Your search resulted in 841 documents. Displaying 25 entries per page.
Adsorption of ACQ components in wood
2010 - IRG/WP 10-30522
To investigate the chemical adsorption capacity of copper-monoethanolamine (Cu-Mea) components on wood, the Na+ cation exchange capacity (CEC) of red pine (Pinus resinosa Ait.) was determined and compared to the adsorption capacity of free Mea and Cu-Mea complexes. The CEC increased with increasing pH. Free Mea adsorption as a function of pH followed the sodium adsorption curve except at pH over 9...
Myung Jae Lee, P Cooper
A comparison of the chemistry of alkaline copper and micronized copper treated wood
2010 - IRG/WP 10-30528
This paper discusses the chemistry of the reaction of alkaline copper and micronized copper with wood. The objective of this study is to examine the copper species produced in wood during the fixation reaction using electron paramagnetic resonance (EPR) spectroscopy. The initial experiments (phases 1 to 2) were designed to confirm the effect of time of treatment and solution concentration on the s...
Wei Xue, P Kennepohl, J N R Ruddick
Evaluation of ACQ-D treated Chinese fir and Mongolian Scots pine with different post-treatments after 20 months of exposure
2010 - IRG/WP 10-30530
The performance of alkaline copper quat-type D (ACQ-D) treated Chinese fir (Cunninghamia lanceolata Hook.) and Mongolian Scots pine (Pinus sylvestris Linn. var. mongolica Litv.) stakes after 20 months exposure in Chengdu and Guangzhou of southern China were evaluated according to AWPA standard E07-07. The ACQ-D treatments used two concentration levels (0.5 and 1.0%) and four different post-treatme...
Lili Yu, Jinzhen Cao, Wei Gao, Haitao Su
Distribution and availability of preservative components in ACQ treated wood - effects of coatings and weathering
2010 - IRG/WP 10-30537
Copper and quaternary ammonium compound (quat) distributions across lumber (gradients) and availability, as measured by amount removed by intensive leaching of wood flour, were measured in ACQ treated southern pine lumber. Samples were evaluated just after treatment and stabilization, or after 3 years of laboratory storage, or after 3 years of natural weathering exposure. The objective was to in...
T Ung, M Nejad, P Cooper
A Comparison of the Performance of Related Copper Based Preservatives against Soft Rot
2010 - IRG/WP 10-30540
The performance of pine and beech wood treated with either a soluble copper + quat (ACQ type D) preservative system or a particulate copper + quat system was evaluated in unsterile soil using the European standard ENV 807 soft rot decay test procedure.
In addition, to compare soft rot performance of soluble and particulate copper directly without the influence of co-biocides, beech and pine test...
M Ray, D Dickinson, K Archer
Extruded wood plastic composites based on ACQ and MCQ-treated wood materials
2010 - IRG/WP 10-40495
This paper deals with wood plastic composites manufactured using ACQ and MCQ-treated wood fibers recovered from a wood treatment plant. The goal was to investigate the effect of coupling treatments on the properties of manufactured wood plastic composites (WPCs) through injection molding and to manufacture co-extruded WPC with treated wood fibers. The result demonstrated sound mechanical propertie...
Qinglin Wu, Fei Yao, K Ragon, J Curole, M Voitier, T Shupe
Influence of Copper Preservative Type on Earlywood and Latewood Distribution of Copper in Treated Wood
2010 - IRG/WP 10-40507
Some of the new water based copper containing wood preservative systems use particulate “micronized” copper as the primary biocide instead of the more traditional soluble amine copper based systems. Studies were conducted to investigate how this difference in the type of copper system might impact both initial and post drying distribution of the preservatives in wood. Of specific interest wa...
A Zahora
A comparison of the corrosion of alkaline copper and micronized copper treated wood
2010 - IRG/WP 10-40515
With the replacement of chromate copper arsenate (CCA) by alkaline copper wood preservatives, there have been reports of increasing corrosion of metal fasteners and connectors in contact with treated wood. This may be explained by the presence of more mobile copper in the treated wood. One novel industrial response has been to develop a wood preservative based on an aqueous solution containing sus...
M Kofoed, J N R Ruddick
Optimization of oxalic acid production for bioleaching of metal components from CCA-treated wood by an unknown Polyporales sp. KUC8959
2010 - IRG/WP 10-50266
A brown-rot fungus, an unknown Polyporales sp. KUC8959, has recently been identified and proven as a prominent fungal species for bioremediation of CCA-treated wood wastes in our Lab. The fungus produced a larger amount of oxalic acid than other fungi tested, and removed 90 % or more of chromium, copper and arsenic from CCA-treated wood sawdust through bioleaching process. The bioleaching process ...
Yong-Seok Choi, Min-Ji Kim, Jae-Jin Kim, Gyu-Hyeok Kim
Microwave-Assisted Organic Acids Extraction of Chromate Copper Arsenate (CCA)-Treated Southern Pine
2010 - IRG/WP 10-50267
The extraction effects of acid concentration, reaction time and temperature in a microwave reactor on recovery of CCA-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from chromated copper arsenate (CCA)-treated southern pine wood samples with two different organic acids (i.e., acetic acid and oxalic acid) was investigated using a microwave reactor. Oxalic acid was e...
Bin Yu, Chung Y Hse, T F Shupe
Chapter 10 - Preservation of muli bamboo
2007 - IRG/WP 07-10635-10
Environmentally and economically very important mulibamboo
(Melocanna baccifera) grown in Bangladesh was fond to be easily
pressure treatable with CCA-C at green and air dry conditions. The
green and air-dried bamboo treated at same treating conditions and
concentration showed 110 per cent (2.10-times) higher retention in
air-dried bamboo than green one. Adequate lower retention
equivalent t...
A K Lahiry
Chapter 11 - Preservation of talla bamboo
2007 - IRG/WP 07-10635-11
Researches revealed that the talla bamboo (Bambusa tulda Roxb.))
in Bangladesh could be full-cell pressure treated with CCA in green
and dry conditions. The dry bamboo gives higher loading
absorptions than green one when impregnated at same treating
conditions. Also higher absorptions are obtained at nodes rather
than internodes. Adequate penetration and retention results for
ground and wate...
A K Lahiry
Chapter 12 - Treatment Groups of Bamboo
2007 - IRG/WP 07-10635-12
Study on distribution of CCA in three major bamboo species in
Bangladesh, full-cell pressure treated at green and dry conditions
revealed two treatment groups and some treating principles. Higher
adequate treatment for ground and water contact use is only
possible by treating problematic bamboo species pre-kiln dried up to
half of its FSP and non-problematic species pre-dried up to FSP
(20% ...
A K Lahiry
Chapter 13 - Slow fixation of CCA-treated bamboo
2007 - IRG/WP 07-10635-13
Chromated copper arsenate (CCA) leachability tests on full-cell
pressure impregnated (with 2-3% CCA solution) and slow dried (six
months air-drying under cover) bamboo block of three major
bamboo species of Bangladesh revealed initial insignificant leaching
of CCA within first week and no leaching in next week. Use of low
concentration of CCA, release of particle form of CCA due to
exposure ...
A K Lahiry
Chapter 14 - Accelerated fixation of CCA-treated bamboo
2007 - IRG/WP 07-10635-14
Chromated copper arsenate type C (CCA-C) fixation study on
impregnated (with adequate w/v 6% CCA solution) then boiled,
oven-dried, normal, air-dried and steamed bamboo slices of airdried
borakbamboo (Bambusa balcooa Roxb.) of Bangladesh,
revealed almost complete fixation in steamed (accelerated fixation)
and air-dried (3 weeks, slow fixation) bamboo slices compared to
moderate to low fixati...
A K Lahiry
Fungal biodegradation of CCA-treated wood wastes
2011 - IRG/WP 10-50276
Fungal biodegradation could be employed as a pretreatment method to alleviate problems caused by landfill disposal of CCA-treated wood wastes (e.g. a shortage of landfill space and a release of leacheate). It could be used to decrease the volume of waste and to remove metals from waste simultaneously. We have screened hundreds of decay fungi, including fungi isolated from CCA-treated wood in servi...
Gyu-Hyeok Kim, Yong-Seok Choi, Jae-Jin Kim
Novel Approaches to the Development and Testing of Anti After-glow Additives for CCA-based Treatments of Poles
2011 - IRG/WP 11-30561
In this paper, a field fire stake testing screen method is described. This method uses stake samples from matched wood sources allowing replicates from different boards to be included. The method is easy to control and can provide quick comparative fire resistance test results. The parameters measured from the tests are percentage weight loss, minimum residual circumference and residual thicknes...
L Jin, P Walcheski, A Preston
Laboratory study of toxicity or tolerance of CCA preservative and heavy metal constituents copper, chromium and arsenic to Malaysian tropical fungi
2011 - IRG/WP 11-30579
CCA preservative and its constituent heavy metal tolerance and toxicity to 3 Malaysian isolates Phialophora fastigiata (soft rot fungus), Paecilomyces variotii (mould fungus) and an unidentified white rot Basidiomycete, was investigated by the modified ‘Strange-Smith’ agar-well-plate technique with 1.6% CCA concentration and the malt-agar-plate bioassay technique with a range of CCA and consti...
A H H Wong, T Mark Venås, N Morsing, C C L Tan, P K F Chong
Further Studies on the Distribution of Copper in Treated Wood Using an XRF Microscope Technique
2011 - IRG/WP 11-40549
There are two distinct forms of copper in aqueous copper based wood preservative systems that are currently used in the United States for treatment of southern pine lumber. These are systems using either soluble copper (typically amine based) or the more recent particulate or “micronized” copper as the primary biocide. Studies reported last year showed that there were distinct differences in...
A Zahora
Characterizing long term leaching behaviour of copper from preservative treated wood in a practical exposure scenario
2011 - IRG/WP 11-50278
To investigate the prediction of the long term emission of copper from preservative treated wood in a Use Class Class 3 scenario, treated boards were exposed vertically above ground to natural weather conditions. The study included two products; an amine copper ACQ-type formulation, air-dried after treatment to a 22 kg/m3 retention, and the same formulation which was hot oil vacuum dried after tre...
T Mark Venås, M Klamer
A survey on Bio-Resistance of Oak and Elm in Caspian Sea Water
2012 - IRG/WP 12-20483
Logs of Oak (Quercus castanifolia) and Elm (Zelkova carpinifolia) have been cut to lumbers with dimensions of 300×100×30 mm. The oven dried samples have been impregnated with CCA (Chrome–Cupper-Arsenic). Treated and untreated (natural as a control) woods have been established for 3, 6, 9 and 12 months in Amirabad beach of Behshare under fishing environment. The observation results shows that i...
S M Kazemi
Performance superiority of CCA-C treated wooden jetty poles and piles used for 30 years in Bangladesh against marine borers
2012 - IRG/WP 12-30582
Observational study along with previous investigation and records revealed that chromated copper arsenate type C (CCA-C) impregnated southern pine poles and piles of jetty constructed in most vulnerable brackish water in Bangladesh are stable and resistant to attack of all types of marine borers after 30 years of use. It is evident from the service records of other construction materials that CCA-...
A K Lahiry
Mold Control for Treated Lumber in Block-Stack Storage Conditions
2012 - IRG/WP 12-30588
The mold development and control for freshly treated and block-stacked wood have been evaluated using a green house mold testing method. The results for the mold resistance of several commonly used water boron preservative treatment systems, such as ACQ, Copper Azole, and borates with and without inclusion of mold inhibitors are presented. The data suggest that the different preservative treatme...
L Jin, P Walcheski, A Preston
Environmental safeness of 60% and 72% concentrated CCA-C solution and paste for wood treatment
2012 - IRG/WP 12-50284
In this study 30-years practical and observational experience of the present author about using of 72% concentrated CCA-C paste for preparing treating solutions and for treating wooden poles, anchor logs and cross arms has revealed that the 60% concentrated CCA-C solution is superior to the 72% concentrated CCA-C paste regarding solubility, homogeneity, cleanliness, treatability, sludge formation,...
A K Lahiry
Biodegration of treated wood waste by native fungal communities of tropical soil in French Guiana
2012 - IRG/WP 12-50285
Woods have been protected with fungicides for a long time, and the effects of these fungicides on soil after being leached into the ground have turned out to be a true environmental issue. It is in this perspective that we are proposing to study fungal communities of these contaminated woods in a purpose of bioremediation. Most of precedent studies have focused on ability of some Basidiomycetes an...
A Zaremski, L Gastonguay, C Zaremski, F Chaffannel, J Beauchêne, G LeFloch