Your search resulted in 806 documents. Displaying 25 entries per page.
Surface accumulation of copper on CCA-impregnated Pinus patula stakes during marine preservative trials in the southern hemisphere
1992 - IRG/WP 92-4181
Pinus patula stakes treated with CCA to target retentions of 30 kg/m³ salts were exposed to sea water in marine and estuarine ecosystems off the coast of Southern Africa for two years. Samples were then analysed for copper and arsenic. Analysis of samples from the marine ecosystem showed (IRG/WP/4167) that arsenic was longitudinally and transversely leached from the wood, whereas the copper was r...
G D Shelver, C D McQuaid, M Tarin, A A W Baecker
Preservative treatment of green timber by diffusion
1984 - IRG/WP 3291
The preservative treatment of green timber by diffusion is reviewed together with criteria which influence the economics of the process. New process options are described which should overcome some of the technical and economic disadvantages of double diffusion. These include the use of coagulating agents which increase the viscosity of the preservative solution and facilitate treatment by momenta...
P Vinden
Chemical treatment of ten Amazonian timber species of low natural durability
1991 - IRG/WP 3640
The objective of this work was to evaluate the performance of 10 amazonian wood species of low natural durability, to treatment with CCA preservative (2% concentration): it was concluded that all species studied are easily treated with this preservative. The sapwood showed high absorption and total penetration. The heartwood is relatively easy to preserve, exception to Parkia nitidae (Fava), Quale...
C S Neta, B F Vianez
Effect of test site, preservative and wood species on decay type Glenbervie pastoral and radiata pine forest sites
2000 - IRG/WP 00-30248
Pinus radiata stakes were treated with 0.8, 1.2, 1.8, 2.7 and 4.1 kg/m3 of CCA and Fagus sylvatica with 2.7, 4.1 and 6.1 kg/m3 of CCA. Both wood species were also treated with equivalent retentions of a copper plus triazole preservative (CT) (0.89, 1.3, 2 and 3 kg/m3 of copper for pine & 2.5 and 4 for beech) and chlorothalonil plus chlorpyriphos in oil (CC) (1.4, 2.1, 3.2 and 4.8 kg/m3 of chlo...
R N Wakeling
The effect of composition on the effectiveness and fixation of CCA and copper/chrome preservatives. Part 1: Effectiveness. Part 2: Selective absorption and fixation
1973 - IRG/WP 324
A preliminary study of a wide range of copper-chrome-arsenic formulations indicates that the most effective are in the region, CuSO4 · 5H2O - 35 to 45 per cent; K2Cr2O7 - 40 per cent and above; As2O5 · 2H2O - 25 to 15 per cent or less. Effectiveness appears to depend more on the copper content than the copper - arsenic. Observations on selective absorption and leaching suggest that the chromium ...
D N R Smith, A I Williams
The effect of chemical treatment on the moisture distribution of Pinus radiata D.Don subjected to wick action
1999 - IRG/WP 99-40135
Radiata pine sapwood stakes were treated with a range of chemicals, including an ammoniacal copper quaternary ammonium compound (ACQ), a copper-chrome and arsenic (CCA) solution and a CCA-oil treatment, potassium linoleate copper linoleate, a paraffin wax and a proprietary alkyd resin. The effect of these treatments on the extent of water absorption and moisture movement through the stakes was inv...
J Hann, P Vinden
Sphaeroma terebrans Bate: A note on distribution and preservative tolerance in Florida coastal waters
1987 - IRG/WP 4135
Treated test panels were installed in January 1984 in a Florida estuary where Sphaeroma terebrans had severely damaged pilings treated with copper chromate arsenate (CCA). Test treatments were CCA at three retentions, coal-tar creosote at three retentions, creosote with chlorpyrifos, dual treatment with CCA and creosote, and three types of chemical modification of the wood test panels. We describe...
B R Johnson, E D Estevez, S A Rice
Corrosion of fasteners in treated wood
1971 - IRG/WP 303
Surveying tests for determining the corrosion rates of some metals and alloys in wood untreated as well as treated have been made. It is shown that ordinary steel corrodes faster than other common fastener metals such as copper, brass, aluminium and stainless steel do. Zinc coatings, however, will prevent the steel corrosion effectively provided that the coatings are thick sufficiently. Catalytic ...
T Wallin
Non leachability of arsenic, copper and chromium from 15 years old CCA-C treated southern pine poles used in brackish water as jetty piles in Bangladesh
1998 - IRG/WP 98-50103
Revealed that chromated copper arsenate type C (CCA-C) treated southern pine poles used in Central Warehouse Jetty of REB, Khulna are stable and resistant to chemical and biological attack without loss of any component from outer 0-12.5 mm zone after 15y of use. Slightly reduced retention (4.44% less) was noted in above water location of piles (bottom end of tree) which would be due to continuous ...
A K Lahiry
Notes on a wood preservation industry in Medan, North Sumatera, Indonesia
1987 - IRG/WP 3405
This paper deals with a descriptive account on the development of a wood preservation industry in Medan, North Sumatera (Indonesia). The industry was established in 1974 when the State Owned Electicity Corporation decided to use wooden power poles for their distribution network in North Sumatera province. However, the use of wooden power poles was discontinued in 1981, so as the preservation indus...
N Supriana, A Murad
The performance of metal-chromium-arsenic formulations after 32 to 38 years' in-ground exposure in Australia
2000 - IRG/WP 00-30240
Two trials of metal-chromium-arsenic preservatives were exposed in-ground in Australia. In Trial 1, Pinus radiata stakes treated with Boliden K.33, Boliden S.25, Celcure A, Tanalith C and Tanalith CA were installed at Sydney and Narrandera in 1961/1962. In Trial 2, P. radiata and Eucalyptus regnans sapwood were treated with Celcure A, Celcure A21-N, Celcure A 21-O and Tanalith CA (new) and install...
G C Johnson, J D Thornton, J Beesley
Effect of water repellents on leaching of CCA from treated fence and deck units - An update
1997 - IRG/WP 97-50086
In an earlier study, it was shown that CCA leaching losses could be reduced over an accelerated leaching and short term natural weathering exposures by post treatment application of a commercial water repellent. In this report, the effects of this coating and two commercial CCA solution water repellent additives are evaluated after two years of natural weathering. Wood boards were pressure treated...
P A Cooper, Y T Ung, R M Vicar
Susceptibility of CCA treated North American hardwoods to Chaetomium globosum decay
1998 - IRG/WP 98-10278
Seven species of hardwood, Beech (Fagus grandifolia), Basswood (Tilia americana), Maple (Acer rubrum), Oak (Quercus rubra), Trembling Aspen (Populus tremuloides), White birch (Betula papyrifera) and Yellow poplar (Liriodendron tulipifera) were vacuum or pressure impregnated with CCA, at four retention levels. The CCA was allowed to fix in the wood at 35°C. Red pine (Pinus resinosa) was also inclu...
U Srinivasan, Y T Ung, P A Cooper
A methodology for the life-cycle assessment of treated timber products
1993 - IRG/WP 93-50001-01
Using case studies of CCA-treated motorway fenceposts and creosote-treated electricity transmission poles, the paper suggests an approach to evaluation of the overall environmental impact of treated timber products, utilising the emerging systems analysis method of life-cycle assessment (LCA). The development and application of LCA methodologies to date is reviewed and the key features identified....
S R Smith, R J Murphy, D J Dickinson
Performance of different treatments and finishes on wood out of ground contact. Preliminary results
1984 - IRG/WP 2221
Pinus and Eucalyptus L-joints treated with CCA, a water dispersable PCP and untreated ones were painted according to seven different finish's schedules and exposed at two sites in State of Sao Paulo. After ten months of exposure, it was possible to verify that preservative treatment improve the performance of both wood and finish. It was also possible to observe that wood substrate, prese...
S Milano
Preliminary PIXE micro-analysis of copper-chrome-arsenic preservative treated Malaysian hardwoods
1999 - IRG/WP 99-20169
The novel nuclear microscopy, essentially the Particle-induced X-ray Emission (PIXE) system, was applied for examining the macro-distribution and micro-analysis of copper-chrome-arsenic (CCA) preservative in Malaysian hardwoods Koompassia malaccensis, K. excelsa, Alstonia spp. and Dipterocarpus spp., and one temperate pinewood Pinus sylvestris, where the preservative retention differed between the...
A H H Wong, R B Pearce, G W Grime, F Watt
Factors affecting decay rates in a fungus cellar II
1986 - IRG/WP 2259
Tests were initiated to investigate the influence of various factors on the decay rate in a "Fungus Cellar". Birch and pine stakes treated with chromated copper arsenate and didecyldimethyl ammronium chloride, as well as untreated control stakes, were incubated in two soils in a Fungus Cellar test and installed at two field sites for comparative purposes. The visual rating vs actual stake weight l...
P A McKaig
Waterborne preservative treatability of tamarack (Larix laricina (Du Roi) K.Koch)
1998 - IRG/WP 98-40112
Eastern larch or tamarack (Larix laricina (Du Roi) K.Koch) lumber from New Brunswick, Canada was evaluated for preservative treatability with chromated copper arsenate (CCA-C) and ammoniacal copper arsenate (ACA). The fixation and leaching characteristics of CCA-C treated tamarack sapwood and heartwood were also evaluated. CCA-C penetration into both sapwood and heartwood was poor. ACA fully penet...
A Taylor, Y T Ung, P A Cooper
Performance of Paraserianthus falcataria treated with ACZA, ACQ, CC or CCA and exposed in Krishnapatnam harbour, India
2005 - IRG/WP 05-30382
Paraserianthus falcataria (=Albizia falcataria) treated to two retentions with ammoniacal copper zinc arsenate (ACZA), ammoniacal copper quaternary (ACQ), ammoniacal copper citrate (CC) and chromated copper arsenate (CCA) was assessed over 34 months in a tropical marine waters at Krishnapatnam harbour on the east coast of India. ACZA treatment showed comparatively better resistance than CCA, ACQ a...
B Tarakanadha, K S Rao, J J Morrell
Relative tolerance of CCA by larvae and adults of the common shipworm, Bankia gouldi
1992 - IRG/WP 92-4174
Southern pine sapwood "2 x 4´s" were created by bolting together four panels 13 mm thick by 89 mm wide by 457 mm long. The two outer laminates were untreated and the two inner laminates were each treated to different CCA retentions, ranging from 8.0 to 43.2 kg/m³. Test specimens were exposed from May to October in a tributary of the Chesapeake Bay. Larvae were unable to settle on and burrow into...
B R Johnson
Effect of climate, species, preservative concentration and water repellent on leaching from CCA-treated lumber exposed above ground
2001 - IRG/WP 01-50178
Few studies have examined leaching of chromated copper arsenate (CCA) from treated wood in above ground exposures due to the assumption that leaching is less severe compared to wood in continuous contact with soil or water. However, a significant portion of CCA treated wood is used for above ground applications, exposing considerable volumes of the preservative to precipitation and potential leach...
J L Taylor, P A Cooper
Kinetics and mechanism of fixation of Cu-Cr-As wood preservatives. Part 6: The length of the primary precipitation period
1975 - IRG/WP 359
The end of the primary precipitation fixation period of CCA preservatives coincides with the first peak in pH versus time. This offers a simple way of estimating the duration of the period. The duration is determined by a number of factors and their interactions, the most important of which are: wood species (anatomy, natural pH, accessibility of reducing agents), preservative type, preservative c...
S-E Dahlgren
Leaching amount of wood preservatives from treated wood in different size during outdoor exposure for 6 months
2000 - IRG/WP 00-50160
Eighteen impregnated specimens with CCA, ACQ, and BAAC preservatives were subjected to a outdoor leaching test. Test specimens, 10 x 10 x 25 cm3, 5 x 10 x 25 cm3, 2 x 10 x 25 cm3 in size, were cut from Japanese cedar (Cryptomeria japonica). Both of end surfaces were sealed with a silicone sealer in the half number of specimens. Total leaching amounts of copper from the open-end ACQ specimens of 10...
K Yamamoto, S Motegi, A Inai
Heat transfer and wood moisture effects in moderate temperature fixation of CCA treated wood
1994 - IRG/WP 94-40022
Practical aspects of heat transfer and fixation of wood exposed to drying conditions after CCA treatment are considered. The rates of heat transfer and CCA fixation are substantially influenced by the cooling effect of water evaporating from the wood surface when drying occurs during fixation. At least in the early stages of fixation, the wood temperature approaches the wet bulb temperature, rathe...
J Chen, M Kaldas, Y T Ung, P A Cooper
Difference of CCA efficacy among coniferous wood species
1990 - IRG/WP 3601
Wood blocks of Cryptomeria japonica, Tsuga heterophylla, and Pinus radiata successively extracted with n-hexane, ether, and methanol were treated with various concentrations of CCA type 3, which were subjected to the decay by Tyromyces palustris. The weight loss were different among species and kinds of extraction. Cryptomeria japonica treated with CCA had higher fungal resistance than Tsuga heter...
K Yamamoto, M Inoue