Effects of hard water, sea water and humic acid on the release of CCA components from treated wood
2005 - IRG/WP 05-50228
Leaching medium is an important factor affecting release of preservative components from treated wood because physical and chemical characteristics of medium increase or decrease the solubility of fixed preservative components. This study evaluated the leaching properties of copper, chromium and arsenic elements from chromated copper arsenate (CCA)-treated wood specimens subjected to laboratory le...
S N Kartal, W J Hwang, Y Imamura
Wood preservation sites polluted by CCA. Is potassium diphosphate incubation a catalyst for the electrodialytic remediation of these soils?
1998 - IRG/WP 98-50106
As part of an evaluation of a newly developed electrodialytic soil remediation technique, we investigated the incubation of a contaminated soil (from a Portuguese wood preservation site polluted with CCA) with potassium diphosphate as a possible catalyst for the removal of heavy metals and metalloids. A chemical sequential extraction scheme (SE) applied to the soil has shown that the potassium dip...
A B Ribeiro, G Bech-Nielsen, A Villumsen, A Réfega, J Vieira e Silva
The influence of cement and calcium compounds on the performance of CCA preservatives
1983 - IRG/WP 3221
The influence of cement and calcium compounds on the durability of untreated and CCA treated wood is considered. Calcium compounds were found to reduce the toxicity of a CCA preservative to a soft rot fungus at copper to calcium ratios of 1:1 and 1:10 using a cellulose filter paper technique. Further studies are outlined and some possible mechanisms by which cement and calcium compounds may affect...
R J Murphy
Efficacy of a novel copper-based organic solvent preservative in laboratory and fungus cellar tests
1995 - IRG/WP 95-30071
The efficacy of Chemicca 4, a novel copper-based organic solvent preservative, was compared with that of other LOSP in pure culture laboratory decay tests and with that of CCA and TBTO in a fungus cellar exposure. It was markedly superior to copper and zinc naphthenates at equivalent metal retentions in laboratory decay tests, and similar in activity to TBTO. After 60 months' fungus cella...
M E Hedley, P N Maynard
A physiological role of the glyoxylate and TCA cycles in fruitbody formation of the coppertolerant brown-rot fungus Fomitopsis palustris
2002 - IRG/WP 02-10430
Changes in activity of the representative enzymes involved in biosynthesis of oxalic acid (oxalate) and carbon metabolism of glucose were investigated in relation to the fruit body formation of the copper-tolerant brown-rot fungus Fomitopsis palustris. Changes in specific activities of the two glyoxylate (GLOX) cycle key enzymes (isocitrate lyase (ICL) and malate synthase (MS)), the two oxalate-fo...
Jeong-Jun Yoon, T Hattori, M Shimada
Termite resistance of borate-treated lumber in a three-year above-ground field test in Hawaii
2000 - IRG/WP 00-30236
A protected above-ground field test simulating the sill plate (dodai) used in conventional Japanese housing construction was established in both Hawaii and Japan to examine the efficacy of disodium octaborate tetrahydrate (DOT, 2% and 3% shell and through) wood treatments. In Hawaii, chromated copper arsenate (CCA, 4 kg/m3) and ammoniacal copper zinc arsenate (ACZA, 4 kg/m3) were included in the t...
J K Grace, R J Oshiro, A Byrne, P I Morris, K Tsunoda
Borate Protection and Termites: Variation in Protection Thresholds Explained
2006 - IRG/WP 06-20324
Laboratory and field data reported in the literature are confusing with regard to ‘adequate’ protection thresholds for borate timber preservatives against subterranean termites. The confusion is compounded by differences in termite species, timber species and test methodology. Laboratory data indicate a borate retention of 0.5% mass/mass (m/m) boric acid equivalent (BAE) would cause > 90% t...
B C Peters, C J Fitzgerald
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
The role of oxalic acid in tolerance to N’N-naphthaloylhydroxylamine in Tyromyces palustris
2006 - IRG/WP 06-10584
Certain wood decay fungi exhibit tolerance to one or more wood preservatives. Copper tolerance of brown-rot fungi has been studied in our laboratory for the past six years. We have observed some degree of tolerance to N’N-naphthaloylhydroxamine (NHA), a recently patented termite bait, by the brown-rot fungus Tyromyces palustris TYP-6137. In an effort to try and confirm this tolerance in other is...
R A Arango, C A Clausen, F Green III
Is Field Test Data from 20 x 20mm Stakes Reliable? Effects of Decay Hazard, Decay Type and Preservative Depletion Hazard
2006 - IRG/WP 06-20327
Effects of decay hazard, decay type and preservative depletion hazard on the performance of variously preservative treated 20 x 20 x 500 mm Radiata pine and Fagus sylvatica test stakes across 13 field test sites in New Zealand and Queensland Australia were determined.
Radiata pine treated with an ammoniacal copper quaternary preservative (ACQ) (1.56% m/m a.i.) and copper chrome arsenate (CCA) (...
R Wakeling
The Use of Modulus of Elasticity and Modulus of Rupture to Assess Wood Decay in Laboratory Soil-Bed Test
2006 - IRG/WP 06-20338
The efficacy of wood preservatives were determined in a soil-bed test. Samples of alder wood sapwood (Alnus glutinosa subsp. barbata) (5x10x100 mm) were treated with Solutions of CCA (1 % and 2 %), ACQ-1900 (2 % and 3 %), ACQ-2200 (1 % and 2 %), Tanalith E 3491 (2 % and 2.8 %), Wolmanit CX-8 (% 1 and 2 %). Modulus of Elasticity, modulus of rupture, mass loss and decay rate according to AWPA E7 wer...
A Temiz, Ü C Yildiz
Measuring Soil Respiration as a New Approach to Describe the Interaction Between Wood (Treated and Untreated) and Microbiologically Active Soil
2006 - IRG/WP 06-20344
Soil respirometry was employed to examine the relationship between both the performance of copper organic preservatives in contact with and the amount of carbon dioxide evolved from soil and the effect of wood treated with preservatives on carbon turnover in soil. Wood was treated with a range of copper organic preservatives intended for use in ground contact as well as an organic preservative in...
I Stephan, W Mierke
Qualitative and quantitative assessment of chemicals used for wood durability improvement by Near Infrared Spectroscopy
2006 - IRG/WP 06-20349
The Near infrared spectroscopy (NIRS) could be a suitable technique to assess chemicals used for wood durability improvement in the forest products industry. NIRS methodology can be used to obtain results more quickly, less costly and without damaging the wood. In this study, wood samples selected from heartwood and sapwood of Maritime Pine (Pinus pinaster) were prepared to assess the artificial d...
S Zahri, F Charrier, H Baillères, B Charrier
Performance of borate-treated lumber after 8 years in an above-ground termite field test in Hawaii
2006 - IRG/WP 06-30390
We report eight years of field study results from a protected above-ground field test in Hawaii simulating the sill plate (dodai) used in conventional Japanese housing construction. Field tests were established in both Hawaii and Japan to examine the efficacy of disodium octaborate tetrahydrate (DOT, 2% and 3% BAE shell and through) wood treatments. In Hawaii, chromated copper arsenate (CCA, 4 kg...
J K Grace, A Byrne, P I Morris, K Tsunoda
Performance of borate-treated lumber in a protected, above-ground field test in Japan
2006 - IRG/WP 06-30395
This document is supplemental to the previous IRG document (Tsunoda et al. 2004).
An experiment to simulate the sill plate (dodai) of the Japanese houses was conducted at the termite field test site of the Research Institute for Sustainable Humanosphere of Kyoto University in Kagoshima Pref., Japan where two economically important subterranean termite species [Coptotermes formosanus Shiraki and R...
K Tsunoda, A Byrne, P I Morris, J K Grace
Preliminary screening of a boron based wood preservative for biological efficacy (fungicidal) in treated timber
2006 - IRG/WP 06-30396
The resistance of Pinus radiata D.Don sapwood blocks, treated with a boron based preservative, to attack by five wood destroying fungi (Fomitopsis lilacino-gilva, Coniophora olivacea, Gloeophyllum abietinum (boron resistant), Serpula lacrymans and Perenniporia tephropora) was investigated. A phenyl pyrazole termiticide (fipronil) was also incorporated into the formulation to examine if its presen...
S R Przewloka, J A Hann, P Vinden
One year performance of graveyard stakes in the Northern Territory of Australia
2006 - IRG/WP 06-30398
This paper presents the one year progress performance of in ground graveyard stakes exposed to numerous termite species and decay fungi in tropical field conditions. The field study examines the efficacy of a new timber preservative formulation developed at the University of Melbourne, Australia. The biocides used in the formulation are fipronil (a phenyl pyrazole) and trimethyl borate. The pre...
B Ahmed, J Hann, S Przewloka, P Vinden, P Blackwell, P Plews
Above and Below-Ground Depletion of Copper, Chromium and Arsenic from Pinus radiata and Fagus sylvatica at Thirteen Test Sites in New Zealand and Australia
2006 - IRG/WP 06-30402
The objective was to determine the significance of site and wood species on preservative depletion for a copper chrome arsenate preservative (CCA) from 20 x 20 x 500 mm field test stakes after 5.5 and 4.5 years for pine and beech respectively. At least 5 sacrificial stakes were used to produce site means. Site and wood species had a major effect on copper, chromium and arsenic loss from CCA treate...
R Wakeling
Addition of boron compounds and octanoic acid for improvement of biocidal properties and copper fixation at copper-ethanolamine based wood preservatives
2006 - IRG/WP 06-30408
Copper-ethanolamine based wood preservatives became important active substance (formulation) for wood protection, novelty. As copper itself can not ensure sufficient protection against wood destroying organisms and fixation in wood we combine it with other biocides like ethanolamine, boron and octanoic acid. This investigates were performance on spruce wood impregnated with different combination o...
F Pohleven, M Humar
Long term marine performance of ACZA treated Hem fir in Krishnapatnam harbour, east coast of India
2006 - IRG/WP 06-30409
The performance of Hem fir (Tsuga heterophylla) and Southern pine (Pinus sp.) treated with ammoniacal copper zinc arsenate (ACZA) and copper dimethyldithio carbamate (CDDC) at two retention levels of each preservative was assessed in tropical marine waters at Krishnapatnam harbour on the east coast of India. Panels treated with ACZA of lower loadings (23.1 Kg/m3) had failed in 38 months while the ...
B Tarakanadha, K S Rao, J J Morrell
CCB Preservative treatment of split muli (Melocanna baccifera ) bamboo by soaking process
2006 - IRG/WP 06-40336
This study was carried out in order to investigate the retention of chemicals inside the split muli ( Melocanna baccifera ) bamboo after preservative treatment by soaking process. Treatment with 10% aqueous solution of CCB (copper-chrome-boron) was applied in split bamboo of two sizes (1/4 part and 1/8 part) at three different moisture contents and five time periods (24, 48, 72, 96, 120 hours). It...
K Akhter, M H Chowdhury
Non-pressure preservation technique of five less durable timber species – Kadam (Anthocephalus cadamba), Shimul (Bombax ceiba), Pithalu (Trewia nudiflora), Am (Mangifera indica) and Boroi (Ziziphus jujube) of Bangladesh
2006 - IRG/WP 06-40322
Wood is a versatile renewable resource, which has been extensively used as a reliable construction material as well in furniture ever since the beginning of civilization.
The Major disadvantage of wood is its susceptibility to biodeterioration by fungi, insects and bacteria. In tropical countries like Bangladesh, fungi is the most significant of these biodeterioration agents. Kadam (Anthocephalus...
G N M Ilias, A H Kabir, F Begum, M F Alam
The Effect of Wick Action upon Moisture Distribution in Ellagate Treated Pinus radiata Wood
2006 - IRG/WP 06-40328
Sapwood stakes of Pinus radiata D. Don were treated with water-soluble tetraguanidinium, tetracholine and tetrakis-benzyltrimethylammonium ellagates. The effect of these treatments upon moisture distribution was investigated by wick action. Given that chemical reactions within the wood substrate between nutrients and treatment solutions may alter the properties of the wood with regard to moistur...
S R Przewloka, B J Shearer, J A Hann
Corrosiveness of metal by copper-based preservatives
2006 - IRG/WP 06-40329
The corrosive rates of 4 types of metal as well as epoxy-coated metal by a variety of preservatives derived from different copper source and ingredients were conducted in this paper. The main results shown that: CCA is less corrosive to red brass and Q235A steel than other copper formulations; Copper-based preservatives such as ACQ and copper azole derived from basic cupric carbonate or cupric hyd...
Ying Zhang, Mingliang Jiang
Wood-Plastic Composites and the Durability Dilemma: Observations from the Field
2006 - IRG/WP 06-40351
Wood-Plastic Composites (WPCs) used for decking, window & door moldings have experienced dramatic growth in North America over the last several years, with annual production increasing at rates greater than 20% per annum since 1998. A key factor contributing to this growth has been the successfully communicated message that they are "virtually maintenance free". The common perception being t...
M J Manning, F M Ascherl, M E Mankowski