Wood preservation sites polluted by CCA. Is potassium diphosphate incubation a catalyst for the electrodialytic remediation of these soils?
1998 - IRG/WP 98-50106
As part of an evaluation of a newly developed electrodialytic soil remediation technique, we investigated the incubation of a contaminated soil (from a Portuguese wood preservation site polluted with CCA) with potassium diphosphate as a possible catalyst for the removal of heavy metals and metalloids. A chemical sequential extraction scheme (SE) applied to the soil has shown that the potassium dip...
A B Ribeiro, G Bech-Nielsen, A Villumsen, A Réfega, J Vieira e Silva
The influence of cement and calcium compounds on the performance of CCA preservatives
1983 - IRG/WP 3221
The influence of cement and calcium compounds on the durability of untreated and CCA treated wood is considered. Calcium compounds were found to reduce the toxicity of a CCA preservative to a soft rot fungus at copper to calcium ratios of 1:1 and 1:10 using a cellulose filter paper technique. Further studies are outlined and some possible mechanisms by which cement and calcium compounds may affect...
R J Murphy
Efficacy of a novel copper-based organic solvent preservative in laboratory and fungus cellar tests
1995 - IRG/WP 95-30071
The efficacy of Chemicca 4, a novel copper-based organic solvent preservative, was compared with that of other LOSP in pure culture laboratory decay tests and with that of CCA and TBTO in a fungus cellar exposure. It was markedly superior to copper and zinc naphthenates at equivalent metal retentions in laboratory decay tests, and similar in activity to TBTO. After 60 months' fungus cella...
M E Hedley, P N Maynard
A physiological role of the glyoxylate and TCA cycles in fruitbody formation of the coppertolerant brown-rot fungus Fomitopsis palustris
2002 - IRG/WP 02-10430
Changes in activity of the representative enzymes involved in biosynthesis of oxalic acid (oxalate) and carbon metabolism of glucose were investigated in relation to the fruit body formation of the copper-tolerant brown-rot fungus Fomitopsis palustris. Changes in specific activities of the two glyoxylate (GLOX) cycle key enzymes (isocitrate lyase (ICL) and malate synthase (MS)), the two oxalate-fo...
Jeong-Jun Yoon, T Hattori, M Shimada
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
The role of oxalic acid in tolerance to N’N-naphthaloylhydroxylamine in Tyromyces palustris
2006 - IRG/WP 06-10584
Certain wood decay fungi exhibit tolerance to one or more wood preservatives. Copper tolerance of brown-rot fungi has been studied in our laboratory for the past six years. We have observed some degree of tolerance to N’N-naphthaloylhydroxamine (NHA), a recently patented termite bait, by the brown-rot fungus Tyromyces palustris TYP-6137. In an effort to try and confirm this tolerance in other is...
R A Arango, C A Clausen, F Green III
Is Field Test Data from 20 x 20mm Stakes Reliable? Effects of Decay Hazard, Decay Type and Preservative Depletion Hazard
2006 - IRG/WP 06-20327
Effects of decay hazard, decay type and preservative depletion hazard on the performance of variously preservative treated 20 x 20 x 500 mm Radiata pine and Fagus sylvatica test stakes across 13 field test sites in New Zealand and Queensland Australia were determined.
Radiata pine treated with an ammoniacal copper quaternary preservative (ACQ) (1.56% m/m a.i.) and copper chrome arsenate (CCA) (...
R Wakeling
The Use of Modulus of Elasticity and Modulus of Rupture to Assess Wood Decay in Laboratory Soil-Bed Test
2006 - IRG/WP 06-20338
The efficacy of wood preservatives were determined in a soil-bed test. Samples of alder wood sapwood (Alnus glutinosa subsp. barbata) (5x10x100 mm) were treated with Solutions of CCA (1 % and 2 %), ACQ-1900 (2 % and 3 %), ACQ-2200 (1 % and 2 %), Tanalith E 3491 (2 % and 2.8 %), Wolmanit CX-8 (% 1 and 2 %). Modulus of Elasticity, modulus of rupture, mass loss and decay rate according to AWPA E7 wer...
A Temiz, Ü C Yildiz
Measuring Soil Respiration as a New Approach to Describe the Interaction Between Wood (Treated and Untreated) and Microbiologically Active Soil
2006 - IRG/WP 06-20344
Soil respirometry was employed to examine the relationship between both the performance of copper organic preservatives in contact with and the amount of carbon dioxide evolved from soil and the effect of wood treated with preservatives on carbon turnover in soil. Wood was treated with a range of copper organic preservatives intended for use in ground contact as well as an organic preservative in...
I Stephan, W Mierke
Qualitative and quantitative assessment of chemicals used for wood durability improvement by Near Infrared Spectroscopy
2006 - IRG/WP 06-20349
The Near infrared spectroscopy (NIRS) could be a suitable technique to assess chemicals used for wood durability improvement in the forest products industry. NIRS methodology can be used to obtain results more quickly, less costly and without damaging the wood. In this study, wood samples selected from heartwood and sapwood of Maritime Pine (Pinus pinaster) were prepared to assess the artificial d...
S Zahri, F Charrier, H Baillères, B Charrier
Above and Below-Ground Depletion of Copper, Chromium and Arsenic from Pinus radiata and Fagus sylvatica at Thirteen Test Sites in New Zealand and Australia
2006 - IRG/WP 06-30402
The objective was to determine the significance of site and wood species on preservative depletion for a copper chrome arsenate preservative (CCA) from 20 x 20 x 500 mm field test stakes after 5.5 and 4.5 years for pine and beech respectively. At least 5 sacrificial stakes were used to produce site means. Site and wood species had a major effect on copper, chromium and arsenic loss from CCA treate...
R Wakeling
Addition of boron compounds and octanoic acid for improvement of biocidal properties and copper fixation at copper-ethanolamine based wood preservatives
2006 - IRG/WP 06-30408
Copper-ethanolamine based wood preservatives became important active substance (formulation) for wood protection, novelty. As copper itself can not ensure sufficient protection against wood destroying organisms and fixation in wood we combine it with other biocides like ethanolamine, boron and octanoic acid. This investigates were performance on spruce wood impregnated with different combination o...
F Pohleven, M Humar
Long term marine performance of ACZA treated Hem fir in Krishnapatnam harbour, east coast of India
2006 - IRG/WP 06-30409
The performance of Hem fir (Tsuga heterophylla) and Southern pine (Pinus sp.) treated with ammoniacal copper zinc arsenate (ACZA) and copper dimethyldithio carbamate (CDDC) at two retention levels of each preservative was assessed in tropical marine waters at Krishnapatnam harbour on the east coast of India. Panels treated with ACZA of lower loadings (23.1 Kg/m3) had failed in 38 months while the ...
B Tarakanadha, K S Rao, J J Morrell
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
CCB Preservative treatment of split muli (Melocanna baccifera ) bamboo by soaking process
2006 - IRG/WP 06-40336
This study was carried out in order to investigate the retention of chemicals inside the split muli ( Melocanna baccifera ) bamboo after preservative treatment by soaking process. Treatment with 10% aqueous solution of CCB (copper-chrome-boron) was applied in split bamboo of two sizes (1/4 part and 1/8 part) at three different moisture contents and five time periods (24, 48, 72, 96, 120 hours). It...
K Akhter, M H Chowdhury
Non-pressure preservation technique of five less durable timber species – Kadam (Anthocephalus cadamba), Shimul (Bombax ceiba), Pithalu (Trewia nudiflora), Am (Mangifera indica) and Boroi (Ziziphus jujube) of Bangladesh
2006 - IRG/WP 06-40322
Wood is a versatile renewable resource, which has been extensively used as a reliable construction material as well in furniture ever since the beginning of civilization.
The Major disadvantage of wood is its susceptibility to biodeterioration by fungi, insects and bacteria. In tropical countries like Bangladesh, fungi is the most significant of these biodeterioration agents. Kadam (Anthocephalus...
G N M Ilias, A H Kabir, F Begum, M F Alam
The Effect of Wick Action upon Moisture Distribution in Ellagate Treated Pinus radiata Wood
2006 - IRG/WP 06-40328
Sapwood stakes of Pinus radiata D. Don were treated with water-soluble tetraguanidinium, tetracholine and tetrakis-benzyltrimethylammonium ellagates. The effect of these treatments upon moisture distribution was investigated by wick action. Given that chemical reactions within the wood substrate between nutrients and treatment solutions may alter the properties of the wood with regard to moistur...
S R Przewloka, B J Shearer, J A Hann
Corrosiveness of metal by copper-based preservatives
2006 - IRG/WP 06-40329
The corrosive rates of 4 types of metal as well as epoxy-coated metal by a variety of preservatives derived from different copper source and ingredients were conducted in this paper. The main results shown that: CCA is less corrosive to red brass and Q235A steel than other copper formulations; Copper-based preservatives such as ACQ and copper azole derived from basic cupric carbonate or cupric hyd...
Ying Zhang, Mingliang Jiang
Leaching of CCA from Paraserianthus falcataria panels exposed to field conditions at Krishnapatnam harbour, Andhra Pradesh
2006 - IRG/WP 06-50241
This study assessed the leaching of copper, chrome and arsenic (CCA) from Paraserianthus falcataria (=Albizia falcataria) panels exposed to marine condition at Krishnapatnam harbour on the east coast of India. Metal loss was assessed in test panels after 6, 12, 24 and 36 months of exposure using Atomic Absorption spectrophotometer (AAS). The metal loss was found slightly higher in panels treated ...
B Tarakanadha, K S Rao
Corrosion of metal fasteners in contact with copper preservative treated wood
2007 - IRG/WP 07-20370
The corrosion rates of metal fasteners in contact with alkaline copper quat (ACQ) treated wood with or without commercially available water repellent was compared to that of cedar. In this experiment, fasteners were sandwiched between two pieces of treated wood and exposed to a humid environment at a slightly elevated temperature. The use of a “sandwich” design allowed periodic examination of ...
BaekYong Choi, J N R Ruddick
Use of the Digital Refractometer for the On-site Analysis of Copper-based Preservative Systems
2007 - IRG/WP 07-20371
In some counties, there are no on-site chemical analysis methods available for treatment plants to use to determine the key active ingredients in the preservative treatment solutions. The complexity of the sophisticated methodology; cost of analytical instruments and training required for operating these instruments in treating plant level are the reasons for lacking such practice. In this paper...
L Jin, T Cashman, A Preston, J Trompetter, H Trompetter
Preservative treatment of Golla cane (Daemonorops jenkinsiana) by pressure process
2007 - IRG/WP 07-40379
The feasibility of preservative treatment of golla cane (Daemonorops jenkinsiana (Griff) Mart). by pressure process has been studied using water borne preservatives CCB (copper-chrome-boron). Cane samples of three different lengths 1m, 2m and 3 m. were treated at different pressure and time period to evaluate the extent of penetration and retention of preservative chemicals. It was observed that t...
K Akhter, M Hoque Chowdhury
Influence of ethanolamine on lignin depolymerization and copper leaching from treated Norway spruce and beech wood
2007 - IRG/WP 07-30423
Copper-ethanolamine based wood preservatives are replacing several classical copper-chromium based solutions, due to foreseen ban of chromium. Fixation of copper-ethanolamine based wood preservatives is not as good as fixation of copper-chromium ones. The main object of this manuscript was to prove, that ethanolamine is the prime reason for insufficient fixation of copper-ethanolamine formulations...
M Humar, B Bucar, M Zupancic, D Žlindra, F Pohleven
Copper fixation in ACQ-D treated Chinese fir at various temperature and relative humidity conditions
2007 - IRG/WP 07-30436
In this study, the effect of different conditions of temperature, relative humidity, and duration of post-treatments on accelerating copper fixation in ACQ-D treated Chinese fir wood blocks was investigated. The conditions include the combination of three temperatures (21, 50, and 70?) and two relative humidity levels (20% and 80%), also include four temperatures (50, 70, 90, and 110?) without con...
Jinzhen Cao, Lili Yu
Micro-Distribution of Metals in Wood Treated with a Nano-Copper Wood Preservative
2007 - IRG/WP 07-40360
The microdistribution of copper in southern pine treated with a newly-developed nano-copper wood preservative was examined to determine if it differed from that reported for wood treated with conventional copper-based wood preservatives. Field Emission Scanning Electron Microscopy (FE-SEM) in combination with x-ray microanalysis (EDX) revealed the presence of nano-sized copper and iron particles i...
H Matsunaga, M Kiguchi, P Evans