Adhesion and performance of exterior wood coatings on chemically and thermally modified wood – Results from 5.5 years outdoor exposure
2023 - IRG/WP 23-40964
Non-durable softwood and hardwood species were treated with the water-soluble cyclic N-methylol compounds 1,3-dimethylol-4,5-dihydroxyethyleneurea (DMDHEU) and methylated DMDHEU. One half of the modified specimens were coated with a waterborne acrylic coating system prior a natural weathering for 5.5 years according to EN 927-3 (2020). By frequent evaluations, the impact of chemical modifications ...
L Emmerich, H Militz
New wood-modification process based on grafted urethane groups: Durability of carbamamylated Scots pine (Pinus sylvestris L.) wood
2023 - IRG/WP 23-40974
Substituting commonly used toxic preservatives with wood modification treatments can make the wood material less prone to water and moisture uptake. This approach favours a more sustainable protection of wood against biodegradation. In this study, Scots pine sapwood was full-cell impregnated with an aqueous solution of urea (30%), dried at 40°C for 24h, and subsequently heat-treated at 150°C for...
C-F Lin, O Myronycheva, O Karlsson, D Jones, D Sandberg
Failure characteristics of thermally modified poplar wood subjected to mechanical tests
2023 - IRG/WP 23-40983
Poplar (Populus spp.) are among the fastest growing timber species and have been widely planted for use in plywood, composites, pallets, furniture components and paper production. However, the low density of the wood limits many structural applications and the wood has little resistance to biodegradation. Thermal modification represents one approach to improving durability by changing the moistur...
E Bari, M Ghorbanian Far, N Moradi, J J Morrell, G Daniel, B Mohebby, R Hosseinpourpia, M Humar
Relationships between deterioration part and structural performance in wooden houses
2023 - IRG/WP 23-50376
Based on the survey examples, there are four patterns of deterioration that tend to occur in plywood bearing walls of wooden houses in Japan. The first is a pattern in which wall is in a whole deterioration. It is a no damage wall or test specimen. The second is a pattern in which only the sill is deteriorating. It is caused by moisture or termites from ground to the base. In addition, there is a ...
Y Ota, H Ishiyama, S Okamoto
Exposure tests on railroad ties treated with DOT
2024 - IRG/WP 24-20705
Keruing railroad ties were treated with disodium octaborate tetrahydrate (DOT) to retentions of 0.7 to 1.7% boric acid equivalent (BAE) and selected borate treated ties were subsequently over treated with creosote/diesel fuel mixture. The treated ties were exposed in a simulated railway track test bed in Malaysia. The leaching of borate was measured over 5 years. BAE in the ties after 5 years of e...
L Arthur, J-W Kim
Barriers of polyglycol/borate treated wood prevent termite attack to untreated wood above them in 10-year field tests
2024 - IRG/WP 24-20709
As a pioneer in wood protection and borate research Terry Amburgey, a lifetime member of the IRG, had many projects where borates were used in subsequently commercially very successful applications. This paper is one of the initial research projects that lead to polyglycol borates being used as a standalone treatment to protect against termites in new homes which has now been well proven over the ...
K W Ragon, J D Lloyd, T L Amburgey
Potential of heartwood extracts as wood preservatives combined with linseed oil in 8-year above-ground and in-ground field trials
2024 - IRG/WP 24-20719
The current study assessed the efficacy of heartwood extracts from Tectona grandis, Dalbergia sissoo, Cedrus deodara, and Pinus roxburghii, combined with linseed oil, as protectants for two non-durable wood species against termites and decay fungi. Stakes measuring 45.7 × 1.9 × 1.9 cm and blocks measuring 12.5 × 3.75 × 2.5 cm of the sapwood of southern pine (Pinus sp.) and cottonwood (Populus ...
M E Mankowski, G T Kirker, B Hassan
Evaluation of the water exclusion ability and inherent bioactivity of heartwood against decay in Japanese and European wood species via above-ground exposure and water absorption tests
2024 - IRG/WP 24-40998
The natural durability of wood has been thought to mainly depend on bioactive extractives and the water exclusion ability. To clarify the contribution of each factor to wood durability, above-ground exposure tests were conducted on Japanese and European wood species. A double-layer test was carried out using heartwood specimens of four wood species, i.e., Japanese cedar, Japanese cypress, Scots pi...
T Osawa, R Noda, K Yamamoto
Field facility for conducting wood durability tests at LSU Agricultural Center
2024 - IRG/WP 24-41012
Efforts by Louisiana State University Agricultural Center (LSU AgCenter) to conduct wood durability research on C. formosanus and other wood-related topics, have led to establishing three field research sites to test wood products against Formosan subterranean termites (New Orleans, La), and native subterranean termites (Franklinton, LA), and to test utility poles for outdoor exposure, decay resis...
Q Wu, J Curole