Collaborative soft rot tests: Final Report
1978 - IRG/WP 2106
Since preparation of Document No: IRG/WP/258 results have been received from the remaining collaborators. Thus there is a little further to add to the conclusions already derived, those in Document No: IRG/WP/251 being as follows: 1) the exposure system used sometimes resulted in excessive weight gains in the sterile check blocks. Consequently the corrected loss in weight of the test blocks could ...
J G Savory, J K Carey
On the use of probit analysis for assessing the toxicity of wood preservatives
1974 - IRG/WP 244
To elucidate the general character of the action of the toxic material on the fungus, it is sufficient to carry out preservative tests using the previously described procedure, but in doing so, it is necessary somewhat to change the number of specimens and their arrangement in jars. Five concentrations of toxic material are tested simultaneously. For the testing of one preservative ten jars should...
D A Belenkov
Leaching of copper-chrome-arsenic treated timber: Simulated rainfall testing
1996 - IRG/WP 96-50074
Six kiln dried radiata pine sapwood packs of timber were preservative treated with copper-chrome-arsenic preservative using a modified Bethell treatment schedule. The packs were then subjected to simulated rain leaching at specified periods after treatment. Higher chromium leachate was obtained when higher volumes of simulated rainfall were applied. Lower chromium leachate was obtained for timber ...
S Walley, P R S Cobham, P Vinden
Preservative treatment specifications in Fiji
1982 - IRG/WP 3190
The preservative treatment specification used in Fiji is outlined. Reference is made to a basic end use classification and to locally approved treatment processes, preservatives and retention levels. Amenability ratings are defined and penetration requirements for broad commodities indicated. Currently commercial operations rely entirely on pressure treatment with copper-chrome-arsenic multisalts ...
A S Alston
A comparison of the leaching resistance of copper 2-ethanolamine and copper ethylenediamine treated Scots pine
2000 - IRG/WP 00-30233
The depletion of copper from copper 2-ethanolamine and copper ethylenediamine treated Scots pine blocks was investigated. A greater leaching resistance was found for copper 2-ethanolamine, which retained ca. 86% and ca. 50% copper after water and buffer leaching, respectively. Leached amine treated blocks also contained significant residual amine. This was consistent with other observations linked...
Xiao Jiang, J N R Ruddick
Comments on soft rot attack in timbers treated with CCA preservatives: A document for discussion
1982 - IRG/WP 1167
This paper is not based on any particular results but rather on several observations of soft-rot during many years of studies, and on a review of the existing literature. The short time available has unfortunately not permitted a detailed review of the literature. Data and knowledge of important facts are lacking for several aspects of soft-rot attack and for reactions occurring in the wood as a r...
T Nilsson
Some fundamental thoughts on the prediction of field performance from lab-testing based on comparison of lab and field test results of some copper-free materials
2003 - IRG/WP 03-20269
In the paper results from lab testing (ENV 807 and EN 113) are compared with field results (EN 252) of differently treated wood. Depending on the type of the organic biocide containing material and depending on type of soil and type of decay differences were found in suitability of the lab methods to predict field performance. The attempt is made to interpret the found differences. Furthermore it ...
A O Rapp, U Augusta
Effects of soil physical and chemical characteristics on adsorption of leached CCA and ACQ preservative components
2003 - IRG/WP 03-50200
The objective of this study was to examine the effect of soil characteristics on adsorption of wood preservative components from CCA and ACQ preservative systems. Adsorption of leached CCA and ACQ preservative components in soils with different characteristics were studied. Three soils (clay, sandy and organic) were investigated using different concentrations of leach water of CCA and ACQ wood pr...
S Stefanovic, P A Cooper
The effect of acid rain on CCA treated timber
1990 - IRG/WP 3579
The effect of acid precipitation on the leaching of copper, chromium and arsenic from timber treated with different CCA preservatives was studied in the presence of three types of soil under simulated field conditions. Pine sapwood, embedded in soil, was subjected to simulated rainfall at three different levels of acidity. The CCA preservative formulations tested were:- American Wood Preservers&am...
R J Murphy, D J Dickinson
Evaluation of the protective means of some wood preservatives by means of accelerated tests
1973 - IRG/WP 232
In site conditions of the eastern site in the forest-steppe part of the Krasnovarsk region, the relative effectiveness of a series of wood preservatives was obtained by means of field tests. To obtain a more accurate evaluation of the protective qualities of these accelerated tests were carried out in laboratory conditions. In 9 boxes filled with non-sterile soil taken from the site, 72 samples of...
I A Petrenko
Biological resistance of electrolessly plated wood (1). Preliminary report
1994 - IRG/WP 94-40024
Surface metal coating is considered to improve biological resistance of wood as some metal ions are fungitoxic. Six wood species (three softwoods: Cryptomeria japonica, Tsuga heterophylla and Larix spp; three hardwoods: Fagus crenata, Acer mono and Betula platyphylla) were electrolessly plated with nickel or copper, and those were served for laboratory evaluation of their resistance against decay ...
M Hasegawa, K Tsunoda, T Yoshimura
The effect of soil pre-exposure on the results of laboratory Basidiomycete testing
1991 - IRG/WP 2385
Scots pine sapwood blocks were treated with several concentrations of copper chrome arsenic (CCA), copper chrome boron (CCB) and a copper modified quaternary ammonium compound (CMAAC). Leached and unleached samples were exposed in a basidiomycete monoculture test using Coniophora puteana, a copper tolerant brown rot. Prior to testing half of the blocks were buried in unsterile soil for 4 weeks. Th...
S M Gray
The relationship between preservative type and surface degrade in Pinus radiata
1980 - IRG/WP 3158
Samples of Pinus radiata D. Don were impregnated with one of two preservative types, a copper chrome arsenic salt and a light organic solvent preservative. The panels were exposed to the weather for 4-5 years at a site near Sydney, Australia. Macroscopic and microscopic examinations showed different rates and patterns of weathering between the samples treated with each preservative and an untreate...
R S Johnstone, R K Bamber
Biological and chemical investigations for the assessment of the environmental impact of wood preservative components
1999 - IRG/WP 99-50127
This study was carried out in order to investigate the suitability of biological and chemical techniques to evaluate the environmental impact of wood preservatives depleted from impregnated wood. Small specimens (15*25*50 mm3) of Scots pine sapwood (Pinus sylvestris) were treated with a CCB salt. After fixation the treated and untreated samples were washed-out according EN 84, and the different le...
E Melcher, H-W Wegen
Leaching of CCA from Bombax ceiba catamarans in operation for 15 years
2002 - IRG/WP 02-50191
Core samples of wood at random were collected from all the timber pieces of each of the three catamarans made of CCA treated logs of Bombax ceiba put to continuous service for the last 15 years at the Lawson's Bay fishing village, Visakhapatnam. The samples were dried to constant weight, powdered, digested and analyzed for the residual salts of the preservative. The residual content of ...
V Kuppusamy, M Balaji, M V Rao, K S Rao
Biodetioration and strength reductions in preservative treated aspen waferboard
1983 - IRG/WP 2195
Experimental aspen waferboards, bonded with liquid or powdered phenol formaldehyde resins and treated by various methods with a wide selection of preservatives, were tested for fungal resistance in accelerated laboratory trials. Mold growth on the surface as well as weight and strength losses due to the actions of decay fungi were determined. Testing of board strength after decay in high and moder...
E L Schmidt, H J Hall, R O Gertjejansen, R C De Groot
Microwave modification of Yellow Stringybark (Eucalyptus Muelleriana) posts for impregnation with Copper-Chrom-Arsenic (CCA) preservatives
2000 - IRG/WP 00-40185
Yellow Stringybark posts with diameters ranging from 60-100 mm were microwave conditioned using a 60 kW microwave (MW) generator. A substantial improvement in heartwood penetration of preservatives and relaxation of growth stresses was indicated such that there was no split formation following drying of the posts. High preservative absorption of copper-chrome-arsenic (CCA) was achieved ranging fro...
G Torgovnikov, P Vinden
Recycling and disposal of timber treated with waterborne copper based preservatives
1993 - IRG/WP 93-50008
Recycling and disposal technologies are briefly reviewed. Details are given of chemical extraction techniques suitable for recovery of copper from timber treated with a new copper based preservative, and traditional chromium based products. Details of thermal decomposition tests according to the DIN 53436 protocol under flaming and non-flaming conditions are given. The decomposition products were ...
J A Cornfield, S Vollam, P Fardell
Further steps in the development of above ground wood preservative systems
2002 - IRG/WP 02-30300
Metal and organo-metallic wood preservative systems have provided the consumer with cost effective wood preservative systems which satisfy the performance requirements in a wide range of end uses.
With increasing environmental and legislative control, metal-free formulations have emerged as the dominant preservative systems for the protection of timber in the lower hazard classes.
In higher ha...
P Warburton, A S Hughes
A comparison of the diffusion of boron from two types of solid preservative rods into the heartwood of 3 Eucalypt pole species
2000 - IRG/WP 00-30227
The ability of boron to diffuse from polyborate and boron/fluoride rods through the heartwood of three eucalypt pole species (blackbutt, red ironbark and spotted gum) was examined. The aim was simply to determine the effects of rod type, wood species and time on the longitudinal diffusion of boron in eucalypt heartwood. Rapid diffusion of boron from polyborate or boron/fluoride preservative rods o...
P J Beutel, P D Evans
The Protection of Plywood with Benzalkonium Chloride (BAC) Wood Preservative
2002 - IRG/WP 02-40219
Alkyldimethylbenzyl ammonium chloride (benzalkonium chloride) (BAC) and alkyldimethylamine acetates were approved by the Timber Preservation Authority of New Zealand in 1978 for the protection of radiata pine that was destined for above ground, weather exposed applications. As a result of continuing failures, the use of AACs was stopped in New Zealand in the mid 1980s.
The Plywood Association of ...
J Norton
An appraisal of anti-sapstain chemicals in Queensland, Australia
1985 - IRG/WP 3331
Eleven formulations were tested in the field for effectiveness against sapstain, mould and fungi on Pinus elliottii in Queensland. The commercially used sodium pentachlorophenoxide (0.5% a.i.) and Captafol (0.2% a.i.) performed well. Busan 1009 (0.3% a.i.), Protek T (5.0% a.i.), Woodgard E.S. and E.C. (0.8% a.i.), together with sodium tetrachlorophenoxide (0.5% a.i.) offer potential as anti-sapsta...
L E Leightley
Inorganic preservative levels in soil under treated wood decks after 8 years natural exposure in Borås, Sweden
2005 - IRG/WP 05-50233
Inorganic preservative components (Cu, Cr and As) were measured to a depth of 150 mm under deck structures made with Scots pine lumber treated with several different wood preservatives and installed in Borås Sweden 8 years ago. Higher contaminant levels were observed mainly under the drip lines and in the top 50 mm of soil. Under CCA treated decks, soil arsenic concentrations increased from ba...
P A Cooper, Y T Ung, M-L Edlund, J Jermer
Modelling of copper emission fron treated wood leached according to NEN 7345 and ENV 1250.2
1996 - IRG/WP 96-20097
A series of water leaching experiments is carried out investigating pine and spruce treated and fixed using different copper-containing preservative solutions and process technologies. Water changes took place as prescribed in the Dutch standard NEN 7345 and the European test method ENV 1250.2, each of the leachates being chemically analysed for their copper content. Irrespective of the preservati...
G M F Van Eetvelde, S G L Michon, M Stevens
Tropical In-Ground Durability of Structural Sarawak Hardwoods Impregnated to High Retention with CCA-salts, CCA-oxide and FCAP after 20 Years Exposure
2005 - IRG/WP 05-30384
Statistical analysis (ANOVA) was conducted on durability (termite and decay combined) rating data collected over 20 years exposure period of over 140 species of Sarawak timbers with altogether 30,000 stake specimens, at the Forest Department’s Sibu “graveyard” stake test sites from 1977. About 20 replicated stakes were pressure-treated to refusal with 10% g/ml concentration of up to 3 CCA-sa...
Wang Choon Ling, A H H Wong