Moisture content development in lap-joints of different wood species in outside exposure trials
1998 - IRG/WP 98-20143
Lap-joint trails (following European Standard EN 12037) were set up with 11 different softwood and hardwood species. Half of the number of the lap-joint specimens were coated with an alkyd coating. The moisture development has been followed during a 19 months period. In this paper, the out comes of different moisture contents evaluations are presented. The results show, that the moisture content o...
H Militz, M Broertjes, C J Bloom
Rainfall simulation to assess CCA permanence
1991 - IRG/WP 2373
During experimental work on accelerated fixation of chromium containing preservatives a method has been developed which compares the degree of preservative levels of contamination of simulated preservative fixation in timber with the levels of simulated rainfall. This method uses commercial sized wood sections wetted in a way that simulates actual rainfall and relates the associated run-off contam...
P Warburton, J A Cornfield
Surface accumulation of copper on CCA-impregnated Pinus patula stakes during marine preservative trials in the southern hemisphere
1992 - IRG/WP 92-4181
Pinus patula stakes treated with CCA to target retentions of 30 kg/m³ salts were exposed to sea water in marine and estuarine ecosystems off the coast of Southern Africa for two years. Samples were then analysed for copper and arsenic. Analysis of samples from the marine ecosystem showed (IRG/WP/4167) that arsenic was longitudinally and transversely leached from the wood, whereas the copper was r...
G D Shelver, C D McQuaid, M Tarin, A A W Baecker
Preservative treatment of green timber by diffusion
1984 - IRG/WP 3291
The preservative treatment of green timber by diffusion is reviewed together with criteria which influence the economics of the process. New process options are described which should overcome some of the technical and economic disadvantages of double diffusion. These include the use of coagulating agents which increase the viscosity of the preservative solution and facilitate treatment by momenta...
P Vinden
Chemical treatment of ten Amazonian timber species of low natural durability
1991 - IRG/WP 3640
The objective of this work was to evaluate the performance of 10 amazonian wood species of low natural durability, to treatment with CCA preservative (2% concentration): it was concluded that all species studied are easily treated with this preservative. The sapwood showed high absorption and total penetration. The heartwood is relatively easy to preserve, exception to Parkia nitidae (Fava), Quale...
C S Neta, B F Vianez
New boron-based biocides for the protection of wood
2002 - IRG/WP 02-30283
Boric acid and other simple inorganic oxides of boron are amongst the oldest wood preservatives currently in use. Their relatively low toxicity and broad-spectrum activity are just some of their desirable characteristics. The primary disadvantage associated with conventional boron-based preservatives is their lack of permanence in exposed applications. A collaborative project between CSIRO and the...
D G Humphrey, P J Duggan, E M Tyndall, J M Carr, L J Cookson
The effect of chemical treatment on the moisture distribution of Pinus radiata D.Don subjected to wick action
1999 - IRG/WP 99-40135
Radiata pine sapwood stakes were treated with a range of chemicals, including an ammoniacal copper quaternary ammonium compound (ACQ), a copper-chrome and arsenic (CCA) solution and a CCA-oil treatment, potassium linoleate copper linoleate, a paraffin wax and a proprietary alkyd resin. The effect of these treatments on the extent of water absorption and moisture movement through the stakes was inv...
J Hann, P Vinden
Sphaeroma terebrans Bate: A note on distribution and preservative tolerance in Florida coastal waters
1987 - IRG/WP 4135
Treated test panels were installed in January 1984 in a Florida estuary where Sphaeroma terebrans had severely damaged pilings treated with copper chromate arsenate (CCA). Test treatments were CCA at three retentions, coal-tar creosote at three retentions, creosote with chlorpyrifos, dual treatment with CCA and creosote, and three types of chemical modification of the wood test panels. We describe...
B R Johnson, E D Estevez, S A Rice
The comparative resistance to fungi of the wood munika (Pinus heldreichii Christ.), fir (Abies alba Mill.) and spruce (Picea excelsa Poir.) compared with Pinus sylvestris L. and some physical and mechanical characteristics of munika
1981 - IRG/WP 1129
The munika (Pinus heldreichii Christ.) is situated primarily in the Balkans, and partially in the south of the Apenine peninsula. As an endemic species, with a very little annual increment, it has not been used enough as a timber for mechanical conversion up till now, although the oldest trees can grow to 27 m in height, with a diameter at breast height of about 60 cm. According to data of many Ba...
M Petrovic, M Miric
Non leachability of arsenic, copper and chromium from 15 years old CCA-C treated southern pine poles used in brackish water as jetty piles in Bangladesh
1998 - IRG/WP 98-50103
Revealed that chromated copper arsenate type C (CCA-C) treated southern pine poles used in Central Warehouse Jetty of REB, Khulna are stable and resistant to chemical and biological attack without loss of any component from outer 0-12.5 mm zone after 15y of use. Slightly reduced retention (4.44% less) was noted in above water location of piles (bottom end of tree) which would be due to continuous ...
A K Lahiry
Emissions from the combusting of boron and fluoride containing wood
1995 - IRG/WP 95-50040-18
The combustion properties of waste wood and wood residues containing wood preservatives were investigated in several test series after having been blended with untreated wood at a ratio of 1:4. The results for CFB, SF and boric salt show that, provided an optimized combustion, the concentrations of the stack pollutants correspond approximately with those found for untreated wood. Only during the c...
T Salthammer, H Klipp, R-D Peek
The performance of metal-chromium-arsenic formulations after 32 to 38 years' in-ground exposure in Australia
2000 - IRG/WP 00-30240
Two trials of metal-chromium-arsenic preservatives were exposed in-ground in Australia. In Trial 1, Pinus radiata stakes treated with Boliden K.33, Boliden S.25, Celcure A, Tanalith C and Tanalith CA were installed at Sydney and Narrandera in 1961/1962. In Trial 2, P. radiata and Eucalyptus regnans sapwood were treated with Celcure A, Celcure A21-N, Celcure A 21-O and Tanalith CA (new) and install...
G C Johnson, J D Thornton, J Beesley
Differential susceptibility of living and dead timber to colonisation by sapstain and mould fungi
1998 - IRG/WP 98-10288
Field studies have revealed that when timber is irradiated (i.e. killed) it is more susceptible to colonisation by mould fungi than sapstain fungi. By comparison, freshly sawn timber shows very little mould colonisation, tending to be colonised by sapstain fungi. It appears, therefore that the physiological state of the wood may influence the pattern of colonisation. A laboratory trial was underta...
J R Williams, D J Dickinson, J F Webber
Immuno-electron microscopic localization of extracellular metabolites in spruce wood decayed by brown-rot fungus Postia placenta
1990 - IRG/WP 1441
Degradation by Postia placenta in spruce and birch wood was shown to occur not only in the wood cell wall but also in the middle lamellae region. Middle lamellae was often found to be degraded along the centerline so that cells could separate along this line. Extracellular membrane structures were found surrounding the hyphae and this matrix labelled positively with antisera produced to Postia pla...
Y S Kim, B Goodell, J Jellison
Micromorphology of Schizophyllum commune attack in pine (Pinus sylvestris) wood
1983 - IRG/WP 1184
The decay pattern caused by Schizophyllum commune in pine latewood tracheids was studied using both light and transmission electron microscopy. The attack began as isolated concentric slits within the S2 layer with extensive lamellation and separation of individual wall layers observed in subsequent stages of decay. The slits resulting from attack appeared to be formed in thin, regular concentric ...
T Nilsson, G F Daniel
Natural durability of Norwegian wood species for above ground applications – Project presentation and preliminary results
2006 - IRG/WP 06-10594
In Norway exterior wood structures have traditionally nearly exclusively been made of treated and untreated Norway spruce (Picea abies (L.) Karst) and Scots pine (Pinus sylvestris L.). In recent years there has been a tendency that other tree species, like various domestic hardwoods and imported species have been used in exterior above ground applications, often unfinished. For several wood speci...
P O Flæte, G Alfredsen, F G Evans
Influence of different resin treatments on the dimension stability of wood
1997 - IRG/WP 97-40090
The dimension stability of wood is considered to be an important contribution to its durability and its performance in practice. A number of different treatments have been developed to improve the dimension stability of wood. One applied method is the treatment of wood with monomers or resins. The application of appropriate impregnation conditions seemed to be essential to enhance the efficiency o...
M Sailer, A O Rapp
Respiration measurement of dry-rot
1995 - IRG/WP 95-10095
Methods for measuring the production of carbondioxide from wood infected with the dry-rot fungus were evaluated. By enclosing whole wood blocks and measuring the concentration of gas in the headspace by gas chromatography, an exponential increase in the concentration of CO2 was observed for at least 2 months. This technique could therefore present a method for evaluating various treatments of dry-...
L Toft
Water-Borne Copper Naphthenate: An Emerging Wood Preservative
2002 - IRG/WP 02-30280
Waterborne copper naphthenate (WB Cu-N) was used to treat southern yellow pine (Pinus spp) and red maple (Acer rubrum) stakes. The treated stakes were exposed in test sites located in Florida, Michigan and Mississippi for 3 to 6 years. Copper Chromium Arsenate (CCA),
Ammoniacal Copper Quat (ACQ) and Oil-borne Copper Naphthenate (OB Cu-N) were also used to treat some stakes for comparison. Results...
P Nzokou, D P Kamdem, M H Freeman
Durability of heat-treated wood
1999 - IRG/WP 99-40145
Heat-treated wood from the French process were laboratory tested against decay using agar block test and a modified soil block test. Water absorption, bending strength, lignin content and acid number were also determined to evaluate the effect of heat treatment. Heat treated samples exhibit a higher lignin content and a lower acid number compared to untreated control indicating the degradation of ...
D P Kamdem, A Pizzi, R Guyonnet, A Jermannaud
The Protection of Wood with Oxy-aluminium Compounds
2002 - IRG/WP 02-30286
Wood inorganic composites (WICs) containing aluminium compounds were developed and tested in relation to some essential requirements of preservative treated wood. Four different oxy-aluminium treatments were developed and identified according to the final insoluble compounds formed (sodium aluminate, aluminium hydroxide, magnesium aluminate and aluminium borate) in wood. Vacuum impregnation or dou...
F A Ximenes, P D Evans
A dynamic approach to assess the modulus of elasticity in wood decay testing
1998 - IRG/WP 98-20139
In this study, the changes in elastic behaviour and mass losses of different hardwood and softwood species exposed to decay in a laboratory soil tests were assessed. Wood decay was monitored using different assessment methods, namely: mass loss and changes in elastic behaviours (MOE) determination. Elastic changes were determined by static and dynamic methods, for the latter, acoustic technique wa...
L Machek, H Militz, R Sierra-Alvarez
Leachability of didecyldimethylammonium chloride (a quaternary ammonium compound) from four wood species
1982 - IRG/WP 3204
Sapwood blocks prepared from red pine, ponderosa pine, southern yellow pine and hem-fir (a commercial mixture of western hemlock and amabilis fir) were treated with didecyldimethylammonium chloride, (an alkylammonium compound, AAC). After oven drying the blocks were vacuum impregnated with distilled water and subjected to a static leach cycle for 48 hours. The leachate was analyzed and the amount ...
J N R Ruddick, A R H Sam
Effect of water repellents on leaching of CCA from treated fence and deck units - An update
1997 - IRG/WP 97-50086
In an earlier study, it was shown that CCA leaching losses could be reduced over an accelerated leaching and short term natural weathering exposures by post treatment application of a commercial water repellent. In this report, the effects of this coating and two commercial CCA solution water repellent additives are evaluated after two years of natural weathering. Wood boards were pressure treated...
P A Cooper, Y T Ung, R M Vicar
Susceptibility of CCA treated North American hardwoods to Chaetomium globosum decay
1998 - IRG/WP 98-10278
Seven species of hardwood, Beech (Fagus grandifolia), Basswood (Tilia americana), Maple (Acer rubrum), Oak (Quercus rubra), Trembling Aspen (Populus tremuloides), White birch (Betula papyrifera) and Yellow poplar (Liriodendron tulipifera) were vacuum or pressure impregnated with CCA, at four retention levels. The CCA was allowed to fix in the wood at 35°C. Red pine (Pinus resinosa) was also inclu...
U Srinivasan, Y T Ung, P A Cooper