LOSP for glulam, when should the treatment be applied?
2011 - IRG/WP 11-30555
Treatment options for outdoor above-ground (H3) exposed glulam of Pinus radiata and P. elliottii were examined. Beams were treated with azole LOSP (containing a zinc tracer) aiming for retentions of 35-40 l/m3 or 70-80 l/m3. Treatment was conducted either before or after gluing. TBTN LOSP and CCA were included as comparative treatments. Test specimens for exposure were cut after treatment, while w...
L J Cookson
Influence of wood swelling agents on penetration and copper leaching of copper-ethanolamine based wood preservatives
2011 - IRG/WP 11-30556
Copper ethanolamine based preservatives are currently the most important solutions for impregnation of wood in ground contact in Europe. One of the issues related to those and similar water based solutions is insufficient penetration to refractory wood species like Norway spruce. In order to elucidate this issue, commercial copper ethanolamine based solution was supplemented with five different wo...
M Humar, N Thaler, B Lesar
Effect of P/F ratio, PF concentration and treating method on boron leaching from wood treated with PF modified boron compounds
2011 - IRG/WP 11-30559
In order to immobilize boron in wood, three kinds of resol-type phenol-formaldehyde (PF) resin with different P/F ratios were synthesized in laboratory and incorporated with three types of boron compounds to treat wood. The used boron compounds included boric acid (BA), borax (BX) and disodium octaborate tetrahydrate (DOT). The leaching test of boron from wood blocks was performed according to the...
Liping Yu, Jinzhen Cao
Standardized Field Trials with Micronized Copper
2011 - IRG/WP 11-30564
In 2008, an extensive review of all available data from standardized tests of micronized copper systems was published and there has been considerable work since then. This paper discusses over 20 field stake trials underway in well-known sites such as Gainesville, FL, Hilo, HI and the Dorman and Saucier sites in MS as well as tests from Australia and New Zealand. In addition, 4 ground proximity ...
C R McIntyre, M H Freeman
Copper Nanoparticles in Southern Pine Wood Treated with a Micronised Preservative: Nanodistribution of Copper in the Pit Membrane and Border of an Earlywood Bordered Pit
2011 - IRG/WP 11-30566
Copper nanoparticles can penetrate the cell walls of unlignified parenchyma cells in southern pine wood treated with a micronised wood preservative, but they are excluded from lignified tracheid walls. This paper extends these observations to include the cell wall layers of the bordered pit. Focused ion beam and ion milling were used to make an ultra-thin section of the cell wall layers of an earl...
H Matsunaga, Y Kataoka, M Kiguchi, P Evans
Tannin resin-boron for outdoor wood protection and fire retardancy
2011 - IRG/WP 11-30567
Boron in the form of boric acid is well known for its efficacy against wood destroying organisms, as well as for its high leachability from treated wood when in outside exposure. Moreover, due to the European directive 2008/58/EC, boric acid is only authorized at low levels. In order to keep considering boric acid as an interesting active ingredient for wood protection, the issue is now to fix it ...
M-F Thévenon, G Tondi, N Leménager, S Wieland, A Pizzi
The potential for using CuO nanoparticles as a wood preservative
2011 - IRG/WP 11-30569
The potential for using nano-copper particles for wood protection was investigated using mini-agar slant and wood block tests with Gloeophyllum trabeum or Trametes versicolor. Nano-copper was more effective against G. trabeum than T. versicolor, although neither of these fungi would be considered copper tolerant. Nano-copper solutions were stable over a 17 week storage period, but precipitated w...
I S Weitz, K Knani, M Maoz, C Freitag, J J Morrell
The case for using borates in termite control in tropical Australia
2011 - IRG/WP 11-30573
A brief historical overview of boron based wood preservatives efficacy against subterranean termite management worldwide, and in Australia, is presented. The boron based compounds to be used in H2 hazard conditions, may be applied as a surface treatment by dip, flood coat or spray, and rapidly penetrates to the centre of timber substrates, whether containing sapwood or heartwood. However, section ...
B M Ahmed (Shiday), J R J French
Design, synthesis, characterisation and effectiveness of ‘Locked-in-Boron’ chemicals for H3.2 level of wood protection
2011 - IRG/WP 11-30577
Boratrane molecules with five-membered and six-membered molecular ring systems, and with various ring substituents were synthesised, characterised and formulated for wood treatment for accelerated laboratory bioassays using wood decay fungi as test organisms. Six-membered ring boratranes showed lower efficacy in laboratory assays than five-membered ring boratranes. One alkyl-substituted boratran...
R Franich, H Kroese, S Gallagher, S Hill, B Kelly, G Billett, R Meder, W Rae
Laboratory study of toxicity or tolerance of CCA preservative and heavy metal constituents copper, chromium and arsenic to Malaysian tropical fungi
2011 - IRG/WP 11-30579
CCA preservative and its constituent heavy metal tolerance and toxicity to 3 Malaysian isolates Phialophora fastigiata (soft rot fungus), Paecilomyces variotii (mould fungus) and an unidentified white rot Basidiomycete, was investigated by the modified ‘Strange-Smith’ agar-well-plate technique with 1.6% CCA concentration and the malt-agar-plate bioassay technique with a range of CCA and consti...
A H H Wong, T Mark Venås, N Morsing, C C L Tan, P K F Chong
Further Studies on the Distribution of Copper in Treated Wood Using an XRF Microscope Technique
2011 - IRG/WP 11-40549
There are two distinct forms of copper in aqueous copper based wood preservative systems that are currently used in the United States for treatment of southern pine lumber. These are systems using either soluble copper (typically amine based) or the more recent particulate or “micronized” copper as the primary biocide. Studies reported last year showed that there were distinct differences in...
A Zahora
Quantification of mobile copper (II) levels in micronized copper treated wood
2011 - IRG/WP 11-40550
The purpose of this study is to quantify the mobile copper(II) levels in micronized copper treated wood using electron paramagnetic resonance (EPR) spectroscopy. A correlation between EPR and EDX intensities on mobile copper levels in a series of copper sulphate treated wood was created as a calibration standard. Laboratory treatments using micronized copper formulations were then carried out and ...
Wei Xue, P Kennepohl J N R Ruddick
Ambient-temperature borate dip-diffusion treatment of green railroad crossties
2011 - IRG/WP 11-40556
In the USA, borates are increasingly being applied prior to air seasoning and creosote treatment of railroad ties (railway sleepers). Borates are typically applied to green ties by vacuum pressure application at 1 to 10% disodium octaborate tetrahydrate (DOT) concentration or by traditional dip-diffusion treatments at elevated temperatures. Higher temperatures are used to maintain the 30 to 50% so...
Jae-Woo Kim, A M Taylor, C Köse
Characterizing long term leaching behaviour of copper from preservative treated wood in a practical exposure scenario
2011 - IRG/WP 11-50278
To investigate the prediction of the long term emission of copper from preservative treated wood in a Use Class Class 3 scenario, treated boards were exposed vertically above ground to natural weather conditions. The study included two products; an amine copper ACQ-type formulation, air-dried after treatment to a 22 kg/m3 retention, and the same formulation which was hot oil vacuum dried after tre...
T Mark Venås, M Klamer
Copper Migration from Micronized Copper Preservatives Treated Wood in soil contact:
2011 - IRG/WP 11-50280
Emerging formulations of preservatives made with micronized basic copper carbonates with azoles and/or quat to control copper tolerant fungi have been used to replace formulations containing soluble copper to reduce the leaching of copper and the corrosion of metal in contact with wood. This study proposes to use laboratory soil leaching test AWPA standard (E20-08) to estimate the amount of copper...
Lei Wang, D P Kamdem
Inhibition of Basidiospore Germination by Copper from MCQ, ACQ and CCA Leachates
2012 - IRG/WP 12-10778
The long-term decay resistance of refractory wood shell-treated with chromated copper arsenate (CCA) in above-ground exposures has been attributed to mobile copper that migrates into checks and inhibits the germination of basidiospores. Copper from micronized copper quat (MCQ) has also been shown to migrate into checks suggesting similar performance as a shell treatment, but questions have been ra...
R Stirling, J Drummond, P I Morris
Use of X-Ray Micro-Computed Tomography to Visualize Copper in Preservative Treated Wood
2012 - IRG/WP 12-20488
This study tests the hypothesis that X-ray micro-computed tomography will be able to visualize the distribution of copper in wood treated with a micronized wood preservative containing copper carbonate. A small wood block measuring 12 x 12 x 19 mm was cut from a 2.4 m x 51 mm x 51 mm southern pine batten that had been treated with a micronized wood preservative. Tomograms of the wood block were ob...
P D Evans, A Limaye, H Averdunk, M Turner, T J Senden, M A Knackstedt
Performance of boron diffused wood products used indoors for 144 months in Bangladesh
2012 - IRG/WP 12-30581
In this service performance study of boron diffused hardwoods, boron in the form of boric acid (H3BO3) was applied separately through paste and through wet cloth. The born diffused woods were kept indoors for 144-months in Bangladesh to ascertain the performance of treated wood against wood destroying insects. The new easy application processes of cost effectual boric acid have been found effectiv...
A K Lahiry, T Lahiry
Tannin resin-boron associations: Leaching and biological resistance
2012 - IRG/WP 12-30587
The easy leaching of boron in wood preservation formulations has allowed to use this fungicide only for short term applications. The recently discovered adduct with flavonoids allows boron to resist longer periods of time within wood and consequently extend its life. Two different leaching treatments were compared and the fungal and termite decay was examined. The biological tests have shown extre...
G Tondi, S Wieland, N Lemenager, A Petutschnigg, A Pizzi, M-F Thevenon
Smart hydrogels from low molecular weight amphiphilic compounds: toward a solution to decrease leachability and increase efficacy of boron preservatives?
2012 - IRG/WP 12-30589
A new catanionic system associating amphiphilic carnosine (AlaHisC8) and lauric acid forms supramolecular hydrogel at very low concentration. This gel was investigated and we have checked the validity of the concept of hydrogels utilization to reduce boron leachability and to develop new wood protection treatments. Impregnation with 5% aqueous borax solution (w/w) and 0.3% gelator agent (...
F Obounou Akong, P Gérardin, C Gérardin-Charbonnier
Termite resistance of copper-based preservative supplemented aspen strandboards
2012 - IRG/WP 12-30594
Termite resistance of aspen strandboards treated with various copper-based preservative systems was evaluated in field exposure tests. Five copper-based chemicals or zinc borate were blended into aspen furnish at three retention levels prior to pressing. Tebuconazole or 4,5-dichloro-2-N-octyl-4-isothiazolin-3-one (DCOI) were added as co-biocides to selected copper-based treatments. Sections from...
J J Morrell, C Vidrine, A Preston, L Jin
Mobilized copper(II) concentrations in earlywood and latewood of micronized copper treated red pine
2012 - IRG/WP 12-30596
Electron paramagnetic resonance (EPR) was used in conjunction with energy dispersive x-ray spectroscopy (EDX) to quantify total copper and mobilized copper retentions in MCQ and MCA treated red pine. The MCQ treated red pine was found to have higher copper retention than that of the MCA treated one. Earlywood in general had higher total copper content than latewood. The mobilized and complexed cop...
Wei Xue, P Kennepohl, J N R Ruddick
The Effects of Industrial-Scale Heat Treatment and Impregnation with Boron Compounds on Water Uptake and Tangential Swelling of Some Wood Species
2012 - IRG/WP 12-40599
This study evaluated the effects of boron impregnation and heat treatment on water uptake and tangential swelling of spruce (Picea orientalis), pine (Pinus nigra), beech (Fagus orientalis) and poplar (Populus deltoides) wood species. The samples (10 x 5 x 40 - tangential x radial x longitudinal cm) were impregnated with 4 % boric acid and 4 % borax according to the ASTM D-1413 standard method. Aft...
A Can, S Yildiz, Ü C Yildiz
KERUING and APITONG: A Timely Review of the Perfect Choice Wood Species for Crossarms and Brace Arms, Including Data on Copper Naphthenate Treatments
2012 - IRG/WP 12-40603
Apitong or the wood species more commonly known as Keruing is an important tropical hardwood known for its high strength to weight ratio and its reasonable durability and preservative treatability. This wood has been exported from managed permanent forest estates in Malaysia into the United States for over 4 decades for its widespread use in wooden utility industry brace arms and crossarms, yet cu...
A Wong, M Freeman
Scale-up of a chemical process for copper-based preservative-treated wood wastes recycling
2012 - IRG/WP 12-50286
In recent years, the development of appropriate wood waste disposal options has been encouraged by severe regulations and expensive fees associated with wastes landfilling or burning. An efficient and economically attractive leaching process was developed at laboratory scale (200 mL) for CCA-, ACQ- and CA-treated wood wastes recycling. This leaching process consisted of three leaching steps of 2 h...
L Coudert, L Gastonguay, J F Blais, G Mercier, P Cooper, P Morris, A Janin, N Reynier