A wood preservative for the future: Copper dimethyldithiocarbamate
1994 - IRG/WP 94-30045
The development of a new wood preservative, copper dimethyl-dithiocarbamate (CDDC) is reviewed in this paper. CDDC is formed in situ by dual pressure treatments. Laboratory and field efficacy trials, physical and chemical properties of the preservative solutions and treated wood, and plant handling characteristics of the system are examined....
D K Stokes, M H Freeman, T L Woods, R D Arsenault
Soil-bed studies (Part 3): A cause of failure of multisalt preservatives following soil-bed exposure
1983 - IRG/WP 3261
P Vinden, J F Levy, D J Dickinson
Assessment of contamination of soil and water at a CCA treatment plant: A demonstration project
1996 - IRG/WP 96-50067
Soil, sludge, dust and water samples were collected at a copper/chromium/arsenic wood preservation plant. Contamination of soil, sludge, dust and surface water with copper, chromium and arsenic was detected. Levels of contamination were sufficiently high to require remediation. Contamination originated from preservative solution dripping from recently treated wood. Migration of contaminants was vi...
P N Durrant, D C R Sinclair, G M Smith
The effective control of moulds on freshly impregnated wood
2004 - IRG/WP 04-30352
Beside natural timber it is known, that moulds can also groth at the surface of impregnated wood. This material shows “defects” like resistant dark spots or color changes and causes complaints. During the last years, the problem by moulds seems to increase.
Laboratory studies were carried out to show the effect of impregnations against moulds. Wood samples (Pinus sylvestris L.) were impregn...
G Cofta, K Lutomski, P Jüngel
Oxalic acid production of fifteen brown-rot fungi in copper citrate- treated southern yellow pine
2001 - IRG/WP 01-10388
Non-arsenical copper-based wood preservatives have grown in number since the 1980's as a response to environmental concerns posed by arsenicals. Interest in copper tolerant decay fungi has increased accordingly. Oxalic acid (OA) production by brown-rot fungi has been proposed as one mechanism of copper tolerance. Fifteen brown-rot fungi representing the genera Postia, Wolfiporia, Serpula,...
F Green III, C A Clausen
Minutes of the meetings of WG II
1977 - IRG/WP 295
IRG Secretariat
Abstracts of some papers promised for IRG 22, Part II
1991 - IRG/WP 5370
IRG Secretariat
Examen chimique du traitement de poteaux effectué à St-Michel s/Meurthe
1974 - IRG/WP 337
J Guillemain-Thévenot, C Jacquiot
Rapid leaching test
1991 - IRG/WP 2367
An accelerated test which is suitable for measuring the extent of metal fixation in both chromium and non chromium containing preservatives is described....
J A Cornfield, M Bacon, A Lyman, C Waldie, M R Gayles
Performance of chromated copper arsenate-treated aspen fence posts installed in Forintek's Eastern test plot from 1951 to 1963
1984 - IRG/WP 3272
Aspen poplar fence posts were pressure treated by the full cell process using three formulations of copper chrome arsenate wood preservative. A total of one hundred and fifty nine of the posts were installed in service in Forintek's Chalk River post plot from 1951 to 1962. During the 1982 general inspection of the post plot all 159 posts were still in service. A groundline inspection was ...
C D Ralph
Literature survey on the permanence and distribution of salt-type wood preservatives
1969 - IRG/WP III 1B
The objective of this survey is generally to review some of the more important published work dealing with the distribution and permanence of salt-type waterborne wood preservatives in treated timber. The survey is limited to the major chrome-containing formulations and the classification system proposed by Becker (1964) has been adopted throughout.
CK - chromium, copper (copper, chrome); CKA - c...
Anonymous
Migration of Metals from Douglas-fir Lumber Treated with ACZA or Pentachlorophenol Using Best Management Practices: Preliminary Tests
2005 - IRG/WP 05-50224-4
The potential for migration of preservative components from ammoniacal copper zinc arsenate (ACZA) and pentachlorophenol treated Douglas-fir lumber in non-soil contact exposure was assessed in a simulated rainfall device. Metal levels from ACZA treated wood were elevated for the first 30 minutes of rainfall and then declined sharply. Repeated cycles of rainfall led to declines in initial metal l...
J J Morrell, Hua Chen, J Simonsen
A study of salt imbalances observed in recycled copper/chrome/arsenic preservative solutions in commercial practice
1987 - IRG/WP 3461
The study reported monitored tank solutions, sludge and other by-products using a standard CCA solution, when recycled. This recycling of the CCA solution is quite usual in between any commercial treatment schedules. Salt imbalances were observed and the possible reasons for such phenomena were studied. The paper discusses the procedure followed, the method of sampling the liquid after the charge ...
V R Sonti, S Sonti, B Chatterjee
Agenda WG II
1975 - IRG/WP 245
IRG Secretariat
IRG Working Group II. Co-operative leaching test (letter to collaborators)
1974 - IRG/WP 239
J W W Morgan
Minutes of the Meetings of WG II 1973
1973 - IRG/WP 226
IRG Secretariat
Minutes of the meetings of WG II
1985 - IRG/WP 2246
IRG Secretariat
Minutes of the Meeting of WG II 1970
1970 - IRG/WP 26
IRG Secretariat
Copper binding capacity of modified wood flour
1992 - IRG/WP 92-3709
Wood flour was modified by reaction with oxidising agents and CCA preservative. The copper chromium and arsenic were removed from the CCA treated wood flour by an acid leaching procedure. The modified wood flours were allowed to react with copper acetate solution and the level of copper fixation achieved was determined. The modified wood flours had greater affinity for copper ions present in solut...
N C Milowych, W B Banks, J A Cornfield
Minutes of the meetings of WG II
1987 - IRG/WP 2296
IRG Secretariat
Use of the Pilodyn to assess deterioration of treated aspen waferboard after 30 months of outdoor exposure
1986 - IRG/WP 2254
Samples of preservative treated aspen waferboard exposed outdoors for 30 mo. were compared using pin penetrations of the 6 Joule Pilodyn. These results correlated well with rankings of treatment performance based on more laborious standard mechanical tests, and demonstrate the potential for use of the Pilodyn as a tool to evaluate wood composites in test exposures with minimal destruction....
E L Schmidt, M G Dietz
Treatability of Siberian larch and spruce with chromated copper arsenate
1996 - IRG/WP 96-40060
Heartwood of Siberian larch (Larix gmelini) and spruce (Picea jezoensis) was pressure treated with chromated copper arsenate (CCA) Type B using a full cell process. Larch heartwood was somewhat difficult to treat than the spruce, although both species did not meet a minimum requirements of penetration and retention specified by the American Wood Preservers' Association (AWPA) for difficul...
Gyu-Hyeok Kim, Woo-Gue Jee, Jae-Jin Kim
Fungi associated with groundline soft rot decay in copper/chrome/arsenic treated heartwood utility poles of Malaysian hardwoods
1992 - IRG/WP 92-1567
Copper-chrome-arsenic treated heartwood from Malaysian hardwood utility poles in service for 8-23 y at two localities in the wet tropical Peninsula Malaysia were surveyed for soft rot in the ground-contact region. Soft rot decay was detected in all the poles. Isolation studies indicated the ability of a variety of microfungi and basidiomycetes to colonize treated heartwood. Most isolates exhibited...
A H H Wong, R B Pearce, S C Watkinson
Water-borne preservative marine trials in Western Canada
1981 - IRG/WP 470
Red pine boards treated with chromated copper arsenate, ammoniacal copper arsenate, copper zinc arsenic additive, a modified ammoniacal copper arsenate, and zinc arsenic additive, have been installed in a marine field test at West Vancouver, British Columbia. After two and a quarter years exposure, all the test samples are in excellent condition with the exception of those treated with the zinc ar...
J N R Ruddick
Recycling of impregnated timber: Part 2: Combustion trial
1999 - IRG/WP 99-50132
Totally 270 m3 (61,3 t) of CCA impregnated wood was chipped and incinerated at the combustion plant of Jalasjärvi. After the normal gas cleaning venture scrubbers were tested. After the trial a metal balance was calculated. Ash was treated at the copper smelter of Outokumpu Harjavalta Metals Oy. Condensate waters were transfered to the Outokumpu's CCA production plant and utilized by the...
L Lindroos