The effect of wick action on the moisture distribution in heartwood and sapwood stakes of Pinus radiata D. Don.
1999 - IRG/WP 99-40139
The pattern of moisture distribution in stakes of Pinus radiata D. Don. subjected to "wick action" is investigated. There was incomplete saturation of the stakes even after 93 days of continual soaking. Maximum moisture absorption occurred at the base of the stake and at the air/water interface of the stake. Incomplete saturation of the stake was thought to be due to air embolism within the wood. ...
J Hann, P Vinden
An illustrated comment on the soft rot problem in Australia and Papua New Guinea
1977 - IRG/WP 296
A brief survey of soft rot is presented, with particular reference to attack of preservative treated hardwood transmission poles in Australia. Possible explanations of why the preservatives are failing to protect the poles are discussed, together with current efforts to produce control measures. Examples of soft rot in variously treated eucalypt or pine specimens are shown to illustrate the morpho...
H Greaves
Feasibility study for a dedicated pressure treated wood waste management system
2005 - IRG/WP 05-50224-22
For the creosote treated wood coming out of service, it has been estimated an amount of 200 000 t per year for the next twenty years, and 100 000 t per year afterwards. With a limited number of actors, mainly SNCF (as producer and as user), no importations, and available energy recovery options, it appears possible for setting a dedicated wood waste management system, if the SNCF agrees to.
For t...
C Cornillier, I Buda, E Heisel, G Labat
Corrosion of zinc-coated nails used with preservative-treated western red cedar shakes in service
1982 - IRG/WP 3197
The corrosion of metal fasteners used with certain wood species and with preservative-treated woods can be a serious problem. The chemical reactivity of western red cedar (Thuja plicata Donn) extractives to iron and copper is well documented and wood preservative treatments containing copper, chromium, and/or ammonium hydroxide can be expected to similarly attack some metals. This problem is compo...
R S Smith, E L Johnson, A J Cserjesi
A termite field test with diffusion treated lumber
1991 - IRG/WP 3648
Douglas fir lumber, diffusion treated with concentrated sodium octaborate solutions, was tested against Coptotermes formosanus in an above ground field test wherein the samples were not exposed to a direct leaching hazard during the test period. After 2.5 years exposure, the untreated control samples were almost completely destroyed while poorly treated controls pressure treated with chromated cop...
K J Archer, D A Fowlie, A F Preston, P J Walcheski
Removal of CCA from Spent CCA-Treated Wood
2002 - IRG/WP 02-50192
A novel method for the removal of CCA components from spent CCA-treated wood has been developed. The CCA-treated wood was first converted into liquid in the presence of polyethylene glycol and glycerin at mild temperatures (120 – 150 0C) by using sulfuric acid as catalyst. The resulting viscous liquefied wood was then resolved in acetone/water solvent. The hazardous components (i.e., Cr, As, and...
Lianzhen Lin, Chung-Yun Hse
Bioprocessing preservative-treated waste wood
2000 - IRG/WP 00-50145
Disposal of preservative-treated waste wood is a growing problem worldwide. Bioprocessing the treated wood offers one approach to waste management under certain conditions. One goal is to use wood decay fungi to reduce the volume of waste with an easily managed system in a cost-effective manner. Wood decay fungi were obtained from culture collections in the Mycology Center and Biodeterioration res...
B Illman, V W Yang, L Ferge
Moisture uptake and volumetric swelling as probable factors also affecting leaching in CCA-treated wood. A preliminary study of treated Eucalyptus saligna sapwood
2003 - IRG/WP 03-30318
IRG/WP 03-30318
A number of factors affecting leaching of CCA from treated wood have been variously investigated and discussed. However, the possible effects of moisture movement in treated timbers on leaching have not received attention yet. The present study examines and compares moisture uptake and volumetric swelling in CCA-treated and untreated sapwood of Eucalyptus saligna, and tries to establish a correl...
R Venkatasamy
Final proposals for a field experiment to determine the performance of preservative treated hardwoods with particular reference to soft rot
1976 - IRG/WP 367
A series of hardwood stakes have been prepared and treated in the UK from samples (mainly sapwood) supplied from participants around the world. The stakes include 4 reference species common to each site and, in most cases, at least 2 local species of importance. The treated stakes will be despatched to the co-operating scientists and installed under local conditions. It is hoped that with periodic...
D J Dickinson
Laboratory evaluation of borate formulations as wood preservatves to control the subterranean termite coptotermes acinaciformis (isoptera: Rhinotermitidae) in Australia
2001 - IRG/WP 01-30266
The termiticidal efficacy of Borocol (sodium octaborate tetrahydrate), boric acid, bore-ester-7 and tri- methyl borate was evaluated in laboratory bioassays against Coptotermes acinaciformis (Froggatt). Seasoned sapwood blocks of Pinus radiata D. Don, and Eucalyptus regnans (F. Muell) were impregnated with the various borate compounds. There were marked differences in mass loss and mortality rate ...
B M Ahmed, J R J French, P Vinden
Report on the burning of wood treated with wood preservatives containing copper, chromium and arsenic
1976 - IRG/WP 379
Mixtures of copper, chromium and arsenic salts are used extensively in the UK to preserve timber. This report is concerned with the fate of these metals when timber treated with these salts is burned. A large percentage of the arsenic present in the timber is shown to be volatilised during combustion and the potential environmental implications of this are assessed by comparison with the release o...
A J Dobbs, C Grant
Fixation and leaching of selected Malaysian tropical hardwood after treated with CCA
2001 - IRG/WP 01-40207
The objective of this study is to investigate the fixation and leaching properties of selected Malaysian tropical hardwood (sentang wood (sapwood and heartwood) and rubberwood) after being treated with copper chrome arsenate (CCA) type-C preservative. The samples were treated with retention level of 0.5%, 2.0% and 5.0%. The samples were leached and the leachate were analyzed by AAS and the amount ...
R Hashim, O Sulaiman, Tan Siew Ching, K Yamamoto
Leaching of Arsenic from Mulch Made from Recycled Construction and Demolition Wood
2005 - IRG/WP 05-50232
Mulch made from recycled construction and demolition (C&D) wood has been reported to contain chromated copper arsenate (CCA)-treated wood and potentially release arsenic in the leachate by rainfall. Such recycled wood mulch is commonly masked with iron-oxide colorant, which is known to combine with arsenic. The objective of this study was to evaluate the levels of arsenic leaching from C&...
T Shibata, H M Solo-Gabriele, T G Townsend, B Dubey
Field stake test assessment with the Pilodyn
1980 - IRG/WP 2136
The Pilodyn, which was originally developed to estimate the degree of soft rot in wooden poles, was thought to have potential for giving a quantitative measure of the extent or depth of decay in field test stakes. In the present work a 2-joule Pilodyn with 2.0-mm diameter pin was used in an attempt to limit depth of pin penetration (to 10-15 mm) without reducing scale sensitivity. The results show...
M E Hedley, R W Naish
Laboratory tests on light organic solvent preservatives for use in Australia. - Part 6: Soft rot resistance of three fully formulated preservatives on different timber substrates
2000 - IRG/WP 00-30245
The above-ground soft rot resistance of substrates treated with three fully formulated light organic solvent preservatives (Cuprivac Green WR, Impresol WR 205 and Vacsol) was studied using a modified vermiculite burial method. The substrates were sapwood of Pinus elliottii and P. radiata and heartwood of Eucalyptus regnans, Pseudotsuga menziesii, Shorea sp. (a lower and a higher density source) an...
G C Johnson, M A Tighe, J D Thornton
Influence of pre-swelling conditioning on swellometer results for CCA and water repellent additive treated wood
1997 - IRG/WP 97-20125
The pre-test moisture content and conditioning history of wafers cut from wood treated with CCA and an emulsion water repellent additive can dramatically influence swelling curves generated using a standard swellometer apparatus. The rate of water uptake and swelling increased significantly as wafers were dried to lower moisture contents prior to immersion swelling. The pre-swelling conditioning h...
A R Zahora
Performance of non-incised CCA-treated hem-fir decking
1993 - IRG/WP 93-40004
The question of what preservative penetration will provide an acceptable service life for treated wood in residential above-ground applications is topical in North American standards committees. Non-incised CCA-treated nominal 2 x 4 inch² hem-fir decking with penetrations close to the proposed CSA O80 2 decking standard of 80% over 5 mm, has remained without decay after 10 years exposure in south...
P I Morris, J N R Ruddick
Evaluation of the corrosivity of the treated wood - Laboratory vs field test methodologies
2000 - IRG/WP 00-20211
The corrosivity of treated wood to fasteners has been evaluated using laboratory test procedures, including AWPA Standard E12-94. The standard method was modified in order to allow detailed study of commercial metal fasteners in terms of sample types, installation configuration and exposure conditions. Parallel field tests were also performed. The experimental results generated from these tests su...
L Jin, A F Preston
An evaluation of chemical treatments for the protection of radiata pine logs from fungal degrade
1986 - IRG/WP 3377
Busan 30, Busan 1009, Mitrol PQ375. and sodium pentachlorophenoxide (NaPCP) plus have been evaluated as antisapstain treatments for the long-term protection of debarked radiata pine logs. After 3 months' winter-spring storage, treated debarked logs had less surface and internal sapstain than 'control' logs. After 6 months' storage all logs had internal sapstain ...
J A Drysdale, M E Hedley, J A Butcher
Service life of pressure treated deckings of spruce in direct contact with the ground
1988 - IRG/WP 3463
For decking outdoors in Sweden, pressure treated Scots pine (Pinus sylvestris L.) is used, on account of its treatability. The feasibility of using instead the refractory Norway spruce (Picea abies Karst.) is tested in a field trial. The spruce decks were treated together with pine decks with an ordinary Bethell process. As yet, after more than four years of exposure, neither in the battens nor in...
J B Boutelje, T Sebring
Effect of mobile fungicides on fungal pre-infection in radiata pine billets.
1999 - IRG/WP 99-30191
In New Zealand, fungal infection of logs begins directly after felling and whilst severe degrade can be prevented if antisapstain-treated within 24 hours, such short turn-around times of logs are not always practicable. However, conventional antisapstain formulations in use only provide an envelope of protection on the log surface but are unable to control pre-infections below the surface. The obj...
D R Eden, T Singh, B Kreber
The possible role of mobile CCA components in preventing spore germination in checked surfaces, in treated wood exposed above ground
2001 - IRG/WP 01-30263
Untreated check surfaces are often exposed in CCA-treated lumber of refractory species used above ground since, during weathering, some checks develop beyond the preservative penetrated zone. However, decay is seldom observed in these checks even after many years of exposure. It is hypothesized that minor amounts of mobile CCA preservative components redistribute during weathering into checks, and...
S Choi, J N R Ruddick, P I Morris
A suggestion for the improvement of the chemical protection of wooden poles
1987 - IRG/WP 3445
Insufficient drying of white poles in Sweden causes inadequate penetration of the impregnation compounds, CCA salts and creosote, in a varying proportion of the treated poles, and with pretreatment decay present, sooner or later, internal fungal attack in the ground-line zone of the standing poles is the result. The application of a diffusing fungicide in the ground-line zone in connection with th...
H Friis-Hansen
The influence of soil pH on leaching of CCA elements from pressure-treated Eucalyptus saligna sapwood: environmental implication
2003 - IRG/WP 03-50203
Evidence is accumulating as to poor distribution and fixation of CCA in tropical hardwoods, and there is therefore a necessity to investigate the permanency of CCA in tropical hardwoods. The relationship between soil pH and leaching of Cu, Cr and As from CCA pressure-treated sapwood of Kenyan-grown Eucalyptus saligna was tested under laboratory conditions. Small sapwood samples were pressure-tre...
R Venkatasamy, D N Okwara
Effects of surfactants and ultrasonic energy on the treatment of wood with chromated copper arsenate
1977 - IRG/WP 3108
Sugar pine stakes 1'' x 1" x 16" were treated by a hot-water bath followed by soaking in cold CCA solution for 10 to 30 minutes. A similar number of stakes were treated by a cold-cold bath. Half of the stakes were subjected to ultrasonic energy during the CCA bath. The mean absorption for stakes given the hot-cold bath was 18.52 pcf (297 kg/m³) and 4.64 pcf (74 kg/m³) for those...
C S Walters