Your search resulted in 178 documents. Displaying 25 entries per page.
Changes of copper and chromium content after leaching in wood impregnated with the CCB and CB preservatives
2000 - IRG/WP 00-50147
The objective of the study was impregnated with CCB and CB preservatives pine wood of moisture content varying from 12% to 55% subjected to leaching. Losses of copper and chromium were determined for individual layers of wood up to 3 cm from the girth. The results were compared to the total amount of metals determined in water extracts. The degree of leaching of metal ions from wood of 55% moistur...
B Mazela
Leaching tests on CCA-treated wood using inorganic salt solutions
1984 - IRG/WP 3310
Pinus radiata sapwood treated to approximately 10 kg/m³ with Tanalith NCA or Tanalith C-type CCA preservatives was ground to a fine powder and samples were then leached with solutions of calcium chloride, calcium nitrate, magnesium nitrate, or a mixture of potassium di-hydrogen orthophosphate and di-potassium hydrogen orthophosphate, at 0.03M-1.00M solution concentrations. Leached wood samples we...
D V Plackett
Fixation of chromated wood preservatives through technical drying
1990 - IRG/WP 3623
Twin samples of sawn timber of Pinus sylvestris and Picea sp. were treated with copper-chromate-containing wood preservatives and subsequently kiln resp. air dried. After drying, the distribution of preservative and rate of fixation were determined. Drying of freshly treated wood in a condenser type kiln at temperatures of 60°C and 80°C and in a vacuum type kiln at 55°C with a pressure of about...
R-D Peek, H Klipp
Wood preservation in Uruguay
1987 - IRG/WP 3404
The purpose of this paper is a brief description of the current status of wood treatment in Uruguay. The forest resources of the country are summarized, the environment, their economic importance and future potential. The present wood treating facilities are described, together with the chemicals used and the standards generally accepted. Wood treated products used in the Uruguayan market are cite...
G Baillod
The influence of UV and IR radiation on leaching of copper and chromium from preservative-treated pine and spruce
1992 - IRG/WP 92-3687
The influence of artifical UV- and IR-radiation on the leaching of copper and chromium components of a CCB-preservative from freshly treated pine and spruce was evaluated. On small pinewood samples it could be shown, that the leaching of copper and chromium can considerabely be reduced by UV-radiation. A Philips HPA lamp type reduced the leaching most effective. IR-radiation lead to higher leachin...
H Militz
A comparison of shower test results from CCF, CCZF, CCB and Cu-quat treated timber
1995 - IRG/WP 95-50054
The shower test quantifies the amount of specific preservative components which leach from treated timber under simulated open storage conditions. The test method measures leaching from both organic and inorganic salt treated timber. Shower tests of CCF, CCZF, CCB and Cu-quat treated timber which have been performed over the last 5 years by TNO are reviewed and compared. Leached components are qua...
M J Boonstra, A J Pendlebury, P Esser
The role of chromium in wood preservatives - The situation and new results concerning biological efficacy
2006 - IRG/WP 06-30397
A heavy discussion about the status of chromium-containing compounds in wood preservatives has ensued in the European Union since the Biocidal Product Directive 98/8/EG has come into force.The origin of this discussion is the fact that according to the Biocidal Product Directive chromium trioxide and sodium dichromate have been identified as active ingredients and therefore the placement of wood p...
P Jüngel, H Härtner, E Melcher
CCB Preservative treatment of split muli (Melocanna baccifera ) bamboo by soaking process
2006 - IRG/WP 06-40336
This study was carried out in order to investigate the retention of chemicals inside the split muli ( Melocanna baccifera ) bamboo after preservative treatment by soaking process. Treatment with 10% aqueous solution of CCB (copper-chrome-boron) was applied in split bamboo of two sizes (1/4 part and 1/8 part) at three different moisture contents and five time periods (24, 48, 72, 96, 120 hours). It...
K Akhter, M H Chowdhury
Non-pressure preservation technique of five less durable timber species – Kadam (Anthocephalus cadamba), Shimul (Bombax ceiba), Pithalu (Trewia nudiflora), Am (Mangifera indica) and Boroi (Ziziphus jujube) of Bangladesh
2006 - IRG/WP 06-40322
Wood is a versatile renewable resource, which has been extensively used as a reliable construction material as well in furniture ever since the beginning of civilization.
The Major disadvantage of wood is its susceptibility to biodeterioration by fungi, insects and bacteria. In tropical countries like Bangladesh, fungi is the most significant of these biodeterioration agents. Kadam (Anthocephalus...
G N M Ilias, A H Kabir, F Begum, M F Alam
Comparative study between dipping and boucherie method of bamboo preservation
2006 - IRG/WP 06-40324
A comparative study has been carried out between dipping and boucherie method for three major bamboo species namely borak (Bambusa balcooa Roxb.), talla (Bambusa tulda Roxb.) and jawa (Bambusa salarkhanii Alam) with CCB (Chromated-copper-boron). Preservative treatment has been carried out with five different concentrations of preservative (2%, 3%, 4%, 5% and 6%) and four different durations of dip...
A S M A Huda, S M Mithue, M N Islam, M O Hannan
Antifungal activity of plant derived extracts against G. trabeum
2007 - IRG/WP 07-30433
While synthetic chemicals have provided excellent protection to woods used in adverse environments, the general public remains interested in naturally derived wood protectants. There are diverse arrays of possible candidates, but many of these compounds are not readily water soluble and efforts to render them soluble often reduce biological activity. In this report, we describe efforts to enhance ...
M Maoz, I Weitz, M Blumenfeld, C Freitag, J J Morrell
Synthesis of boric acid ammonium oleate salt for wood preservation: Leachability and termite resistance test
2007 - IRG/WP 07-30435
A new chemical compound coupling boric acid and oleic acid through a joint of ammonium salt has been produced and its synthesis followed and validated by Fourier Transformed Infra Red (FTIR). This compound named ammonium borate oleate (BAO) combining biocidal properties of boron and water repellence of fatty acids has then been studied as a wood preservative.
Synthesis of BAO involved different...
F Lyon, A Pizzi, Y Imamura, M F Thevenon, S N Kartal, J Gril
Tropical In-Ground Durability of CCB-treated Keruing and other Structural Sarawak Timbers after 8 – 10 Years Exposure
2007 - IRG/WP 07-30439
The heartwood of 12 mainly low-durability native timber species of Sarawak [4 Dipterocarpus (Keruing) species, Anisoptera grossivenia (Mersawa kunyit), Canarium apertum (Seladah), Dacryodes incurvata (Seladah laut), Dryobalanops oblongifolia (Kapur kelansau), Mesua macrantha (Mergasing), Podocarpus micropedunculatus (Kayu cina), Shorea compressa (Engkabang langgai), and Pterospermum javanicum (Ba...
A H H Wong, Ling Wang Choon
Effects of CCB on wood strength of Eastern spruce (Picea orientalis L.)
2008 - IRG/WP 08-40416
The effects of CCB (chromate copper boron) on the static bending properties of Eastern spruce (Picea orientalis L.) based on MOE (modulus of elasticity) and MOR (modulus of rupture) were evaluated after full-cell vacuum/pressure treatment using a 3.0 % concentration followed by kiln-drying at 15 and 30 % moisture contents with heating the preservative at 30 and 40 ºC. The results showed that MOE ...
I Usta, M Hale
Utilidad práctica de mini estacas en ensayos de campo
2009 - IRG/WP 08-20395
For testing chemicals for the wood against degradation agents of biotic, known as preservatives, both testing in the laboratory and in the fields are used. Field trials (Cemetery stakes) are often accepted as more "real" whose frequency of observation is set to more or less a year in temperate climates and six months or less in tropical situations, taking into accounts the aggressiveness of the so...
O Encinas, J V Puentes, N K Sarmiento, N Mora
Prolongación de la vida util de la madera de Pino Caribe de plantaciónes con sales CCB
2008 - IRG/WP 08-30482
Three concentrations of CCB were evaluated for their efficacy to protect Caribbean pine against fungal attack. Standardized laboratory tests (EN 113) were used to assess CCB effectiveness against a white-rot fungus (Trametes versicolor), and a brown-rot fungus Gloeophyllum trabeum. After 12 weeks, treated cubes of Caribbean pine exposed to the brown-rot fungus had between 2-8% weight losses while ...
A P Sanabria Sanabria, R Arévalo
Effectiveness of MOQ® OX 50 (CCB-Oxide) wood preservative – Part 2: Field tests
2008 - IRG/WP 08-30483
MOQ® OX 50 is a chromated copper borate preservative known around the world as CCB. In Brazil, this product is the only CCB-oxide type preservative with fungicide and insecticide properties registered at the Brazilian Institute for the Environment and Renewable Resources (IBAMA) that complies with the requirements of the Brazilian and European markets for preserved wood. For over five decades, s...
A Gandolfi Jr, C Salvela, D R Macedo, J M Vidal
Effects of concentration and temperature of CCA and CCB on wood strength of Turkish fir (Abies bornmulleriana Mattf.)
2009 - IRG/WP 09-40450
The purpose of this study was to present evidence for the effects of concentration and temperature of solutions of water-borne preservatives (chromated copper arsenate, CCA and chromated copper boron, CCB) on the static bending properties (modulus of elasticity, MOE and modulus of rupture, MOR) of Turkish fir (Abies bornmulleriana Mattf.). Wood samples were mechanically tested after a mild full ce...
I Usta, M Hale
Utilidad práctica de mini estacas en ensayos de campo
2008 - IRG/WP 08-20395
For testing chemicals for the wood against degradation agents of biotic, known as preservatives, both testing in the laboratory and in the fields are used. Field trials (Cemetery stakes) are often accepted as more "real" whose frequency of observation is set to more or less a year in temperate climates and six months or less in tropical situations, taking into accounts the aggressiveness of the so...
O Encinas, J V Puentes, N K Sarmiento, N Mora
Liquefaction - a functional way to manage CCB containing post-consumed wood?
2012 - IRG/WP 12-50288
The need for increased use of renewable resources put quite some attention to liquefaction of biomass, including wood. Several possible applications of liquefied wood as an alternative to petroleum based derivatives have been considered in recent years. In this paper, possibilities of wood liquefaction to manage post-consumed CCB (copper, chromium, boron) containing wood are considered, with a foc...
M Petrič, F Budija, D Hrastnik, M Humar, B Lesar
Effectiveness of CCA-C and CCB preservatives after a 30 years stake test
2012 - IRG/WP 12-30606
The objective of this experiment was to assess the durability of four pine species treated with waterborne preservatives. In order to determinate this, a stake field test, following the IUFRO (International Union of Forestry Research Organizations) recommendations, was installed at Experimental Station of Luiz Antonio (21º 32’ S and 47º 42’ W), State of São Paulo, Brazil.
Species under t...
I PJankowsky, E S Lepage, C Salvela, J M Vidal, S Takeshita
Interaction between Aspergillus niger fungus and other filamentous fungi on salt-agar medium and their growth on natural wood and wood treated with fungicide
2015 - IRG/WP 15-20569
Aspergillus niger (An) is very often used alone or in mixture with other filamentous fungi of the genus in testing biocides in disinfection procedures, safety, hygiene, medical fields as well as for testing resistance of wood and wood-based materials to moulds. Softwood species as well as hardwood are overgrown with An fungus very easily, causing drop of mainly the aesthetic value of wood product....
A Fojutowski, A Kropacz, A Koziróg
Above ground field testing: results of experiments in Brazil after one year
2015 - IRG/WP 15-30660
After the development of new products they need to be field-tested to assess their efficacy under diverse conditions of climate, comparing them with a preservative with proven efficacy. In some testing sites, decay occurs very slowly. The solution would be to bring these tests to locations that are conducive to biodeterioration, like tropical climates. Tropical sites provide higher temperature and...
M F Natale, J M Vidal
Properties of Wood Plastic Composites Made of Recycled HDPE and Remediated Wood Flour from CCA/CCB Treated Wood Removed from Service
2016 - IRG/WP 16-40747
Chromated copper arsenate (CCA) and copper, chromium and boron (CCB) have been widely used in pressure treated wood as a heavy duty preservative to protect wood against insects and fungi for more than 60 years. Although many attempts have been done to solve the problems related to out-service treated wood, the problem still remains. Only a few studies were done to utilize the out-of service treate...
E D Gezer, S Akbaş, M Tufan, A Temiz
Evaluation of coating applied in treated wood: experiences in Brazil
2017 - IRG/WP 17-40814
Weathering assays study the coating degradation caused by its exposure to the action of ultraviolet radiation, winds, heat and humidity. The use of test specimens in different arrangements and exposure angles is intended to reproduce various conditions in which a product can be used. The purpose of this paper is to present the efficacy of an oil-borne varnish applied on treated wood exposed to wea...
M F Natale, J M Vidal