Your search resulted in 915 documents. Displaying 25 entries per page.
Volumes and weights of different CCA-C treated wood poles, anchor logs and crossarms of REB at air dry condition
1996 - IRG/WP 96-40073
Researches revealed the unit volumes and weights at air-dry condition (12% MC) of different poles, anchor logs and crossarms species of REB from this world. The softwood products are lighter than hardwood products. Inversely the unit volumes of softwood poles are higher than those of hardwood poles. Red pine (Pinus resinosa), radiata pine (Pinus radiata), blue pine (Pinus wallichiana), fir (Abies ...
A K Lahiry
Leaching of CCA components from treated wood under acidic conditions
1993 - IRG/WP 93-50004
The leaching of CCA components from treated wood under acidic conditions were investigated. Western hemlock treated with three types of CCA and two levels of target retention was subjected to leaching at four different levels of pH. After leaching tests, leached samples were subjected to laboratory decay and soft rot tests. The amount of CCA components leached was dependent on acidity of leaching ...
Jae-Jin Kim, Gyu-Hyeok Kim
Artificial drying of impregnated wood
1987 - IRG/WP 3448
Sawn timber (Pinus Sylvestris) of dimension 50x150 mm was impregnated with CCA by a full-cell process. The timber was then dried in a conventional kiln or a special vacuum kiln where the timber was dried by circulating superheated steam. Drying time was 16 days and 2 days respectively. The aim of the investigation was to compare the physical appearence of the wood after drying by the two methods w...
M-L Edlund
The course of fixation of Cu-Cr-As wood preservatives
1972 - IRG/WP 307
Copper-chrome-arsenic (CCA) preservatives in contact with wood result in an instant extensive increase of pH, because of ion-exchange and adsorption reactions with the wood. During precipitation of the active elements the pH continuously increases but reaches a maximum, when all chrome is consumed. Some of the early reaction products are unstable and slowly convert via dissolution into stable comp...
S-E Dahlgren
Effects of artificial UV weathering and soft rot decay on heat treated wood
2005 - IRG/WP 05-40302
Oil and inert gas oven heat treated pine wood strips 100 µm thick were mildly heat treated (200°C, 30 mins linseed oil, 120 mins oven). Following treatment, specimens were exposed to UV weathering (300 hours) and decay by the soft rot fungus, Chaetomium globosum. The effects of each treatment were assessed by zero span tensile testing, microscopy and by FTIR.
Tensile testing of heat treated s...
M D C Hale, S C Ghosh, M J Spear
Relative performances of DNBP and CCA wood preservatives in accelerated decay tests
1988 - IRG/WP 3496
The effectiveness of 2-sec-butyl-4,6-dinitrophenol (DNBP) was compared with that of CCA. Test blocks of Pinus patula and Eucalyptus grandis were impregnated to precisely known retentions of approximately 3, 6, and 10 kg/m³ CCA and solvent-borne DNBP respectively. They were then challenged in decay tests comprising soil burial and exposure to monocultures of Chaetomium globosum, Coriolus versicolo...
W H Schnippenkoetter, L D Abraham, A A W Baecker
Chemical analyses of IRG/COIPM INTERNATIONAL MARINE TEST (to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water) samples
1987 - IRG/WP 4114
Chemical analysis of CCA and CCB treated timber was carried out after exposure at tropical and temperate marine sites. Results indicated that losses of all elements had occurred. In particular, losses of boron were severe. Arsenic and copper were also lost. The chromium components in both formulations was the most dominant metal remaining. The results suggest that chromium modification was importa...
L E Leightley
Polyflavonoid tannins - From a cause of CCA soft-rot failure to the "missing link" between lignin and microdistribution theories
1986 - IRG/WP 3359
Polyflavonoid tannins are proven to be fast-reacting with CCA solutions and hence, to be strong competitors of the structural wood constituents for fixation of CCA preservatives. The consequence of this effect is that even relatively small amounts of tannin cause severe undertreatment of the structural wood constituents which in turn badly affects the long term durability of CCA-treated timber. Th...
A Pizzi, W E Conradie, M Bariska
The performance of water repellants on radiata pine exposed to the weather
1989 - IRG/WP 3553
The effectiveness and resistance to weathering of four water repellent treatments, a commercial timber stain, and an oil-based clear finish, was assessed using 20x20x6 mm³ samples of untreated, copper-chrome-arsenic (CCA)-treated, and tributyltin oxide (TBTO)-treated radiata pine exposed to the weather over a four month period. The water repellency of each preservative/water repellent combination...
D V Plackett, F M Cameron
Chapter 6 - Preservatives of bamboo
2007 - IRG/WP 07-10635-06
Almost all currently available oil-borne, water-borne and
compound types of preservatives suitable for the
preservation of bamboo or wood have been described along
with their classifications, applications, formulations, merits
and demerits, history of invention or discovery and
development. The preservatives suitable for wood are also
considered suitable for bamboo....
A K Lahiry
Chapter 9 - Preservation of borak bamboo
2007 - IRG/WP 07-10635-09
Adequate penetration and retention of CCA and CCB have been
obtained in pre-dried Borak bamboo (Bambusa balcooa Roxb. See
Fig. below), abundantly grown in Bangladesh, with full-cell pressure
process. The treated bamboo can be used as building materials; the
sufficient treatability ensured its long-term best utilization at ground
contact and indoors. This will keep the environmental and socioe...
A K Lahiry
Comparative environmental impact analysis of telecommunication utility poles: Treated wood and fibreglass
1999 - IRG/WP 99-50136
This study is aimed at providing the information necessary to assess the main environmental implications of different materials utilised in construction of utility poles. The study was performed on fibreglass and CCA treated poles timber. The work has been carried out by identifying and quantifying energy and materials used and wasted released during the entire life of the pole. The interactions w...
A Cugliandolo, M Onofrio, A Quaglino
Soft rot decay of Eucalyptus maculata Hook. in different soils from Queensland, Australia
1980 - IRG/WP 1113
In the present work, different Queensland soils were chosen and their gross effects on the decay of treated and untreated Eucalyptus maculata examined. The soils were also amended with various levels of phosphate to study the response of the wood decay mycota to an increasing supply of this nutrient. Phosphate amendment was chosen because of the wide-scale use of superphosphate on Queensland soils...
L E Leightley, I W Russell
Chromium on the surface of CCA-treated wood
1978 - IRG/WP 386
Chromium in solutions of CCA preservatives is predominantly in the hexavalent state (Cr VI). It is well known that Cr VI is associated with dermatitis and skin ulceration in workers handling chromium containing products and processes. When reduced to the trivalent state, however, chromium is considerably safer. An essential part, therefore, of safety procedures in any chromium - using industry is ...
C R Coggins, P Hiscocks
Effect of incising depth and density on treatment of Douglas fir, hem fir and spruce-pine-fir lumber with CCA, ACZA or ACQ
1997 - IRG/WP 97-40093
Incising markedly improves both the depth and uniformity of preservative treatment of refractory wood species, but there are few studies directly comparing the effects of incising depth and density on penetration and retention of commonly used waterborne preservatives in wood species from the western United States. The effects of two incision densities (7300 and 8900 incisions/square meter) at two...
M Anderson, J J Morrell, J E Winandy
Retention and distribution of copper/chrome/arsenic (CCA) in pressurised sap-displaced UK grown spruce and pine
1986 - IRG/WP 3366
Increment cores were taken from UK grown Scots pine (Pinus sylvestris L.), Corsican pine (Pinus nigra var. maritima Ait), Sitka Spruce (Picea sitchensis (Bong) Carr), and Norway spruce (Picea abies (L) Karst) distribution poles treated by pressurised sap-displacement using a 1.8% copper, chrome, arsenic (CCA) solution. Each increment core was sectioned radially and the copper, chrome, and arsenic ...
P D Evans, G M Smith, B King
Comparisons of differences in electrical conductivity and corrosivity between CCA-oxide and CCA-salt treated wood
1981 - IRG/WP 3178
CCA preservatives have served well in many applications throughout the world. In developed areas it is the preservative in demand for clean dry paintable surfaces with long durability. In developing areas it is widely used for economic and logistical reasons. With the current emphasis on energy resources, the CCA preservatives are gaining greater acceptance as a substitute for hydrocarbon-related ...
J A Taylor
Examination of the Pilodyn as a non-destructive test method for detecting decay in CCA treated eucalypt poles
1982 - IRG/WP 2177
Below groundline condition of 274 CCA treated eucalypt poles comprising 13 different species was examined using 6 and 12 Joule Pilodyn units with 2 and 2.5 mm diameter pins. The data obtained was used to calculate regressions of density on pin penetration. A decrease in density was accompanied by an increase in pin penetration. The best correlation was found using the 6 Joule, 60 x 2.5 mm² diamet...
L E Leightley
The volatilization of arsenic on burning copper-chrome-arsenic (CCA) treated wood
1978 - IRG/WP 3111
Small scale burning experiments are described involving copper-chrome-arsenic treated wood. Approximately 20 per cent of the arsenic was volatilised when the wood was burned in air but 60 per cent when burned in an oxygen-enriched atmosphere, this increase is attributed to an increase in combustion temperature. Although a small increase in arsenic evolution was found with an increased concentratio...
A-J Dobbs, C Grant
Balance of arsenic and recycling
2002 - IRG/WP 02-50189
Instead of importing considerable quantities of arsenic to Europe, it would be sensible to utilize the arsenic recovered in the recycling process in the manufacture of CCA-wood, in the metallurgical industry as well as in other ways. When copper is also processed into a form easy to
utilize, it may be possible to utilize chrome as well. When these developments are implemented, it can be said th...
L Lindroos
Laboratory bioassay on the termiticidal efficacy of two ACQ formulations
1999 - IRG/WP 99-30199
The termiticidal efficacy of two ammoniacal copper quaternary ammonium formulations (ACQ) was evaluated in a laboratory bioassay using two species of subterranean termites, Mastotermes darwiniensis Froggatt and Coptotermes acinaciformis (Froggatt). Five retentions (1.0, 2.0, 4.0, 6.0 and 8.0 kg/m3 of active ingredient) of each ACQ formulation (MitrexACQ and ACQ97) were assessed in sapwood specimen...
J W Creffield, A F Preston, N Chew
Initial microbial colonisation of CCA-treated, creosote-treated and untreated Pinus sylvestris L. blocks in seawater
1996 - IRG/WP 96-10171
CCA-treated, creosote-treated and untreated Pinus sylvestris sample blocks were immersed in a seawater through-flow system for periods of between 1 and 265 hours. Samples were fixed immediately on removal and examined both qualitatively and quantitatively using the scanning electron microscope. This study of primary microbial colonisation showed differences between treatments in the diversity of m...
K Sturgess, A J Pitman
Bioassays for rapid assessment of heavy metal toxicity in seawater
1998 - IRG/WP 98-50112
In evaluating the effect of CCA leachate on the establishment of fouling communities on wood exposed in the sea, three organisms were assessed as biological indicators of heavy metal toxicity. These were two macroalgae, Fucus serratus and Undaria pinnatifida. and the motile protist thraustochytrid, Schizochytrium aggregatum. The choice of these organisms for the tests carried out was based on the ...
C J Brown, R L Fletcher, R A Eaton
Ultrastructure of degraded, CCA-treated Pinus radiata wood from a marine pile
1990 - IRG/WP 1461
During an inspection of marine piles, 12 years after installation, severe degradation was noted on one of them in the vicinity of a corroded eye-bolt. The wood was dark brown in colour and tended to crumble easily. Wood fragments were examined by light microscopy and scanning and transmission electron microscopy and were also analysed for carbohydrates and lignin. Light microscopy showed numerous ...
A P Singh, M E Hedley
An evaluation of CCA, CCB and CCP preservatives using a "sandwich test"
1991 - IRG/WP 2370
The last two years has seen some important changes in standards and preservative types used in Scandinavia, which have led to a wider choice for specifiers. In order to identify those treatments suitable for replacement or reinforcement of decayed constructional timbers, it was felt necessary to modify the standard EN 113 test. Impregnated blocks were sandwiched between two untreated blocks, previ...
A P Koch, L B Sheard