A study of decay type variability in variously treated Fagus sylvatica and Pinus radiata field test stakes exposed at a vineyard for 30 - 45 months
1998 - IRG/WP 98-10271
Pinus radiata test stakes were treated with 10 kg/m3 of CCA plus 4 lower retentions in a geometric series of 1.5. Fagus sylvatica was treated with 15 kg/m3 and 2 lower retentions. Both timber species were also treated with equivalent retentions of various new generation preservatives (P. radiata was also treated with creosote). Whilst these stakes were exposed at 11 sites in New Zealand (NZ) and 2...
R N Wakeling, A P Singh
Leaching and fixation characteristics of chrome-copper-fluoride-zinc (CCFZ) treated wood
1996 - IRG/WP 96-30096
The leaching characteristics of radiata pine sapwood blocks treated with CCFZ were evaluated by the AWPA standard leaching test. The rate of fixation of the preservative components in CCFZ treated radiata pine were also evaluated by quantitative analysis of solution expressed from the treated wood. Both leaching and fixation characteristics of CCFZ were compared with CCA-Type C treated wood sample...
Gyu-Hyeok Kim, Jong-Bum Ra
Preliminary studies on cellulase production by selected Basidiomycetes and the effect of copper-chrome-arsenate on these enzymes
1980 - IRG/WP 1122
The growth of wood-destroying fungi on ligno-cellulosic materials depends on the production of many enzymes, of which probably the most important is the multi component cellulase system. Within this system, at least three different kinds of enzym are believed to be involved in crystalline cellulose decomposition. These are endo-1,4-glucanase, exo-1,4-ß glucanase and ß-glucosidase. Most of the re...
O Collett
Kiln drying of CCA-treated wood - Some safety and environmental considerations
1987 - IRG/WP 3443
Vapours and condensate from a condenser kiln in which CCA-treated wood was being dried have been collected and analysed. The concentrations of arsenic, copper and chromium found in the vapours from the drying process were well below Swedish threshold limit values. The contents of arsenic and chromium were also low in the condensate, although the copper content was fairly high. The latter result wa...
J Jermer, B Lundberg
Performance of copper-based wood preservatives in above ground and ground contact tests
1994 - IRG/WP 94-30057
The relative performance of a range of copper-based wood preservatives was compared using above ground and ground contact procedures. The data, accumulated after several years' testing, show that on an equivalent active ingredient basis, differences in performance of the preservative systems tested can vary quite markedly. The contribution of co-biocides to the overall performance of thes...
A F Preston, K J Archer, L Jin, W Metzner, D Seepe
Copper naphthenate: An analysis of the materials found in the worldwide marketplace using a new analytical technique
2000 - IRG/WP 00-30224
Naphthenic acid has been recovered from products of petroleum refining for well over 100 years. The metal soaps, specifically copper and zinc naphthenate, have been evaluated and used as commercial wood preservatives for in excess of 60 years. Most of the early data supporting the continued use of copper naphthenate as a wood preservative was based on materials manufactured from naturally occurrin...
J A Brient, R E Moyer, M H Freeman, H Jiang
Fungus cellar testing as an evaluation method for performance of treated timber in ground contact
2001 - IRG/WP 01-20227
A fungus cellar method for the accelerated evaluation of performance of treated wood in ground contact is described. The test soil comprised of sandy loam, vermiculite and Japanese horticulture soil "Kanumatsuchi" in a ratio of 6:2:2 by volume. The soil was inoculated with the dominant test fungus isolated with selective medium from decayed wood samples. Pairs of treated and untreated wood specime...
Y Nagano
Wood Preservatives Science Issues: US EPA’s Perspective
2005 - IRG/WP 05-50224-2
The USEPA Office of Pesticide Programs (OPP), Antimicrobials Division (AD), regulates the use of chemicals registered as wood preservatives in the United States. An overview of the registration and re-registration process is presented. The wood preservatives data requirements include toxicological, human exposure, ecological, and environmental fate data. A detailed discussion of wood preservati...
N Elkassabany
Serviceability of copper naphthenate-treated poles
2000 - IRG/WP 00-30214
Copper naphthenate-treated poles in service were inspected for deterioration, penetration, retention, and serviceability. The study to date has included poles in all hazard zones in the United States. Poles installed by 12 different utilities and eight different treating companies are included in the survey. Both southern pine and Douglas-fir poles and distribution and transmission poles are inclu...
H M Barnes, M H Freeman, J A Brient, C N Kerr Jr
CCA modifications and their effect on soft rot in hardwoods. Part 2
1983 - IRG/WP 3244
The work outlined in this document is a continuation of that presented in Document No: IRG/WP/3201. The findings described in the previous paper are summarised below: a double treatment of CCB followed by arsenic (CCB+A) is more effective than a double treatment of boron followed by CCA (B+CCA) or a single treatment of CCA, CCB or CCAB in controlling soft-rot due to Chaetomium globosum in birch. C...
S M Gray, D J Dickinson
Corrosion of zinc-coated nails used with preservative-treated western red cedar shakes in service
1982 - IRG/WP 3197
The corrosion of metal fasteners used with certain wood species and with preservative-treated woods can be a serious problem. The chemical reactivity of western red cedar (Thuja plicata Donn) extractives to iron and copper is well documented and wood preservative treatments containing copper, chromium, and/or ammonium hydroxide can be expected to similarly attack some metals. This problem is compo...
R S Smith, E L Johnson, A J Cserjesi
The efficacy of remedial treatments for controlling fungal decay in window millwork used in the United States
1987 - IRG/WP 3432
Conventional window millwork was subjected to basidiomycete decay by inoculation and sampled for active growth of the decay fungus before and eight months after remedial preservative treatment with fused disodium octaborate rods (IMPEL) at boric acid levels of 1.5 and 4.0 kg/m³ or liquid bifluoride injections (IMPROSOL) at 1 kg/m³. The elimination of decay fungus after remedial treatment was nea...
M G Dietz, E L Schmidt
Effectiveness of a newly registered antisapstain preservative in preventing stain of Eucalypt timber in Australia
2000 - IRG/WP 00-30229
An antisapstain trial was conducted on two sites (Alexandra and Trentham) in order to establish the concentration of a newly registered antisapstain preservative (consisting of benzalkonium chloride (BAC) & 3-iodo-2-propynyl butyl carbamate (IPBC) & disodium octoborate (boron)) needed to prevent stain of Eucalypt timber. After 20 weeks of exposure at the Trentham site, the water treated bo...
J Snow, P R S Cobham, N Ryan
Incorporation of phenyl boronic acid treatment with vapor phase formalization
1997 - IRG/WP 97-40083
Phenylboronic acid (PBA) treatment was incorporated with vapor phase formalization (VPF) in order to increase dimensional stability and boron fixation as well as enhancement of biological resistance. Five and ten hours VPF were applied after PBA treatment as 0.34, 0.50, 1.00 and 2.00% concs. aqueous solutions. Anti swelling efficiency (ASE) attended to 71% in specimens impregnated with 0.50% PBA s...
M K Yalinkilic, S Yusuf, T Yoshimura, W-Y Su, K Tsunoda, M Takahashi
Effectiveness of copper/chromium salts as wood preservatives against Limnoria tripunctata Menzies in laboratory tests
1977 - IRG/WP 431
During the last joint meeting of IRG and COIPM a co-operative programme of tests with copper/chromium salts as wood preservatives against marine borers was discussed and agreed. In this connection the results of a laboratory test in the BAM with Limnoria tripunctata Menzies will be of interest. But as the respective paper is written in German (H. Kühne; G. Becker: Laboratoriumsversuche über die ...
H Kühne
Safe application of copper-chrome-arsenate preservatives
1975 - IRG/WP 377
All wood preservatives contain biologically active substances and must, by design, be in some measure toxic to man. There is nothing fundamentally difficult, however, about using a wood preservative with complete safety. It depends on knowing the risks to health and/or the environment, which the preservative may present, and planning application accordingly. In this paper we examine these and othe...
I N Stalker, P B Cornwell
Experiences with penetration of copper-based wood preservatives
2001 - IRG/WP 01-20233
In the Nordic countries there is a long tradition of result type based specifications for preservative-treated wood. A common Nordic standard for treated pine (Pinus sylvestris) wood was published in 1976. After a revision in 1989 this standard, then named INSTA 140, defined four classes of treated wood: M, A, AB and B. Treaters producing according to this standard had to be affiliated to a qualit...
J Jermer, F G Evans, I Johansson
Report on the burning of wood treated with wood preservatives containing copper, chromium and arsenic
1976 - IRG/WP 379
Mixtures of copper, chromium and arsenic salts are used extensively in the UK to preserve timber. This report is concerned with the fate of these metals when timber treated with these salts is burned. A large percentage of the arsenic present in the timber is shown to be volatilised during combustion and the potential environmental implications of this are assessed by comparison with the release o...
A J Dobbs, C Grant
Some data on the activity of alternative fungicides for wood preservation
1985 - IRG/WP 3333
Data from laboratory tests against basidiomycete fungi are presented for 9 alternative fungicides in organic solvent formulations and also in water for one product. Results are compared with data for reference preservatives, tributyltin oxide, copper and zinc naphthenates and pentachlorophenol. Of special interest is the apparently better than additive effect of mixing tributyltin naphthenate and ...
A F Bravery, J K Carey
Comparative performance of several ammoniacal copper preservative systems
1997 - IRG/WP 97-30151
The efficacy of several ammoniacal copper-based wood preservative systems was evaluated in this study. The selection of potential co-biocides was based on the results of an agar plate test. Following this, the most promising systems were evaluated in a standard field stake test. Good correlation was found between the agar plate and field stake test results. Of the preservative systems tested, copp...
D D Nicholas, T Schultz
Evaluation of the corrosivity of the treated wood - Laboratory vs field test methodologies
2000 - IRG/WP 00-20211
The corrosivity of treated wood to fasteners has been evaluated using laboratory test procedures, including AWPA Standard E12-94. The standard method was modified in order to allow detailed study of commercial metal fasteners in terms of sample types, installation configuration and exposure conditions. Parallel field tests were also performed. The experimental results generated from these tests su...
L Jin, A F Preston
Copper leaching from Kemwood ACQ and Embalit CBC treated wood products
2000 - IRG/WP 00-50150
TNO has performed a study on the leaching of copper from Kemwood ACQ and Embalit CBC treated wood products, further referred to as ACQ and CBC. The sawn dry wood has been impregnated using an industrial vacuum-pressure process with ACQ (with or without Ultrawood 4) or with CBC, under supervision of Flexchemie B.V. After treatment samples have been transported and subjected to leaching tests at TNO...
P Esser, W L D Suitela, H Trompetter
Evaluating the natural durability of native and tropical wood species against Reticulitermes flavip
2004 - IRG/WP 04-10539
Environmental pressures to eliminate arsenate from wood preservatives has resulted in voluntary removal of CCA for residential applications in the United States. A new generation of copper organic preservatives has been formulated to replace CCA for decking and in-ground applications but there is no guarantee that these preservatives represent a permanent solution to all related problems. There...
R A Arango, F Green III, K Hintz, R B Miller
Lifetime of impels in poles maintenance cycles for utility poles
2001 - IRG/WP 01-30258
In 1992-98 15.000-20.000 utility poles in Denmark received remedial treatment against decay with fused Boron-rods (IMPEL®). Economically simple, the Impel-rods are placed with the PillarTreat Method as concentrated depots in the ground-line. From there it is distributed by diffusion through the natural moisture in the wood, which ensures that it reaches moist wood in that parts of the pole where ...
A Peylo, C G Bechgaard
A suggestion for the improvement of the chemical protection of wooden poles
1987 - IRG/WP 3445
Insufficient drying of white poles in Sweden causes inadequate penetration of the impregnation compounds, CCA salts and creosote, in a varying proportion of the treated poles, and with pretreatment decay present, sooner or later, internal fungal attack in the ground-line zone of the standing poles is the result. The application of a diffusing fungicide in the ground-line zone in connection with th...
H Friis-Hansen