-30623
Sea water applications of wood are among the most challenging ones. Impregnated wood is exposed to leaching and to variety of marine borers, Limnoria sp. and Teredo sp. being the most important. In the present research, durability of pine wood impregnated with copper-amine based preservative solution (Silvanolin) of different concentrations, exposed to the sea water, was investigated according to ...
M Humar, M Petrič, J Adamek, B Lesar
Combined effects of thermal modification and ACQ-D impregnation on properties of southern yellow pine wood
2013 - IRG/WP 13-40637
In this study, samples of southern yellow pine sapwood were first thermally modified and then treated by the alkaline copper quat-type D (ACQ-D) wood preservative. Two heating temperature (180℃ and 220℃) and two concentrations of ACQ-D solution (0.9% and 1.35%) were used in the experiments. The combined effects of thermal modification and ACQ-D on leaching performance, mechanical prope...
Wang Wang, Yuan Zhu, Jinzhen Cao
Performance of Coatings on Wood Treated with Carbon-Based Preservatives
2013 - IRG/WP 13-40638
Wood treated with carbon-based preservatives is often used in applications where coatings are required, yet few studies have examined the effect of such treatment on coating performance. Users need to be confident that coatings on carbon-based preservative-treated wood will perform as well as or better than those on untreated wood. The present study examines the performance of three coatings on un...
R Stirling, P I Morris
Visualization of Copper in the Voids and Cell Walls of Treated Wood using X-Ray Micro-Computed Tomography
2013 - IRG/WP 13-40640
This study extends our observations of the distribution of copper in treated wood. A small wood block was cut from a southern pine batten that had been treated with a particulate-copper preservative and similar sized block was cut from a batten that had been treated with a copper-amine preservative. Both blocks were imaged using X-ray micro-computed tomography. We obtained tomograms of each treate...
P D Evans, A Limaye, H Averdunk, M Turner, T J Senden
Quantification of copper and chromium in field stakes after different exposure times: Remaining metal content and distribution
2013 - IRG/WP 13-50291
In order to determine the distribution of copper and chromium as well as their remaining concentration EN 252 specimens and thicker pine sapwood stakes (non standard format) were treated with a commercial CC salt in a vacuum pressure process. The stakes were installed in the test field of the Institute of Wood Research, Hamburg, in August 2010. In all cases three stakes were removed after 4, 8, 12...
T Liese, M Bahmani, E Melcher
Removal of nano- and micronized-copper from treated wood by chelating agents
2013 - IRG/WP 13-50294
Micronized and nano-copper (Cu)-based and arsenic and chromium-free systems have received much attention for wood protection in recent years. Because they have different fixation, and micro-distribution properties, such copper systems may be more or less subject to release using known remediation methods than soluble forms of Cu. This study evaluated Cu recovery from wood treated with micronized- ...
S N Kartal, E Terzi, B Woodward, C A Clausen, S T Lebow
Durability of alternatives to CCA-treated wood - Results from field tests after 11 years exposure
2013 - IRG/WP 13-30633
The present study was initiated as a consequence of restrictions against the use of CCA-type
wood preservatives in Sweden in the 1990s. New copper-based formulations were introduced on
the market and to some extent, also alternatives to preservative-treated wood, such as thermally
and chemically modified and linseed oil treated wood as well as heartwood of non-tropical
naturally durable wood s...
P Larsson Brelid, M-L Edlund
Effect of Nano-silver and Nano-copper and Nano-zinc oxide on Paulownia wood exposed to white-rot fungus
2013 - IRG/WP 13-30635
Paulownia is known as a fast growing tree and it can be used in several applications. The present study investigated the effect of Nano-silver and Nano-copper and Nano- zinc oxide on resistance of Paulowina (Paulownia fortunei) wood against the white rot fungus (Coriolus versicolor). Wood specimens with a dry density of 0.37g/cm3 were impregnated with a 400 ppm aqueous suspension of micronized na...
M Akhtari, M Ganjipour
On-site remediation treatments for framing timber in leaky buildings
2014 - IRG/WP 14-20549
Weathertightness failures in New Zealand buildings due to the combined effects of cladding choices, design and construction faults and the use of untreated framing timber has led to the so called ‘leaky building syndrome’. The latest estimated cost of the leaky building crisis in New Zealand is about NZ$11 billion.
This research was conducted to provide a better understanding of the option...
T Singh, D Page, A Bennett
Effectiveness of Copper Indicators in Treated Wood Exposed to Copper Tolerant Fungi
2014 - IRG/WP 14-20554
Wood treated with a copper based wood preservative will typically turn a green color. While the depth of copper penetration can be readily discerned from the green color of the copper it is standard practice in research and commercial treating plants to make use of a color reagent such as Chrome Azurol S, Rubeanic acid or PAN indicator to reveal the penetration more clearly. When copper treat...
L Jin, K Brown, A Zahora, K Archer
Efficacy of commercial wood preservatives against Bursaphelenchus xylophilus, a quarantine organism in Europe
2014 - IRG/WP 14-30638
Bursaphelenchus xylophilus (Steiner and Buhrer 1934) Nickle, 1970, pine wilt nematode (PWN), is a quarantine organism with a high potential to damage Conifer forests in Europe. This has driven the European Union to protect forest stands from the propagation and dispersion of this pathogen. Since the nematode was detected in Europe, eradication measures were taken. However, these measures were unsu...
C S Arcos, A Navas, L Robertson, M T Troya, M Conde, F Llinares
Ammoniacal Copper Zinc Arsenate Preservative Treated Wood Ties Their Performance in Testing and Track
2014 - IRG/WP 14-30636
While not a new preservative system, Ammoniacal Copper Zinc Arsenate (ACZA), had not previously been used to protect crossties. Its performance in treating difficult or refractory species of wood has been documented through its wide range of uses approved in AWPA. The establishment of appropriate testing for railroad material use was put in place and includes laboratory, field as well as commercia...
T Carey
Copper naphthenate treatment for wood crossties and timbers
2014 - IRG/WP 14-30647
Copper naphthenate (CuN) has a long history in wood preservation and is recently finding increased usage as a treatment for wooden crossties and timbers. One of the principal reasons that CuN has gained market acceptance, in addition to its efficacy against decay fungi and wood-destroying insects, is its low mammalian toxicity and environmental impact. CuN is a well proven non-restricted use pres...
J Brient
Chemistry of copper preservative treated wood
2014 - IRG/WP 14-30651
The reaction chemistry of micronized copper wood preservatives is fundamentally different from any previous inorganic preservative system. In order to study the chemistry, analytical procedures had to be developed which allowed the determination of the total copper as well as the copper which reacted with the wood forming copper-wood complexes. With the success of this approach it also became poss...
Wei Xue, P Kennepohl, J N R Ruddick
Laboratory Study of Relative Leachability of Chromated Copper Arsenate Preservative from Treated Woods among Soil Types of Sarawak
2014 - IRG/WP 14-50307
Wood and soils are important natural resources from the environment and serves mankind well respectively as structural materials and natural platform erecting such materials. With shortfalls of naturally durable timber species for protected in-ground uses under Malaysian environments, Chromated Copper Arsenate (CCA) treated woods are widely used instead, incurring serious potential threats of pres...
A H H Wong, P K F Chong
Douglas-fir PSL Treated with Oilborne Copper Naphthenate – Treatment Experience & Efficacy
2014 - IRG/WP 14-40687
Treating characteristics, field stake efficacy and the results from treatment trials for oilborne copper naphthenate (CuNap) and Douglas-fir parallel strand lumber (PSL) are summarized in this paper. Treatment with a P9 Type-C based solution in laboratory tests showed full cross section penetration of large cross sections could be achieved. Commercial treatment trials using a P9 Type-A solution ...
G P Merrick
Evaluation of color and gloss in decorative applied to cases of Pinus radiata wood impregnated (D. Don) copper type C azole micronized
2015 - IRG/WP 15-20571
Six treatments (one control and five decoration coatings) were applied to radiata pine wood treated with micronized copper azole (uCA-C), for outdoor use (R3) at a rate of 3.08 kg/m3 retention (T2). One decoration coating was applied before impregnation treatment: Prestain P (T3), and two, were applied in mixture with the uCA-C preservative Black Cylinder (T5) and Red Cylinder (T4). Two varnish we...
R Garay, M Inostroza
Performance of kiln-dried and air-dried anti-sapstain treated pallet timber under use scenarios against wood discolouring fungi
2015 - IRG/WP 30669
During their lifespan there is a high probability that wooden pallets and packaging material will be exposed to rainfall or rewetting conditions, increasing the risk of growth of discolouring fungi. Kiln-drying of wooden pallets and packaging material without anti-sapstain treatment does not give efficient protection against wood discolouring fungi during rewetting periods. However additional temp...
A Steitz, E Stoyanova, N Pfabigan, R Gründlinger
Search for an anti-sapstain treatment for fresh radiata pine wood in compliance with European BPD norms: Field Tests
2015 - IRG/WP 15-30673
In response to the impending restrictions on the use of pesticide active ingredients developed to control the staining of fresh wood, as a result of regulation issued in 2009 by the European Union, a project was proposed to test an alternative anti-sapstain treatment that meets both the European restrictions and the performance required for an export-quality radiata pine fresh wood treatment. A se...
P Montes C, T Hanke W
Polyamidoamines (PAA) functionalized with siloxane fragments as potential wood preservatives
2015 - IRG/WP 15-40708
Polyamidoamines (PAAs) utilized in this research were obtained by the reaction between N,N-methyl-bis-acrylamide (MBA) and Ethanolalmine (EtA) and/or aminopropytriethoxysilane (APTES). Different combinations between them were tested as wood preservatives against fungal decay. First, in situ impregnations of PAAs, with the reagents above described in different ratio, were performed and the effectiv...
S Palanti, G Predieri, E Feci, L Bergamonti
A Green and Novel Technology for Recovering Copper and Wood from Treated Waste - Part I
2015 - IRG/WP 15-50309
Preservative treatment of wood extends its service life. The US consumes about 70 million pounds of copper and produces about 7 billion board feet of treated wood annually. Burning and reusing CCA and copper treated wood wastes are disallowed by US EPA due to health and environmental concerns. Millions of pounds of copper and wood are disposed by landfill annually. The objective of this study was...
S Chen
Release of Copper from Pressure Treated Wood
2016 - IRG/WP 16-20584
Micronized copper based wood preservatives including micronized copper quat (MCQ) and micronized copper azole (MCA) have been introduced commercially to the North American market since 2006 as alternatives to alkaline copper quat (ACQ) or soluble copper azole (CA) preservatives. Unlike ACQ or CA, MCQ and MCA use dispersed particulate copper particles rather than soluble ionic copper to make treat...
Jun Zhang, J Horton