Five years field test results for CCA and ACQ preservatives fixed in different climates
1999 - IRG/WP 99-30208
During assessment of the ground contact stakes in the Norwegian test field, we have found that very often the first visual rot attack is in the zone of the stakes were the stakes have been in contact with each other during the fixation. These parts are usually light green, caused by the lack of light during fixation, compared to the rest of the stake surface, which has a darker colour. To investig...
F G Evans
Inorganic preservative levels in soil under treated wood decks after 8 years natural exposure in Borås, Sweden
2005 - IRG/WP 05-50233
Inorganic preservative components (Cu, Cr and As) were measured to a depth of 150 mm under deck structures made with Scots pine lumber treated with several different wood preservatives and installed in Borås Sweden 8 years ago. Higher contaminant levels were observed mainly under the drip lines and in the top 50 mm of soil. Under CCA treated decks, soil arsenic concentrations increased from ba...
P A Cooper, Y T Ung, M-L Edlund, J Jermer
Tropical In-Ground Durability of Structural Sarawak Hardwoods Impregnated to High Retention with CCA-salts, CCA-oxide and FCAP after 20 Years Exposure
2005 - IRG/WP 05-30384
Statistical analysis (ANOVA) was conducted on durability (termite and decay combined) rating data collected over 20 years exposure period of over 140 species of Sarawak timbers with altogether 30,000 stake specimens, at the Forest Department’s Sibu “graveyard” stake test sites from 1977. About 20 replicated stakes were pressure-treated to refusal with 10% g/ml concentration of up to 3 CCA-sa...
Wang Choon Ling, A H H Wong
Enhanced removal of CCA from treated wood by Bacillus licheniformis in continuous culture
1997 - IRG/WP 97-50083
A gram positive, spore-forming bacterium, which was isolated from a 20-year-old Forest Service test plot of CCA-treated 2 x 4's in Madison, WI., demonstrated the ability to release copper, chromium, and arsenic from CCA-treated wood in liquid culture. CCA-treated sawdust was exposed to this organism, which has been presumptively identified as Bacillus licheniformis. Analysis of the sawdus...
C A Clausen
Investigation of temperature effect on fixation of Celcure preservative (ACC) in Hornbeam (Carpinus betulus I)
2003 - IRG/WP 03-30304
In this research, the fixation speed of Celcure 2 % (ACC) preservative salt, under temperature of 30 ºC, 40 ºC and 50 ºC on intact wood specimens of hornbeam was investigated. For this purpose, blocks of wood with 2Í 2 Í2 cm dimensions of hornbeam were prepared and saturated with 2% ACC concentration by full-cell process. The specimens were put in three incubators at the above-mentioned temperatures. For measuring the percentage of fixation through time, the specimens were extracted by using hydraulic pressure equipment, under 70 Mpa pressure. The PH of extraction was measured with the method of Diphenyl Carbazid and by using spectrophotometer. This measurement was done continuously and the amount of 6-valence chromium concentration present in the extract was compared with the amount of chromium concentration in the primary solution and then the percentage of fixation was calculated.
The results showed that the decrease in 6-valence chromium is accompanied with increase of PH, this due to absorption of positive hydrogen ion by 6-valence chromium for reduction to 3-valence chromium and also ion –exchange of active components with wood during the primary phase of fixation. Also, the time necessary for reaching complete fixation in intact wood in the fixation temperature conditions of 30, 40, 50 ºC were 98, 52, 24 hours, respectively. In general, the results showed that temperature has effective role accelerating of fixation process.
R Imani, R E Majdar, A Karimi
Variation in biological performance of CCA caised by preservative application method
1996 - IRG/WP 96-40072
A series of laboratory studies to investigate the influence of treatment application method on CCA performance in Cosican pine has been completed. Biological decay tests, such as serial exposures, were used to induce decay in wood at preservative retentions of up to 10 kg/m³ CCA salts. Significant differences in performance of the preservative against either brown, white or soft rot decay fungi w...
P R Newman, R J Murphy
Laser incising of spruce lumber for improved preservative penetration
1991 - IRG/WP 3646
Red spruce heartwood specimens were incised using a range of laser beam power levels and pulse durations. The penetration of CCA through these holes into the wood was monitored after pressure treatment. In addition, green and dried spruce samples were incised using two patterns with incision densities of either 16.1 holes/in² or 21.3 holes/in². Following CCA pressure treatment the samples were t...
B Goodell, F A Kamke, Jing Liu
A new preservative - A double-edged sword
1990 - IRG/WP 3573
Increasing environmental pressures on the use of pesticides throughout the world will impact more on the use of all wood preservatives. In particular the use of traditional wood preservatives and methods of application are under close scrutiny. The industry is responding to the challenge of developing alternative products and systems but faces great problems due to the excellent performance and sa...
M Connell, J A Cornfield, G R Williams
A review of the implementation of results-based standards for preservative treated timber
1999 - IRG/WP 99-20156
European standards for the specification of preservative treated timber are written in terms of the results achieved in the commodity by the treatment process. This is described in terms of penetration and retention of preservative. Results from a study on the commercial application of this approach in the UK show the difficulties associated with applying the new European standards; particularly w...
E D Suttie, A S Hughes, R J Orsler
Soft rot test of copper/chrome/arsenic treated heartwood of three Malaysian timbers by the vermiculite-burial method. (+ correction document of 25 July 1990)
1990 - IRG/WP 2354
Heartwood of copper-chrome-arsenic (CCA) treated kempas (Koompassia malaccensis), tualang (Koompassia excelsa) and keruing (Dipterocarpus spec.) was found to be susceptible to soft rot in recent pole surveys. Standardized heartwood blocks were impregnated with 0 to 6.3% (w/v) CCA and challenged to decay for twelve weeks by a mixed inocula of Chaetomium globosum, Glenospora graphii, Humicula grisea...
R-D Peek, A H H Wong
Multiple-Phase Pressure (MPP) Process: One-stage CCA treatment and accelerated fixation process. 4. MPP compared with other processes for achieving acceptable treatment of radiata pine heartwood
1998 - IRG/WP 98-40115
Although radiata pine sapwood is very amenable to preservative treatment, it is often difficult to achieve the required standard for heartwood treatment.
A preliminary investigation showed that to achieve the NZ Timber Preservation Council minimum penetration requirements for radiata pine heartwood using the Multiple-Phase Pressure (MPP) Process, a hydraulic pressure of at least 1250 kPa for 20 m...
K Nasheri, J A Drysdale, G Durbin, M E Hedley
Differential retention and leaching of CCA (C) in sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii)
2005 - IRG/WP 05-30371
Retention and leaching of CCA(C) in small samples of sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii) were tested under laboratory conditions. Clear samples (100mm x 30mm x 40mm) were removed from the sapwood and heartwood of sampled defect-free and sound plantation trees of the two species. These were separately air-dried to 15% MC, end-seal...
R Venkatasamy
The examination of preservative-treated radiata pine using electron spin resonance spectroscopy
1987 - IRG/WP 3423
Electron spin resonance spectroscopy (ESR) may be used to characterise the molecular environment of chemical species containing unpaired electrons. These species include free radicals, bi-radicals, point defects in solids, localised crystal imperfections and many transition metal ions. ESR has previously been applied to the examination of wood weathering or wood pyrolysis and now FRI and Massey Un...
D V Plackett, E W Ainscough, A M Brodie
A technique for measuring preservative loss or redistribution during leaching
1983 - IRG/WP 2199
Radiata pine sapwood stakes were treated with benzalkonium chloride (AAC) or copper-chrome-arsenate (CCA). After fixation and drying the outer 2 mm and 2-4 mm layers were removed from one radial longitudinal face. The planed face was coated with a waterproof coating and AAC-treated stakes were leached for 6, 12 or 18 weeks; 12 weeks for the CCA-treated stakes. After airdrying three 2 mm layers (0-...
J A Drysdale
Performance of preservative-treated rubberwood (Hevea brasiliensis) in Goa and Kochi waters (west coast of India).
1997 - IRG/WP 97-20104
Performance of rubberwood (Hevea brasiliensis) against biodeterioration, when pressure-treated with Copper-Chrome-Arsenic (CCA) and Copper-Chrome-Boric (CCB) and exposed in Mandovi estuary (Goa) and in Kochi waters for a period of 32 months and 9 months respectively, has been discussed. The control panels were completely destroyed within a period of 4 to 6 months at both the localities. The resist...
L N Santhakumaran, M V Rao
Copper based wood preservative - A new approach using fixation with resin acids of rosin
2000 - IRG/WP 00-30249
Copper soaps with carboxylic acid groups of resin acids of rosin were shown to be potential long-term wood preservatives. The principle involved is the attachment of copper to the network formed by the inorganic part of the preservative (rosin) through the -COOH groups. The mechanisms of fixation have been studied, and it has been shown that this association could be obtained : (1) by forming the ...
C Roussel, J P Haluk, A Pizzi, M-F Thévenon
Performance of Copper-Chrome-Arsenic (CCA) and Copper-Chrome-Boric (CCB) treated panels of Bombax ceiba and Paraserianthus falcataria against bio-deterioration at Krishnapatnam harbour, east coast of India
2003 - IRG/WP 03-30310
Results of investigations on the durability of light weight timber species (Specific gravity below 0.4) i.e., Bombax ceiba and Paraserianthus falcataria in treated and untreated condition conducted at Krishnapatnam harbour (Lat 13o28’ to 13o59’ N; Long: 80o10’ to 80o16’E) along the east coast of India are reported in the paper. Exposure trails were conducted with panels (Size: 30 x 3.8 x...
B Tarakanadha, N R Raveendra Prasad, K S Rao
Effect of leaching temperature and water acidity on the loss of metal elements from CCA treated timber in aquatic applications. Part 1: Laboratory scale investigation
1995 - IRG/WP 95-50046
In order to investigate the applicability of current prestandard leaching test methods, a series of experiments has been performed on CCA impregnated wood dealing with the influence of pH, temperature and agitation of the surrounding water. The leaching method used in this first part of the investigation is the European prestandard drafted by CEN/TC38/WG11, a short term dynamic leaching test under...
G M F Van Eetvelde, R J Orsler, G E Holland, M Stevens
Less pollution due to technical approaches on accelerated steam fixation of chromated wood preservatives
1988 - IRG/WP 3487
Steaming of freshly treated wood at 100°C to 120°C initiates a spontaneous fixation of copper-chromate-containing wood preservatives. For the performance, a suitable anticorrosive equipment is necessary. Good results can be achieved using a separate steaming equipment which allows a rapid heating of the wood. While warming-up, in the wood some preservative solution extends and can be partly extr...
H Willeitner, R-D Peek
Influence of water soluble extractives on CCA fixation and leaching performance of red maple and red oak
1997 - IRG/WP 97-30133
We have observed several peculiarities in relation to CCA fixation in red maple and red oak woods such as high variability in fixation rates and leaching performance in maple and precipitate formation in solutions expressed from CCA treated red oak wood blocks at different stages of fixation. We have postulated that the extractives could be the factor of influence, as this has already been reporte...
T Stevanovic-Janezic, P A Cooper, Y T Ung
The use of low cost X-ray fluorescence instruments in the determination of copper chromium and arsenic in preservative treated wood
1987 - IRG/WP 2278
Internal quality control in timber treatment plants can be pursued by analysis of preservative treatment solutions and treated timber. Treaters must proceed with costly and lengthy analyses through analytical laboratories. An alternative approach for the timber treater, is to use low cost analysers (L.C.A.'s) based upon x-ray fluorescence. Detailed comparisons have been made between stand...
J Norton, L E Leightley
LCA examination of preservative treated timber products and alternatives; initial results
1995 - IRG/WP 95-50040-04
Co-operative development of an LCA methodology suitable for application to preservative treated products has been carried out, based on scoping assessments of two products, CCA treated fenceposts and creosote treated distribution poles. The general results of these scoping exercices are described, based on the CCA case study. These include the identification of critical stages in the life-cycle on...
W Hillier, R J Murphy, D J Dickinson, J N B Bell
Effects of pre-harvest girdling on selected properties of red pine, red maple and Eastern larch
1999 - IRG/WP 99-40137
Trees of three species - tamarack (Larix laricina), soft maple (Acer rubrum) and red pine (Pinus resinosa) - were girdled immediately below the crown,one to two years before felling. The wood from these trees was compared with wood taken from un-girdled control trees felled at the same. Sapwood and heartwood, from the controls, and from above and below the girdle of treated trees, were examined fo...
A Taylor, P A Cooper
CCA removal from treated wood by chemical, mechanical and microbial processing
1998 - IRG/WP 98-50101-26
Most preservative-treated wood produced and consumed in the U.S. is treated with toxic inorganic compounds containing copper, chromium, and arsenic. Because chromated copper arsenate (CCA) is fixed to the wood, treated wood has not been considered toxic or hazardous and is currently landfilled. Increasing public concern about environmental contamination from treated wood combined with increasing q...
C A Clausen, R L Smith
Relating CCA fixation to leaching of CCA components from treated products
1995 - IRG/WP 95-50045
The relationship between chromium fixation in CCA-C treated wood, as determined by CrVI analysis of solution expressed from treated wood and the leaching of Cu, Cr, As and CrVI in a simulated rain test are evaluated for dimension lumber (2"x6") and pole sections. Leachate concentrations after 2 hour exposure to a misting spray (about 300 mm cumulative rainfall) decrease rapidly with increased degr...
P A Cooper, R MacVicar, Y T Ung