Field tests of preservative-treated radiata pine in Japan
1995 - IRG/WP 95-30083
Test stakes of radiata pine treated with various alkyl ammonium compound (AAC) formulations and with copper-chrome-arsenate (CCA) as reference preservative were installed in 3 test sites in Japan in 1981-82. When inspected in 1995, CCA-treated stakes showed less decay at all three sites than stakes treated with other formulations. Ammoniacal copper quaternary (ACQ)- treatment was only slightly les...
M E Hedley, K Tsunoda, K Suzuki
Effect of mobile fungicides on fungal pre-infection in radiata pine billets.
1999 - IRG/WP 99-30191
In New Zealand, fungal infection of logs begins directly after felling and whilst severe degrade can be prevented if antisapstain-treated within 24 hours, such short turn-around times of logs are not always practicable. However, conventional antisapstain formulations in use only provide an envelope of protection on the log surface but are unable to control pre-infections below the surface. The obj...
D R Eden, T Singh, B Kreber
Efficacy of deltamethrin associated with TCMTB and MBT for the temporary protection of timbers immediately following their sawing, in tropical countries
1987 - IRG/WP 1321
K-Othrine bois 2.5 "sciage"Ò containing 2.5 g/l of deltamethrin, 50 g/l of TCMTB and 50 g/l of MBT used at a 6% dilution controls effectively during the drying process of the freshly sawn wood, the insects attacking wet wood, the staining fungi and the rots. The protection lasts 4 months. The efficacy trials carried in 1985 and 1986 in the CTFT ("Centre Technique Forestier Tropical") of Abidjan, ...
J S Duguet, V Dartigues
Lifetime of impels in poles maintenance cycles for utility poles
2001 - IRG/WP 01-30258
In 1992-98 15.000-20.000 utility poles in Denmark received remedial treatment against decay with fused Boron-rods (IMPEL®). Economically simple, the Impel-rods are placed with the PillarTreat Method as concentrated depots in the ground-line. From there it is distributed by diffusion through the natural moisture in the wood, which ensures that it reaches moist wood in that parts of the pole where ...
A Peylo, C G Bechgaard
Acetylated solid wood. Laboratory durability test (part 2) and field trials
1995 - IRG/WP 95-40048
Degradation of acetylated beech, pine and poplar by soft rot fungi was related to strength loss in a laboratory test. No strength loss was noticed for poplar acetylated to a weight percent gain (WPG) of more than 11.2% and beech with a WPG of 12.8%. Several field trials were set up to determine the durability of acetylated products in practice. They included a field test to determine the durabilit...
E P J Beckers, H Militz, M Stevens
Wood-based composites exposed to fungal degradation: Laboratory results
2001 - IRG/WP 01-40215
Oriented strandboard (OSB) and laminated veneer lumber (LVL) are widely used as residential construction materials. The durability of OSB and LVL against biological degradation has not been studied comprehensively. The objective of this research was to investigate the durability of OSB and LVL when exposed to wood decay fungi. Fourteen brown-rot and eight white-rot wood decay fungi were screened f...
V W Yang, B Illman, L A Ferge, R J Ross
Improvement of some technological and biological properties of poplar wood by impregnation with aqueous macromolecular compounds
1992 - IRG/WP 92-3721
Poplars (Populus spp) belong to the most important tree species in afforestation programs of the Netherlands. Due to their rapid growth, the wood quality is usually low. Therefore, studies were performed to elucidate whether some technological properties and the resistance against fungal attack could be improved by impregnation with water-soluble resins. The results showed that swelling and shrink...
R D Peek, H Militz, J J Kettenis
The multi-phase pressure (MPP) process. One stage CCA treatment and accelerated fixation process
- Concepts proved by repetitive pilot plant treatments
1997 - IRG/WP 97-40079
Twenty-four charges of radiate pine roundwood or sawn timber were treated using the MPP Process and hot CCA solution. Treated timber met the CCA retention and penetration requirements of the NZ Timber Preservation Council for Hazard Classes H3 to H5. The objectives of the trials were: (1) To "stress" CCA solution by repetitive heating, treating and cooling to determine its stability in the process...
A J Pendlebury, J A Drysdale, K Nasheri, H Pearson, M E Hedley
Proposals for further co-operative studies on determining toxic values against wood-destroying basidiomycetes (1988)
1988 - IRG/WP 2316
This document sets out proposals for a further series of co-operative tests, based on previous discussions. A basic soil/block test is proposed, to be carried out by all participants using one preservative and four test fungi. Optional additional tests may be carried out using a range of other media (agar, vermiculite, rockwool) additional fungi of choice, additional preservatives of choice and pr...
A F Bravery, J K Carey
Using image analysis to rate wood stain trials
1993 - IRG/WP 93-10034
Assessing the extent of fungal discoloration on wood during laboratory trials is a subjective process which provides an opportunity for considerable variation between individual evaluators of specimens. The development of reliable systems for automatically assessing discoloration would minimize evaluator bias and permit comparisons between results from different laboratories. The use of image anal...
C M Sexton, A G Maristany,C C Brunner, J J Morrell
Test of N-tritylmorpholine in combination with synthetic pyrethroids against marine borers in tropical Australia and Panama
1991 - IRG/WP 4168
Test blocks ol Pinus sylvestris sapwood were pressure impregnated with white spirit solutions of N-tritylmorpholine, either alone or in combination with permethrin, deltamethrin or cypermethrin. They were exposed in the intertidal zone at Mourilyan Harbour, North Queensland, Australia and subtidally at either end of the Panama Canal. After 5 months' exposure at Naos Island at the Pacific ...
S M Cragg, J D Bultman
Fungal-termite associations in the natural resistance of selected eucalypt timbers
1978 - IRG/WP 173
Butt billets of Eucalyptus regnans F. Muell., Eucalyptus grandis W. Hill ex Maiden, and Eucalyptus camaldulensis Dehnh., showing no visible signs of decay, were examined for the presence of fungi in outer, middle and inner heartwood. Fungi obtained in pure culture were characterized. Eucalyptus regnans yielded Cytospora eucalypticola van der Westhuizen, Trichoderma harzianum Rifai and Penicillium ...
D B A Ruyooka
The fungal degradation of quaternary ammonium compounds in wood
1998 - IRG/WP 98-10263
This work focuses on the biodegradation of didecyldimethylammonium chloride (DDAC) by the mould fungus Gliocladium roseum within a woody matrix. Three sawdust types, distinguished by their treatment and amount of DDAC retained, were inoculated with the fungus and their DDAC loss was measured over 11 weeks. The rates of degradation varied depending on the sawdust; however, a significant loss of DDA...
J W Dubois, J N R Ruddick
Fungicidal efficacy of some dimethyldithiocarbamates, dymethylaminopropionitrile and some salts of S-substituted thioglycolic acid
1998 - IRG/WP 98-30180
Screening for fungicidal activity against Trametes versicolor and Coniophora puteana of the following compounds was performed: sodium N,N-dimethyldithiocarbamate, dimethylalkylammonium (C12-C14) N,N-dimethyldithiocarbamate, benzyldimethylalkylammonium (C12-C14) N,N-dimethyldithiocarbamate, N,N-dimethylaminopropionitrile and ammonium, copper and zinc salts of N,N-dimethyldithiocarbamoylacetic acid....
M Petric, F Pohleven, M Humar, U Kolman
Laboratory evaluation of metallic naphthenates as wood preservatives
1991 - IRG/WP 3654
Fungicidal and termiticidal efficacy of copper and zinc naphthenates was appraised according to Japanese standardized laboratory testing methods. Copper and zinc naphthenates succeeded in protecting wood from decay fungi at retentions of 0.5 and 1.0 kg/m³ as metal, respectively. [JIS A 9302 (1976)] when they were applied to vacuum/soak impregnation [JIS A 9301 (1976)]. With respect to the fungici...
K Tsunoda, M Sakurai
Effect of Scytalidium lignicola on decay resistance and strength of wood
1994 - IRG/WP 94-10061
We reported previously that in laboratory tests, pretreatment of Douglas-fir and Southern Pine blocks with Scytalidium lignicola prevented decay. In the present work, we determined 1) the ability of Scytalidium lignicola to colonize and survive in wood exposed in the field, 2) the decay resistance of blocks removed from previously treated Scytalidium lignicola wood and 3) the effect of Scytalidium...
T L Highley
A serial exposure technique for estimating probable service life of treated timber
1978 - IRG/WP 2111
This paper briefly describes part of our preliminary work aimed at developing a test procedure that culd be adopted as a standard method. A detailed version of the work has been submitted for formal publication. In both papers, the aim is to promote interest in extended laboratory testing of wood preservatives. It is believed that this work may provide the basis of a laboratory test procedure from...
J A Butcher
Soft rot - Soil burial - Tests. Influence of the water content of the soil on wood decay
1972 - IRG/WP 212
The decay of wood samples buried in the soil is influenced by various factors. Decisive are the water content, the content of organic substances, pH-value content of mineral nutritive substances etc. of the soil. For the tests, carried out by the EMPA until now, it was always started with a water content of 35%, refered to the dry weight of the EMPA-soil = 75% of its water capacity. In order to in...
O Wälchli
Preliminary results of the treatment of wood with chlorosilanes
1981 - IRG/WP 3172
It is clear from the initial data reported here that the treatment of pine sapwood with chlorosilanes under the reaction conditions employed did not significantly reduce the decay by both white rot and brown rot fungi. Only the dichlorosilane compounds showed to possess some protective action against fungal attack. Before drawing conclusions on the application of organosilicon compounds as potenti...
M Stevens
BRE Experience in monitoring decay in out-of-ground exposure trials
1995 - IRG/WP 95-20077
The outdoor field trial has always been regarded as the ultimate test of performance for assessing the effectiveness of a wood preservative. For this reason, the Building Research Establishment (BRE) has invested much effort in such trials over many years. Emphasis in early trials was on ground contact tests which were the basis both for assessing the likely performance of a preservative in protec...
J K Carey, R J Orsler
Fungal associates of Buprestis langi Mannerheim colonizing stored douglas-fir logs
1997 - IRG/WP 97-10220
Buprestid beetles are important colonizers of dead and dying conifers. The larvae of these beetles initially mine a gallery beneath the bark, then tunnel deep within the log. These beetles can cause extensive damage to wood, but it is their frequent association with internal fungal decay that causes the greatest concern. Many insects are capable of vectoring fungi that enhance their prospects for ...
C M Garcia, M Y Giron, J J Morrell
Comparison of the effects of borate, germanate and tellurate on fungal growth and wood decay
1992 - IRG/WP 92-1533
The tetra-hydroxy borate ion is known to undergo complexation with polyols and has been shown to inhibit dehydrogenase enzymes in this way. It has been previously suggested that this complexation is responsible for the inhibition of fungal growth and the protection of boron treated timber. Other ions that have the ability to complex with polyols have also been shown to inhibit dehydrogenase activi...
J D Lloyd, D J Dickinson
Hygroscopicity of decayed wood - Implications for weight loss determinations
1996 - IRG/WP 96-20085
Hygroscopicity changes were observed in red maple blocks subjected to brown rot, white rot and soft rot. Brown rot reduced hygroscopicity, soft rot increased hygroscopicity, and white rot showed only a very slight increase in hygroscopicity. The effect of these changes on weight loss tests is a slight overestimation of weight loss for brown rot and a slight underestimation for soft rot and white r...
S E Anagnost, W B Smith
Determination of the water sorption properties and preliminary results from field tests above ground of thermally modified material from industrial scale processes
2004 - IRG/WP 04-40279
In this study the differences in moisture behavior and durability above ground of heat treated wood originating from different European industrial heat treatment plants by means of the water sorption properties as well as field tests were examined. The manufacturers of heat treated material were: PLATO Hout B.V./Netherlands, Thermo Wood (Premium wood)/ Finland and Menz Holz/ Germany,
where Oil-...
C R Welzbacher; A O Rapp
Effect of cyclic change of temperature on fungal growth and mass loss
1994 - IRG/WP 94-10065
For estimating the effect of cycling change of temparature on fungal growth, four Japanese species, sugi (Cryptomeria japonica), hinoki (Chamaecyparis obtusa), akamatsu (Pinus densiflora) and buna (Fagus crenata), four fungal species, Tyromyces palustris, Gloeophyllum trabeum, Coriolus versicolor, Pycnoporus coccineus, and five temperature conditions, 10, 20, 27, 35°C and cyclic temperature (20°...
K Suzuki, K Okada